CN108192521A - A kind of PU black foam double-faced adhesive carrying material - Google Patents
A kind of PU black foam double-faced adhesive carrying material Download PDFInfo
- Publication number
- CN108192521A CN108192521A CN201810213072.2A CN201810213072A CN108192521A CN 108192521 A CN108192521 A CN 108192521A CN 201810213072 A CN201810213072 A CN 201810213072A CN 108192521 A CN108192521 A CN 108192521A
- Authority
- CN
- China
- Prior art keywords
- faced adhesive
- black
- double
- layer
- adhesive carrying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of PU black foam double-faced adhesive carrying materials, mutually cohere molding by easy-to-draw viscose material layer, foamed cotton layer, ultra-thin black PET base material layer, shading viscose material layer and double silicon PET release films substrate layers successively from top to bottom；The PU black foam double-faced adhesive carrying material thickness is 0.46~0.86mm.It is detected with reference to test of many times, product of the present invention has following good effect, it is lighter material has been reached, with superior adhesion, it is excellent to the adhesion on thin side, that there is stress abirritation, anti-reflective to stick up performance, resistance to curved surface, anti-repulsive force performance is good and can be safely removed in glass panel and PC, stainless steel, plastic surface, it is excellent to be die cut processing performance, suitable for large scale intelligence TV module group assemblings etc..
Description
Technical field
The present invention relates to adhesive article Material Fields, and in particular to a kind of PU black foam double-faced adhesive carrying material.
Background technology
In recent years, it is large-sized as requirement of the people to the quality of intelligent display image, size, Presence is promoted
It is preferred that liquid crystal display more and more becomes consumer；Liquid crystal display is enable correctly to show image, LCD backlight mould
The design of group is crucial, comprehensive performance and cost, and designer must reasonably select lamp bead, the matched lens of design plus appropriate
Optical device；Backlight source module by wait point light sources be converted to uniform area source, while ensure the necessary efficiency of light energy utilization and
Uniformity.
Since market and client are more and more to the wide viewing angle demand of liquid crystal display, the resolution ratio of liquid crystal module has very
Big raising, liquid crystal module have many advantages, such as wide viewing angle, high brightness and high aperture.Although liquid crystal module has many excellent
Gesture, but the module has stronger sensibility simultaneously, in squeezing action of the liquid crystal module by external force, easily generates light leakage and shows
As (alternatively referred to as stress Mura phenomenons), the visual effect of client is influenced.
Invention content
In order to solve the above technical problems, we have proposed a kind of PU black foam double-faced adhesive carrying material, with reference to test of many times
The effect of generation, it is lighter to have reached material, has a superior adhesion, excellent to the adhesion on thin side, there is stress to mitigate make
It is good and can be moved safely in glass panel and PC, stainless steel, plastic surface that performance, resistance to curved surface, anti-repulsive force performance are stuck up with, anti-reflective
It removes, cross cutting processing performance is excellent, suitable for large scale intelligence TV module group assemblings.
In order to achieve the above objectives, technical scheme is as follows：
A kind of PU black foam double-faced adhesive carrying material, from top to bottom successively by easy-to-draw viscose material layer, foamed cotton layer, ultra-thin black
Color PET base material layer, shading viscose material layer and double silicon PET release films substrate layers mutually cohere molding；The PU black foam is double
Face rubber belt material thickness is 0.46~0.86mm.
Further, in the above-mentioned technical solutions, the easy-to-draw viscose material layer is pure natural rubber cement substrate layer.
Further, in the above-mentioned technical solutions, the shading viscose material layer is acrylate glue water substrate layer.
Further, in the above-mentioned technical solutions, the foamed cotton layer is PU black foam foaming body substrate layers.
Further, in the above-mentioned technical solutions, the ultra-thin black PET base material layer thickness is 0.02-0.05mm.
Further, in the above-mentioned technical solutions, the PU black foam foaming body base material layer thickness is 0.25-
0.65mm。
Further, in the above-mentioned technical solutions, double silicon PET release film base materials layer thickness are 0.075mm.
Further, in the above-mentioned technical solutions, the pure natural rubber cement base material layer thickness is 0.10-0.35mm.
Further, in the above-mentioned technical solutions, the water base material layer thickness of the acrylate glue is 0.03-0.05mm.
Through the above technical solutions, with reference to the effect that test of many times generates, it is lighter to have reached material, there is superior attaching
Property, it is excellent to the adhesion on thin side, that there is stress abirritation, anti-reflective to stick up performance, resistance to curved surface, anti-repulsive force performance is good and in glass
Glass panel and PC, stainless steel, plastic surface can safely remove, and cross cutting processing performance is excellent, suitable for large scale intelligence TV module groups
Dress.
The removable PU black foam double-faced adhesive band of bearing liquid crystal display panel of the present invention, high compression ratio (75%), high thickness
(0.46mm~0.86mm), foam (have been carried out at the same time theory relative to conventional foam by same force compression amount bigger
It calculates and reality measures).Therefore the foam improves module light leakage phenomena superior, not only increases the production efficiency of module and good
Phenomena such as rate, easy-to-draw glue surface can be removed quickly from glass panel in product heavy industry, no residue glue, cut, it is synchronous to improve client
To the visual effect of product.
