CN108191391A - A kind of refractory material - Google Patents
A kind of refractory material Download PDFInfo
- Publication number
- CN108191391A CN108191391A CN201810237812.6A CN201810237812A CN108191391A CN 108191391 A CN108191391 A CN 108191391A CN 201810237812 A CN201810237812 A CN 201810237812A CN 108191391 A CN108191391 A CN 108191391A
- Authority
- CN
- China
- Prior art keywords
- parts
- refractory material
- refractory
- mountain flour
- performance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of refractory materials, which is characterized in that is prepared by the raw material of following parts by weight：35 parts of borax, 13 parts of boron potassium cyanide, 8 15 parts of kaolin, 5 10 parts of zirconium oxide, 10 15 parts of aluminium oxide, 5 10 parts of nano silicon dioxide, 5 10 parts of mountain flour.The present invention provides a kind of refractory material, and property, performance are stablized at high temperature, excellent fire retarding performance, while it also has the characteristics that service life is long, and effective storage life is considerably longer than common refractory currently on the market, thus it has a vast market prospect.
Description
Technical field
The present invention relates to field of material technology more particularly to a kind of refractory materials.
Background technology
Refractory material is widely used in the fields such as steel, non-ferrous metal, glass, cement, ceramics, machinery, electric power, is to ensure
Above-mentioned industry production run and technology develop essential basic material, are played in hot industry production development irreplaceable
Important function.
Not only type is few for the refractory material used at present, but also existing refractory material is generally also short there is service life
Problem.
Invention content
The object of the present invention is to provide a kind of refractory material, property, performance are stablized at high temperature, excellent fire retarding performance,
It also has the characteristics that service life is long simultaneously, and effective storage life is considerably longer than common refractory currently on the market, because
And it has a vast market prospect.
Technical scheme of the present invention：A kind of refractory material, which is characterized in that by the raw material preparation of following parts by weight
Into：3-5 parts of borax, 1-3 parts of boron potassium cyanide, 8-15 parts of kaolin, 5-10 parts of zirconium oxide, 10-15 parts of aluminium oxide, nanometer titanium dioxide
5-10 parts of silicon, 5-10 parts of mountain flour.
A kind of aforementioned refractory material, which is characterized in that the mesh of the granularity of the mountain flour≤400.
A kind of aforementioned refractory material, which is characterized in that the zirconium oxide, aluminium oxide granularity 4000-5000 mesh it
Between.
Beneficial effects of the present invention：Property, performance are stablized at high temperature, excellent fire retarding performance, while it also has use
The characteristics of long lifespan, effective storage life are considerably longer than common refractory currently on the market, thus it is with wide city
Field prospect.
Specific embodiment
The present invention is further illustrated for example below, but is not intended as the foundation limited the present invention.
Embodiment：A kind of refractory material is prepared by the raw material of following parts by weight：3-5 parts of borax, boron potassium cyanide 1-
3 parts, 8-15 parts of kaolin, 5-10 parts of zirconium oxide, 10-15 parts of aluminium oxide, 5-10 parts of nano silicon dioxide, 5-10 parts of mountain flour.
The mesh of the granularity of the mountain flour≤400.
The zirconium oxide, aluminium oxide granularity between 4000-5000 mesh.
Claims (3)
1. a kind of refractory material, which is characterized in that be prepared by the raw material of following parts by weight：3-5 parts of borax, boron potassium cyanide
1-3 parts, 8-15 parts of kaolin, 5-10 parts of zirconium oxide, 10-15 parts of aluminium oxide, 5-10 parts of nano silicon dioxide, 5-10 parts of mountain flour.
A kind of 2. refractory material according to claim 1, which is characterized in that the mesh of the granularity of the mountain flour≤400.
3. a kind of refractory material according to claim 1, which is characterized in that the zirconium oxide, aluminium oxide granularity exist
Between 4000-5000 mesh.