CN108215374A - Composite material, dress ornament and preparation method thereof - Google Patents
Composite material, dress ornament and preparation method thereof Download PDFInfo
- Publication number
- CN108215374A CN108215374A CN201810160473.6A CN201810160473A CN108215374A CN 108215374 A CN108215374 A CN 108215374A CN 201810160473 A CN201810160473 A CN 201810160473A CN 108215374 A CN108215374 A CN 108215374A
- Authority
- CN
- China
- Prior art keywords
- fabric
- cut
- parts
- composite material
- dotted
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides the preparation methods of a kind of composite material, dress ornament and the dress ornament, the composite material includes the first fabric for being stacked and the second fabric and is set between first fabric and the second fabric and to bonding first fabric and the dotted colloid of the second fabric, the dotted colloid including weight fraction be 90%~95% thermoplastic resin and weight fraction be 1%~3% adhesive.The weight composition of the thermoplastic resin includes:Polypropylene 88%~94%, makrolon 4%~6%, nylon 1%~3%, polyether-ether-ketone 0.5~1.5%, polyether sulfone 0.5~1.5%.Composite material and dress ornament soft comfortable provided by the invention, good air permeability, and phenomena such as can effectively avoid crimping and raw edge;And the preparation method concise in technology of dress ornament of the present invention effectively reduces material loss and live human cost.
Description
Technical field
The present invention relates to duds processing technical fields more particularly to a kind of composite material, dress ornament and preparation method thereof.
Background technology
Traditional composite material between two shell fabrics mostly by setting corresponding adhesive layer to be made, corresponding clothing products
Though making moderate progress in terms of warmth retention property, wearability, the moisture-penetrable ventilated property of aforementioned composite material and elasticity are poor, and feel is partially hard,
People's snugness of fit is influenced, limits the application of such composite material.In view of the above-mentioned problems, disclosed in the industry have using dotted viscous
Composite material made from rubber alloy and dress ornament, but corresponding composite material still has elastic deficiency, it is difficult to good support effect is played,
And the problems such as marginal portion crimping and raw edge need to be overcome.Except this, the aforementioned composite material using spot bonding glue, be limited to material and
Adhesive glue is mostly transferred on fabric by preparation process by the way of hot-pressing transfer printing, increases material loss and technique is more complicated,
The transfer film that transfer process leaves also is difficult to recycling of degrading in a short time.
In consideration of it, it is necessary to provide a kind of new composite materials, dress ornament and preparation method thereof.
Invention content
The purpose of the present invention is to provide a kind of composite material, dress ornament and preparation method thereof, soft comfortable, gas permeability is good
Well, phenomena such as and effectively avoiding crimping and raw edge;Concise in technology reduces material loss and live human cost.
For achieving the above object, the present invention provides a kind of composite material, including the first fabric for being stacked with
It second fabric and is set between first fabric and the second fabric and to bonding first fabric and the second fabric
Dotted colloid, the dotted colloid include weight fraction be 90%~95% thermoplastic resin and weight fraction be 1%~3%
Adhesive;
The weight composition of the thermoplastic resin includes:
Polypropylene 88%~94%;
Makrolon 4%~6%;
Nylon 1%~3%;
Polyether-ether-ketone 0.5~1.5%;
Polyether sulfone 0.5~1.5%.
As a further improvement on the present invention, described adhesive is mainly made of natural resin and polyurethane, and described viscous
The mass ratio of natural resin and polyurethane in mixture is 1:2~4.
As a further improvement on the present invention, the dotted colloid is arranged in uniform intervals.
As a further improvement on the present invention, a diameter of 1mm~3mm of the dotted colloid;The adjacent dotted colloid
Between spacing be 1mm~3mm.
As a further improvement on the present invention, the thermoplastic resin further include curing agent, vulcanization accelerator, anti-aging agent and
Emulsifier.
The present invention also provides a kind of dress ornament, at least part region of the dress ornament is made by foregoing composite material.
The present invention also provides a kind of preparation methods of foregoing dress ornament, mainly include:
First fabric is fixed to printing table;
Aqueous binder glue is transferred on the halftone above printing table, then frictioning is at least twice in the same direction so that
Part aqueous binder glue is intervally arranged by screen to print on the first fabric and in dotted, completes printing;
The first fabric for completing printing is dried, so that the dotted aqueous binder glue being intervally arranged is in half on the first fabric
Drying regime;
It provides by the second fabric, and the second fabric is laid in the side that the first fabric is printed with aqueous binder glue, heating pressing
Composite material is made;
Composite material is cut out to obtain the compound cut-parts with set pattern;
Corresponding dress ornament is made using compound cut-parts.
