CN108165108A - A kind of steel pipe anticorrosion paint preparation method - Google Patents
A kind of steel pipe anticorrosion paint preparation method Download PDFInfo
- Publication number
- CN108165108A CN108165108A CN201711451662.0A CN201711451662A CN108165108A CN 108165108 A CN108165108 A CN 108165108A CN 201711451662 A CN201711451662 A CN 201711451662A CN 108165108 A CN108165108 A CN 108165108A
- Authority
- CN
- China
- Prior art keywords
- parts
- steel pipe
- anticorrosion paint
- paint preparation
- pipe anticorrosion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
A kind of steel pipe anticorrosion paint preparation method disclosed by the invention, meter includes following component in parts by weight, 5 15 parts of polyvinyl acetate resin, 13 parts of sodium bicarbonate, 26 parts of phosphomolybdate, 13 parts of sodium chlorate, 39 parts of chlorinated paraffin, 13 parts of silica flour, 5 15 parts of kaolin, 100 300 parts of deionized water, ingredient is simple, configuration is convenient, cost is relatively low, favorable anti-corrosion effect, it is non-hazardous, it is convenient to facilitate, need not coating operation be carried out repeatedly, save a large amount of human and material resources, can more meet the needs of user.
Description
Technical field
The invention belongs to rust remover fields, and in particular to a kind of anticorrosive paint.
Background technology
Anticorrosive paint is generally divided into conventional anticorrosive paint and anticorrosive paint, is essential one kind in paint
Coating.Conventional anticorrosive paint is under general condition, to play the role of the longevity etch-proof, protection non-ferrous metal uses to metal etc.
Life；It for anticorrosive paint refers to relatively conventional anticorrosive paint, can be applied in relatively harsh corrosive environment, and have and can reach
A kind of anticorrosive paint of protection period longer than conventional anticorrosive paint.However existing anticorrosive paint anti-corrosion effect is poor, uses one
The phenomenon that cracking is often generated after the section time and is come off, needs coating repeatedly to can be only achieved corrosion-resistant effect, and cost is higher,
It can not meet the demand of user.
Invention content
In view of the above-mentioned problems, the invention discloses a kind of steel pipe anticorrosion paint preparation methods.
Specific technical solution is as follows：
A kind of steel pipe anticorrosion paint preparation method, preparation method are as follows：
（1）Following components, 5-15 parts of polyvinyl acetate resin, 1-3 parts of sodium bicarbonate, phosphomolybdate 2-6 are weighed by weight
Part, 1-3 parts of sodium chlorate, 3-9 parts of chlorinated paraffin, 1-3 parts of silica flour, 5-15 parts of kaolin, 100-300 parts of deionized water；
（2）Polyvinyl acetate resin, sodium bicarbonate and deionized water are put into reaction kettle, at 20 DEG C -30 DEG C, uniform stirring
10-20min；
（3）After temperature is promoted to 35 DEG C -45 DEG C, phosphomolybdate is added in, continues to stir 5-15 min；
（4）After temperature is promoted to 50 DEG C -60 DEG C, sodium chlorate and chlorinated paraffin are added in, continues to stir 15-45min；
（5）After temperature is promoted to 70 DEG C -80 DEG C, silica flour and kaolin are added in, continues to stir 10-30min；
（6）After temperature is promoted to 85 DEG C -100 DEG C, reaction kettle is closed, reactant is taken out and is positioned over ventilation 7-9h, you can
Finished product.
A kind of above-mentioned steel pipe anticorrosion paint preparation method, wherein, the ratio of the polyvinyl acetate resin and sodium bicarbonate
Example is 5：1.
A kind of above-mentioned steel pipe anticorrosion paint preparation method, wherein, the ratio of the phosphomolybdate and sodium chlorate is 2：1.
A kind of above-mentioned steel pipe anticorrosion paint preparation method, wherein, the ratio of the chlorinated paraffin and silica flour is 3：1.
A kind of above-mentioned steel pipe anticorrosion paint preparation method, wherein, the ratio of the kaolin and deionized water is 1：20.
Beneficial effects of the present invention are：
A kind of steel pipe anticorrosion paint preparation method disclosed by the invention, in parts by weight meter include following component, polyvinyl acetate
5-15 parts of resin, 1-3 parts of sodium bicarbonate, 2-6 parts of phosphomolybdate, 1-3 parts of sodium chlorate, 3-9 parts of chlorinated paraffin, 1-3 parts of silica flour,
5-15 parts of kaolin, 100-300 parts of deionized water, ingredient is simple, and configuration is convenient, and cost is relatively low, favorable anti-corrosion effect, non-hazardous,
It is convenient to facilitate, without repeatedly carry out coating operation, save a large amount of human and material resources, can more meet the needs of user.
