CN108189508A - Paper diaper material and preparation method thereof - Google Patents

Paper diaper material and preparation method thereof Download PDF

Info

Publication number
CN108189508A
CN108189508A CN201810166890.1A CN201810166890A CN108189508A CN 108189508 A CN108189508 A CN 108189508A CN 201810166890 A CN201810166890 A CN 201810166890A CN 108189508 A CN108189508 A CN 108189508A
Authority
CN
China
Prior art keywords
looped pile
polytetrafluoroethylene
paper diaper
polyester taffeta
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810166890.1A
Other languages
Chinese (zh)
Inventor
刘衍华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Weifang New Mstar Technology Ltd Spinning
Original Assignee
Weifang New Mstar Technology Ltd Spinning
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Weifang New Mstar Technology Ltd Spinning filed Critical Weifang New Mstar Technology Ltd Spinning
Priority to CN201810166890.1A priority Critical patent/CN108189508A/en
Publication of CN108189508A publication Critical patent/CN108189508A/en
Pending legal-status Critical Current

Abstract

The present invention proposes a kind of paper diaper material and preparation method thereof, and including looped pile fabric, polytetrafluoroethylene film and Polyester Taffeta, the polytetrafluoroethylene film is between the looped pile fabric and the Polyester Taffeta.Preparation method：By Polyester Taffeta applied atop polytetrafluoroethylene (PTFE), form polytetrafluoroethylene film, the Polyester Taffeta that polytetrafluoroethylene (PTFE) is coated with after drying is carried out compound with looped pile fabric by compounding machine, and the burnishing surface of wherein looped pile fabric is contacted with polytetrafluoroethylene film, and looped pile side is outwardly.Urine pants wash use repeatedly made of the material, do not interfere with waterproof and breathable performance.

