CN108129906A - The ink and preparation method of a kind of high adhesion force - Google Patents
The ink and preparation method of a kind of high adhesion force Download PDFInfo
- Publication number
- CN108129906A CN108129906A CN201810016735.1A CN201810016735A CN108129906A CN 108129906 A CN108129906 A CN 108129906A CN 201810016735 A CN201810016735 A CN 201810016735A CN 108129906 A CN108129906 A CN 108129906A
- Authority
- CN
- China
- Prior art keywords
- parts
- ink
- preparation
- item
- matched
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the ink and preparation method of a kind of high adhesion force, include the component of following parts by weight:20 30 parts of titanium dioxide, 20 30 parts of vinyl chloride-vinyl acetate resin, 10 12 parts of vanillic aldehyde, 46 parts of azone, 46 parts of hydrotalcite, 13 parts of thickener, 23 parts of saturated polyester resin, 12 parts of sulforicinoleic acid, 12 parts of antifoaming agent.Thickener, antifoaming agent are carried out emulsification treatment by the present invention in advance, improve the emulsifying effectiveness after other raw materials add in so that the viscosity of ink obtains the promotion of high degree, so as to enhance the adhesive force of ink;Secondly, antifoaming agent can not only effectively remove the bubble in ink, can also strengthen intensity and hardness after ink setting, further improve adhesive force.
Description
Technical field
The invention belongs to ink manufacturing technology field, more particularly, to the ink and preparation method of a kind of high adhesion force.
Background technology
Ink is the substance that graph text information is used to form in printing process, directly determine printed matter epigraph contrast,
Color, clarity, therefore act in printing process huge.But it is existing some printing ink rate of dryings it is excessively slow, printing
Phenomena such as set-off, page sticking are often resulted in brush.Also some printing ink poor adhesive forces, easily generate printing it is uneven,
Phenomena such as deinking, seriously affects printing quality.
Invention content
The present invention is in order to overcome the deficiencies of the prior art and provide a kind of ink of high adhesion force of strong adhesive force and preparation side
Method.
To achieve these goals, the present invention uses following technical scheme:The ink and preparation method of a kind of high adhesion force,
Include the component of following parts by weight:20-30 parts of titanium dioxide, 20-30 parts of vinyl chloride-vinyl acetate resin, 10-12 parts of vanillic aldehyde, azone 4-
6 parts, 4-6 parts of hydrotalcite, 1-3 parts of thickener, 2-3 parts of saturated polyester resin, 1-2 parts of sulforicinoleic acid, 1-2 parts of antifoaming agent.
Pass through the addition of titanium dioxide, thickener, the viscosity for improving ink of high degree, so that ink is attached in the present invention
Put forth effort to greatly promote, uneven or deinking the situation of printing is less prone to when printing in the later stage, printing effect is good.
Further, the antifoaming agent includes the component based on following weight part ratio:10-15 parts of fluorite, sodium carbonate 2-6
Part, 3-5 parts of hydrophobic silica.
The invention also discloses a kind of preparation methods of ink, include the following steps:
(1)Ionized water is removed, is stirred with dispersion machine, is gradually added neutralizer while stirring, ph is tested after stirring 5-10min
It is worth and stops stirring when 6.5-7.5;
(2)Thickener, antifoaming agent are added in into mixing plant, carry out emulsification treatment after stirring, controlled at 75-80 during emulsification
DEG C, a length of 10-15min during emulsification;
(3)By titanium dioxide, vinyl chloride-vinyl acetate resin, vanillic aldehyde, azone, hydrotalcite, thickener part, saturated polyester resin part, sulfonation
Ricinoleic acid adds in mixing plant, and finished product is obtained after mixing in 75-85 DEG C.
Thickener, antifoaming agent are carried out emulsification treatment by the present invention in advance, improve the emulsification effect after other raw materials add in
Fruit so that the viscosity of ink obtains the promotion of high degree, so as to enhance the adhesive force of ink;Secondly, antifoaming agent not only may be used
The bubble in ink is effectively removed, can also strengthen intensity and hardness after ink setting, further improve adhesive force.
