CN108158130A - A kind of insole of deodorant wear-resisting and preparation method thereof - Google Patents
A kind of insole of deodorant wear-resisting and preparation method thereof Download PDFInfo
- Publication number
- CN108158130A CN108158130A CN201711343075.XA CN201711343075A CN108158130A CN 108158130 A CN108158130 A CN 108158130A CN 201711343075 A CN201711343075 A CN 201711343075A CN 108158130 A CN108158130 A CN 108158130A
- Authority
- CN
- China
- Prior art keywords
- insole
- parts
- bamboo charcoal
- deodorant
- wear
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to insole manufacturing technology fields, and in particular to a kind of insole of deodorant wear-resisting and preparation method thereof；The insole raw material include：Bamboo charcoal micropowder, viscose, 5~10 parts of radix ephedrae, glutinous rice root, 5~15 parts of schizonepeta, safflower 5~10, appropriate deionized water；The present invention provides a kind of insoles of deodorant wear-resisting and preparation method thereof, this method is using bamboo charcoal fiber as the main material that insole is made, and it is internally provided with the liner containing Chinese medicine in insole, wherein radix ephedrae is used in combination with schizonepeta can have the function that hidroschesis decompression and inhibiting bacteria and diminishing inflammation, additionally due to Chinese medicine is carried out to the processing of ashing guarantor property can allow pharmacological property through carbonization outer layer sustained release to outside, so as to prolong the service life, the waste of pharmacological property is not generated, since medicinal material is crushed into powder, therefore carburizing temperature can also decline many, save the energy；In addition the coating process carried out to insole bottom can also permeate up the efficacy of a drug, preferably reach predetermined purpose.
Description
Technical field
The present invention relates to insole manufacturing technology fields, and in particular to a kind of insole of deodorant wear-resisting and preparation method thereof.
Background technology
Insole is widely used in shoe industry, health care and specifically functional, is generally divided into the applied insole of shoe industry and market
Commodity-type both of which.The insole of shoe industry application mainly coordinates shoes outsole, midsole, makes corresponding type body；According to last carving
Bottom plate or panel make size plate, and produce corresponding shape.Marketing type insole mainly insole directly as
A kind of commodity selling, by developing teacher's design, the product to circulate on the market.
Insole can be subdivided by effect：Health insoles, the i.e. insole to human body unsoundness benefit；Such as：Antibacterial insoles,
Antibromic shoe pads, Chinese medicine insole etc.；Functional insole：Have specifically functional footwear to pad.Such as：Antistatic insole, height-increasing insole, waterproof
Insole, air circulation insole etc.；Conventional insole：Do not have the insole of more than characteristic, be the most common type.
Traditional Antibromic shoe pads are mostly used as suction-operated using activated carbon or porous material, but this kind of insole is reached in material
Deodorizing capability is just very faint after to the absorption upper limit, usually replaces again very uneconomical.
Invention content
In view of the deficiencies of the prior art, the present invention provides a kind of insole of deodorant wear-resisting and preparation method thereof, this method
The insole with deodorization functions can be made, the Chinese medicine particle of hidroschesis tonifying Qi is additionally provided in the insole in addition, while deodorization
The generation of stink can fundamentally be reduced.
In order to achieve the above object, the present invention is achieved by the following technical programs：
A kind of insole of deodorant wear-resisting is made of the raw material of following each component number：20~30 parts of bamboo charcoal micropowder, viscose
80~100 parts, 5~10 parts of radix ephedrae, 5~10 parts of glutinous rice root, 5~15 parts of schizonepeta, 5~10 parts of safflower, appropriate deionized water.
