CN108211027A - A kind of manufacture craft of bamboo jar and bamboo jar - Google Patents
A kind of manufacture craft of bamboo jar and bamboo jar Download PDFInfo
- Publication number
- CN108211027A CN108211027A CN201810012087.2A CN201810012087A CN108211027A CN 108211027 A CN108211027 A CN 108211027A CN 201810012087 A CN201810012087 A CN 201810012087A CN 108211027 A CN108211027 A CN 108211027A
- Authority
- CN
- China
- Prior art keywords
- tank
- tank body
- bamboo
- body blank
- mouth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to the manufacture crafts of a kind of bamboo jar and bamboo jar, one of which bamboo jar includes tank body, the tank body is process using natural bamboo, tank body includes the internal cavities for cup, the inner surface of tank body has gradient, so that along internal cavities bottom to the direction of tank mouth, the internal cavities gradually increase, and the thickness distribution of tank wall is uniform；At tank mouth, tank mouth inward flange and tank mouth outer edge are both provided with arc-shaped transition, and at tank bottom, tank bottom inward flange and tank bottom outer edge are both provided with arc-shaped transition；A kind of manufacture craft of bamboo jar provides a kind of rational scheme for bamboo jar making, so that technical process is simple, operability is strong, the bamboo jar produced is rational in infrastructure, intensity is high, service life is long, not only the inner space of bamboo jar can be made effectively to be extended, but also can be in the generation that bamboo jar is used to be effectively prevented from gas leak phenomenon when carrying out cup.
Description
Technical field
The present invention relates to pharmaceutical technology fields, and in particular to the manufacture craft of a kind of bamboo jar and bamboo jar.
Background technology
Cup has a kind of common method of long history and Chinese traditional treatment disease in China；Cup be typically with
Tank is tool, generates negative pressure using the methods of combustion fire, pumping, is allowed to be adsorbed in body surface, causes local stasis of blood, to reach promoting menstruation work
The effects that network, the promoting flow of qi and blood circulation, swelling and pain relieving, expelling wind and clearing away cold.
Common tank tool type is more in cup, there is bamboo jar, glass jar, pumping tank etc.；Wherein, bamboo jar because convenient material drawing,
Make simple, Portable durable, easy to carry, economical and practical, non-breakable, being most widely used in cup；With bamboo jar
When carrying out cup, the adsorption capacity of bamboo jar is larger, in place of can be not only used for the fleshinesses such as the shoulder back of the body, can also be applied to
The few position of the thin skins meat such as wrist, ankle, instep, the back of the hand, shoulder neck, compared with glass jar, pumping tank etc., bamboo jar has in terms of adsorption capacity
There is apparent advantage.
Chinese medicine cup is commonly called as medicinal cupping method, also known as Chinese medicine cupping therapy, refers to using Chinese medicine composition (Chinese medicine preparation) with pulling out
A kind of therapy that tank is combined；The most commonly used is bamboo jars in Chinese medicine cup, before cup, need bamboo jar being placed on Chinese medicine group
It closes and is boiled in object, so that the active ingredient of each component drug is transferred in bamboo jar in Chinese medicine composition, when carrying out cup,
Bamboo jar is pulled when acupuncture points on the human body or body surface, not only can improve local blood cycle by negative pressure, can also be by infiltration in bamboo jar
In effective ingredient work to the acupuncture point of body, channels and collaterals, and given play to the drug effect of each drug in Chinese medicine composition, strengthen
Therapeutic effect.
However, in the prior art, it is smaller for the bamboo jar internal cavities of Chinese medicine cup, it is not easy to carry out cup operation, and
Easily generate gas leakage；And the technical process for making bamboo jar is usually all very coarse, seriously affects the effect of Chinese medicine cup.
Invention content
To improve deficiency of the prior art, the technical solution adopted in the present invention is：
A kind of bamboo jar, including tank body, the tank body is process using natural bamboo, and tank body includes the inside for cup
Cavity, the inner surface of tank body have gradient so that along internal cavities bottom to the direction of tank mouth, the internal cavities gradually increase
Greatly, and the thickness distribution of tank wall is uniform；At tank mouth, tank mouth inward flange and tank mouth outer edge are both provided with arc-shaped transition, tank
Bottom, tank bottom inward flange and tank bottom outer edge are both provided with arc-shaped transition.
Preferably, the ratio of height to diameter of the tank body is 1.5~2.6, wherein, ratio of height to diameter is equal to the height of tank body than upper tank mouth
Outer diameter.
Preferably, the gradient of the tank inner surface is between 0.5 degree~1.5 degree.
Preferably, the arc-shaped transition can be arc-shaped transition or ellipse arc transition.
Preferably, when tank mouth inward flange and tank mouth outer edge use arc transition, the arc radius of tank mouth inward flange is small
In the outer peripheral arc radius of tank mouth；When tank bottom inward flange and tank bottom outer edge use arc transition, the circle of tank bottom inward flange
Arc radius is equal to the outer peripheral arc radius of tank bottom.
A kind of manufacture craft of bamboo jar, comprises the following steps that：
(1) cutting action；Using natural bamboo, bamboo is cut into tank body blank by the ratio of height to diameter of tank body；
(2) epidermis of tank body blank outer surface is removed；
(3) by tank body blank, infusion for a period of time, during infusion, makes tank body blank be immersed in always into the water
In water；
(4) tank body blank from water is taken out, makes tank body blank nature airing；
(5) polishing operation；It polishes tank body blank, to remove the burr on tank body blank, forms the tank body of bamboo jar,
Specifically include following steps：
1. the inner surface for tank body blank of polishing；Internal face polishing amount at tank body blank internal cavities bottom
It is zero, along internal cavities bottom to the direction of tank mouth, the polishing amount of internal face gradually increases, in tank
At the tank mouth of chaeta base, the polishing amount of internal face is no more than the 1/2 of tank body blank sidewall thickness；
2. the outer surface for tank body blank of polishing；In at the polishing amount and tank mouth of tank body blank outer surface bottom
The polishing amount of wall surface is identical, along tank body blank bottom to the direction of tank mouth, tank body blank outer surface
Polishing amount gradually decreases so that the inner surface after outer surface and polishing after polishing is mutually parallel；
3. polish tank body blank on tank mouth inward flange and tank mouth outer edge, with eliminate tank mouth inward flange and
The corner angle of tank mouth outer edge；
4. polish tank body blank on tank bottom inward flange and tank bottom outer edge, with eliminate tank bottom inward flange and
The corner angle of tank bottom outer edge；
(6) mould proof processing；Mould inhibitor is added to the water uniformly mixed, and tank body is soaked for a period of time into the water；
(7) tank body Jing Guo mould proof processing is taken out, makes tank body nature airing.
