CN108130815A - Outdoor high strengthening plate facing body paper and preparation method thereof - Google Patents
Outdoor high strengthening plate facing body paper and preparation method thereof Download PDFInfo
- Publication number
- CN108130815A CN108130815A CN201711402648.1A CN201711402648A CN108130815A CN 108130815 A CN108130815 A CN 108130815A CN 201711402648 A CN201711402648 A CN 201711402648A CN 108130815 A CN108130815 A CN 108130815A
- Authority
- CN
- China
- Prior art keywords
- body paper
- strengthening plate
- plate facing
- facing body
- high strengthening
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention belongs to pulp technology for making paper, and in particular to a kind of open air high strengthening plate facing body paper and preparation method thereof.It is made of following raw material：Wood pulp, filler, auxiliary agent and pigment, auxiliary agent are made of sodium hydroxide, sulfuric acid, aluminum sulfate and wet strength agent；Filler by titanium dioxide, magnesium silicate and kaolin group into.The outdoor high strengthening plate facing body paper that the present invention makes has good covering, fiber distributing homogeneity, paper surface exquisiteness, and corrosion resistance is strong, sun-proof grade is high, Washing is high；PH is dipped into after impregnated melamine veneer from 3.5 10 solution, paper do not occur bubbling, deformation phenomena such as；For sun-proof grade at 6 grades or more, Washing is high.It is highly practical invention also provides the preparation method of outdoor high strengthening plate facing body paper, operate scientific and reasonable, simple possible.
Description
Technical field
The invention belongs to pulp technology for making paper, and in particular to a kind of open air high strengthening plate facing body paper and its preparation side
Method.
Background technology
Common finishing paper is a kind of ornament materials for being widely used in house fitting-up.Body paper prints through downstream, impregnates trimerization
Make ornament materials after cyanamide, veneer, there are surface not anti-pollution, easily fade, it is not corrosion-resistant the shortcomings of.Common ceramic tile, water
The traditional decorations material such as mud, PVC, color and luster is dull, and pattern is old, can not meet the requirement of modern exterior decoration.With section
The continuous development of technology and the continuous improvement of living standards of the people, building decoration is towards environmental protection, high intensity, customization of individual character
The direction of change is developed.
Invention content
In view of the deficiencies of the prior art, the object of the present invention is to provide a kind of outdoor high strengthening plate facing body paper, have
Good covering, fiber distributing homogeneity, paper surface are fine and smooth, and corrosion resistance is strong, good permeability, sun-proof grade are high, washing
Color fastness is high；Highly practical invention also provides the preparation method of outdoor high strengthening plate facing body paper, operation science is closed
Reason, simple possible.
Open air high strengthening plate facing body paper of the present invention, is made of the raw material of following weight percent：
Wherein, auxiliary agent is made of the raw material of following weight percent：
Filler is made of the raw material of following weight percent：
Titanium dioxide 60%-90%
Magnesium silicate 10%-40%
Kaolin 0%-10%.
Preferably, outdoor high strengthening plate facing body paper of the present invention, is made of the raw material of following weight percent：
Filler is made of the raw material of following weight percent：
Titanium dioxide 70%-78%
Magnesium silicate 20%-28%
Kaolin 2%-5%.
The wood pulp is made of the raw material of following weight percent：
Staple fiber wood pulp 90%-100%
Long fibre wood pulp 0%-10%.
Preferably, wood pulp is made of the raw material of following weight percent：
Staple fiber wood pulp 95%-98%
Long fibre wood pulp 2%-5%.
The titanium dioxide is titanium dioxide R796 (suppliers：Dupont titanium dioxide R796), which have passed through table
Bread, which covers processing, particle size, particle diameter distribution, dispersibility, weatherability, oil absorption, whiteness etc., will be better than traditional titanium dioxide, this
The raising of outer high strengthening plate facing body paper covering is mainly used as in invention, improves the fine and smooth degree of paper surface.