A kind of preparation method of the insole of deodorant wear-resisting includes the following steps：
A. it is dry broken：Radix ephedrae, glutinous rice root, schizonepeta and safflower are weighed, and these raw materials are put into baking oven by number
Drying, places into and ball milling is carried out in ball mill；
B. ashing sustainability：The raw material powder obtained through step a is respectively put into baking oven and is toasted, treats powder surface coke
Stop baking after black, obtain medicinal powder a；
C. prepared by bamboo charcoal micropowder lotion：Will bamboo charcoal micropowder add in viscose in, carry out magnetic agitation, it is to be mixed uniformly after again
Become bamboo charcoal fibre yarns a through spinning-drawing machine spinning；
D. batch mixing：Bamboo charcoal fibre yarns are put into the medicinal powder obtained through step b in deionized water and are heated, and are being heated
It is persistently stirred in the process, bamboo charcoal fibre yarns b is obtained after deionized water is evaporated；
E. it weaves：The bamboo charcoal fibre yarns b obtained through step d is woven into insole liner, and weave using bamboo charcoal fibre yarns a
Into insole housing, and using spandex fiber stoste insole bottom is coated to get to finished product insole；
Preferably, the viscose is made of the raw material of following parts by weight：25~35 parts of phthalic anhydride is carried from natural plants
5~15 parts of the furfuryl alcohol taken, 15~25 parts of neoprene, 15~20 parts of dimethyl carbonate, 1~5 part of benzoyl peroxide, acetic acid second
5~10 parts of ester, 10~15 parts of methylcellulose, 20~40 parts of deionized water.
Preferably, the raw material particle size in the step a after ball milling is 100~500 mesh.
Preferably, the temperature set in the step b baking ovens is 300~500 DEG C.
Preferably, heating temperature is 70~90 DEG C in the step d.
Advantageous effect：
The present invention provides a kind of insole of deodorant wear-resisting and preparation method thereof, this method is using bamboo charcoal fiber as being made
The main material of insole, and the liner containing Chinese medicine is internally provided in insole, wherein radix ephedrae is used in combination with schizonepeta and can reach
Hidroschesis is depressured and the effect of inhibiting bacteria and diminishing inflammation, additionally due to Chinese medicine is carried out to the processing of ashing guarantor property can allow pharmacological property through carbonization
Outer layer is sustained to outside, so as to prolong the service life, does not generate the waste of pharmacological property, since medicinal material is crushed into powder, because
This carburizing temperature can also decline many, save the energy；In addition the coating process carried out to insole bottom can also make the efficacy of a drug upward
Infiltration, preferably reaches predetermined purpose.
Specific embodiment
Purpose, technical scheme and advantage to make the embodiment of the present invention are clearer, below in conjunction with the embodiment of the present invention,
Technical solution in the embodiment of the present invention is clearly and completely described, it is clear that described embodiment is the present invention one
Divide embodiment, instead of all the embodiments.Based on the embodiments of the present invention, those of ordinary skill in the art are not making
All other embodiments obtained under the premise of creative work, shall fall within the protection scope of the present invention.
Embodiment 1：
A kind of insole of deodorant wear-resisting is made of the raw material of following each component number：20 parts of bamboo charcoal micropowder, viscose 100
Part, 8 parts of radix ephedrae, 5 parts of glutinous rice root, 15 parts of schizonepeta, 10 parts of safflower, appropriate deionized water.
A kind of preparation method of the insole of deodorant wear-resisting includes the following steps：
A. it is dry broken：Radix ephedrae, glutinous rice root, schizonepeta and safflower are weighed, and these raw materials are put into baking oven by number
Drying, places into and ball milling is carried out in ball mill；
B. ashing sustainability：The raw material powder obtained through step a is respectively put into baking oven and is toasted, treats powder surface coke
Stop baking after black, obtain medicinal powder a；
C. prepared by bamboo charcoal micropowder lotion：Will bamboo charcoal micropowder add in viscose in, carry out magnetic agitation, it is to be mixed uniformly after again
Become bamboo charcoal fibre yarns a through spinning-drawing machine spinning；
D. batch mixing：Bamboo charcoal fibre yarns are put into the medicinal powder obtained through step b in deionized water and are heated, and are being heated
It is persistently stirred in the process, bamboo charcoal fibre yarns b is obtained after deionized water is evaporated；
E. it weaves：The bamboo charcoal fibre yarns b obtained through step d is woven into insole liner, and weave using bamboo charcoal fibre yarns a
Into insole housing, and using spandex fiber stoste insole bottom is coated to get to finished product insole；
Preferably, the viscose is made of the raw material of following parts by weight：30 parts of phthalic anhydride is extracted from natural plants
15 parts of furfuryl alcohol, 20 parts of neoprene, 20 parts of dimethyl carbonate, 2 parts of benzoyl peroxide, 5 parts of ethyl acetate, methylcellulose 15
Part, 30 parts of deionized water.