Preferably, the time of infusion tank body blank described in step (3) is not less than 24 hours.
Preferably, the time of infusion tank body blank described in step (3) is 48 hours.
Preferably, in step (5), at the tank mouth of the tank body blank, the polishing amount of the internal face is tank body blank
The 1/8~3/8 of sidewall thickness.
Preferably, in step (5), at the tank mouth of the tank body blank, the polishing amount of the internal face is tank body blank
The 1/4 of sidewall thickness.
Preferably, in step (5), outside the tank mouth inward flange and tank mouth outer edge and/or tank bottom inward flange and tank bottom
Edge is polished into arc-shaped transition.
Preferably, the arc-shaped transition can be arc-shaped transition or ellipse arc transition；
Preferably, when tank mouth inward flange and tank mouth outer edge use arc transition, the arc radius of tank mouth inward flange is small
In the outer peripheral arc radius of tank mouth；When tank bottom inward flange and tank bottom outer edge use arc transition, the circle of tank bottom inward flange
Arc radius is equal to the outer peripheral arc radius of tank bottom.
Preferably, the soaking time of tank body described in step (6) is not less than 48 hours.
Preferably, the soaking time of tank body described in step (6) is 72 hours.
Compared with prior art, using the manufacture craft of a kind of bamboo jar provided by the invention and bamboo jar, have beneficial below
Effect：
1st, in this bamboo jar, the inner surface setting of tank body is gradient, can effectively extend the internal cavities of tank body, especially
At tank mouth, the internal cavities of tank body is not only caused to generate the negative pressure of bigger, but also convenient for pulling convenient for operating alcohol sponge during cup
The skin area of bigger, so as to be conducive to carry out Chinese medicine cup.
2nd, at the tank mouth of this bamboo jar, after tank mouth inward flange and tank mouth outer edge are respectively provided with arc-shaped transition, side wall at tank mouth
Thinner, when carrying out cup, the out-of-roundness of tank mouth pulls bamboo jar influence smaller on the skin, so that this bamboo jar
More difficult generation gas leak phenomenon.
3rd, bamboo jar manufacture craft provided by the invention is processed into Chinese medicine bamboo jar, technique mistake using the natural old bamboo in ten times
Journey is simple, and operability is strong, and the bamboo jar produced is rational in infrastructure, and intensity is high, and service life is long.
It 4th, can be easily and efficiently according to ratio of height to diameter parameter, technical staff in step (1) in the manufacture craft of this bamboo jar
The reasonable altitudes of tank body are calculated, consequently facilitating being cut into the tank body blank of different dimensional parameters.
5th, it in the manufacture craft of this bamboo jar, needs to carry out infusion to tank body blank in step (3), can both improve different dry
Water content in dry degree tank body blank so that avoid cracking or splitting during polishing due to tank body blank too dry
The phenomenon that seam is scrapped；It again can be with chemical substance contained in itself moisture in thinning tank chaeta base, in order to avoid influence to boil bamboo
The drug effect of the Chinese medicine of tank.
6th, in the manufacture craft of this bamboo jar, the inner surface of polishing tank body blank in step (5) so that along internal cavities bottom
Onto the direction of tank mouth, the internal cavities of tank body blank gradually increase, not only convenient for operating alcohol sponge during cup, but also can be effective
Ground extends the inner space of tank body so that the spatial content bigger of tank body；In addition, by estimating internal face at tank body blank tank mouth
Polishing amount, it is possible to estimate the gradient of tank inner surface, complicated natural measurement of tilt process can be effectively prevented from, quickening is beaten
The speed of mill.
7th, in the manufacture craft of this bamboo jar, the outer surface of polishing tank body blank in step (5) so that the appearance after polishing
Face is mutually parallel with the inner surface after polishing, so that along in tank base to the direction of tank mouth, tank body blank sidewall
Thickness distribution is uniform, and the distribution of weight of tank body blank is uniform, is conducive to bamboo jar when progress cup stands upside down placement, has higher
Stability, avoid the occurrence of that tank body is top-heavy, and from the situation about dropping down pulled on the skin.
8th, in the manufacture craft of this bamboo jar, tank mouth inward flange and tank mouth outer edge, can cause at tank mouth in step (5),
The thickness of tank wall gradually decreases, and during advantageously reducing cup, tank mouth gas leakage happens.
9th, in the manufacture craft of this bamboo jar, mould proof processing has been carried out to tank body in step (6), can effectively kill tank body
On mould or the mycostatic growth of suppression, so as to the long-term preservation of bamboo jar.
Description of the drawings
It in order to illustrate the technical solution of the embodiments of the present invention more clearly, below will be to needed in the embodiment attached
Figure is briefly described, it should be understood that the following drawings illustrates only certain embodiments of the present invention, therefore is not construed as pair
The restriction of range, for those of ordinary skill in the art, without creative efforts, can also be according to this
A little attached drawings obtain other relevant attached drawings.
Fig. 1 is the schematic three dimensional views of a kind of bamboo jar provided in the embodiment of the present invention 1.
Fig. 2 is the vertical view of a kind of bamboo jar provided in the embodiment of the present invention 1.
Fig. 3 is the front view of a kind of bamboo jar provided in the embodiment of the present invention 1.
Fig. 4 is the A-A direction views of Fig. 3.
Fig. 5 is the bottom view of a kind of bamboo jar provided in the embodiment of the present invention 1.