Magnesium silicate (supplier：HUBER)：The magnesium silicate provided using J.M.HUBER INDIAPRIVATE LIMITED,
The bulk and gas permeability of paper are effectively improved, is conducive to surface printing effect and dipping pressing plate processing, while ensure paper
Heat-resistant stability
Kaolin (supplier：The Inner Mongol surpasses board kaolin)：Auxiliary titanium dioxide carries out covering raising in the present invention, promotes
Printing performance improves, and improves ash content of paper content, reduces production cost.
Aluminum sulfate (supplier：Powerful water-purifying material Co., Ltd)：Have the function of to adjust pH value, improve paper pulp mixed liquor electricity
The effect of lotus balance improves the retention of filler, pigment, fiber.
Wet strength agent is polyamide-epoxy chloropropane resin, and Xidan provides, and solid content is for 12.5 ± 0.5%, 25 DEG C of viscosity
35~60cp, pH are 3.5~4.5, are mainly used as improving outdoor high strengthening plate facing body paper wet strength, and have in the present invention
The effect being dehydrated with paper machine is improved.
Pigment (supplier：Lang Sheng)：Main composition iron oxides.The pigment is sun-proof, water-fastness pigment.For open air
High strengthening plate facing body paper provides basic tone.
The sodium hydroxide and sulfuric acid are for adjusting slurry pH value, to improve paper corrosion resistance.
The open air high strengthening plate preparation method of facing body paper of the present invention, includes the following steps：
(1) waterpower size degradation is carried out to wood pulp, adds in pigment, it is spare to squeeze into pulping pond；
(2) it by fillers dilute, stirs, it is spare；
(3) mixture obtained by step (2) is squeezed into and is mixed in pulping pond obtained by step (1)；
(4) pH value of slurry obtained by step (3) is adjusted to 3.5-4 with sulfuric acid solution；Again with sodium hydroxide solution by pH value
It is adjusted to 9.5-10；
(5) by slurry pulping obtained by step (4), slurry beating degree is controlled between 30-45 ° of SR；
(6) between slurry obtained by step (5) being adjusted to 6-6.6 by pH value with aluminum sulfate, wet strength agent is added in；
(7) by slurry obtained by step (6) through being dehydrated, drying, press polish, curling, cutting is to get to outdoor high strengthening plate decorations
Face body paper.
Wherein：
Waterpower size degradation, a concentration of 4.0%-6.0% of size degradation are carried out to wood pulp in step (1).
Step (2) is：By fillers dilute to 50 ± 5% concentration, high-speed stirring is carried out with 1000 ± 50 revs/min of blenders
It mixes 9-11 minutes, it is spare.
The pH value of slurry obtained by step (3) is adjusted to 3.5-4 by step (4) with sulfuric acid solution；It again will with sodium hydroxide solution
PH value is adjusted to 9.5-10；It is that contained substance in slurry cannot be resisted to the ingredient of acid-base property to weed out that it, which is acted on,.
Step (5) slurry beating degree is controlled between 30-45 ° of SR；It is preferred that using the mashing mode of wire-dividing broom purification, effect
It is that fiber can be tightly combined, improves paper strength, reduces gap and improve contamination resistance.Main beating using wire-dividing broom purification
Slurry mode, effect is that fiber can be tightly combined, and improves paper strength, reduces gap and improves contamination resistance.
Dehydration in step (7) is：Online dehydration, vacuum dehydration and press dewatering.
