CN108214770A - A kind of production technology of antiseptic fire-retardation timber - Google Patents
A kind of production technology of antiseptic fire-retardation timber Download PDFInfo
- Publication number
- CN108214770A CN108214770A CN201711459704.5A CN201711459704A CN108214770A CN 108214770 A CN108214770 A CN 108214770A CN 201711459704 A CN201711459704 A CN 201711459704A CN 108214770 A CN108214770 A CN 108214770A
- Authority
- CN
- China
- Prior art keywords
- timber
- fire
- obtains
- retardation
- production technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of production technologies of antiseptic fire-retardation timber, and the key steps such as the assembling of type, the configuration of door core slurry, door core curing conservation and timber are put up including the dry pretreatment of timber steam-injection, fire-retarding preservative configuration, Wooden modifying, wooden door frame.The present invention is added to silver ion and nano silver respectively in fire-retarding preservative and door core slurry, significantly improves the antibacterial ability of timber, fundamentally slows down the rotten speed of timber;Timber is in interlayer structure, and not only sound-insulating effect is good, also as save timber, meets environmentally protective theory.
Description
Technical field
The present invention relates to a kind of timber production technology, especially a kind of production technology of antiseptic fire-retardation timber.
Background technology
Timber always is that the mankind build the important materials that household is made in house over thousand, and manufacture door and window is exactly wherein most heavy
One of application direction wanted.With the development of economy with the raising of living standards of the people, people not only pay attention to timber quality and
Practicability, while there has also been higher expectations to its whole aesthetics and safety.Existing timber production technology is simpler
It is single, and due to material, antiseptic fire-retardation performance influences its service life and whole beauty far away from metallic door.But
It is that timber will not all be eliminated, therefore people are needed to its material since it is different from the texture of metallic door in foreseeable future
Matter is improved to improve its antiseptic fire-retardation performance.
Invention content
In order to overcome the perishable incendive drawback of timber, the present invention provides a kind of production technology of antiseptic fire-retardation timber,
And the silver ion and nano silver adulterated in its structure, compared to the prior art significantly improve the anti-corrosion ability of timber.
The technical solution adopted by the present invention to solve the technical problems is:A kind of production technology of antiseptic fire-retardation timber, tool
Body step is as follows:
The timber of selection is put into dry kiln and is steamed and heat drying by step 1, and steam injection time is 10~20 points
Clock, heat drying time is 15~25 days, until dried timber water content 8~12%, saves backup;
Step 2 adds in raw material in blender in following mass fraction ratio:
Stirring 20~40 minutes, is allowed to uniformly mix, dry, and ball milling 30~90 minutes obtains fire-retarding preservative powder, protects
It deposits spare;
The fire-retarding preservative that step 2 obtains is diluted with water to mass percent solubility as 10~20% mixing by step 3
Maceration extract saves backup;
The desiccated wood that step 1 obtains is put into vacuum impregnation kettle, vacuumizes by step 4, keeps the vacuum degree in kettle
Between -0.05~-0.1MPa, maintain 30~60 minutes, then the mixed impregnant liquor that step 3 obtains is injected into vacuum impregnation
In kettle, timber is totally submerged, vacuum impregnation kettle is then restored into normal pressure, and be heated to 40~80 DEG C, is kept for 2~5 hours, put
Go out remaining mixed impregnant liquor, take out timber, save backup;
The timber that step 4 obtains is transferred in dry kiln by step 5,70~90 DEG C of dryings 3~10 days, until timber contains
Water, to get to fire retardant, anticorrosive timber, is saved backup for 5~10%;
Door-plate and Men Bian, composition wood is made in step 6, the fire retardant, anticorrosive timber thicknesser that step 5 is obtained, cutting, sanding
Door frame, it is spare;
Step 7 prepares raw material by following mass fraction:
Magnesium sulfate is dissolved in water, Adlerika is made, then by other raw materials other than foam-expelling according to the above ratio
Simultaneously uniform stirring is added in, foam is finally proportionally added into and stirs evenly, obtain a core slurry, it is spare;
Step 8, the door core slurry that step 7 obtains is injected into template cure, conserve after to get to Wood door core,
It is spare;
Step 9 combines the Wood door core that step 8 obtains and the timber frame that step 6 obtains, and decorates table
Face is to get to antiseptic fire-retardation timber.