Fig. 6 is the signal of tank body blank being cut into the embodiment of the present invention 3 in the manufacture craft of a kind of bamboo jar that provides
Figure.
Fig. 7 is the main view of tank body blank being cut into the embodiment of the present invention 3 in the manufacture craft of a kind of bamboo jar that provides
Figure.
Fig. 8 is the B-B direction view of Fig. 7.
Fig. 9 is in the manufacture craft of a kind of bamboo jar provided in the embodiment of the present invention 3, needs table in the tank body blank polished
The schematic diagram in face.
Figure 10 is in the manufacture craft of a kind of bamboo jar provided in the embodiment of the present invention 3, and tank body blank inner surface has been polished
Into schematic diagram later.
Figure 11 is in the manufacture craft of a kind of bamboo jar provided in the embodiment of the present invention 3, is needed outside the tank body blank polished
The schematic diagram on surface.
Figure 12 is in the manufacture craft of a kind of bamboo jar provided in the embodiment of the present invention 3, and tank body blank outer surface has been polished
Into schematic diagram later.
Figure 13 is in the manufacture craft of a kind of bamboo jar provided in the embodiment of the present invention 3, outside tank mouth inward flange and tank mouth
Schematic diagram after edge polishing completion.
Figure 14 is in the manufacture craft of a kind of bamboo jar provided in the embodiment of the present invention 3, outside tank bottom inward flange and tank bottom
Schematic diagram after edge polishing completion.
Figure 15 is in the embodiment of the present invention 3 in the manufacture craft of a kind of bamboo jar that provides, bamboo jar complete after knot
Structure schematic diagram.
Description of symbols in figure
Tank body 101, internal cavities 102, inner surface 103, side wall 104, outer surface 105, tank mouth inward flange 106, outside tank mouth
Edge 107, tank bottom inward flange 108, tank bottom outer edge 109, ring 110, internal cavities bottom 111, tank body blank 112.
Specific embodiment
Below in conjunction with attached drawing in the embodiment of the present invention, the technical solution in the embodiment of the present invention is carried out clear, complete
Ground describes, it is clear that described embodiment is only part of the embodiment of the present invention, instead of all the embodiments.Usually exist
The component of the embodiment of the present invention described and illustrated in attached drawing can be configured to arrange and design with a variety of different herein.Cause
This, the detailed description of the embodiment of the present invention to providing in the accompanying drawings is not intended to limit claimed invention below
Range, but it is merely representative of the selected embodiment of the present invention.Based on the embodiment of the present invention, those skilled in the art are not doing
Go out all other embodiments obtained under the premise of creative work, shall fall within the protection scope of the present invention.
Embodiment 1
It please refers to Fig.1, Fig. 2, Fig. 3, Fig. 4 and Fig. 5, a kind of bamboo jar is provided in the present embodiment, including tank body 101, tank
Body 101 is process using natural bamboo, in preferred scheme, natural bamboo using 10 years bamboo ages or more old bamboo；Tank
Body 101 includes the internal cavities 102 for cup, and the inner surface 103 of tank body 101 has gradient so that along internal cavities bottom
111 on the direction of tank mouth, and internal cavities 102 gradually increase, and the thickness distribution of 101 side wall 104 of tank body is uniform, so that
The distribution of weight of tank body 101 is uniform, when using bamboo jar, is conducive to bamboo jar and smoothly realizes that vertical placement and handstand are placed；
At the tank mouth of tank body 101, tank mouth inward flange 106 and tank mouth outer edge 107 are both provided with arc-shaped transition, as shown in figures 2 or 4,
So that the structure of tank body 101 is more continuous, it is rounder and more smooth；At the tank bottom of tank body 101, outside tank bottom inward flange 108 and tank bottom
Edge 109 is both provided with arc-shaped transition, not only convenient for the vertical placement of tank body 101, but also tank body 101 can be made rounder and more smooth, specific such as Fig. 4
Or shown in Fig. 5.
In this bamboo jar, the internal cavities 102 of tank body 101 are larger, especially at tank mouth, both convenient for operating alcohol during cup
Sponge causes the internal cavities 102 of tank body 101 to generate the negative pressure of bigger, and the skin area convenient for pulling bigger；At tank mouth, tank
After mouth inward flange 106 and tank mouth outer edge 107 are respectively provided with arc-shaped transition, side wall 104 is thinner at tank mouth, is carrying out cup
When, the out-of-roundness (tank mouth is usually standard round, as shown in Figure 1) of tank mouth pulls bamboo jar influence smaller on the skin, so as to
Cause the more difficult generation gas leak phenomenon of this bamboo jar.
In the scheme of optimization, the ratio of height to diameter of tank body 101 can be 1.5~2.6, wherein, ratio of height to diameter is equal to the height of tank body 101
Spend the outer diameter than upper tank mouth；Since tank body 101 is made with natural bamboo, and usually there are thicknesses to differ for natural bamboo
Situation, therefore using the tank body 101 that natural bamboo is made there is also situation of different sizes, this programme uses ratio of height to diameter pair
The dimensional parameters of tank body 101 are measured, and can represent the height and outer diameter of tank body 101 simultaneously, the ratio of height to diameter of tank body 101 can
To be set as 1.5~2.6, according to the outer diameter of natural bamboo, different ratio of height to diameter parameters is selected, it is different that height can be produced
Tank body 101, and according to the various outer diameter of different natural bamboos, different ratio of height to diameter parameters is selected, outer diameter and height can be produced
The tank body 101 of the different various specifications of degree, to meet the needs of different occasions.
In the scheme of optimization, the gradient of 101 inner surface 103 of tank body is between 0.5 degree~1.5 degree；As shown in figure 4, figure
Gradients of the middle angle a for 101 inner surface 103 of tank body, the presence of gradient a so that the direction of tank mouth is arrived along internal cavities bottom 111
On, internal cavities 102 gradually increase, and are conducive to bamboo jar and carry out cup.
In the scheme of optimization, arc-shaped transition can be arc-shaped transition or ellipse arc transition；In the present embodiment, arc
Transition is using arc-shaped transition, as shown in Figure 4.