The present invention also provides the preparation methods of another foregoing dress ornament, it is characterised in that:
The first cut-parts cut out by the first fabric are provided, are fixed to printing table;
There is provided with predetermined pattern halftone, installation positioning so that the predetermined pattern of halftone with it is to be printed in first cut-parts
It is corresponding to brush region;
Aqueous binder glue is transferred on the halftone, then frictioning is at least twice in the same direction so that part aqueous binder glue
It is intervally arranged by screen to print in the first cut-parts and in dotted, completes printing;
The first cut-parts for completing printing are dried, so that the dotted aqueous binder glue being intervally arranged is in half in the first cut-parts
Drying regime;
Offer is cut out to obtain the second cut-parts by the second fabric, by the first cut-parts after drying be printed with the side of aqueous binder glue with
The commitment positions contraposition of second cut-parts is placed, and compound cut-parts are made in heating pressing;
Corresponding dress ornament is made using compound cut-parts.
As a further improvement on the present invention, the temperature setting of the baking step is 45 DEG C~55 DEG C, and drying time is
140S~160S.
As a further improvement on the present invention, described plus sintering step temperature setting is 160 DEG C~180 DEG C, pressing
Time is 12S~15S.
The beneficial effects of the invention are as follows:Composite material of the present invention, dress ornament are effectively avoided by improving the composition of dotted colloid
There is phenomena such as crimping, raw edge in the marginal portion of the composite material and dress ornament, and the composite material and dress ornament are more soft
Comfortably, good air permeability improves local support and tensile property, improves dress experience.The present invention is also by by corresponding water
Property adhesive glue be directly printed on the first fabric or the first cut-parts for being cut out by the first fabric on, technique is more succinct, effectively
Reduce material loss and live human cost.
Description of the drawings
Fig. 1 is the structure diagram of composite material of the present invention;
Fig. 2 is the schematic cross-section of composite material of the present invention
Fig. 3 is the floor map of one preferred embodiment of dress ornament of the present invention;
Fig. 4 is the floor map of another preferred embodiment of dress ornament of the present invention;
Fig. 5 is the floor map of dress ornament another embodiment of the present invention;
Fig. 6 is the main flow schematic diagram of one preferred embodiment of preparation method of dress ornament of the present invention;
Fig. 7 is the main flow schematic diagram of another preferred embodiment of preparation method of dress ornament of the present invention.
Specific embodiment
Below with reference to embodiment shown in the drawings, the present invention will be described in detail.But the embodiment is not intended to limit
The present invention, structure that those of ordinary skill in the art are made according to the embodiment, method or transformation functionally are wrapped
Containing within the scope of the present invention.
Join shown in Fig. 1 and Fig. 2, composite material 100 provided by the invention includes the first fabric 10 and second being stacked
It fabric 20 and is set between 10 and second fabric 20 of the first fabric and to bonding first fabric 10 and second
The dotted colloid 30 of fabric 20.The material of first fabric, 10 and second fabric 20 is cotton, Modal, bright and beautiful ammonia or washs ammonia, institute
It states the first fabric 10 and the second fabric 20 may be configured as identical or different and both not silicate-containing oil.The dotted colloid 30 includes
The adhesive that the thermoplastic resin and weight fraction that weight fraction is 90%~95% are 1%~3%.Wherein, the thermoplastic resin
Weight composition include:
Polypropylene 88%~94%;
Makrolon 4%~6%;
Nylon 1%~3%;
Polyether-ether-ketone 0.5~1.5%;
Polyether sulfone 0.5~1.5%.
Described adhesive is mainly made of natural resin and polyurethane, and natural resin and polyurethane in described adhesive
Mass ratio be 1:2~4.Herein, commercially available rosin, Dammar or copal can be used in the natural resin, but not limited to this.
In the present embodiment, the weight composition of the thermoplastic resin is:Polypropylene 91%, makrolon 5%, nylon 2%,
Polyether-ether-ketone 1%, polyether sulfone 1%, but it is not excluded for the presence of trace impurity;The natural resin of described adhesive uses rosin, described
The weight accounting of rosin and polyurethane is 1:3.The weight fraction of thermoplastic resin in the dotted colloid for 92%, it is described viscous
The weight fraction of mixture is 2%, and the dotted colloid further includes curing agent, vulcanization accelerator, anti-aging agent and emulsifier.
The dotted colloid 30 is arranged along the extension plane of sprawling of first fabric 10, the second fabric 20 in uniform intervals
Cloth.A diameter of 1mm~3mm of the dotted colloid 30 while taking into account aesthetics, can realize preferable bond effect.And
And since the spacing between the adjacent dotted colloid 30 is too small, then in dotted 30 preparation process of colloid, point-like glue easily occurs
Adhesion between body 30, and influence the gas permeability of the composite material 100;And the spacing between the adjacent dotted colloid 30 is too
Greatly, then the combined strength bination of the composite material 100 can be influenced, and is easier to the problems such as sealing is insecure occur.Therefore, it is adjacent described
Spacing between dotted colloid 30 is preferably arranged to 1mm~3mm.
