CN108198088A - A kind of UV moldings improve version seam technology - Google Patents
A kind of UV moldings improve version seam technology Download PDFInfo
- Publication number
- CN108198088A CN108198088A CN201711452412.9A CN201711452412A CN108198088A CN 108198088 A CN108198088 A CN 108198088A CN 201711452412 A CN201711452412 A CN 201711452412A CN 108198088 A CN108198088 A CN 108198088A
- Authority
- CN
- China
- Prior art keywords
- version
- gloss oil
- seam
- moldings
- version seam
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Being molded the present invention provides a kind of UV improves version seam technology; belong to UV coating applications; by the way that the joint filling of UV gloss oil and UV lamp is repeatedly used thoroughly to eliminate the version seam on working version according to curing; so as to improve in the prior art because version seam excessive glue leads to equipment downtime or causes product is apparent the situations such as sizing and coining, raising product quality and production efficiency occur.Step of the present invention is simple, easy to operation with realizing, is molded suitable for liquid（Wet pressing）Technique.
Description
Technical field
The present invention relates to UV coating applications, specifically a kind of UV moldings improve version seam technology.
Background technology
UV is coated with moulding film due to excellent appearance and with not reproducible antiforge function, is widely used in various cigarettes
The top grade product packaging such as box, wine box, minaudiere.The processing of UV film productions be successively be coated with, be molded by UV, UV lamp ultraviolet light
It is irradiation curing, vacuum aluminum-coated and etc..It is different with traditional coating machine and moulding press, traditional coating and molding be respectively by
Either simplex sequence produces, and belongs to solid-state molding（Dry-pressing）Technique, UV coating moulding press is direct coating, molding, and two-step is incorporated in
It produces together, belongs to liquid molding（Wet pressing）Therefore technique, is coated in UV films in mold process, version seam is susceptible to excessive glue, leads
Product quality is caused to be difficult to ensure that, can also influence production efficiency.
Based on this, this case application is proposed.
Invention content
Being molded the purpose of the present invention is to provide a kind of UV improves version seam technology, improves the life of version seam excessive glue in the prior art
Production problem improves product quality and production efficiency.
To achieve the above object, the technical solution adopted by the present invention is：Include the following steps：
First, working version is cut according to roller size, the working version both sides edge after cutting is without sawtooth, smooth；
2nd, the working version packet cut out is in roller, version seam interface width requirement 0.1mm ~ 1mm；
3rd, version is sewed up mouth using the UV gloss oil being blended with outsourcing gloss oil by special UV gloss oil to tamp；
4th, it is operated with appropriate board speed after tamping version seam and is irradiated with UV lamp, version is made to sew up the UV gloss oil in mouth and is consolidated
Change；
5th, step 3 ~ step 4 is repeated until version seam thoroughly tamps；
6th, extra, remaining gloss oil is disposed, version is made to stitch flat smooth.Preferably, board manual speed position 6m/min, UV lamp
Include two groups, exposure power is 70w, 80w.
Preferably, the special UV gloss oil and outsourcing gloss oil ratio are 1：1.
Preferably, the working version is made a plate for roller.
Beneficial effects of the present invention：The present invention is by being roller, and UV gloss oil is filled into work by working version processing and fabricating
Make to eliminate version seam among the version seam of version, so as to solve because version seam excessive glue causes product is apparent asking for sizing and coining occur
Topic promotes the speed of production of UV coating moulding press and ensures product quality, meets the needs of customers.
The problem of being shut down due to version seam excessive glue is frequent this invention also solves existing equipment, it is ensured that continuous production, greatly
Improve the qualification rate of product.And the most fast speed of production 35m/min of existing UV coating moulding press is promoted to 55-80m/min,
It can not only significant increase board speed of production, efficiency and production capacity, it is ensured that ample supply of goods；It also is able to reduce waste of material, save
About production cost, makes coating machine more economical environment-protective.
Specific embodiment
To be easy to understand the technical means, the creative features, the aims and the efficiencies achieved by the present invention, tie below
Specific embodiment is closed, the present invention is further explained.
Embodiment 1
A kind of UV moldings improve version seam technology, include the following steps：
First, working version is cut according to roller size, the working version both sides edge after cutting is without sawtooth, smooth；
2nd, the working version packet cut out is in roller, version seam interface width requirement 0.1mm ~ 1mm；
3rd, version is sewed up mouth using the UV gloss oil being blended with outsourcing gloss oil by special UV gloss oil to tamp；
4th, manual control machine platform is operated with the speed of 6m/mi and uses two groups of UV lamps respectively with the exposure of 70w, 80w after tamping version seam
Degree power is irradiated, and version is made to sew up the UV gloss oil curing in mouth；
5th, step 3 ~ step 4 is repeated until version seam thoroughly tamps；
6th, extra, remaining gloss oil is disposed, version is made to stitch flat smooth.
The workflow for being incorporated into UV coating moulding press is as follows：
1st, the first step, working version are cut out by roller perimeter dimension, and the working version packet cut out is coated with moulding press forging printing plate roller in UV
On, install PET chemical films.