In further prioritization scheme, when tank mouth inward flange 106 and the use arc transition of tank mouth outer edge 107, tank
The arc radius of mouth inward flange 106 is less than the arc radius of tank mouth outer edge 107, so as to be conducive to the thickness of side wall 104 at tank mouth
Thinner, more difficult generation gas leakage is spent, as shown in Figure 4；When tank bottom inward flange 108 and tank bottom outer edge 109 use arc transition
When, the arc radius of tank bottom inward flange 108 is equal to the arc radius of tank bottom outer edge 109；So that tank body 101 is rounder and more smooth,
It is more conducive to the smoothly vertical placement of tank body 101.
Embodiment 2
As described in example 1 above, it is typically what is be process using natural bamboo as raw material for the bamboo jar of cup；It is and normal
Size, the height equidimension parameter of bamboo jar be different, and in real life, generally use ratio of height to diameter characterizes bamboo jar
Dimensional parameters, wherein, height and the mean inside diameter of bamboo jar or the ratio of mean outside diameter of the ratio of height to diameter for bamboo jar.
A kind of manufacture craft of bamboo jar is provided in the present embodiment, is comprised the following steps that：
Step (1) cutting action；Using natural bamboo, bamboo is cut into tank body blank by the ratio of height to diameter of tank body 101
112；Natural bamboo usually there is a situation where not of uniform size, and the dimensional parameters of common bamboo jar are also different during cup
's；Technical staff can be according to the internal diameter or outer diameter of different bamboos, with reference to the ratio of height to diameter parameter of common tank body 101 (or bamboo jar)
(in the present embodiment, the ratio of height to diameter of tank body 101 is set as between 1.5~2.6, wherein, ratio of height to diameter is equal to the height of tank body 101
Than the outer diameter of upper tank mouth), calculate rational 101 height of tank body；Technical staff can using the height that calculates as reference, so as to
Accurately bamboo is cut so that can be cut into a tank body blank 112 at each ring 110；It not only improves and cuts
The tank body blank 112 of different dimensional parameters is cut out, and is advantageously implemented accurate cutting, reduces subsequent polishing amount.
In the present embodiment, preferentially bamboo is cut using cutting machine.
In preferably scheme, natural bamboo is preferentially using the natural old bamboo of 10 years or more, time more long bamboo,
Bamboo is older, and the various fibr tissues in bamboo are finer and close, so that bamboo is harder, solid, bamboo is processed into bamboo
After tank, the usage time of bamboo jar can be effectively improved, extends the service life of bamboo jar.
Step (2) removes the epidermis of 112 outer surface 105 of tank body blank；One layer of dark green epidermis outside bamboo leads to
Bamboo blueness is commonly referred to as, bamboo blueness can be used as medicine, have effects that reduce internal heat refrigerant；However it was processed further in tank body blank 112
Cheng Zhong, the epidermis of 112 outer surface 105 of tank body blank can bring the use of subsequent polishing operation and tank body 101 very greatly
Inconvenience, so after 112 excision forming of tank body blank, the epidermis of 112 outer surface 105 of tank body blank need to be removed, commonly use
Method be to be cut with knife.
By tank body blank 112, infusion for a period of time, during infusion, makes tank body blank 112 to step (3) into the water
It impregnates always in water；It is formed since tank body blank 112 is cut using natural bamboo, there are larger for the degree of drying of bamboo
Difference, therefore before the technique for carrying out latter step needs tank body blank 112 being put into clear water infusion for a period of time；In tank body
During the infusion of blank 112, the tank body blank 112 that degree of drying on the one hand can be caused different adequately absorbs moisture, from
And so that the water content between tank body blank 112 approaches or quite, the degree of drying be conducive between each tank body blank 112 tends to
It is identical, consequently facilitating subsequent polishing operation, can be effectively prevented from due to tank body 112 too dry of blank during polishing
The phenomenon that cracked or crack；On the other hand, tank body blank 112 is during infusion, the water of itself in tank body blank 112
Branch adequately mixes and exchanges with extraneous clear water so that the various chemical substances in tank body blank 112 in itself moisture obtain
To dilution, used so as to the later stage of tank body 101, because this tank body 101 is the Chinese medicine tank body 101 for Chinese medicine cup, in tank body
It before 101 uses, needs tank body 101 and Chinese medicine carrying out infusion, so that middle the effective elements of the medicine is penetrated into tank body 101, be formed
Chinese medicine tank body 101 only reduces chemical substance contained in itself moisture in tank body blank 112, can just be effectively prevented from as possible
These chemical substances are to the drug effect of Chinese medicine；In addition, infusion tank body blank 112 tank body 101 can also be played sterilization, disinfection
Effect, while to a certain extent, moreover it is possible to the effect of pre- anti-mildew, is played to tank body 101.
In the scheme of optimization, the time of infusion tank body blank 112 is not less than 24 hours；According in actual use
A host of facts and experience have shown that, when being less than 24 hours the time of infusion tank body blank 112, the water content in tank body blank 112
Saturation state is not achieved, effect is poor；When the time of infusion tank body blank 112 being more than 24 hours, the water in tank body blank 112
Content progressively reaches saturation state, and chemical substance contained in itself moisture in tank body blank 112 has arrived effective dilution,
With the increase of infusion time, water can gradually be evaporated and be lost, at this point it is possible to by adding water that tank body blank 112 is made to impregnate always
In water, after water is added, chemical substance contained in itself moisture can further be diluted in tank body blank 112, be led to
Often when the time of infusion tank body blank 112 reaching 48 hours, the chemical substance contained by itself the interior moisture of tank body blank 112 is
Through very rare, large effect will not be generated to subsequent technique, therefore in the scheme advanced optimized, infusion tank body blank
112 time can be 48 hours.
Step (4) takes out tank body blank 112 from water, makes the natural airing of tank body blank 112；112 infusion of tank body blank
After completion, preferentially tank body blank 112 is dried using natural air drying, i.e., the surface of tank body blank 112 is without apparent water stain
；The techniques such as drying, drying are not used, on the one hand drying or drying technique are likely to result in the water in tank body blank 112
Divide a large amount of losses, be unfavorable for subsequent polishing operation, another aspect or drying or drying technique is also possible to that tank body blank can be caused
112 damage.