A kind of production technology of above-mentioned antiseptic fire-retardation timber, in the step 6 foam by neopelex,
The manufacture of one or more of lauryl sodium sulfate or cetyl trimethylammonium bromide.
A kind of production technology of above-mentioned antiseptic fire-retardation timber, 10~24 hours step 8 hardening times, curing temperature
30~50 DEG C of degree.
A kind of production technology of above-mentioned antiseptic fire-retardation timber, the step 8 curing time 5~10 days, curing temperature 10
~40 DEG C, care environments relative humidity 40~90%.
The invention has the advantages that the silver ion that is added respectively in fire-retarding preservative and door core slurry of the present invention and receiving
Meter Yin, significantly improves the antibacterial ability of timber, fundamentally slows down the rotten speed of timber;Timber is in interlayer structure,
Not only sound-insulating effect is good, also as save timber, meets environmentally protective idea.
Specific embodiment
In order to illustrate more clearly of technical scheme of the present invention, below the present invention is described further, it is clear that
Ground, the embodiments described below are only the section Example of the present invention, for those of ordinary skill in the art,
Under the premise of not paying novelty labour, other embodiments are obtained according to this embodiment, belong to protection scope of the present invention
【Embodiment 1】
A kind of production technology of antiseptic fire-retardation timber, is as follows:
The timber of selection is put into dry kiln and is steamed and heat drying by step 1, and steam injection time is 10~20 points
Clock, heat drying time is 15~25 days, until dried timber water content 8~12%, saves backup;
Step 2 adds in raw material in blender in following mass fraction ratio:
Stirring 30 minutes, is allowed to uniformly mix, dry, and ball milling 80 minutes obtains fire-retarding preservative powder, saves backup;
The fire-retarding preservative that step 2 obtains is diluted with water to mass percent solubility and is mixed with dipping for 10% by step 3
Liquid saves backup;
The desiccated wood that step 1 obtains is put into vacuum impregnation kettle, vacuumizes by step 4, keeps the vacuum degree in kettle
Between -0.05~-0.1MPa, maintain 45 minutes, then the mixed impregnant liquor that step 3 obtains is injected into vacuum impregnation kettle,
Timber is totally submerged, vacuum impregnation kettle is then restored into normal pressure, and be heated to 70 DEG C, is kept for 3 hours, releases remaining mixing leaching
Stain liquid takes out timber, saves backup;
The timber that step 4 obtains is transferred in dry kiln by step 5,80 DEG C of dryings 7 days, until timber water content for 5~
10%, to get to fire retardant, anticorrosive timber, saves backup;
Door-plate and Men Bian, composition wood is made in step 6, the fire retardant, anticorrosive timber thicknesser that step 5 is obtained, cutting, sanding
Door frame, it is spare;
Step 7 prepares raw material by following mass fraction:
Magnesium sulfate is dissolved in water, Adlerika is made, then by other raw materials other than foam-expelling according to the above ratio
Simultaneously uniform stirring is added in, neopelex foam is finally proportionally added into, is uniformly mixing to obtain a core slurry, it is spare;
The door core slurry that step 7 obtains is injected into template by step 8, is cured by 30 DEG C, 24 hours, Yi Ji
It is spare to get to Wood door core after maintenance in 10 days at 80%, 35 DEG C of ambient humidity;
Step 9 combines the Wood door core that step 8 obtains and the timber frame that step 6 obtains, and decorates table
Face is to get to antiseptic fire-retardation timber.
