CN108188524A - A kind of steel stainless steel composite plate plate type radiator - Google Patents
A kind of steel stainless steel composite plate plate type radiator Download PDFInfo
- Publication number
- CN108188524A CN108188524A CN201810043048.9A CN201810043048A CN108188524A CN 108188524 A CN108188524 A CN 108188524A CN 201810043048 A CN201810043048 A CN 201810043048A CN 108188524 A CN108188524 A CN 108188524A
- Authority
- CN
- China
- Prior art keywords
- stainless steel
- plate
- radiator
- composite plate
- steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The embodiment of the invention discloses a kind of steel stainless steel composite plate plate type radiators, it is related to field of electronics, diffusion of the solder to the steel parts of steel stainless steel composite plate can be passed through in Process of Vacuum Brazing, material mouth end steel parts is made to form metallurgical, it is therefore prevented that the corrosion of steel.The present invention includes:The inner wall of steel stainless steel composite plate plate type radiator uses steel stainless steel composite plate.The present invention is suitable for hot-water heating and steam heating radiator.
Description
Technical field
The present invention relates to hot-water heating and steam heating radiators more particularly to a kind of steel stainless steel composite plate making sheet type to radiate
Device.
Background technology
With the increasingly raising of living standard, requirement of the people to living environment is also higher and higher.Simultaneously to radiator
Quality, practicability and decorative requirement are also higher and higher.Because its heat exchange area is big, thin type accounts for traditional steel plate type radiator
It is few with space, it is welcomed by the people.But the fatal defects of product are that corrosion resistance is poor, and easy-to-rust forms secondary pollution to water quality.
In use to water quality requirement height.The main reason for causing steel plate type radiator not anti-corrosion:First, the material of manufacture radiator
Thickness is only 1 ㎜ steel plates;Second is that the constructional aspect of product causes it that can not carry out radiator inwall preservative treatment.Although product by
To the welcome of people, but because product self-corrosion resistance is poor, to water quality requirement height, the using area of product is limited.It is main to use
The area southern area cold for Xia Redong, matches for individual heating.Northern area can not use.
The manufacturing process of conventional steel plate type radiator takes electric resistance welding.The stamping forming radiator fin of two panels is superimposed upon
At first one carries out spot welding using electric resistance welding between two water channels, then the frame of radiator is carried out rolling weldering (electric resistance welding
A kind of mode), manufacture high energy consumption.Product surface can only be sprayed after the completion of welding, product inner wall, which can not carry out application, to be prevented
It is rotten.
Invention content
The embodiment of the present invention provides a kind of steel stainless steel composite plate plate type radiator, is capable of the stainless steel of radiator
Inner wall solves the problems, such as conventional steel plate type radiator inner wall corrosion.
In order to achieve the above objectives, the embodiment of the present invention adopts the following technical scheme that:
The inner wall of steel stainless steel composite plate plate type radiator uses steel stainless steel composite plate;
Further, steel stainless steel composite material radiator is welded using Vacuum Soldering Technology, in firm stainless steel clad plate
It is molded in material plate-making type radiator single-chip manufacturing process using mould punching, the molding firm stainless steel composite plate of two panels is made a plate
Type radiator single-chip is suppressed after being combined preset solder, bound edge, is put into after bound edge in fixture and is used laser spot welding technique
Welding sizing is carried out to radiator water channel, then radiator is sent into vacuum brazing furnace and is welded.
The soldering processes flow of Flat-type heat radiator:
If soldering oven burner hearth effective district is 1200 × 800 × 800cm.
The first step:Block pattern row pattern radiator, single chip architecture can pile up 40;Biplate (between carry radiating fin) 8
Group.
Second step:Nitrogen is inputted to purify burner hearth to burner hearth, and nitrogen supply (NS) amount is the work according to furnace volume and vacuum pump
Make parameter formulation.Stop nitrogen input when vacuum degree is up to standard.
Third walks:Set brazing temperature, time and vacuum degree.1150 DEG C of copper base solder welding temperature, weld interval are 3 points
Clock.Welding temperature is controlled by temperature controller, and weld interval is controlled by time controller.Vacuum degree (MPa) 13.3.Vacuum drying oven is matched
There is switch board that can set vacuum condition in running parameter and display stove.Vacuum brazing temperature is divided into preheating, heat preservation, welding temperature
Degree, cooling, overall process are automatically controlled by temperature controller according to setting program.
4th step:Cooling.The nitrogen type of cooling is taken, opens the nitrogen valve input nitrogen on vacuum drying oven.Work as temperature controller
Display in-furnace temperature completes cooling at 300 DEG C, opens fire door and takes out workpiece.
The beneficial effects of the invention are as follows:By solder to the steel portion of steel stainless steel composite plate in Process of Vacuum Brazing
Divide the diffusion at (mouth end), material mouth end steel parts is made to form metallurgical, it is therefore prevented that the corrosion of steel.In production process
Middle items welding procedure is pollution-free, no discharge, energy conservation and environmental protection.
Description of the drawings
It to describe the technical solutions in the embodiments of the present invention more clearly, below will be to needed in the embodiment
Attached drawing is briefly described, it should be apparent that, the accompanying drawings in the following description is only some embodiments of the present invention, for ability
For the those of ordinary skill of domain, without creative efforts, it can also be obtained according to these attached drawings other attached
Figure.
