CN108193067A - A kind of aluminium alloy innocuous refining flux - Google Patents
A kind of aluminium alloy innocuous refining flux Download PDFInfo
- Publication number
- CN108193067A CN108193067A CN201711489747.8A CN201711489747A CN108193067A CN 108193067 A CN108193067 A CN 108193067A CN 201711489747 A CN201711489747 A CN 201711489747A CN 108193067 A CN108193067 A CN 108193067A
- Authority
- CN
- China
- Prior art keywords
- aluminium alloy
- aluminium
- refining flux
- sodium
- innocuous
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of aluminium alloy innocuous refining flux, it is characterised in that:It is into being grouped as by following weight percents:Hexafluoro sodium aluminate 20 25%, graphite powder 5 10%, silica 1 3%, aluminium oxide 1 3%, sodium chloride 5 10%, sodium nitrate 20 25%, potassium fluosilicate 15 20%, anhydrous nitric acid calcium 1 5%.Preparation method is:It by above-mentioned each component in proportion with postponing, is crushed using pulverizer, and add in suitable quantity of water, is mixed uniformly, press is recycled to be pressed into bulk, finally carries out baking drying.The invention has the advantages that:It avoids that iron content in molten aluminium alloy is exceeded nontoxic, and easy to use, method is simple, at low cost, handling ease, reaches better de-ferrous effect.
Description
Technical field
The present invention relates to refining agent technical fields, and in particular to a kind of aluminium alloy innocuous refining flux.
Background technology
Aluminium and aluminium alloy are that current applications are very extensive, one of most economical applicable material, and the density of aluminium is smaller, though hardness
It is low, but various aluminium alloys are can be made into, such as duralumin, superduralumin, rustproof aluminum alloy, cast aluminium.These aluminium alloys are widely used in aircraft, vapour
The process industries such as vehicle, train, ship.In addition, cosmic rocket, space shuttle, artificial satellite are also closed using a large amount of aluminium and its aluminium
Gold, the electric conductivity of aluminium are only second to silver, copper and gold, have extensively in electric appliance process industry, electric wire industry and radio industry
Purposes, aluminium be heat good conductor, can industrially be constructed of aluminum various heat exchangers, heat sink material and cooker etc..Aluminium has preferably
Ductility (its ductility is only second to Jin Heyin), be widely used in packaging cigarette, candy etc., may also be fabricated which aluminium wire, aluminum strip, and
Various aluminum products can be rolled.The surface of aluminium is not easily susceptible to corrode, is often used to manufacture chemistry because there is fine and close oxide film
Reactor, medical instrument, refrigerating plant, petroleum refining device, oil and natural gas pipeline etc., and in the preparation process of aluminium,
It needs to refine aluminium, its purpose is to remove the field trash in aluminium, to improve the purity of aluminium, but at present for the essence of aluminium
Refining, usually due to the side effect of refining agent, can generate associated toxic substance.
Invention content
The technical problems to be solved by the invention be to provide it is a kind of so that refining product it is nontoxic, reach reduce pollution mesh
Aluminium alloy innocuous refining flux.
In order to solve the above technical problems, technical solution provided by the invention is:A kind of aluminium alloy innocuous refining flux, feature
It is:It is into being grouped as by following weight percents:Hexafluoro sodium aluminate 20-25%, graphite powder 5-10%, silica 1-
3%, aluminium oxide 1-3%, sodium chloride 5-10%, sodium nitrate 20-25%, potassium fluosilicate 15-20%, anhydrous nitric acid calcium 1-5%.
Preferably, it is into being grouped as by following weight percents:It is into being grouped as by following weight percents:Hexafluoro
Sodium aluminate 22%, graphite powder 8%, silica 2%, aluminium oxide 2%, sodium chloride 8%, sodium nitrate 22%, potassium fluosilicate 18%,
Anhydrous nitric acid calcium 3%.
Preparation method is:It by above-mentioned each component in proportion with postponing, is crushed, and is added in appropriate using pulverizer
Water is mixed uniformly, press is recycled to be pressed into bulk, finally carries out baking drying.
The invention has the advantages that:Avoid iron content in molten aluminium alloy exceeded nontoxic, easy to use, method letter
Single, at low cost, handling ease reaches better de-ferrous effect.
Specific embodiment
Embodiment one
A kind of aluminium alloy innocuous refining flux, it is characterised in that:It is into being grouped as by following weight percents:Hexafluoro aluminic acid
Sodium 20%, graphite powder 5%, silica 1 %, aluminium oxide 1%, sodium chloride 5%, sodium nitrate 20%, potassium fluosilicate 15% are anhydrous
Calcium nitrate 1%.
Preparation method is:It by above-mentioned each component in proportion with postponing, is crushed, and is added in appropriate using pulverizer
Water is mixed uniformly, press is recycled to be pressed into bulk, finally carries out baking drying.
Embodiment two
A kind of aluminium alloy innocuous refining flux, it is characterised in that:It is into being grouped as by following weight percents:Hexafluoro aluminic acid
Sodium 22%, graphite powder 8%, silica 2%, aluminium oxide 2%, sodium chloride 8%, sodium nitrate 22%, potassium fluosilicate 18% are anhydrous
Calcium nitrate 3%.
Preparation method is:It by above-mentioned each component in proportion with postponing, is crushed, and is added in appropriate using pulverizer
Water is mixed uniformly, press is recycled to be pressed into bulk, finally carries out baking drying.
Embodiment three
A kind of aluminium alloy innocuous refining flux, it is characterised in that:It is into being grouped as by following weight percents:Hexafluoro aluminic acid
Sodium 25%, graphite powder 10%, silica 3%, aluminium oxide 3%, sodium chloride 10%, sodium nitrate 25%, potassium fluosilicate 20%, nothing
Water calcium nitrate 5%.
Preparation method is:It by above-mentioned each component in proportion with postponing, is crushed, and is added in appropriate using pulverizer
Water is mixed uniformly, press is recycled to be pressed into bulk, finally carries out baking drying.
In order to become apparent from, completely illustrate present disclosure, specific embodiment is provided below to illustrate present inventive concept.
Certainly, the design that embodiment is intended to illustrate invention is provided, is not the whole of designing scheme of the present invention, less should
It is considered as the limitation of design content of the present invention.Under the enlightenment of the embodiment provided, made any scheme belongs to this
The protection domain of invention.
Claims (3)
1. a kind of aluminium alloy innocuous refining flux, it is characterised in that:It is into being grouped as by following weight percents:Hexafluoro sodium aluminate
20-25%, graphite powder 5-10%, silica 1-3%, aluminium oxide 1-3%, sodium chloride 5-10%, sodium nitrate 20-25%, fluorine
Potassium silicate 15-20%, anhydrous nitric acid calcium 1-5%.
2. a kind of aluminium alloy innocuous refining flux according to claim 1, it is characterised in that:It is by following weight percents
Into being grouped as:Hexafluoro sodium aluminate 22%, graphite powder 8%, silica 2%, aluminium oxide 2%, sodium chloride 8%, sodium nitrate 22%,
Potassium fluosilicate 18%, anhydrous nitric acid calcium 3%.
3. a kind of aluminium alloy innocuous refining flux according to claim 1, it is characterised in that:Preparation method is:It will be above-mentioned
Each component with postponing, is crushed, and add in suitable quantity of water in proportion using pulverizer, is mixed uniformly, is recycled press
Bulk is pressed into, finally carries out baking drying.