【Embodiment 2】
A kind of production technology of antiseptic fire-retardation timber, is as follows:
The timber of selection is put into dry kiln and is steamed and heat drying by step 1, and steam injection time is 20 minutes, is added
The heated drying time is 25 days, until dried timber water content 8~12%, saves backup;
Step 2 adds in raw material in blender in following mass fraction ratio:
Stirring 40 minutes, is allowed to uniformly mix, dry, and ball milling 90 minutes obtains fire-retarding preservative powder, saves backup;
The fire-retarding preservative that step 2 obtains is diluted with water to mass percent solubility and is mixed with dipping for 20% by step 3
Liquid saves backup;
The desiccated wood that step 1 obtains is put into vacuum impregnation kettle, vacuumizes by step 4, keeps the vacuum degree in kettle
Between -0.05~-0.1MPa, maintain 60 minutes, then the mixed impregnant liquor that step 3 obtains is injected into vacuum impregnation kettle,
Timber is totally submerged, vacuum impregnation kettle is then restored into normal pressure, and be heated to 80 DEG C, is kept for 5 hours, releases remaining mixing leaching
Stain liquid takes out timber, saves backup;
The timber that step 4 obtains is transferred in dry kiln by step 5,90 DEG C of dryings 10 days, until timber water content is 5
~10%, to get to fire retardant, anticorrosive timber, saves backup;
Door-plate and Men Bian, composition wood is made in step 6, the fire retardant, anticorrosive timber thicknesser that step 5 is obtained, cutting, sanding
Door frame, it is spare;
Step 7 prepares raw material by following mass fraction:
Magnesium sulfate is dissolved in water, Adlerika is made, then by other raw materials other than foam-expelling according to the above ratio
Simultaneously uniform stirring is added in, foam is finally proportionally added into and stirs evenly, obtain a core slurry, it is spare;
The door core slurry that step 7 obtains is injected into template by step 8, is cured by 45 DEG C, 15 hours, Yi Ji
It is spare to get to Wood door core after maintenance in 8 days at 60%, 20 DEG C of ambient humidity;
Step 9 combines the Wood door core that step 8 obtains and the timber frame that step 6 obtains, and decorates table
Face is to get to antiseptic fire-retardation timber.
Claims (4)
1. a kind of production technology of antiseptic fire-retardation timber, is as follows:
The timber of selection is put into dry kiln and is steamed and heat drying by step 1, and steam injection time is 10~20 minutes, is added
The heated drying time is 15~25 days, until dried timber water content 8~12%, saves backup;
Step 2 adds in raw material in blender in following mass fraction ratio:
Stirring 20~40 minutes, is allowed to uniformly mix, dry, and ball milling 30~90 minutes obtains fire-retarding preservative powder, preserves standby
With;
The fire-retarding preservative that step 2 obtains is diluted with water to mass percent solubility and is mixed with dipping for 10~20% by step 3
Liquid saves backup;
The desiccated wood that step 1 obtains is put into vacuum impregnation kettle, vacuumizes by step 4, keep kettle in vacuum degree-
Between 0.05~-0.1MPa, maintain 30~60 minutes, then the mixed impregnant liquor that step 3 obtains is injected into vacuum impregnation kettle
In, timber is totally submerged, vacuum impregnation kettle is then restored into normal pressure, and be heated to 40~80 DEG C, is kept for 2~5 hours, is released
Remaining mixed impregnant liquor takes out timber, saves backup;
The timber that step 4 obtains is transferred in dry kiln by step 5,70~90 DEG C of dryings 3~10 days, until timber water content
For 5~10% to get to fire retardant, anticorrosive timber, save backup;
Door-plate and Men Bian is made in step 6, the fire retardant, anticorrosive timber thicknesser that step 5 is obtained, cutting, sanding, forms wooden door frame
Frame, it is spare;
Step 7 prepares raw material by following mass fraction:
Magnesium sulfate is dissolved in water, Adlerika is made, then add in other raw materials other than foam-expelling according to the above ratio
And uniform stirring, it is finally proportionally added into foam and stirs evenly, obtain a core slurry, it is spare;
Step 8, the door core slurry that step 7 obtains is injected into template cure, conserve after to get to Wood door core, it is spare;
Step 9 is combined the Wood door core that step 8 obtains and the timber frame that step 6 obtains, combination with decorative surfaces, i.e.,
Obtain antiseptic fire-retardation timber.
2. the production technology of a kind of antiseptic fire-retardation timber according to claim 1, which is characterized in that steeped in the step 6
Foam is by the manufacture of one or more of neopelex, lauryl sodium sulfate or cetyl trimethylammonium bromide.
A kind of 3. production technology of antiseptic fire-retardation timber according to claim 1, which is characterized in that the step 8 curing
10~24 hours time, 30~50 DEG C of solidification temperature.
A kind of 4. production technology of antiseptic fire-retardation timber according to claim 1, which is characterized in that the step 8 maintenance
5~10 days time, 10~40 DEG C of curing temperature, care environments relative humidity 40~90%.