Description of the drawings
In order to illustrate more clearly about the embodiment of the present invention or technical scheme of the prior art, to embodiment or will show below
There is technology is required in describing to be briefly described using figure, it should be apparent that, the figure in being described below is only the present invention's
Some embodiments, for those of ordinary skill in the art, without creative efforts, can also be according to this
A little figures obtain other figures.
Fig. 1 is that a kind of PU black foam double-faced adhesive carrying material disclosed in the embodiment of the present invention 1 forms diagrammatic cross-section；
Corresponding component title in figure represented by number：
1. natural rubber latex water substrate layer；2.PU foam foaming body substrate layers；3. ultra-thin black PET base material layer；4. propylene
Sour glue substrate layer；5. pair silicon PET release film substrate layers.
Specific embodiment
Below in conjunction with the attached drawing in the embodiment of the present invention, the technical solution in the embodiment of the present invention is carried out clear, complete
Site preparation describes, it is clear that described embodiment is only part of the embodiment of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, those of ordinary skill in the art are obtained every other without creative efforts
Embodiment shall fall within the protection scope of the present invention.
The present invention provides a kind of PU black foam double-faced adhesive carrying material, structural principle is by PU black foam double-faced adhesives
Carrying material successively by stacking gradually arrangement, the natural rubber latex water substrate layer 1 and the ultra-thin black PET base material from top to bottom
PU foam foaming bodies substrate layer 2, the ultra-thin black PET base material layer 3 and double silicon PET release film bases are provided between layer 3
Acrylate glue water substrate layer 4 is provided between material layer 5；With reference to the effect that test of many times generates, it is lighter to have reached material, has had excellent
Adhesion more is excellent to the adhesion on thin side, there is stress abirritation, anti-reflective to stick up performance, resistance to curved surface, anti-repulsive force performance
Good and can be safely removed in glass panel and PC, stainless steel, plastic surface, cross cutting processing performance is excellent, with reference to embodiment and
The present invention is described in further detail for specific embodiment.
Wherein, pure natural rubber cement substrate layer linear thickness is 0.15-0.2mm；Linear density is not less than 1.8g/cm3.
The water base material layer linear thickness of acrylate glue is 0.05mm；Linear density is not less than 1.6g/cm3.
Pure natural rubber cement substrate layer and acrylate glue water substrate layer temperature tolerance：85 DEG C of (day or week) for a long time；In short term
120 DEG C of (hour divides).
Embodiment 1
As shown in Figure 1, a kind of PU black foam double-faced adhesive carrying material is successively by easy-to-draw viscose material layer, foamed cotton layer, ultra-thin
Black PET base material layer, shading viscose material layer and double silicon PET release films substrate layers stack gradually arrangement and mutually cohere from top to bottom
Molding.The easy-to-draw viscose material layer is pure natural rubber cement substrate layer.The shading viscose material layer is acrylic acid glue
Substrate layer.The foamed cotton layer is PU black foam foaming body substrate layers.The natural rubber latex water substrate layer 1 and the ultra-thin black
PU foam foaming bodies substrate layer 2, the ultra-thin black PET base material layer 3 and double silicon PET are provided between color PET base material layer 3
Acrylate glue water substrate layer 4 is provided between release film substrate layer 5；Material designation item number is TYBK-T-046；Material overall thickness
0.46mm, the margin of tolerance 10%
Wherein, 1 thickness of natural rubber latex water substrate layer is 0.16mm；The PU black foam foaming body substrate layer 2
Thickness is 0.25mm；Ultra-thin 3 thickness of black PET base material layer is 0.03mm；4 thickness of acrylate glue water substrate layer is
0.03mm；Double 5 thickness of silicon PET release films substrate layer are 0.075mm.
Embodiment 2
A kind of PU black foam double-faced adhesive carrying material is successively by easy-to-draw viscose material layer, foamed cotton layer, ultra-thin black PET base material
Layer, shading viscose material layer and double silicon PET release films substrate layers stack gradually arrangement and mutually cohere molding from top to bottom.It is described easy
It is pure natural rubber cement substrate layer to draw viscose material layer.The shading viscose material layer is acrylate glue water substrate layer.It is described
Foamed cotton layer is PU black foam foaming body substrate layers.Material designation item number is TYBK-T-066；Material overall thickness 0.66mm, tolerance
Range 10%
0024 wherein, and 1 thickness of natural rubber latex water substrate layer is 0.20mm；The PU black foam foaming body base material
2 thickness of layer are 0.40mm；Ultra-thin 3 thickness of black PET base material layer is 0.03mm；4 thickness of acrylate glue water substrate layer
For 0.03mm；Double 5 thickness of silicon PET release films substrate layer are 0.075mm.
