CN108178955A - A kind of woodenware special coating - Google Patents
A kind of woodenware special coating Download PDFInfo
- Publication number
- CN108178955A CN108178955A CN201810275404.XA CN201810275404A CN108178955A CN 108178955 A CN108178955 A CN 108178955A CN 201810275404 A CN201810275404 A CN 201810275404A CN 108178955 A CN108178955 A CN 108178955A
- Authority
- CN
- China
- Prior art keywords
- parts
- acrylic emulsion
- woodenware
- special coating
- aqueous
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention provides a kind of woodenware special coating, is made of the raw material of following parts by weight：14 18 parts of Ludox, 48 parts of tin oxide, 13 19 parts of poly- lotion, 10 16 parts of phenolic resin, 12 16 parts of feldspar powder, 15 19 parts of acrylic emulsion, 13 parts of coupling agent, 16 20 parts of aqueous acrylic emulsion, 57 parts of sodium tripolyphosphate, 12 16 parts of epoxy curing agent, 68 parts of aqueous color paste, 26 parts of grease, 48 parts of emulsifier, 35 parts of Antisepticize and mildew preventive, 9 13 parts of magnesium stearate.Absorption property of the present invention is good, and weatherability and closure are good, the paint film fast drying formed after use, can permanent retention uniform and smooth, there is the soft visual effect of low light, rich in gloss, can prevent dirt from adhering to.
Description
Technical field
The invention belongs to paint fields, and in particular to a kind of woodenware special coating.
Background technology
Coating is to be coated in the body surface protected or decorated, and can form the continuous thin of firm attachment with coated article
Film typically based on resin or oil or lotion, adds or does not add pigment, filler, add corresponding additive, use organic solvent
Or the thick liquid that water is formulated.And woodwork coating is used exclusively for a kind of material of timber-work surface spary, for U.S.
Change the surface of timber-work, and protect timber-work, there are the characteristics such as moisture-proof, water-fast, oil resistant, anti-corrosion.Commercially available woodenware applies
Although material contains the substance being harmful on a small quantity to human body and environment or environmental protection mostly but price is not cheap, some woodwork coatings
Not only complex procedures, and it is shorter to the protection period of timber-work, easily come off, it is impossible to digital preservation is carried out to timber, it can not
Meet technological requirement well.
Invention content
In order to solve prior art problem, the present invention provides a kind of woodenware special coating, and absorption property is good, weatherability and envelope
Closing property is good, the paint film fast drying formed after use, can permanent retention uniform and smooth, there is the soft visual effect of low light, it is rich
It is glossy, it can prevent dirt from adhering to.
To achieve the above object, technical solution provided by the present invention is：A kind of woodenware special coating, by following parts by weight
Raw material be made：14-18 parts of Ludox, 4-8 parts of tin oxide, lotion 13-19 parts poly-, 10-16 parts of phenolic resin, feldspar powder 12-
16 parts, 15-19 parts of acrylic emulsion, 1-3 parts of coupling agent, 16-20 parts of aqueous acrylic emulsion, 5-7 parts of sodium tripolyphosphate, epoxy
12-16 parts of resin curing agent, 6-8 parts of aqueous color paste, 2-6 parts of grease, 4-8 parts of emulsifier, 3-5 parts of Antisepticize and mildew preventive, stearic acid
9-13 parts of magnesium.
Preferably, the woodenware special coating is made of the raw material of following parts by weight：14 parts of Ludox, 4 parts of tin oxide,
Poly- 13 parts of lotion, 10 parts of phenolic resin, 12 parts of feldspar powder, 15 parts of acrylic emulsion, 1 part of coupling agent, aqueous acrylic emulsion 16
Part, 5 parts of sodium tripolyphosphate, 12 parts of epoxy curing agent, 6 parts of aqueous color paste, 2 parts of grease, 4 parts of emulsifier, Antisepticize and mildew preventive 3
Part, 9 parts of magnesium stearate.
Preferably, the woodenware special coating is made of the raw material of following parts by weight：16 parts of Ludox, 6 parts of tin oxide,
Poly- 16 parts of lotion, 13 parts of phenolic resin, 14 parts of feldspar powder, 17 parts of acrylic emulsion, 2 parts of coupling agent, aqueous acrylic emulsion 18
Part, 6 parts of sodium tripolyphosphate, 14 parts of epoxy curing agent, 7 parts of aqueous color paste, 4 parts of grease, 6 parts of emulsifier, Antisepticize and mildew preventive 4
Part, 11 parts of magnesium stearate.
Preferably, the woodenware special coating is made of the raw material of following parts by weight：18 parts of Ludox, 8 parts of tin oxide,
Poly- 19 parts of lotion, 16 parts of phenolic resin, 16 parts of feldspar powder, 19 parts of acrylic emulsion, 3 parts of coupling agent, aqueous acrylic emulsion 20
Part, 7 parts of sodium tripolyphosphate, 16 parts of epoxy curing agent, 8 parts of aqueous color paste, 6 parts of grease, 8 parts of emulsifier, Antisepticize and mildew preventive 5
Part, 13 parts of magnesium stearate.The present invention has the advantages that compared with prior art：
The present invention provides a kind of woodenware special coating, and absorption property is good, and weatherability and closure are good, the paint formed after use
Film fast drying, can permanent retention uniform and smooth, there is the soft visual effect of low light, rich in gloss, can prevent dirt from gluing
It is attached.