Preferably, the raw material particle size in the step a after ball milling is 500 mesh.
Preferably, the temperature set in the step b baking ovens is 400 DEG C.
Preferably, heating temperature is 90 DEG C in the step d.
After tested, extracting 30, there is the people of foot odour and pin sweat symptom to use the insole prepared by embodiment 1, make daily
With the insole five hours or more, to be paid a return visit after treatment in 30 days, the pin sweat symptom that 22 people are shared through investigation obtains significant changes,
The pin sweat symptom of 4 people to slight relief, 2 people are without substantially changeing；The foot odour of 24 people is relieved, and the foot odour of 6 people obtains
Slight relief is arrived.
Embodiment 2：
A kind of insole of deodorant wear-resisting is made of the raw material of following each component number：25 parts of bamboo charcoal micropowder, viscose 90
Part, 10 parts of radix ephedrae, 8 parts of glutinous rice root, 10 parts of schizonepeta, 5 parts of safflower, appropriate deionized water.
A kind of preparation method of the insole of deodorant wear-resisting includes the following steps：
A. it is dry broken：Radix ephedrae, glutinous rice root, schizonepeta and safflower are weighed, and these raw materials are put into baking oven by number
Drying, places into and ball milling is carried out in ball mill；
B. ashing sustainability：The raw material powder obtained through step a is respectively put into baking oven and is toasted, treats powder surface coke
Stop baking after black, obtain medicinal powder a；
C. prepared by bamboo charcoal micropowder lotion：Will bamboo charcoal micropowder add in viscose in, carry out magnetic agitation, it is to be mixed uniformly after again
Become bamboo charcoal fibre yarns a through spinning-drawing machine spinning；
D. batch mixing：Bamboo charcoal fibre yarns are put into the medicinal powder obtained through step b in deionized water and are heated, and are being heated
It is persistently stirred in the process, bamboo charcoal fibre yarns b is obtained after deionized water is evaporated；
E. it weaves：The bamboo charcoal fibre yarns b obtained through step d is woven into insole liner, and weave using bamboo charcoal fibre yarns a
Into insole housing, and using spandex fiber stoste insole bottom is coated to get to finished product insole；
Preferably, the viscose is made of the raw material of following parts by weight：35 parts of phthalic anhydride is extracted from natural plants
10 parts of furfuryl alcohol, 25 parts of neoprene, 15 parts of dimethyl carbonate, 5 parts of benzoyl peroxide, 8 parts of ethyl acetate, methylcellulose 12
Part, 25 parts of deionized water.
Preferably, the raw material particle size in the step a after ball milling is 400 mesh.
Preferably, the temperature set in the step b baking ovens is 300 DEG C.
Preferably, heating temperature is 80 DEG C in the step d.
After tested, extracting 30, there is the people of foot odour and pin sweat symptom to use the insole prepared by embodiment 2, make daily
With the insole five hours or more, to be paid a return visit after treatment in 30 days, the pin sweat symptom that 24 people are shared through investigation obtains significant changes,
The pin sweat symptom of 4 five people to slight relief, 2 people are without substantially changeing；The foot odour of 26 people is relieved, the foot odour of 4 people
Slight relief is obtained.
Embodiment 3：
A kind of insole of deodorant wear-resisting is made of the raw material of following each component number：30 parts of bamboo charcoal micropowder, viscose 80
Part, 5 parts of radix ephedrae, 10 parts of glutinous rice root, 5 parts of schizonepeta, 8 parts of safflower, appropriate deionized water.
