CN108179255A - A kind of clutch of motorcycle control stick normalizing process - Google Patents
A kind of clutch of motorcycle control stick normalizing process Download PDFInfo
- Publication number
- CN108179255A CN108179255A CN201711497626.8A CN201711497626A CN108179255A CN 108179255 A CN108179255 A CN 108179255A CN 201711497626 A CN201711497626 A CN 201711497626A CN 108179255 A CN108179255 A CN 108179255A
- Authority
- CN
- China
- Prior art keywords
- control stick
- clutch
- motorcycle
- heating
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to motorcycle accessories manufacturing technology field, especially a kind of clutch of motorcycle control stick normalizing process includes the following steps：S1, dimension control；S2, upper tooling are fixed；S3, spraying antioxidation coating；S4, heating heating；S5, Heat preservation；S6, cooling are come out of the stove.The present invention carries out protection against oxidation by spraying antioxidation coating and injection protection gas two ways to control stick, so as to effectively improve its oxidation resistance, improves its service life.
Description
Technical field
The present invention relates to motorcycle accessories manufacturing technology field more particularly to a kind of positive firers of clutch of motorcycle control stick
Skill.
Background technology
Motorcycle is driven by gasoline engine, and by the two-wheeled or tricycle of bar handle front-wheel steer, light and flexible, traveling is fast
Speed is widely used in patrol, passenger and freight transportation etc., also serves as sports movement apparatus.Generally, motorcycle is divided into street
Vehicle, racing cycle motorcycle, off-road motorcycle, cruise vehicle, station wagon etc..
Clutch of motorcycle control stick is one of accessory of motorcycle, and normalizing is its common process, it is existing just
Ignition technique lacks the protection to it, and final product quality is reduced so as to which it be made easily to be aoxidized.
Invention content
The purpose of the present invention is to solve shortcoming in the prior art, and a kind of clutch of motorcycle behaviour proposed
Vertical pole normalizing process.
To achieve these goals, present invention employs following technical solutions：
A kind of clutch of motorcycle control stick normalizing process is designed, is included the following steps：
S1, dimension control；
S2, upper tooling are fixed：By clutch of motorcycle control stick be fixed to positioning tool on, between adjacent control stick between
Away from maintenance 8-12cm；
S3, spraying antioxidation coating：Even application is carried out using electrostatic gun to the surface of clutch of motorcycle control stick to prevent
Oxide layer, spraying process make tooling at the uniform velocity be rotated together with clutch of motorcycle control stick by rotating mechanism, and rotating speed maintains
20-30rpm, so that each surface of control stick can be directed onto antioxidation coating；
S4, heating heating：Heating in-furnace temperature is risen to 700 DEG C, and protective gas is continuously passed through into heating furnace；
S5, Heat preservation：The control stick for spraying completion is sent into heating furnace, is heated to 800-950 DEG C, and keep the temperature 4-
8h；
S6, cooling are come out of the stove：Heating in-furnace temperature is quickly cooled to 400 DEG C, control stick is taken out later, is air-cooled to room temperature.
Preferably, the ingredient of antioxidant is as follows in parts by weight：10-15 parts of aluminate, 4-5 parts of ceramic,
20-30 parts of silicate, 0.5-1.5 parts of potassium fluoborate, 0.5-1.5 parts, 10-15 parts water of boron carbide.
Preferably, the volume ratio of mixed gas of the protective gas for nitrogen and helium, nitrogen and helium is 2: 1, protects gas
The flow of body is 15L/min.
Preferably, heating speed is 200-300 DEG C/h during Heat preservation.
Preferably, the specific practice of dimension control is：The size that drawing measures clutch of motorcycle control stick is compareed, control
Technological standards are determined if within fabrication error, arrange to reprocess it if beyond standard.
A kind of clutch of motorcycle control stick normalizing process proposed by the present invention, advantageous effect are：The present invention passes through spray
It applies antioxidation coating and injection protection gas two ways carries out control stick protection against oxidation, it is anti-oxidant so as to effectively improve its
Ability improves its service life.
Specific embodiment
The technical solution in the embodiment of the present invention is clearly and completely described below, it is clear that described embodiment
Only part of the embodiment of the present invention, instead of all the embodiments.