As a kind of perferred technical scheme, the preparation method of outdoor high strengthening plate facing body paper of the present invention,
Include the following steps：
(1) waterpower size degradation is carried out to wood pulp, a concentration of 4-6% of pulping adds in pigment, it is spare to squeeze into pulping pond；
(2) by fillers dilute to 50 ± 5% concentration, high-speed stirred 9-11 is carried out with 1000 ± 50 revs/min of blenders
Minute, it is spare；
(3) mixture obtained by step (2) is squeezed into and is mixed 5-6 minutes in pulping pond obtained by step (1)；
(4) pH value of slurry obtained by step (3) is adjusted to 3.5-4 with sulfuric acid solution, recycled 20-22 minutes；Hydrogen-oxygen is used again
Change sodium solution and pH value is adjusted to 9.5-10 cycles 20-22 minutes；
(5) by slurry obtained by step (4) after fiberizer mashing processing, slurry beating degree is controlled between 30-45 ° of SR；
(6) slurry obtained by step (5) is squeezed into and is filled with pond, between pH value is adjusted to 6-6.6 with aluminum sulfate, added in wet strong
Agent；
(7) slurry pumping obtained by step (6) to head box is dried through dehydration of surfing the Internet, vacuum dehydration, press dewatering, baking oven
Dry, press polish, curling, cutting are to get to outdoor high strengthening plate facing body paper.
Outdoor high strengthening plate is 70-100g/m with the grammes per square metre of facing body paper2, wet tensile strength >=7N, content of ashes 20%-
45%, smoothness 200-400S, sun-proof grade >=6 grade.
Compared with prior art, the present invention has the following advantages：
(1) present invention is using titanium dioxide Du Pont R796, magnesium silicate and height of the addition by surface cladding processing in wood pulp
The fillers such as ridge soil effectively increase the covering that outdoor high strengthening plate facing body paper needs, gas permeability, corrosion resistance, thermostabilization
Property and the printability of printing.Sunlight fastness can reach outdoor requirement up to 6 grades or more, washing fastness up to height.It is outdoor
The manufacture raw material of high strengthening plate facing body paper is after soda acid is handled, and substance is stablized in slurry, can resist open-air conditions variation,
Accomplish not react, is colour-fast.
(2) the outdoor high strengthening plate facing body paper that the present invention makes pastes decoration after printing, impregnated melamine
On material, traditional finishing material such as ceramics, glass, cement, plastics, marble can be substituted completely from effect, and have
Have that environmentally protective, color is beautiful, a great variety of models, can realize the features such as private customized, meet people to personalized pursuit.Together
When body paper have the characteristics that after dipping is fabricated to finished product surface be not easy to stain, high strengthening, fabrication and installation standardization, have significantly
Economic benefit and social benefit.
(3) the outdoor high strengthening plate facing body paper that makes of the present invention have good covering, fiber distributing homogeneity,
Paper surface is fine and smooth, and corrosion resistance is strong, sun-proof grade is high, Washing is high.The outdoor high strengthening plate decorations that the present invention makes
Phenomena such as face body paper is dipped into PH from the solution of 3.5-10 after impregnated melamine veneer, and bubbling, deformation do not occur for paper；
It is detected through fade-o-meter, sun-proof grade is more than or equal to 6 grades；The outdoor high strengthening plate made through 24 hours underground water to the present invention
Thick china carries out water-wash test made of facing body paper, after testing aberration △ E≤0.2, and washing color does not change, and washes color
Fastness is high.
(4) invention also provides the preparation methods of outdoor high strengthening plate facing body paper.The present invention is highly practical, behaviour
Make scientific and reasonable, simple possible.
Specific embodiment
With reference to embodiment, the present invention will be further described.
Embodiment 1
(1) to wood pulp by long fibre wood pulp 10%, the accounting of staple fiber wood pulp 90% carries out waterpower size degradation, and pulping is a concentration of
4.5%, 4910 pigment 2% of iron oxide yellow is added in, it is spare to squeeze into pulping pond；
(2) filler being accounted for 70% by R796, magnesium silicate accounts for 25%, and kaolin accounts for 5% ratio, is diluted to 50% concentration,
High-speed stirred is carried out with 1000 revs/min of blenders 10 minutes, it is spare；
(3) mixture obtained by step (2) is squeezed into and is mixed 5 minutes in pulping pond obtained by step (1)；
(4) pH value of slurry obtained by step (3) is adjusted to 3.5 with sulfuric acid solution, recycled 20 minutes；It is molten with sodium hydroxide again
PH value is adjusted to 9.5 cycle 20 minutes by liquid；
(5) by slurry obtained by step (4) after fiberizer mashing processing, slurry beating degree is controlled between 35 ° of SR；
(6) slurry obtained by step (5) is squeezed into and is filled with pond, pH value is adjusted to 6.6 with aluminum sulfate, slurry per ton adds in wet strong
Agent 100kg；
(7) slurry pumping obtained by step (6) to head box is dried through dehydration of surfing the Internet, vacuum dehydration, press dewatering, baking oven
Dry, press polish, curling, cutting are to get to outdoor high strengthening plate facing body paper.