A kind of preparation method of the insole of deodorant wear-resisting includes the following steps：
A. it is dry broken：Radix ephedrae, glutinous rice root, schizonepeta and safflower are weighed, and these raw materials are put into baking oven by number
Drying, places into and ball milling is carried out in ball mill；
B. ashing sustainability：The raw material powder obtained through step a is respectively put into baking oven and is toasted, treats powder surface coke
Stop baking after black, obtain medicinal powder a；
C. prepared by bamboo charcoal micropowder lotion：Will bamboo charcoal micropowder add in viscose in, carry out magnetic agitation, it is to be mixed uniformly after again
Become bamboo charcoal fibre yarns a through spinning-drawing machine spinning；
D. batch mixing：Bamboo charcoal fibre yarns are put into the medicinal powder obtained through step b in deionized water and are heated, and are being heated
It is persistently stirred in the process, bamboo charcoal fibre yarns b is obtained after deionized water is evaporated；
E. it weaves：The bamboo charcoal fibre yarns b obtained through step d is woven into insole liner, and weave using bamboo charcoal fibre yarns a
Into insole housing, and using spandex fiber stoste insole bottom is coated to get to finished product insole；
Preferably, the viscose is made of the raw material of following parts by weight：30 parts of phthalic anhydride is extracted from natural plants
5 parts of furfuryl alcohol, 15 parts of neoprene, 15 parts of dimethyl carbonate, 1 part of benzoyl peroxide, 7 parts of ethyl acetate, methylcellulose 12
Part, 20 parts of deionized water.
Preferably, the raw material particle size in the step a after ball milling is 100 mesh.
Preferably, the temperature set in the step b baking ovens is 500 DEG C.
Preferably, heating temperature is 90 DEG C in the step d.
After tested, extracting 30, there is the people of foot odour and pin sweat symptom to use the insole prepared by embodiment 3, make daily
With the insole five hours or more, to be paid a return visit after treatment in 30 days, the pin sweat symptom that 21 people are shared through investigation obtains significant changes,
The pin sweat symptom of 5 people to slight relief, 4 people are without substantially changeing；The foot odour of 23 people is relieved, and the foot odour of 6 people obtains
Slight relief is arrived, the foot odour of 1 people is without significant change.
Embodiment 4：
A kind of insole of deodorant wear-resisting is made of the raw material of following each component number：20 parts of bamboo charcoal micropowder, viscose 90
Part, 5 parts of radix ephedrae, 10 parts of glutinous rice root, 10 parts of schizonepeta, 5 parts of safflower, appropriate deionized water.
A kind of preparation method of the insole of deodorant wear-resisting includes the following steps：
A. it is dry broken：Radix ephedrae, glutinous rice root, schizonepeta and safflower are weighed, and these raw materials are put into baking oven by number
Drying, places into and ball milling is carried out in ball mill；
B. ashing sustainability：The raw material powder obtained through step a is respectively put into baking oven and is toasted, treats powder surface coke
Stop baking after black, obtain medicinal powder a；
C. prepared by bamboo charcoal micropowder lotion：Will bamboo charcoal micropowder add in viscose in, carry out magnetic agitation, it is to be mixed uniformly after again
Become bamboo charcoal fibre yarns a through spinning-drawing machine spinning；
D. batch mixing：Bamboo charcoal fibre yarns are put into the medicinal powder obtained through step b in deionized water and are heated, and are being heated
It is persistently stirred in the process, bamboo charcoal fibre yarns b is obtained after deionized water is evaporated；
E. it weaves：The bamboo charcoal fibre yarns b obtained through step d is woven into insole liner, and weave using bamboo charcoal fibre yarns a
Into insole housing, and using spandex fiber stoste insole bottom is coated to get to finished product insole；
Preferably, the viscose is made of the raw material of following parts by weight：25 parts of phthalic anhydride is extracted from natural plants
9 parts of furfuryl alcohol, 20 parts of neoprene, 20 parts of dimethyl carbonate, 2 parts of benzoyl peroxide, 10 parts of ethyl acetate, methylcellulose 10
Part, 40 parts of deionized water.
Preferably, the raw material particle size in the step a after ball milling is 200 mesh.
Preferably, the temperature set in the step b baking ovens is 450 DEG C.
Preferably, heating temperature is 70 DEG C in the step d.