Step (5) polishing operation；It polishes tank body blank 112, to remove the burr on tank body blank 112, is formed
The tank body 101 of bamboo jar, specifically includes following steps：
1. the inner surface 103 for tank body blank 112 of polishing；Internal face polishing at 112 internal cavities bottom 111 of tank body blank
Amount is zero, and along internal cavities bottom 111 to the direction of tank mouth, the polishing amount of internal face gradually increases, in tank body blank 112
At tank mouth, the polishing amount of internal face is no more than the 1/2 of 112 side wall of tank body blank, 104 thickness.So that along internal cavities bottom
111 on the direction of tank mouth, and the internal cavities 102 of tank body blank 112 gradually increase, and the inner surface 103 of tank body blank 112 has
Larger gradient；On the one hand, it is carved since the cotton ball soaked in alcohol during cup, lighted needs to stretch into revolving fragment in bamboo jar, with
The oxygen in internal cavities 102 is consumed, then take out cotton ball soaked in alcohol rapidly and bamboo jar is buckled in the specific channels and collaterals of human body and acupuncture points on the human body
On, improve local blood cycle using negative pressure, so as to fulfill the purpose of cup；In this process, if bamboo jar tank body 101
It is larger at tank mouth, convenient for cotton ball soaked in alcohol rotation with quickly removing；It is on the other hand, if larger at the tank mouth of bamboo jar tank body 101,
The internal cavities 102 of tank body 101 can effectively be expanded so that the internal cavities 102 of tank body 101 can accommodate more skies
Gas, consequently facilitating generating the negative pressure of bigger in cup so that the effect of cup is more preferable；In the art, the tank body hair of bamboo jar
Base 112 is formed using natural bamboo cutting, due in the short transverse along bamboo, bamboo internal diameter or outer diameter variation compared with
It is small, and the limited height of each tank body blank 112 so that the internal cavities 102 of tank body blank 112 are usually oblique with very little
It spends and (is less than 0.5 degree) or substantially without gradient (internal cavities 102 are cylindrical)；Based on the considerations of this three aspect, Ke Yi
In the process of tank body blank 112 of polishing, the inner surface 103 for tank body blank 112 of polishing first so that along 101 bottom of tank body to tank
On the direction of mouth, the internal cavities 102 of tank body blank 112 gradually increase, so that the inner surface 103 of tank body blank 112 is oblique
Degree can be more than 0.5 degree, and the internal cavities 102 of tank body blank 112 are effectively extended, and the tank mouth of tank body blank 112
The cross-sectional area at place is more than the cross-sectional area of 112 bottom of tank body blank.
In the scheme of optimization, at the tank mouth of tank body blank 112, the polishing amount of internal face is 112 side wall of tank body blank
The 1/8~3/8 of 104 thickness；It, both can be at this point, the gradient of 101 inner surface 103 of tank body is generally between 0.5 degree~1.5 degree
Expand the internal cavities 102 of tank body 101, and the polishing amount of internal face can be reduced, thus will not be to the rigidity of tank body blank 112
Cause too much influence；In addition, during polishing, the gradient of 101 inner surface 103 of tank body is not needed to specifically measure, only
It need to be by estimating the polishing amount of internal face at 112 tank mouth of tank body blank, it is possible to the gradient of 101 inner surface 103 of tank body is estimated,
For example, when the polishing amount of internal face is the 1/8~3/8 of 112 side wall of tank body blank, 104 thickness at 112 tank mouth of tank body blank, tank
The gradient of 101 inner surface 103 of body is usually just between 0.5 degree~1.5 degree；So as to greatly simplify bruting process.
2. the outer surface 105 for tank body blank 112 of polishing；At the polishing amount and tank mouth of 112 outer surface of tank body blank, 105 bottom
The polishing amount of internal face is identical, along tank body blank 112 bottom to the direction of tank mouth, the polishing of 112 outer surface 105 of tank body blank
Amount gradually decreases so that the outer surface 105 after polishing is mutually parallel with the inner surface 103 after polishing.On the one hand, previous step
After polishing is completed, since the inner surface 103 of tank body blank 112 has larger gradient so that the side wall of tank body blank 112
104 is in uneven thickness, i.e., along tank body 101 bottom to the direction of tank mouth, the thickness of 112 side wall 104 of tank body blank gradually decreases,
This causes the lighter in weight at 112 tank mouth of tank body blank, and the heavier-weight at 112 tank bottom of tank body blank is arrived along 101 bottom of tank body
On the direction of tank mouth, the distribution of weight of tank body blank 112 is uneven, so as to be not easy to cup process, especially when bamboo jar pulls
When on the skin, the tank body 101 of bamboo jar is in handstand state, so as to the phenomenon that top-heavy occur, pulls tank on the skin
Body 101 is easy to drop down from skin, makes troubles for cup；For this purpose, in this step, need tank body blank of polishing
112 outer surface 105 so that the outer surface 105 of tank body blank 112 is mutually parallel with the inner surface 103 of tank body blank 112, and
With identical gradient, at this point, 104 thickness distribution of side wall of tank body blank 112 is than more uniform.On the other hand, polishing tank body hair
The outer surface 105 of base 112 advantageously reduces the roughness of the outer surface 105 of tank body blank 112 so that outside tank body blank 112
Surface 105 is more smooth, convenient for holding bamboo jar during cup.
3. the tank mouth inward flange 106 and tank mouth outer edge 107 polished on tank body blank 112, to eliminate tank mouth inward flange 106
And the corner angle at tank mouth outer edge 107.Tank body blank 112 is cut down from natural bamboo, the notch of tank body blank 112
Place can generate corner angle and many burrs, at the tank mouth inward flange 106 and tank mouth outer edge 107 especially on tank body blank 112,
Burr is more, easily hurts hand or skin in use, therefore need will be at tank mouth inward flange 106 and tank mouth outer edge 107
Corner angle polish off；
In the scheme of optimization, can polish tank mouth inward flange 106 and tank mouth outer edge 107 camber, using arc
The burr and corner angle on tank body blank 112 are eliminated in transition；And after arc-shaped transition polishing is completed, the thickness of side wall 104 at tank mouth
Thinner, when carrying out cup, the air-tightness that the out-of-roundness of tank mouth pulls bamboo jar on the skin influences smaller, so as to be conducive to drop
During low cup, the generation of tank mouth gas leak phenomenon.