Embodiment 1
A kind of clutch of motorcycle control stick normalizing process, includes the following steps：
S1, dimension control；
S2, upper tooling are fixed：By clutch of motorcycle control stick be fixed to positioning tool on, between adjacent control stick between
Away from maintenance 8cm；
S3, spraying antioxidation coating：Even application is carried out using electrostatic gun to the surface of clutch of motorcycle control stick to prevent
Oxide layer, spraying process make tooling at the uniform velocity be rotated together with clutch of motorcycle control stick by rotating mechanism, and rotating speed maintains
20rpm, so that each surface of control stick can be directed onto antioxidation coating；
S4, heating heating：Heating in-furnace temperature is risen to 700 DEG C, and protective gas is continuously passed through into heating furnace；
S5, Heat preservation：The control stick for spraying completion is sent into heating furnace, is heated to 800 DEG C, and keep the temperature 4h；
S6, cooling are come out of the stove：Heating in-furnace temperature is quickly cooled to 400 DEG C, control stick is taken out later, is air-cooled to room temperature.
The ingredient of antioxidant is as follows in parts by weight：10 parts of aluminate, 4 parts of ceramic, 20 parts of silicate, fluorine
0.5 part of potassium borate, 0.5 part, 10 parts water of boron carbide.
The volume ratio of mixed gas of the protective gas for nitrogen and helium, nitrogen and helium is 2: 1, the flow of protective gas
For 15L/min.
Heating speed is 200 DEG C/h during Heat preservation.
The specific practice of dimension control is：The size that drawing measures clutch of motorcycle control stick is compareed, compares technique mark
Standard is determined if within fabrication error, arranges to reprocess it if beyond standard.
Embodiment 2
A kind of clutch of motorcycle control stick normalizing process, includes the following steps：
S1, dimension control；
S2, upper tooling are fixed：By clutch of motorcycle control stick be fixed to positioning tool on, between adjacent control stick between
Away from maintenance 10cm；
S3, spraying antioxidation coating：Even application is carried out using electrostatic gun to the surface of clutch of motorcycle control stick to prevent
Oxide layer, spraying process make tooling at the uniform velocity be rotated together with clutch of motorcycle control stick by rotating mechanism, and rotating speed maintains
22rpm, so that each surface of control stick can be directed onto antioxidation coating；
S4, heating heating：Heating in-furnace temperature is risen to 700 DEG C, and protective gas is continuously passed through into heating furnace；
S5, Heat preservation：The control stick for spraying completion is sent into heating furnace, is heated to 850 DEG C, and keep the temperature 5h；
S6, cooling are come out of the stove：Heating in-furnace temperature is quickly cooled to 400 DEG C, control stick is taken out later, is air-cooled to room temperature.
The ingredient of antioxidant is as follows in parts by weight：12 parts of aluminate, 4 parts of ceramic, 22 parts of silicate, fluorine
0.6 part of potassium borate, 0.6 part, 12 parts water of boron carbide.
The volume ratio of mixed gas of the protective gas for nitrogen and helium, nitrogen and helium is 2: 1, the flow of protective gas
For 15L/min.
Heating speed is 220 DEG C/h during Heat preservation.
The specific practice of dimension control is：The size that drawing measures clutch of motorcycle control stick is compareed, compares technique mark
Standard is determined if within fabrication error, arranges to reprocess it if beyond standard.
Embodiment 3
A kind of clutch of motorcycle control stick normalizing process, includes the following steps：
S1, dimension control；
S2, upper tooling are fixed：By clutch of motorcycle control stick be fixed to positioning tool on, between adjacent control stick between
Away from maintenance 11cm；
S3, spraying antioxidation coating：Even application is carried out using electrostatic gun to the surface of clutch of motorcycle control stick to prevent
Oxide layer, spraying process make tooling at the uniform velocity be rotated together with clutch of motorcycle control stick by rotating mechanism, and rotating speed maintains
25rpm, so that each surface of control stick can be directed onto antioxidation coating；
S4, heating heating：Heating in-furnace temperature is risen to 700 DEG C, and protective gas is continuously passed through into heating furnace；
S5, Heat preservation：The control stick for spraying completion is sent into heating furnace, is heated to 900 DEG C, and keep the temperature 6h；
S6, cooling are come out of the stove：Heating in-furnace temperature is quickly cooled to 400 DEG C, control stick is taken out later, is air-cooled to room temperature.
The ingredient of antioxidant is as follows in parts by weight：14 parts of aluminate, 5 parts of ceramic, 25 parts of silicate, fluorine
1.2 parts of potassium borate, 1.2 parts, 14 parts water of boron carbide.