Fig. 1 is steel stainless steel composite plate plate-making type radiator schematic diagram provided by the invention;
Fig. 2 illustrates for steel stainless steel composite plate plate-making type radiator vacuum brazing solder preset position provided by the invention
Figure;
Fig. 3 is Vacuum Soldering Technology schematic diagram.
Specific embodiment
For those skilled in the art is made to more fully understand technical scheme of the present invention, below in conjunction with the accompanying drawings and specific embodiment party
Formula is described in further detail the present invention.Embodiments of the present invention are described in more detail below, the embodiment is shown
Example is shown in the drawings, wherein same or similar label represents same or similar element or with identical or class from beginning to end
Like the element of function.It is exemplary below with reference to the embodiment of attached drawing description, is only used for explaining the present invention, and cannot
It is construed to limitation of the present invention.Those skilled in the art of the present technique are appreciated that unless expressly stated, odd number shape used herein
Formula " one ", "one", " described " and "the" may also comprise plural form.It is to be further understood that the specification of the present invention
The middle wording " comprising " used refers to there are the feature, integer, step, operation, element and/or component, but it is not excluded that
Other one or more features of presence or addition, integer, step, operation, element, component and/or their group.It should be understood that
When we claim element to be " connected " or during " coupled " to another element, it can be directly connected or coupled to other elements or
There may also be intermediary elements.In addition, " connection " used herein or " coupling " can include wireless connection or coupling.Here make
Wording "and/or" includes any cell of one or more associated list items and all combines.The art
Technical staff is appreciated that unless otherwise defined all terms used herein have (including technical terms and scientific terms)
The meaning identical with the general understanding of the those of ordinary skill in fields of the present invention.It should also be understood that such as general
Those terms defined in dictionary, which should be understood that, to be had a meaning that is consistent with the meaning in the context of the prior art, and
Unless being defined as here, will not be explained with the meaning of idealization or too formal.
The embodiment of the present invention provides a kind of steel stainless steel composite plate plate type radiator, as shown in Figure 1, including:Steel is not
The inner wall of rust plastics composite plate plate type radiator uses steel stainless steel composite plate;Further, steel stainless steel composite material
Radiator is welded using Vacuum Soldering Technology.As shown in Fig. 2, it was made in firm stainless steel composite plate plate-making type radiator single-chip
It is molded, the molding firm stainless steel composite plate plate-making type radiator single-chip of two panels is combined preset using mould punching in journey
It is suppressed after solder, bound edge, is put into after bound edge in fixture and welding sizing is carried out to radiator water channel using laser spot welding technique,
Then radiator is sent into vacuum brazing furnace and welded.
The soldering processes flow of Flat-type heat radiator:
If 1200 × 800 × 800cm of soldering oven burner hearth effective district.
The first step:Block pattern row pattern radiator, single chip architecture can pile up 40;Biplate (between carry radiating fin) 8
Group.
Second step:Nitrogen is inputted to purify burner hearth to burner hearth, and nitrogen supply (NS) amount is the work according to furnace volume and vacuum pump
Make parameter formulation.Stop nitrogen input when vacuum degree is up to standard.
Third walks:Set brazing temperature, time and vacuum degree.1150 DEG C of copper base solder welding temperature, weld interval are 3 points
Clock.Welding temperature is controlled by temperature controller, and weld interval is controlled by time controller.Vacuum degree (MPa) 13.3.Vacuum drying oven is matched
There is switch board that can set vacuum condition in running parameter and display stove.Vacuum brazing temperature is divided into preheating, heat preservation, welding temperature
Degree, cooling, overall process are automatically controlled by temperature controller according to setting program.
4th step:Cooling.The nitrogen type of cooling is taken, opens the nitrogen valve input nitrogen on vacuum drying oven.Work as temperature controller
Display in-furnace temperature completes cooling at 300 DEG C, opens fire door and takes out workpiece.
Each embodiment in this specification is described by the way of progressive, identical similar portion between each embodiment
Point just to refer each other, and the highlights of each of the examples are difference from other examples.Especially for equipment reality
For applying example, since it is substantially similar to embodiment of the method, so describing fairly simple, related part is referring to embodiment of the method
Part explanation.The above description is merely a specific embodiment, but protection scope of the present invention is not limited to
This, any one skilled in the art in the technical scope disclosed by the present invention, the variation that can readily occur in or replaces
It changes, should be covered by the protection scope of the present invention.Therefore, protection scope of the present invention should be with the protection model of claim
Subject to enclosing.
Claims (2)
1. a kind of steel stainless steel composite plate plate type radiator, which is characterized in that including:The steel stainless steel composite plate system
The inner wall of plate type radiator uses steel stainless steel composite plate.
2. a kind of steel stainless steel composite plate plate type radiator according to claim 1, which is characterized in that the steel is stainless
Steel composite material radiator is welded using Vacuum Soldering Technology, in the firm stainless steel composite plate plate-making type radiator single-chip system
It is molded during making using mould punching, the molding firm stainless steel composite plate plate-making type radiator single-chip of two panels is combined
It is suppressed after preset solder, bound edge, is put into after bound edge in fixture and radiator water channel is welded using laser spot welding technique
Then radiator is sent into vacuum brazing furnace and is welded by sizing.