In further prioritization scheme, arc-shaped transition can be arc-shaped transition or ellipse arc transition；It not only can be with
The burr at tank mouth inward flange 106 and tank mouth outer edge 107 is eliminated, it is also possible that tank mouth inward flange 106 and tank mouth outer edge
107 have arc-shaped transition, so as to effectively eliminate the corner angle at tank mouth inward flange 106 and tank mouth outer edge 107 so that bamboo
When tank is pulled on the skin, skin is more comfortable to the sense of touch of bamboo jar.
In further prioritization scheme, during using arc-shaped transition, the arc radius of tank mouth inward flange 106 is less than tank
The arc radius of mouth outer edge 107, so as to more beautiful, practical.
4. the tank bottom inward flange 108 and tank bottom outer edge 109 polished on tank body blank 112, to eliminate tank bottom inward flange 108
And the corner angle at tank bottom outer edge 109.It is similar with previous step, after tank body 112 excision forming of blank, tank body blank 112
Many burrs are equally existed at tank bottom inward flange 108 and tank bottom outer edge 109, both easily hurt hand or skin in use
Skin, and it is not easy to the placement of bamboo jar tank body 101；
In the scheme of optimization, can polish tank bottom inward flange 108 and tank bottom outer edge 109 camber, using arc
The burr and corner angle on tank body blank 112 are eliminated in transition；
In further prioritization scheme, arc-shaped transition can be arc-shaped transition or ellipse arc transition；It not only can be with
The corner angle and burr at tank bottom inward flange 108 and tank bottom outer edge 109 are eliminated, it is also possible that tank bottom inward flange 108 and tank bottom
Outer edge 109 has arc-shaped transition so that entire bamboo jar tank body 101 is rounder and more smooth.
In further prioritization scheme, during using arc-shaped transition, the arc radius of tank bottom inward flange 108 is equal to tank
The arc radius of bottom outer edge 109, so as to more beautiful, practical.
At this point, the polishing of tank body blank 112 finishes, the tank body blank 112 after polishing, the internal cavities 102 of tank body 101
To effectively extending, 101 distribution of weight of tank body is uniform, and 101 surface of tank body is round and smooth, does not have any corner angle, not only beautiful, but also convenient for making
With.
In the present embodiment, it is preferentially polished using sander tank body blank 112, since need to polish is tank body
The endoporus sander of profession may be used, such as staight shank sander in 101 internal cavities 102.
Step (6) mould proof processing；Mould inhibitor is added to the water uniformly mixed, and tank body 101 is impregnated one section into the water
Time.After above-mentioned processing step (1) to step (5), contained moisture is more in bamboo jar tank body 101, does not make for a long time
During with bamboo jar, tank body 101 may mould growth, so tank body 101 polishing molding after, it is necessary to tank body 101 is carried out
Mould proof processing, common means are：Mould inhibitor is added to the water it is uniformly mixed, and when tank body 101 to be impregnated to one section into the water
Between, during immersion so that mould inhibitor enters in tank body 101 or is attached to 101 surface of tank body, kills on tank body 101
Mould or the mycostatic growth of suppression, so as to effectively act as mould proof effect.
In the present embodiment, mould inhibitor is preferentially using the mould inhibitor for being used for food, fruit, cosmetics, this kind of mould inhibitor pair
Person poultry harmless, and the term of validity is long, has broad spectrum activity to mould.
In the scheme of optimization, the soaking time of tank body 101 is not less than 48 hours.Only when the soaking time of tank body 101
When enough, can be only achieved mould proof effect, according to a host of facts in actual use and experience have shown that, when tank body 101
When soaking time is not less than 48 hours, the anti-mold effect of tank body 101 is preferable, and mould inhibitor is longer to the effective protection phase of tank body 101；
In further prioritization scheme, the soaking time of tank body 101 is 72 hours；At this point, the anti-mold effect of tank body 101
Optimum state can be reached.
Step (7) takes out the tank body 101 Jing Guo mould proof processing, makes the natural airing of tank body 101；This step and step (4) class
Seemingly, after tank body 101 impregnates completion, preferentially tank body 101 is dried using natural air drying；Bamboo jar tank body 101 after airing
It can be used for boiling Chinese medicine bamboo jar, carry out Chinese medicine cup.
In the art, water used can be tap water or pure water or mineral water etc..
Embodiment 3
In the present embodiment, the bamboo in 10 year time is employed, is processed into bamboo jar, a certain section thick bamboo tube is outer on bamboo
Diameter is 35mm, and 104 thickness of side wall of bamboo is 3mm；When this bamboo is processed into bamboo jar, comprise the following steps that：
Step (1) cutting action；Using natural bamboo, bamboo is cut into tank body blank by the ratio of height to diameter of tank body 101
112；According to the dimensional parameters of selected bamboo, with reference to the ratio of height to diameter parameter of common tank body 101, in the prior art, common tank body
Between 101 ratio of height to diameter is 1.5~2.6, wherein, ratio of height to diameter is equal to the height of tank body 101 than the outer diameter of upper tank mouth, can calculate
Go out the reasonable altitudes of tank body 101, specifically, in the present embodiment, the ratio of height to diameter of setting tank body 101 is 1.5, can be calculated
The height of tank body 101 is 1.5 × 35=52.5mm, and in common bamboo jar, the distance of ring 110 to 101 bottom of tank body is usually 5
~10mm, in the present embodiment, the distance of setting ring 110 to 101 bottom of tank body is usually 5mm, and technical staff can basis
These data cut bamboo using cutting machine, to be cut into tank body blank 112 from bamboo, tank body blank 112
Schematic diagram is as shown in Fig. 6, Fig. 7 and Fig. 8.