Specific embodiment
A kind of steel pipe anticorrosion paint preparation method, preparation method are as follows：
（1）Following components, 5-15 parts of polyvinyl acetate resin, 1-3 parts of sodium bicarbonate, phosphomolybdate 2-6 are weighed by weight
Part, 1-3 parts of sodium chlorate, 3-9 parts of chlorinated paraffin, 1-3 parts of silica flour, 5-15 parts of kaolin, 100-300 parts of deionized water；
（2）Polyvinyl acetate resin, sodium bicarbonate and deionized water are put into reaction kettle, at 20 DEG C -30 DEG C, uniform stirring
10-20min；
（3）After temperature is promoted to 35 DEG C -45 DEG C, phosphomolybdate is added in, continues to stir 5-15 min；
（4）After temperature is promoted to 50 DEG C -60 DEG C, sodium chlorate and chlorinated paraffin are added in, continues to stir 15-45min；
（5）After temperature is promoted to 70 DEG C -80 DEG C, silica flour and kaolin are added in, continues to stir 10-30min；
（6）After temperature is promoted to 85 DEG C -100 DEG C, reaction kettle is closed, reactant is taken out and is positioned over ventilation 7-9h, you can
Finished product.
A kind of above-mentioned steel pipe anticorrosion paint preparation method, wherein, the ratio of the polyvinyl acetate resin and sodium bicarbonate
Example is 5：1.
A kind of above-mentioned steel pipe anticorrosion paint preparation method, wherein, the ratio of the phosphomolybdate and sodium chlorate is 2：1.
A kind of above-mentioned steel pipe anticorrosion paint preparation method, wherein, the ratio of the chlorinated paraffin and silica flour is 3：1.
A kind of above-mentioned steel pipe anticorrosion paint preparation method, wherein, the ratio of the kaolin and deionized water is 1：20.
A kind of steel pipe anticorrosion paint preparation method disclosed by the invention, in parts by weight meter include following component, poly-vinegar acid
5-15 parts of vinyl, 1-3 parts of sodium bicarbonate, 2-6 parts of phosphomolybdate, 1-3 parts of sodium chlorate, 3-9 parts of chlorinated paraffin, silica flour 1-
3 parts, 5-15 parts of kaolin, 100-300 parts of deionized water, ingredient is simple, and configuration is convenient, and cost is relatively low, favorable anti-corrosion effect, no danger
Evil, it is convenient to facilitate, without repeatedly carry out coating operation, save a large amount of human and material resources, can more meet the needs of user.
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto,
Any one skilled in the art in the technical scope disclosed by the present invention, the change or replacement that can be readily occurred in,
Should all it cover within the scope of the present invention.Therefore, protection scope of the present invention should be with the protection domain of claims
Subject to.
Claims (5)
1. a kind of steel pipe anticorrosion paint preparation method, it is characterized in that, preparation method is as follows：
（1）Following components, 5-15 parts of polyvinyl acetate resin, 1-3 parts of sodium bicarbonate, phosphomolybdate 2-6 are weighed by weight
Part, 1-3 parts of sodium chlorate, 3-9 parts of chlorinated paraffin, 1-3 parts of silica flour, 5-15 parts of kaolin, 100-300 parts of deionized water；
（2）Polyvinyl acetate resin, sodium bicarbonate and deionized water are put into reaction kettle, at 20 DEG C -30 DEG C, uniform stirring
10-20min；
（3）After temperature is promoted to 35 DEG C -45 DEG C, phosphomolybdate is added in, continues to stir 5-15 min；
（4）After temperature is promoted to 50 DEG C -60 DEG C, sodium chlorate and chlorinated paraffin are added in, continues to stir 15-45min；
（5）After temperature is promoted to 70 DEG C -80 DEG C, silica flour and kaolin are added in, continues to stir 10-30min；
（6）After temperature is promoted to 85 DEG C -100 DEG C, reaction kettle is closed, reactant is taken out and is positioned over ventilation 7-9h, you can
Finished product.
2. a kind of steel pipe anticorrosion paint preparation method as described in claim 1, it is characterized in that, the polyvinyl acetate resin with
The ratio of sodium bicarbonate is 5：1.
3. a kind of steel pipe anticorrosion paint preparation method as described in claim 1, it is characterized in that, the phosphomolybdate and sodium chlorate
Ratio be 2：1.
4. a kind of steel pipe anticorrosion paint preparation method as described in claim 1, it is characterized in that, the chlorinated paraffin and silica flour
Ratio be 3：1.
5. a kind of steel pipe anticorrosion paint preparation method as described in claim 1, it is characterized in that, the kaolin and deionized water
Ratio be 1：20.