As shown in Figures 3 to 5, the present invention also provides a kind of dress ornaments, and at least part region of the dress ornament is by described compound
Fabric is made.Wherein, Fig. 3(a), Fig. 4(a), Fig. 5(a)The front view of dress ornament in respectively each embodiment;Fig. 3(b), Fig. 4(b)、
Fig. 5(b)The front view of dress ornament in respectively each embodiment.Preferably, the composite material 100 may be disposed at the dress ornament and be hit by a bullet
Property, the higher region of support degree demand, suppression or the edge closing in position that the composite material 100 is set to the dress ornament
It puts.
Join shown in Fig. 6, the preparation method of the dress ornament mainly includes:
First fabric 10 is provided, is fixed to printing table;
Suitable halftone is provided, is installed to the top of printing table, the printing zone of the halftone and first fabric 10
Printing region is corresponding;
Deployed aqueous binder glue is transferred to above the halftone, then frictioning is at least twice in the same direction so that part
Aqueous binder glue is intervally arranged by screen to print on the first fabric and in dotted, completes printing;
The first fabric for completing printing is dried, so that the dotted aqueous binder glue being intervally arranged is in half on the first fabric
Drying regime;
It provides by the second fabric 20, and the second fabric 20 is laid in the side that the first fabric 10 is printed with aqueous binder glue, add
Composite material 100 is made in hot pressing;
Composite material 100 is cut out to obtain the compound cut-parts with set pattern;
Corresponding dress ornament is made using compound cut-parts.
Wherein, the printing zone of the halftone is formed with equally distributed mesh, and the mesh number of the mesh is set as 80~
280.During printing operation, herein using scraper made from resin material under the effect of uniform pressure frictioning three in the same direction
It is secondary, so that suitable aqueous binder glue through mesh is printed on the first fabric 10 and partial penetration is to first fabric 10
Inside, secure bond.
Preferably, the temperature setting of the baking step is 45 DEG C~55 DEG C, and drying time is 140~160S, so that
The aqueous binder glue drying on 10 surface of the first fabric is printed on to 90% or so, the aqueous binder glue surface solidification of dotted arrangement but
Sizing is not fully cured.Also, to further improve drying efficiency, first fabric 10 can be laid in corresponding drying and set
It is standby interior, and keep back and forth at the uniform velocity moving.At this point, the first taking-up in time of fabric 10 completed need to will be dried, it is fixed after bouncing back naturally
To pressing platform, and the second fabric 20 is aligned to the top for being laid in first fabric.Described plus sintering step temperature
Degree is set as 160 DEG C~180 DEG C, and pressing time is 12S~15S, and pressure is set as 6 kilograms.After completing heating pressing, aforementioned point
Shape aqueous binder glue mutually bonds 10 and second fabric 20 of the first fabric, and the dotted aqueous binder glue is also accordingly converted
Into the dotted colloid 30, the composite material 100 is made.
The composite material 100 expires width printing using full slice system, can directly cut arbitrary shape, then cutting
To compound cut-parts be applied in dress ornament, use is more flexible, also for the design of clothing products research and development bring more selections with
Thinking.
Certainly, for set dress ornament, aqueous binder glue can be also directly printed in the cut-parts cut by we.Ginseng figure
Shown in 7, the present invention also provides another preferable preparation methods of the dress ornament, mainly include:
The first cut-parts cut out by the first fabric 10 are provided, are fixed to printing table;
There is provided with predetermined pattern halftone, installation positioning so that the predetermined pattern of halftone with it is to be printed in first cut-parts
It is corresponding to brush region;
Aqueous binder glue is transferred on the halftone, then frictioning is at least twice in the same direction so that part aqueous binder glue
It is intervally arranged by screen to print in the first cut-parts and in dotted, completes printing;
The first cut-parts for completing printing are dried, so that the dotted aqueous binder glue being intervally arranged is in half in the first cut-parts
Drying regime;
Offer is cut out to obtain the second cut-parts by the second fabric 20, and the first cut-parts after drying are printed with to the side of aqueous binder glue
It aligns and places with the commitment positions of the second cut-parts, compound cut-parts are made in heating pressing;
Corresponding dress ornament is made using compound cut-parts.
Herein, it dries plus the selection of the process conditions of sintering step is similar with previous embodiment.It is by adjusting change net
The required compound cut-parts with set pattern also can be conveniently made in the predetermined pattern of version.Aqueous binder glue is directly printed on
In the first cut-parts cut, it is the second cut-parts heating pressing, the compound cut-parts can obtain corresponding through bonding sewing again
Dress ornament.