It is appreciated that set remaining ratio of height to diameter parameter that also there is identical effect, such as the ratio of height to diameter of setting tank body 101
It is 2.0, then the height of tank body 101 is 2.0 × 35=70.0mm；It is also understood that selecting the bamboo of remaining diameter also has
Identical effect, such as the outer diameter of bamboo is 60mm, the ratio of height to diameter of setting tank body 101 is 1.7, then the height of tank body 101 is 1.7
Which is not described herein again by × 60=102mm ... ....
Step (2) removes the epidermis of 112 outer surface 105 of tank body blank.
Step (3) is by infusion 48 hours into the water of tank body blank 112, during infusion, by the way that water is added to make tank body
Blank 112 impregnates in water always.
Step (4) takes out tank body blank 112 from water, makes the natural airing of tank body blank 112.
Step (5) polishing operation；It polishes tank body blank 112, to remove the hair of the incision on tank body blank 112
Thorn makes tank body blank 112 become the tank body 101 of bamboo jar, specifically includes following steps：
1. the inner surface 103 for tank body blank 112 of polishing, the internal face polishing at 112 internal cavities bottom 111 of tank body blank
Amount is zero, and along internal cavities bottom 111 to the direction of tank mouth, the polishing amount of internal face gradually increases, in tank body blank 112
At tank mouth, the polishing amount of internal face is no more than the 1/2 of 112 side wall of tank body blank, 104 thickness；So that along internal cavities bottom
111 on the direction of tank mouth, and the internal cavities 102 of tank body blank 112 gradually increase, and the inner surface 103 of tank body blank 112 has
Larger gradient.
In the scheme of optimization, at the tank mouth of tank body blank 112, the polishing amount of internal face is 112 side wall of tank body blank
The 1/8~3/8 of 104 thickness.
In the present embodiment, the internal face polishing amount at 112 internal cavities bottom 111 of tank body blank is zero, along internal sky
In bottom of chamber portion 111 to the direction of tank mouth, the polishing amount of internal face gradually increases, at the tank mouth of tank body blank 112, internal face
Polishing amount is the 1/4 of 112 side wall of tank body blank, 104 thickness；As shown in figure 9, the dotted line in figure is exactly the tank body hair that will be polished
The schematic lines of the inner surface 103 of base 112 as shown in Figure 10, the signal after the inner surface 103 of tank body blank 112 are completed for polishing
Scheme, as it can be seen that along internal cavities bottom 111 to the direction of tank mouth in figure, the thickness of tank body blank 112 gradually decreases, and tank body
The internal cavities 102 of blank 112 are gradual increase, and the inner surface 103 of tank body blank 112 has larger gradient, both just
In the operation of cotton ball soaked in alcohol, and the internal cavities 102 convenient for expanding tank body 101 so that the internal cavities 102 of tank body 101 can be with
More air are accommodated, consequently facilitating generating the negative pressure of bigger in cup so that the effect of cup is more preferable.
2. the outer surface 105 for tank body blank 112 of polishing；At the polishing amount and tank mouth of 112 outer surface of tank body blank, 105 bottom
The polishing amount of internal face is identical, along tank body blank 112 bottom to the direction of tank mouth, the polishing of 112 outer surface 105 of tank body blank
Amount gradually decreases so that the outer surface 105 after polishing is mutually parallel with the inner surface 103 after polishing.Therefore in the present embodiment
In, the polishing amount of 112 outer surface of tank body blank, 105 bottom is identical with the polishing amount of internal face at tank mouth, is tank body blank 112
The 1/4 of 104 thickness of side wall, as shown in figure 11, the dotted line in figure are exactly showing for 112 outer surface 105 of tank body blank that will polish
It anticipates line, as shown in figure 12, completes the schematic diagram behind the outer surface 105 of tank body blank 112 for polishing, as it can be seen that along tank body 101 in figure
On bottom to the direction of tank mouth, the thickness distribution of 112 side wall 104 of tank body blank is than more uniform, and distribution of weight is also than more uniform；No
Only so that 112 shape of tank body blank is more beautiful, and the use for bamboo jar of being more convenient for.
3. the tank mouth inward flange 106 and tank mouth outer edge 107 polished on tank body blank 112, to eliminate tank mouth inward flange 106
And the corner angle at tank mouth outer edge 107；Can also polish tank mouth inward flange 106 and tank mouth outer edge 107 camber, using arc
The burr on tank body blank 112 is eliminated in shape transition；
In prioritization scheme, arc-shaped transition can be arc-shaped transition or ellipse arc transition；In the present embodiment, tank mouth
Inward flange 106 and tank mouth outer edge 107 are all polished into arc, specifically, using arc-shaped transition, can not only disappear
Except the corner angle at tank mouth inward flange 106 and tank mouth outer edge 107, the burr on tank body blank 112 can also be effectively eliminated.
In the present embodiment, the arc radius of tank mouth inward flange 106 is less than the arc radius of tank mouth outer edge 107, specifically
For, the arc radius of tank mouth inward flange 106 is 0.4mm, and the arc radius of tank mouth outer edge 107 is 0.6mm, such as Figure 13 institutes
Show；At this point, at tank mouth side wall 104 it is thinner, it is narrower with the tank mouth width of skin contact when carrying out cup, tank mouth
The air-tightness that out-of-roundness pulls bamboo jar on the skin influences smaller, so as to be effectively reduced the hair of tank mouth gas leak phenomenon
It is raw.
4. the tank bottom inward flange 108 and tank bottom outer edge 109 polished on tank body blank 112, to eliminate tank bottom inward flange 108
And the corner angle at tank bottom outer edge 109；It is similar with previous step, tank bottom inward flange 108 and tank bottom outer edge 109 can be polished into
Arc eliminates the burr on tank body blank 112 using arc-shaped transition；
In the scheme of optimization, arc-shaped transition can be arc-shaped transition or ellipse arc transition；In the present embodiment, tank
Bottom inward flange 108 and tank bottom outer edge 109 are all polished into arc, specifically, using arc-shaped transition, further
Ground, in the present embodiment, the arc radius of tank bottom inward flange 108 are equal to the arc radius of tank bottom outer edge 109, are 0.4mm,
As shown in figure 14.