Description

Paper diaper material and preparation method thereof
Technical field
The invention belongs to paper diaper technical fields, and in particular to a kind of paper diaper material and preparation method thereof.
Background technology
Paper diaper include baby paper diaper and adult diaper.The basic structure of paper diaper includes the solid positioned at top layer Edge, the pellicle below the three-dimensional edge, the absorptive core below the pellicle, positioned at the absorption It is notacoria below core, the adhesive tape below the notacoria, included positioned at I-shaped arranged on left and right sides solid edge top Elastic rib A, the elastic rib B between the I-shaped arranged on left and right sides solid edge and notacoria, the table positioned at I-shaped top Elastic rib C between film and notacoria.
The core key technology of paper diaper is " core ".For technological layer, paper diaper core experienced three altogether so far Secondary revolution.Paper diaper are disposable rear i.e. droppable products.With non-woven fabrics, toilet paper, Time of Fluff Slurry, macromolecule water uptake tree The materials such as fat, PE films, rubber band are made.Due to disposably using a large amount of wastes for causing resource.
Invention content
The present invention proposes a kind of paper diaper material, and urine pants wash use repeatedly made of the material, do not interfere with waterproof Permeability.
The technical proposal of the invention is realized in this way：
A kind of paper diaper material, including looped pile fabric, polytetrafluoroethylene film and Polyester Taffeta, the polytetrafluoroethylene film position Between the looped pile fabric and the Polyester Taffeta.
Preferably, the looped pile fabric is knitted loop fabric.
It is also another object of the present invention to provide a kind of preparation methods of paper diaper material, include the following steps：It will wash Tower husband's applied atop polytetrafluoroethylene (PTFE) forms polytetrafluoroethylene film, and the Polyester Taffeta and hair of polytetrafluoroethylene (PTFE) are coated with after drying Circle fabric is carried out compound by compounding machine, and the burnishing surface of wherein looped pile fabric is contacted with polytetrafluoroethylene film, and looped pile side is outwardly .
Preferably, it is compound the specific steps are：The pressure between composite roll on compounding machine is 3~4KG/m2, use Adhesive glue is for epoxide-resin glue with lac resin glue according to 1：4 ratio mixing, drying temperature are 80~100 DEG C.
Preferably, the temperature dried after coating is 70~80 DEG C.
Beneficial effects of the present invention：
The paper diaper of the present invention include looped pile fabric, polytetrafluoroethylene film and Polyester Taffeta, the polytetrafluoroethylene (PTFE) with material Film is between the looped pile fabric and the Polyester Taffeta.Looped pile fabric appearance is soft, preferable with skin-friendly, as inside fabric； Outside is Polyester Taffeta and polytetrafluoroethylene film composite material, with waterproof but also can not only be breathed freely.Polytetrafluoroethylene (PTFE) film-strength is high, tough Property is good, ageing-resistant, washs use repeatedly convenient for urine pants, does not interfere with waterproof and breathable performance.
Description of the drawings
In order to illustrate more clearly about the embodiment of the present invention or technical scheme of the prior art, to embodiment or will show below There is attached drawing needed in technology description to be briefly described, it should be apparent that, the accompanying drawings in the following description is only this Some embodiments of invention, for those of ordinary skill in the art, without creative efforts, can be with Other attached drawings are obtained according to these attached drawings.
Fig. 1 is the structure diagram of paper diaper material of the present invention.
Attached drawing indicates：1st, knitted loop fabric, 2, polytetrafluoroethylene film, 3, Polyester Taffeta.
Specific embodiment
Below in conjunction with the attached drawing in the embodiment of the present invention, the technical solution in the embodiment of the present invention is carried out clear, complete Site preparation describes, it is clear that described embodiment is only part of the embodiment of the present invention, instead of all the embodiments.It is based on Embodiment in the present invention, those of ordinary skill in the art are obtained every other without making creative work Embodiment shall fall within the protection scope of the present invention.
Embodiment 1
With reference to Fig. 1, a kind of paper diaper material, including knitted loop fabric 1, polytetrafluoroethylene film 2 and Polyester Taffeta 3, institute Polytetrafluoroethylene film 2 is stated between the knitted loop fabric 1 and the Polyester Taffeta 3.
Preparation method：By Polyester Taffeta applied atop polytetrafluoroethylene (PTFE), polytetrafluoroethylene film, drying, the temperature of drying are formed It it is 75 DEG C, the Polyester Taffeta for being then coated with polytetrafluoroethylene (PTFE) carries out compound, wherein looped pile face with looped pile fabric by compounding machine The burnishing surface of material is contacted with polytetrafluoroethylene film, and looped pile side is outwardly.The pressure between composite roll on compounding machine is 3KG/m2, the adhesive glue that uses be epoxide-resin glue with lac resin glue according to 1：4 ratio mixing, drying temperature are 100 DEG C.
Embodiment 2
With reference to Fig. 1, a kind of paper diaper material, including knitted loop fabric 1, polytetrafluoroethylene film 2 and Polyester Taffeta 3, institute Polytetrafluoroethylene film 2 is stated between the knitted loop fabric 1 and the Polyester Taffeta 3.
Preparation method：By Polyester Taffeta applied atop polytetrafluoroethylene (PTFE), polytetrafluoroethylene film, drying, the temperature of drying are formed It it is 70 DEG C, the Polyester Taffeta for being then coated with polytetrafluoroethylene (PTFE) carries out compound, wherein looped pile face with looped pile fabric by compounding machine The burnishing surface of material is contacted with polytetrafluoroethylene film, and looped pile side is outwardly.The pressure between composite roll on compounding machine is 4KG/m2, the adhesive glue that uses be epoxide-resin glue with lac resin glue according to 1：4 ratio mixing, drying temperature are 90 DEG C.
Embodiment 3
With reference to Fig. 1, a kind of paper diaper material, including knitted loop fabric 1, polytetrafluoroethylene film 2 and Polyester Taffeta 3, institute Polytetrafluoroethylene film 2 is stated between the knitted loop fabric 1 and the Polyester Taffeta 3.
Preparation method：By Polyester Taffeta applied atop polytetrafluoroethylene (PTFE), polytetrafluoroethylene film, drying, the temperature of drying are formed It it is 80 DEG C, the Polyester Taffeta for being then coated with polytetrafluoroethylene (PTFE) carries out compound, wherein looped pile face with looped pile fabric by compounding machine The burnishing surface of material is contacted with polytetrafluoroethylene film, and looped pile side is outwardly.The pressure between composite roll on compounding machine is 3.5KG/m2, the adhesive glue that uses be epoxide-resin glue with lac resin glue according to 1：4 ratio mixing, drying temperature 80 ℃。
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all essences in the present invention With within principle, any modification, equivalent replacement, improvement and so on should all be included in the protection scope of the present invention god.

Claims (5)

1. a kind of paper diaper material, which is characterized in that including looped pile fabric, polytetrafluoroethylene film and Polyester Taffeta, described poly- four Fluoride film is between the looped pile fabric and the Polyester Taffeta.
2. paper diaper material according to claim 1, which is characterized in that the looped pile fabric is knitted loop fabric.
3. the preparation method of paper diaper material as described in claim 1, which is characterized in that include the following steps：Tower will be washed Husband's applied atop polytetrafluoroethylene (PTFE) forms polytetrafluoroethylene film, and the Polyester Taffeta and looped pile of polytetrafluoroethylene (PTFE) are coated with after drying Fabric is carried out compound by compounding machine, and the burnishing surface of wherein looped pile fabric is contacted with polytetrafluoroethylene film, and looped pile side is outwardly It can.
4. the preparation method of paper diaper material according to claim 3, which is characterized in that it is compound the specific steps are： The pressure between composite roll on compounding machine is 3~4KG/m2, and the adhesive glue used is pressed for epoxide-resin glue and lac resin glue According to 1：4 ratio mixing, drying temperature are 80~100 DEG C.
5. the preparation method of paper diaper material according to claim 3, which is characterized in that the temperature dried after coating is 70~80 DEG C.
CN201810166890.1A 2018-02-28 2018-02-28 Paper diaper material and preparation method thereof Pending CN108189508A (en)