In conclusion composite material 100 of the present invention, using the dress ornament of the composite material 100 by improving dotted colloid
30 composition effectively avoids the marginal portion of the composite material 100 and dress ornament from phenomena such as crimping, raw edge occur, and causes institute
Composite material 100 and dress ornament more soft comfortable are stated, good air permeability improves local support and tensile property, improves dress
Experience, can be widely used in all kinds of daily dress ornaments and functional movement dress ornament, have higher economic value.The system of dress ornament of the present invention
Preparation Method the aqueous binder glue is directly printed on the first fabric 10 or the first cut-parts for being cut out by the first fabric 10 on,
Concise in technology, it is more environmentally-friendly, effectively reduce material loss and live human cost.
It should be appreciated that although this specification is described in terms of embodiments, but not each embodiment only includes one
A independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should will say
For bright book as an entirety, the technical solution in each embodiment may also be suitably combined to form those skilled in the art can
With the other embodiment of understanding.
Those listed above is a series of to be described in detail only for feasibility embodiment of the invention specifically
Bright, they are not to limit the scope of the invention, all equivalent implementations made without departing from skill spirit of the present invention
Or change should all be included in the protection scope of the present invention.
Claims (10)
1. a kind of composite material, including the first fabric and the second fabric being stacked, it is characterised in that:The composite material is also
Including being set between first fabric and the second fabric and to bonding first fabric and the point-like glue of the second fabric
Body, the dotted colloid include the adhesive that the thermoplastic resin that weight fraction is 90%~95% and weight fraction are 1%~3%;
The weight composition of the thermoplastic resin includes:
Polypropylene 88%~94%;
Makrolon 4%~6%;
Nylon 1%~3%;
Polyether-ether-ketone 0.5~1.5%;
Polyether sulfone 0.5~1.5%.
2. composite material according to claim 1, it is characterised in that:Described adhesive is mainly by natural resin and polyurethane
Composition, and natural resin in described adhesive and the mass ratio of polyurethane are 1:2~4.
3. composite material according to claim 1, it is characterised in that:The dotted colloid is arranged in uniform intervals.
4. composite material according to claim 1, it is characterised in that:A diameter of 1mm~3mm of the dotted colloid;Phase
Spacing between the adjacent dotted colloid is 1mm~3mm.
5. composite material according to claim 1, it is characterised in that:The thermoplastic resin further includes curing agent, vulcanization
Accelerating agent, anti-aging agent and emulsifier.
6. a kind of dress ornament, it is characterised in that:At least part region of the dress ornament is compound by claim 1-5 any one of them
Fabric is made.
7. a kind of preparation method of dress ornament as claimed in claim 6, it is characterised in that:
First fabric is fixed to printing table;
Aqueous binder glue is transferred on the halftone above printing table, then frictioning is at least twice in the same direction so that
Part aqueous binder glue is intervally arranged by screen to print on the first fabric and in dotted, completes printing;
The first fabric for completing printing is dried, so that the dotted aqueous binder glue being intervally arranged is in half on the first fabric
Drying regime;
It provides by the second fabric, and the second fabric is laid in the side that the first fabric is printed with aqueous binder glue, heating pressing
Composite material is made;
Composite material is cut out to obtain the compound cut-parts with set pattern;
Corresponding dress ornament is made using compound cut-parts.
8. a kind of preparation method of dress ornament as claimed in claim 6, it is characterised in that:
The first cut-parts cut out by the first fabric are provided, are fixed to printing table;
There is provided with predetermined pattern halftone, installation positioning so that the predetermined pattern of halftone with it is to be printed in first cut-parts
It is corresponding to brush region;
Aqueous binder glue is transferred on the halftone, then frictioning is at least twice in the same direction so that part aqueous binder glue
It is intervally arranged by screen to print in the first cut-parts and in dotted, completes printing;
The first cut-parts for completing printing are dried, so that the dotted aqueous binder glue being intervally arranged is in half in the first cut-parts
Drying regime;
Offer is cut out to obtain the second cut-parts by the second fabric, by the first cut-parts after drying be printed with the side of aqueous binder glue with
The commitment positions contraposition of second cut-parts is placed, and compound cut-parts are made in heating pressing;
Corresponding dress ornament is made using compound cut-parts.
9. preparation method according to claim 7 or 8, it is characterised in that:The temperature setting of the baking step is 45 DEG C
~55 DEG C, drying time is 140S~160S.
10. preparation method according to claim 7 or 8, it is characterised in that:The temperature setting of described plus sintering step is
160 DEG C~180 DEG C, pressing time is 12S~15S.