The grammes per square metre of this outdoor high strengthening plate facing body paper after testing：85g/m2, wet tensile strength：8N, content of ashes：35%,
Smoothness：260S, air permeability 40S/100mL, sun-proof class 6 grade.
PH is dipped into after impregnated melamine veneer from the solution of 3.5-10, it is existing that bubbling, deformation etc. do not occur for paper
As；It is detected through fade-o-meter, sun-proof class 6 grade；The outdoor high strengthening plate that the present invention makes is adornd through 24 hours underground water
Thick china made of the body paper of face carries out water-wash test, after testing aberration △ E≤0.2, and washing color does not change, Washing
It is high.
Embodiment 2
(1) to wood pulp by long fibre wood pulp 2%, the accounting of staple fiber wood pulp 98% carries out waterpower size degradation, and pulping is a concentration of
4.8%,
4910 pigment 5% of iron oxide yellow is added in, it is spare to squeeze into pulping pond；
(2) filler being accounted for 75% by R796, magnesium silicate accounts for 22%, and kaolin accounts for 3% ratio, is diluted to 50% concentration,
High-speed stirred is carried out with 1000 revs/min of blenders 10 minutes, it is spare；
(3) mixture obtained by step (2) is squeezed into and is mixed 5 minutes in pulping pond obtained by step (1)；
(4) pH value of slurry obtained by step (3) is adjusted to 4 with sulfuric acid solution, recycled 20 minutes；Sodium hydroxide solution is used again
PH value is adjusted to 9.8 cycle 20 minutes；
(5) by slurry obtained by step (4) after fiberizer mashing processing, slurry beating degree is controlled between 41 ° of SR；
(6) slurry obtained by step (5) is squeezed into and is filled with pond, pH value is adjusted to 6.2 with aluminum sulfate, slurry per ton adds in wet strong
Agent 150kg；
(7) slurry pumping obtained by step (6) to head box is dried through dehydration of surfing the Internet, vacuum dehydration, press dewatering, baking oven
Dry, press polish, curling, cutting are to get to outdoor high strengthening plate facing body paper.
The grammes per square metre of this programme open air high strengthening plate facing body paper after testing：80g/m2, wet tensile strength：9N, content of ashes：
39%, smoothness：350S, air permeability：42S/100mL, sun-proof grade:7 grades.
PH is dipped into after impregnated melamine veneer from the solution of 3.5-10, it is existing that bubbling, deformation etc. do not occur for paper
As；It is detected through fade-o-meter, sun-proof 7 grades of grade；The outdoor high strengthening plate that the present invention makes is adornd through 24 hours underground water
Thick china made of the body paper of face carries out water-wash test, after testing aberration △ E≤0.2, and washing color does not change, Washing
It is high.
Claims (10)
1. a kind of open air high strengthening plate facing body paper, it is characterised in that：It is made of the raw material of following weight percent：
Wherein, auxiliary agent is made of the raw material of following weight percent：
Filler is made of the raw material of following weight percent：
Titanium dioxide 60%-90%
Magnesium silicate 10%-40%
Kaolin 0%-10%.
2. open air high strengthening plate facing body paper according to claim 1, it is characterised in that：
The wood pulp is made of the raw material of following weight percent：
Staple fiber wood pulp 90%-100%
Long fibre wood pulp 0%-10%；
The titanium dioxide is titanium dioxide R796.