The volume ratio of mixed gas of the protective gas for nitrogen and helium, nitrogen and helium is 2: 1, the flow of protective gas
For 15L/min.
Heating speed is 280 DEG C/h during Heat preservation.
The specific practice of dimension control is：The size that drawing measures clutch of motorcycle control stick is compareed, compares technique mark
Standard is determined if within fabrication error, arranges to reprocess it if beyond standard.
Embodiment 4
A kind of clutch of motorcycle control stick normalizing process, includes the following steps：
S1, dimension control；
S2, upper tooling are fixed：By clutch of motorcycle control stick be fixed to positioning tool on, between adjacent control stick between
Away from maintenance 12cm；
S3, spraying antioxidation coating：Even application is carried out using electrostatic gun to the surface of clutch of motorcycle control stick to prevent
Oxide layer, spraying process make tooling at the uniform velocity be rotated together with clutch of motorcycle control stick by rotating mechanism, and rotating speed maintains
30rpm, so that each surface of control stick can be directed onto antioxidation coating；
S4, heating heating：Heating in-furnace temperature is risen to 700 DEG C, and protective gas is continuously passed through into heating furnace；
S5, Heat preservation：The control stick for spraying completion is sent into heating furnace, is heated to 950 DEG C, and keep the temperature 8h；
S6, cooling are come out of the stove：Heating in-furnace temperature is quickly cooled to 400 DEG C, control stick is taken out later, is air-cooled to room temperature.
The ingredient of antioxidant is as follows in parts by weight：15 parts of aluminate, 5 parts of ceramic, 30 parts of silicate, fluorine
1.5 parts of potassium borate, 1.5 parts, 15 parts water of boron carbide.
The volume ratio of mixed gas of the protective gas for nitrogen and helium, nitrogen and helium is 2: 1, the flow of protective gas
For 15L/min.
Heating speed is 300 DEG C/h during Heat preservation.
The specific practice of dimension control is：The size that drawing measures clutch of motorcycle control stick is compareed, compares technique mark
Standard is determined if within fabrication error, arranges to reprocess it if beyond standard.
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto,
Any one skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (5)
1. a kind of clutch of motorcycle control stick normalizing process, which is characterized in that include the following steps：
S1, dimension control；
S2, upper tooling are fixed：Clutch of motorcycle control stick is fixed on positioning tool, the spacing dimension between adjacent control stick
Hold 8-12cm；
S3, spraying antioxidation coating：It is anti-oxidation that even application is carried out to the surface of clutch of motorcycle control stick using electrostatic gun
Layer, spraying process make tooling at the uniform velocity be rotated together with clutch of motorcycle control stick by rotating mechanism, and rotating speed maintains 20-
30rpm, so that each surface of control stick can be directed onto antioxidation coating；
S4, heating heating：Heating in-furnace temperature is risen to 700 DEG C, and protective gas is continuously passed through into heating furnace；
S5, Heat preservation：The control stick for spraying completion is sent into heating furnace, is heated to 800-950 DEG C, and keep the temperature 4-8h；
S6, cooling are come out of the stove：Heating in-furnace temperature is quickly cooled to 400 DEG C, control stick is taken out later, is air-cooled to room temperature.
2. a kind of clutch of motorcycle control stick normalizing process according to claim 1, which is characterized in that antioxidant
Ingredient is as follows in parts by weight：10-15 parts of aluminate, 4-5 parts of ceramic, 20-30 parts of silicate, potassium fluoborate 0.5-
1.5 parts, 0.5-1.5 parts, 10-15 parts water of boron carbide.
3. a kind of clutch of motorcycle control stick normalizing process according to claim 1, it is characterised in that：Protective gas is
The volume ratio of the mixed gas of nitrogen and helium, nitrogen and helium is 2: 1, and the flow of protective gas is 15L/min.
4. a kind of clutch of motorcycle control stick normalizing process according to claim 1, it is characterised in that：Heat preservation mistake
Heating speed is 200-300 DEG C/h in journey.
5. a kind of clutch of motorcycle control stick normalizing process according to claim 1, which is characterized in that dimension control
Specific practice is：The size that drawing measures clutch of motorcycle control stick is compareed, control technological standards are determined if in technique
Within error, arrange to reprocess it if beyond standard.