Embodiment 3
A kind of PU black foam double-faced adhesive carrying material is successively by easy-to-draw viscose material layer, foamed cotton layer, ultra-thin black PET base material
Layer, shading viscose material layer and double silicon PET release films substrate layers stack gradually arrangement and mutually cohere molding from top to bottom.It is described easy
It is pure natural rubber cement substrate layer to draw viscose material layer.The shading viscose material layer is acrylate glue water substrate layer.It is described
Foamed cotton layer is PU black foam foaming body substrate layers.Material designation item number is TYBK-T-086；Material overall thickness 0.86mm, tolerance
Range 10%
0026 wherein, and 1 thickness of natural rubber latex water substrate layer is 0.25mm；The PU black foam foaming body base material
2 thickness of layer are 0.55mm；Ultra-thin 3 thickness of black PET base material layer is 0.03mm；4 thickness of acrylate glue water substrate layer
For 0.03mm；Double 5 thickness of silicon PET release films substrate layer are 0.075mm.
Embodiment 4
A kind of PU black foam double-faced adhesive carrying material is successively by easy-to-draw viscose material layer, foamed cotton layer, ultra-thin black PET base material
Layer, shading viscose material layer and double silicon PET release films substrate layers stack gradually arrangement and mutually cohere molding from top to bottom.It is described easy
It is pure natural rubber cement substrate layer to draw viscose material layer.The shading viscose material layer is acrylate glue water substrate layer.It is described
Foamed cotton layer is PU black foam foaming body substrate layers.Between the natural rubber latex water substrate layer 1 or 0.1-0.35mm
Other thickness；Other thickness between the PU foams foaming body substrate layer 2 or 0.15-0.65mm；The propylene
Sour glue substrate layer may be other thickness between 0.02-0.05mm；Special limitation will not be done herein, these are equally all
It belongs to the scope of protection of the present invention.
Embodiment 5
The pure natural rubber cement substrate layer of the present invention is a kind of completely new environmentally friendly adhesive backers, has unique fast rebound
With stronger cohesive force, through the above technical solutions, the present invention by by PU black foam double-faced adhesive carrying materials successively by natural
Rubber cement substrate layer 1, PU foam foaming bodies substrate layer 2, ultra-thin black PET base material layer 3, acrylate glue water substrate layer 4 and double
Silicon PET release films substrate layer 5 mutually coheres molding；Stack gradually arrangement from top to bottom, the natural rubber latex water substrate layer 1 with
Be provided with PU foam foaming bodies substrate layer 2 between the ultra-thin black PET base material layer 3, the ultra-thin black PET base material layer 3 with
Acrylate glue water substrate layer 4 is provided between double silicon PET release films substrate layers 5；With reference to the effect that test of many times generates, reach
It is lighter to have arrived material, there is superior adhesion, it is excellent to the adhesion on thin side, have stress abirritation, anti-reflective stick up performance,
Resistance to curved surface, anti-repulsive force performance are good and can be safely removed in glass panel and PC, stainless steel, plastic surface, are die cut processing performance
It is excellent, suitable for large scale intelligence TV module group assemblings.
PU black foam double-faced adhesive band TYBK-T-046, TYBK-T-066, TYBK- prepared by the embodiment of the present invention 1,2,3
The performance parameter of T-086 refers to following table.
One project of table and method
Two dynamic tensile data of table
The adhesion force data of table three
Four dynamic tear data of table
Five holding power data of table
Above-described is only a kind of PU black foam double-faced adhesive carrying material preferred embodiment of the present invention, should be referred to
Go out, for those of ordinary skill in the art, without departing from the concept of the premise of the invention, can also make several
Modification and improvement, these belong to protection scope of the present invention.
Claims (9)
1. a kind of PU black foam double-faced adhesive carrying material, it is characterised in that：From top to bottom successively by easy-to-draw viscose material layer, foam
Layer, ultra-thin black PET base material layer, shading viscose material layer and double silicon PET release films substrate layers mutually cohere molding；The PU is black
Color foam double-faced adhesive carrying material thickness is 0.46~0.86mm.
A kind of 2. PU black foam double-faced adhesive carrying material according to claim 1, which is characterized in that the easy-to-draw viscose material
The bed of material is pure natural rubber cement substrate layer.
A kind of 3. PU black foam double-faced adhesive carrying material according to claim 1, which is characterized in that the shading viscose material
The bed of material is acrylate glue water substrate layer.
4. a kind of PU black foam double-faced adhesive carrying material according to claim 2, which is characterized in that the foamed cotton layer is PU
Black foam foaming body substrate layer.
A kind of 5. PU black foam double-faced adhesive carrying material according to claim 3, which is characterized in that the ultra-thin black
PET base material layer thickness is 0.02-0.05mm.
A kind of 6. PU black foam double-faced adhesive carrying material according to claim 4, which is characterized in that the PU black foam
Foaming body base material layer thickness is 0.25-0.65mm.
7. according to a kind of PU black foam double-faced adhesive carrying material of claim 1-6 any one of them, which is characterized in that described double
Silicon PET release film base materials layer thickness is 0.075mm.
A kind of 8. PU black foam double-faced adhesive carrying material according to claim 2, which is characterized in that the pure natural rubber
Glue base material layer thickness is 0.10-0.35mm.
A kind of 9. PU black foam double-faced adhesive carrying material according to claim 3, which is characterized in that the acrylic acid glue
Base material layer thickness is 0.03-0.05mm.