2nd, second step, coating chute install gloss oil, are stirred 5 minutes with mesh roller, reach gloss oil and become milky and viscosity
Not less than 28 seconds（Examine No. two cups of grace）.
3rd, third walks, and board circuit system and UV lamp be tuned into manual mode, and board manual speed is transferred to 6m/min, and 1
Lamp, 2 lamp exposure power are transferred to 70W, 80W respectively.With weight ratio 1:The 1 special gloss oil of company is sufficiently mixed with outsourcing gloss oil
And stir evenly, for filling version seam.When filling version seam, often fill out and once be required for being operated with appropriate board speed and use corresponding
UV power light irradiations it is primary, with reach version seam tamp, the cured purpose of gloss oil.Tool handle is more by hand after version seam gloss oil curing
Remaining version seam residual light oil processing is clean, accomplishes that version stitches flat smooth.
4th, the 4th step, 5mm white edges are respectively stayed on requirement coating placed in the middle, both sides when UV is coated with, and line carries out working version mould after coating
Pressure and UV lamp cure, and the holographic information on working version, which is transferred on coating, forms UV coating moulding films.
5th, the 5th step, vacuum aluminum-coated, coating mold pressing surface is aluminized, speed 400m/min, 50 ± 5cm/min of wire feed rate.
6th, the 6th step, rewinding detect film quality and cut as required.
Embodiment 2
A kind of UV moldings improve version seam technology, include the following steps：
First, working version is cut according to roller size, the working version both sides edge after cutting is without sawtooth, smooth；
2nd, the working version packet cut out is in roller, version seam interface width requirement 0.1mm ~ 1mm；
3rd, it is blended 1 using by special UV gloss oil and outsourcing gloss oil:Version is sewed up mouth and tamped by 1 UV gloss oil；
4th, manual control machine platform is operated with the speed of 6m/mi and uses two groups of UV lamps respectively with the exposure of 70w, 80w after tamping version seam
Degree power is irradiated, and version is made to sew up the UV gloss oil curing in mouth；
5th, step 3 ~ step 4 is repeated until version seam thoroughly tamps；
6th, extra, remaining gloss oil is disposed, version is made to stitch flat smooth.
Embodiment 3
A kind of UV moldings improve version seam technology, include the following steps：
First, working version is cut according to roller size, the working version both sides edge after cutting is without sawtooth, smooth；
2nd, the working version packet cut out is in roller, version seam interface width requirement 0.1mm ~ 1mm；
3rd, version is sewed up mouth using the UV gloss oil being blended with outsourcing gloss oil by special UV gloss oil to tamp；
4th, it is operated with appropriate board speed after tamping version seam and is irradiated with UV lamp, version is made to sew up the UV gloss oil in mouth and is consolidated
Change；
5th, step 3 ~ step 4 is repeated until version seam thoroughly tamps；
6th, extra, remaining gloss oil is disposed, version is made to stitch flat smooth.
Based on above-mentioned, the present invention provides a kind of UV molding version seam technologies, by the way that the joint filling of UV gloss oil and UV lamp is repeatedly used to shine
Curing thoroughly eliminates the version seam on working version, and avoiding the occurrence of version seam excessive glue leads to equipment downtime or cause product is apparent to glue
The situation of material and coining occurs, so that it is guaranteed that product quality and improving production efficiency, step is simple, easy to operation, uses effect
Fruit is good.
As known by the technical knowledge, the present invention can pass through the embodiment party of other essence without departing from its spirit or essential feature
Case is realized.Therefore, embodiment disclosed above, all things considered are all merely illustrative, not the only.Institute
Have within the scope of the present invention or be included in the invention in the change being equal in the scope of the present invention.
Claims (4)
1. a kind of UV moldings improve version seam technology, it is characterised in that：Include the following steps：
First, working version is cut according to roller size, the working version both sides edge after cutting is without sawtooth, smooth；
2nd, the working version packet cut out is in roller, version seam interface width requirement 0.1mm ~ 1mm；
Three, it version is sewed up by mouth using the UV gloss oil being blended by special UV gloss oil with outsourcing gloss oil tamps；
4th, it is operated with appropriate board speed after tamping version seam and is irradiated with UV lamp, version is made to sew up the UV gloss oil in mouth and is consolidated
Change；
5th, step 3 ~ step 4 is repeated until version seam thoroughly tamps；
6th, extra, remaining gloss oil is disposed, version is made to stitch flat smooth.
2. a kind of UV moldings as described in claim 1 improve version seam technology, it is characterised in that：The board manual speed position
6m/min, UV lamp include two groups, and exposure power is 70w, 80w.
3. a kind of UV moldings as described in claim 1 improve version seam technology, it is characterised in that：The special UV gloss oil and outsourcing
Gloss oil ratio is 1：1.
4. a kind of UV moldings as described in claim 1 improve version seam technology, it is characterised in that：The working version is roller system
Version.