At this point, the polishing of tank body blank 112 finishes, the tank body blank 112 after polishing, the internal cavities 102 of tank body 101
To effectively extending, 101 distribution of weight of tank body is uniform, and 101 surface of tank body is round and smooth, does not have any corner angle, not only beautiful, but also convenient for making
With.
In the present embodiment, it is preferentially polished using sander tank body blank 112, since need to polish is tank body
The endoporus sander of profession may be used, such as staight shank sander in 101 internal cavities 102.
Step (6) mould proof processing；Mould inhibitor is added to the water uniformly mixed, and tank body 101 is impregnated one section into the water
Time, during immersion so that mould inhibitor enters in tank body 101 or is attached to 101 surface of tank body, kills on tank body 101
Mould or the mycostatic growth of suppression, so as to effectively act as mould proof effect；In the present embodiment, mould inhibitor is preferentially adopted
With for food, fruit, cosmetics mould inhibitor, this kind of mould inhibitor is to person poultry harmless, and the term of validity is long, to mould have wide spectrum
Property；In the present embodiment, soaking time of the tank body 101 in mould inhibitor is 72 hours.
Step (7) takes out the tank body 101 Jing Guo mould proof processing, makes the natural airing of tank body 101, the structure diagram of bamboo jar
As shown in figure 15, the bamboo jar tank body 101 after airing can be used for boiling Chinese medicine bamboo jar, carry out Chinese medicine cup.
In the present embodiment, used water is tap water.
The above description is merely a specific embodiment, but protection scope of the present invention is not limited thereto, any
Those familiar with the art in the technical scope disclosed by the present invention, can readily occur in change or replacement, should all contain
Lid is within protection scope of the present invention.
Claims (10)
1. a kind of bamboo jar, which is characterized in that including tank body, the tank body is process using natural bamboo, and tank body includes being used for
The internal cavities of cup, the inner surface of tank body have gradient so that along internal cavities bottom to the direction of tank mouth, the inside
Cavity gradually increases, and the thickness distribution of tank wall is uniform；At tank mouth, tank mouth inward flange and tank mouth outer edge are both provided with arc
Shape transition, at tank bottom, tank bottom inward flange and tank bottom outer edge are both provided with arc-shaped transition.
2. the manufacture craft of bamboo jar according to claim 1 and bamboo jar, which is characterized in that the ratio of height to diameter of the tank body is
1.5~2.6, wherein, ratio of height to diameter is equal to outer diameter of the height than upper tank mouth of tank body.
3. the manufacture craft of bamboo jar according to claim 2 and bamboo jar, which is characterized in that the gradient of the tank inner surface
Between 0.5 degree~1.5 degree.
4. according to the manufacture craft of any bamboo jars of claim 1-3 and bamboo jar, which is characterized in that the arc-shaped transition is
Arc-shaped transition or ellipse arc transition.
5. the manufacture craft of bamboo jar according to claim 4 and bamboo jar, which is characterized in that when outside tank mouth inward flange and tank mouth
When edge uses arc transition, the arc radius of tank mouth inward flange is less than the outer peripheral arc radius of tank mouth；When tank bottom inward flange
When using arc transition with tank bottom outer edge, the arc radius of tank bottom inward flange is equal to the outer peripheral arc radius of tank bottom.
6. a kind of manufacture craft of bamboo jar, which is characterized in that comprise the following steps that：
(1) cutting action；Using natural bamboo, bamboo is cut into tank body blank by the ratio of height to diameter of tank body；
(2) epidermis of tank body blank outer surface is removed；
(3) by tank body blank, infusion for a period of time, during infusion, makes tank body blank be immersed in water always into the water
In；
(4) tank body blank from water is taken out, makes tank body blank nature airing；
(5) polishing operation；It polishes tank body blank, to remove the burr on tank body blank, forms the tank body of bamboo jar, specifically
Include the following steps：
1. the inner surface for tank body blank of polishing；Internal face polishing amount at tank body blank internal cavities bottom is zero, along internal sky
In bottom of chamber portion to the direction of tank mouth, the polishing amount of internal face gradually increases, at the tank mouth of tank body blank, the polishing amount of internal face
No more than the 1/2 of tank body blank sidewall thickness；
2. the outer surface for tank body blank of polishing；The polishing amount of tank body blank outer surface bottom and the polishing amount phase of internal face at tank mouth
Together, along tank body blank bottom to the direction of tank mouth, the polishing amount of tank body blank outer surface gradually decreases so that after polishing
Outer surface is mutually parallel with the inner surface after polishing；
3. the tank mouth inward flange and tank mouth outer edge polished on tank body blank, to eliminate tank mouth inward flange and tank mouth outer edge
Corner angle；
4. the tank bottom inward flange and tank bottom outer edge polished on tank body blank, to eliminate tank bottom inward flange and tank bottom outer edge
Corner angle；
(6) mould proof processing；Mould inhibitor is added to the water uniformly mixed, and tank body is soaked for a period of time into the water；
(7) tank body Jing Guo mould proof processing is taken out, makes tank body nature airing.
7. the manufacture craft of bamboo jar according to claim 6 and bamboo jar, which is characterized in that endured described in the step (3)
The time for boiling tank body blank is not less than 24 hours.
8. the manufacture craft of bamboo jar according to claim 7 and bamboo jar, which is characterized in that in the step (5), described
At the tank mouth of tank body blank, the polishing amount of the internal face is the 1/8~3/8 of tank body blank sidewall thickness.
9. the manufacture craft of bamboo jar according to claim 8 and bamboo jar, which is characterized in that in the step (5), the tank
Mouth inward flange and tank mouth outer edge and/or tank bottom inward flange and tank bottom outer edge are polished into arc-shaped transition.
10. according to the manufacture craft of any bamboo jars of claim 6-9 and bamboo jar, which is characterized in that in the step (6)
The soaking time of the tank body is not less than 48 hours.