3. open air high strengthening plate facing body paper according to claim 2, it is characterised in that：
Filler is made of the raw material of following weight percent：
Titanium dioxide 70%-78%
Magnesium silicate 20%-28%
Kaolin 2%-5%；
Wood pulp is made of the raw material of following weight percent：
Staple fiber wood pulp 95%-98%
Long fibre wood pulp 2%-5%.
4. open air high strengthening plate facing body paper according to claim 1, it is characterised in that：Wet strength agent is polyamide-ring
Oxygen chloropropane resin, solid content are that 12.5 ± 0.5%, 25 DEG C of viscosity are 35~60cp, and pH is 3.5~4.5.
5. a kind of preparation method of any outdoor high strengthening plate facing body paper of claim 1-4, it is characterised in that：Packet
Include following steps：
(1) waterpower size degradation is carried out to wood pulp, adds in pigment, it is spare to squeeze into pulping pond；
(2) it by fillers dilute, stirs, it is spare；
(3) mixture obtained by step (2) is squeezed into and is mixed in pulping pond obtained by step (1)；
(4) pH value of slurry obtained by step (3) is adjusted to 3.5-4 with sulfuric acid solution；PH value is adjusted to sodium hydroxide solution again
9.5-10；
(5) by slurry pulping obtained by step (4), slurry beating degree is controlled between 30-45 ° of SR；
(6) between slurry obtained by step (5) being adjusted to 6-6.6 by pH value with aluminum sulfate, wet strength agent is added in；
(7) by slurry obtained by step (6) through being dehydrated, drying, press polish, curling, cutting is to get to outdoor high strengthening plate facing original
Paper.
6. the preparation method of open air high strengthening plate facing body paper according to claim 5, it is characterised in that：Step (1)
In to wood pulp carry out waterpower size degradation, a concentration of 4.0%-6.0% of size degradation.
7. the preparation method of open air high strengthening plate facing body paper according to claim 5, it is characterised in that：Step (2)
For：By fillers dilute to 50 ± 5% concentration, high-speed stirred is carried out 9-11 minutes with 1000 ± 50 revs/min of blenders, it is standby
With.
8. the preparation method of open air high strengthening plate facing body paper according to claim 5, it is characterised in that：Step (7)
In dehydration be：Online dehydration, vacuum dehydration and press dewatering.
9. the preparation method of open air high strengthening plate facing body paper according to claim 5, it is characterised in that：It is outdoor high-strength
It is 70-100g/m to change plate with the grammes per square metre of facing body paper2, wet tensile strength >=7N, content of ashes 20%-45%, smoothness 200-400S,
Sun-proof grade >=6 grade.
10. the preparation method of open air high strengthening plate facing body paper according to claim 5, it is characterised in that：Step is such as
Under：
(1) waterpower size degradation is carried out to wood pulp, a concentration of 4-6% of pulping adds in pigment, it is spare to squeeze into pulping pond；
(2) by fillers dilute to 50 ± 5% concentration, high-speed stirred is carried out 9-11 minutes with 1000 ± 50 revs/min of blenders,
It is spare；
(3) mixture obtained by step (2) is squeezed into and is mixed 5-6 minutes in pulping pond obtained by step (1)；
(4) pH value of slurry obtained by step (3) is adjusted to 3.5-4 with sulfuric acid solution, recycled 20-22 minutes；Sodium hydroxide is used again
PH value is adjusted to 9.5-10 and recycled 20-22 minutes by solution；
(5) by slurry obtained by step (4) after fiberizer mashing processing, slurry beating degree is controlled between 30-45 ° of SR；
(6) slurry obtained by step (5) is squeezed into and is filled with pond, between pH value is adjusted to 6-6.6 with aluminum sulfate, according to outdoor high strengthening
Plate is required to add in wet strength agent with facing body paper；
(7) by slurry pumping obtained by step (6) to head box through dehydration of surfing the Internet, vacuum dehydration, press dewatering, baking oven drying, pressure
Light, curling, cutting are to get to outdoor high strengthening plate facing body paper.