Specific embodiment
With reference to specific embodiment, the invention will be further described：
Embodiment 1：A kind of woodenware special coating, is made of the raw material of following parts by weight：14 parts of Ludox, 4 parts of tin oxide,
Poly- 13 parts of lotion, 10 parts of phenolic resin, 12 parts of feldspar powder, 15 parts of acrylic emulsion, 1 part of coupling agent, aqueous acrylic emulsion 16
Part, 5 parts of sodium tripolyphosphate, 12 parts of epoxy curing agent, 6 parts of aqueous color paste, 2 parts of grease, 4 parts of emulsifier, Antisepticize and mildew preventive 3
Part, 9 parts of magnesium stearate.
Embodiment 2：A kind of woodenware special coating, is made of the raw material of following parts by weight：16 parts of Ludox, 6 parts of tin oxide,
Poly- 16 parts of lotion, 13 parts of phenolic resin, 14 parts of feldspar powder, 17 parts of acrylic emulsion, 2 parts of coupling agent, aqueous acrylic emulsion 18
Part, 6 parts of sodium tripolyphosphate, 14 parts of epoxy curing agent, 7 parts of aqueous color paste, 4 parts of grease, 6 parts of emulsifier, Antisepticize and mildew preventive 4
Part, 11 parts of magnesium stearate.
Embodiment 3：A kind of woodenware special coating, is made of the raw material of following parts by weight：18 parts of Ludox, 8 parts of tin oxide,
Poly- 19 parts of lotion, 16 parts of phenolic resin, 16 parts of feldspar powder, 19 parts of acrylic emulsion, 3 parts of coupling agent, aqueous acrylic emulsion 20
Part, 7 parts of sodium tripolyphosphate, 16 parts of epoxy curing agent, 8 parts of aqueous color paste, 6 parts of grease, 8 parts of emulsifier, Antisepticize and mildew preventive 5
Part, 13 parts of magnesium stearate.
The examples of implementation of the above are only the preferred embodiments of the invention, and the implementation model of the present invention is not limited with this
It encloses, therefore the variation that all shape, principles according to the present invention are made, it should all cover within the scope of the present invention.
Claims (4)
1. a kind of woodenware special coating, which is characterized in that be made of the raw material of following parts by weight：14-18 parts of Ludox, tin oxide
4-8 parts, lotion 13-19 parts poly-, 10-16 parts of phenolic resin, 12-16 parts of feldspar powder, 15-19 parts of acrylic emulsion, coupling agent 1-3
Part, 16-20 parts of aqueous acrylic emulsion, 5-7 parts of sodium tripolyphosphate, 12-16 parts of epoxy curing agent, 6-8 parts of aqueous color paste,
2-6 parts of grease, 4-8 parts of emulsifier, 3-5 parts of Antisepticize and mildew preventive, 9-13 parts of magnesium stearate.
2. a kind of woodenware special coating according to claim 1, which is characterized in that be made of the raw material of following parts by weight：
14 parts of Ludox, 4 parts of tin oxide, 13 parts of poly- lotion, 10 parts of phenolic resin, 12 parts of feldspar powder, 15 parts of acrylic emulsion, coupling agent
1 part, 16 parts of aqueous acrylic emulsion, 5 parts of sodium tripolyphosphate, 12 parts of epoxy curing agent, 6 parts of aqueous color paste, 2 parts of grease,
4 parts of emulsifier, 3 parts of Antisepticize and mildew preventive, 9 parts of magnesium stearate.
3. a kind of woodenware special coating according to claim 1, which is characterized in that be made of the raw material of following parts by weight：
16 parts of Ludox, 6 parts of tin oxide, 16 parts of poly- lotion, 13 parts of phenolic resin, 14 parts of feldspar powder, 17 parts of acrylic emulsion, coupling agent
2 parts, 18 parts of aqueous acrylic emulsion, 6 parts of sodium tripolyphosphate, 14 parts of epoxy curing agent, 7 parts of aqueous color paste, 4 parts of grease,
6 parts of emulsifier, 4 parts of Antisepticize and mildew preventive, 11 parts of magnesium stearate.
4. a kind of woodenware special coating according to claim 1, which is characterized in that be made of the raw material of following parts by weight：
18 parts of Ludox, 8 parts of tin oxide, 19 parts of poly- lotion, 16 parts of phenolic resin, 16 parts of feldspar powder, 19 parts of acrylic emulsion, coupling agent
3 parts, 20 parts of aqueous acrylic emulsion, 7 parts of sodium tripolyphosphate, 16 parts of epoxy curing agent, 8 parts of aqueous color paste, 6 parts of grease,
8 parts of emulsifier, 5 parts of Antisepticize and mildew preventive, 13 parts of magnesium stearate.