After tested, extracting 30, there is the people of foot odour and pin sweat symptom to use the insole prepared by embodiment 4, make daily
With the insole five hours or more, to be paid a return visit after treatment in 30 days, the pin sweat symptom that 23 people are shared through investigation obtains significant changes,
The pin sweat symptom of five people to slight relief, 2 people are without substantially changeing；The foot odour of 25 people is relieved, and the foot odour of 5 people obtains
Slight relief is arrived.
It should be noted that herein, relational terms such as first and second and the like are used merely to a reality
Body or operation are distinguished with another entity or operation, are deposited without necessarily requiring or implying between these entities or operation
In any this practical relationship or sequence.Moreover, term " comprising ", "comprising" or its any other variant are intended to
Non-exclusive inclusion, so that process, method, article or equipment including a series of elements not only will including those
Element, but also including other elements that are not explicitly listed or further include as this process, method, article or equipment
Intrinsic element.In the absence of more restrictions, the element limited by sentence "including a ...", it is not excluded that
Also there are other identical elements in process, method, article or equipment including the element.
The above embodiments are merely illustrative of the technical solutions of the present invention, rather than its limitations；Although with reference to the foregoing embodiments
The present invention is described in detail, it will be understood by those of ordinary skill in the art that：It still can be to aforementioned each implementation
Technical solution recorded in example modifies or carries out equivalent replacement to which part technical characteristic；And these modification or
It replaces, the spirit and scope for various embodiments of the present invention technical solution that it does not separate the essence of the corresponding technical solution.
Claims (6)
1. a kind of insole of deodorant wear-resisting, which is characterized in that be made of the raw material of following each component number：Bamboo charcoal micropowder 20~30
Part, 80~100 parts of viscose, 5~10 parts of radix ephedrae, 5~10 parts of glutinous rice root, 5~15 parts of schizonepeta, 5~10 parts of safflower, deionization
Appropriate amount of water.
2. a kind of insole of deodorant wear-resisting, which is characterized in that preparation method includes the following steps：
A. it is dry broken：Radix ephedrae, glutinous rice root, schizonepeta and safflower are weighed, and these raw materials are put into baking oven and are dried by number,
It places into and ball milling is carried out in ball mill；
B. ashing sustainability：The raw material powder obtained through step a is respectively put into baking oven and is toasted, after burned black after powder surface
Stop baking, obtain medicinal powder a；
C. prepared by bamboo charcoal micropowder lotion：Will bamboo charcoal micropowder add in viscose in, carry out magnetic agitation, it is to be mixed uniformly after again through spin
The spinning of silk machine becomes bamboo charcoal fibre yarns a；
D. batch mixing：Bamboo charcoal fibre yarns are put into the medicinal powder obtained through step b in deionized water and are heated, and in heating process
In be persistently stirred, bamboo charcoal fibre yarns b is obtained after deionized water is evaporated；
E. it weaves：The bamboo charcoal fibre yarns b obtained through step d is woven into insole liner, and be woven into footwear using bamboo charcoal fibre yarns a
Housing is padded, and using spandex fiber stoste insole bottom is coated to get to finished product insole.
3. the insole of a kind of deodorant wear-resisting according to claim 1, which is characterized in that prepared by viscose：The viscose
It is made of the raw material of following parts by weight：25~35 parts of phthalic anhydride, 5~15 parts of furfuryl alcohol, the neoprene extracted from natural plants
15~25 parts, 15~20 parts of dimethyl carbonate, 1~5 part of benzoyl peroxide, 4~10 parts of ethyl acetate, methylcellulose 10~
15 parts, 20~40 parts of deionized water.
A kind of 4. insole of deodorant wear-resisting according to claim 2, which is characterized in that the original in the step a after ball milling
Material grain size is 100~500 mesh.
5. the insole of a kind of deodorant wear-resisting according to claim 2, which is characterized in that set in the step b baking ovens
Temperature is 300~500 DEG C.
6. the insole of a kind of deodorant wear-resisting according to claim 2, which is characterized in that heating temperature is in the step d
70~90 DEG C.