Further, the neutralizer includes the component based on following weight part ratio:10-15 parts of aliphatic acid, more ethylene are more
5-8 parts of amine, 2-3 parts of oleic imidazolinone
Further, the mixing plant includes pedestal, contains liquid part and contains the matched stirring parts of liquid part with described;The Sheng liquid
Part outer wall is equipped with holding division, and the pedestal is equipped with and the matched fixing piece of the holding division;The pedestal, which is equipped with, to be used
In the driving mechanism for driving the fixing piece up and down;By setting holding division and fixing piece, it is caught in by fixing piece to card
Gu in portion, so as to realize fixation to containing liquid part, ensure that ink barrel will not be subjected to displacement, and then can ensure that stirring in whipping process
Device stirring efficiency, while fixing piece is caught in holding division, is from top to bottom blocked and is contained liquid part, therefore Sheng liquid part can not be transported upwards
It is dynamic, it realizes and is fixed to containing liquid part, agitating paddle is hardly damaged, and service life is long;Driving part is set simultaneously, control can be convenient for solid
It is up and down to determine part, so control fixing piece be caught in holding division, convenient for need to by contain liquid part be removed from pedestal cleaning and
It replaces and contains liquid part.
Further, the pedestal is equipped with a placed cavity, and the driving mechanism is set in the placed cavity;The driving machine
Structure include transmission parts and with the matched driving part of the transmission parts;The driving mechanism is located in placed cavity again, can
It is hidden to driving mechanism progress, ink is avoided to drop in driving mechanism, driving mechanism is caused to corrode, driving mechanism is protected
Shield, the appearance of disaster agitating device are more beautiful;And set transmission parts can by the power transmission of driving part to fixing piece, into
And realize that fixing piece is up and down, while transmission parts can also be ensured and are caught in fixing piece to holding division, fixing piece will not
It is happened at movement, it is ensured that fixing piece is compressible to contain liquid part.
Further, the transmission parts include the first drive matched with the fixing piece, are passed with described first
Driving wheel is matched to be driven item and with being driven matched second drive of item;Second drive can be effectively by driving portion
The power transmission of part gives transmission item, and power is rotated through the first drive, and then by the first drive by being driven item, is made
It is up and down to obtain fixing piece, and then driving part can drive fixing piece to be caught in holding division, realize fixing piece card jail.
Further, the driving part includes driving item and drives the matched actuator of item with described;The driving
Item is matched with second drive;Actuator can effectively make driving item be moved forward and backward, by drive a fore-aft motion into
And the rotation of the second drive is driven, so as to which fixing piece be driven to act, block fixed part;Actuator is cylinder simultaneously, passes through cylinder
Setting, the active force of cylinder is big, therefore when not controlling, and fixing piece can clamping holding division.
Further, a support element is equipped in the placed cavity, movable cavity is set on the support element, the transmission item is set on
In the activity cavity;By the setting of support element, transmission item can be effectively supported, convenient for transmission item along the length of support element
Direction moves, and avoids transmission item that left and right offset occurs.
Further, the first limiting section is extended to form in the movable cavity interior walls phase, the activity cavity bottom is upward
Extend to form the second limiting section;The transmission item, which is equipped with, to be set between the first limiting section and the second limiting section;First limiting
Portion and the second limiting section match, and are limited so as to be driven item, and transmission item is avoided to occur to shake up and down, causes connection unstable
It is fixed;The first limiting section is extended inwardly to form by inner wall simultaneously, and the second limiting section has bottom to upwardly extend to be formed, effective to ensure
Support element fastness.
Further, the transmission item is equipped with movable part, which is set on first limiting section and the second limiting
Between portion;The movable part is equipped with multiple through-holes, and ball, first limiting section and the second limiting section are equipped in the through-hole
Between be equipped with and the matched sliding slot of the ball;Through-hole is set to fix ball, ball is avoided to be split away off from movable part, is protected
The stability of transmission item movement is hindered.
Further, the holding division, which is equipped with, fixes groove, and the fixing piece is equipped with and the fixing recess
The clamping part of conjunction;The clamping part side wall is equipped with arc-shaped depression portion, and the fixing groove inner wall is equipped with and the arc-shaped depression portion
Matched arc protrusion;Audit fabrication consolidate groove and can be penetrated convenient for holding division to groove, thus fixing piece be caught in it is more firm
Gu and setting arc-shaped depression portion and arc protrusion, arc protrusion are caught in arc-shaped depression portion, so as to being caught in fixing piece to groove
Later, it realizes secondary fixation, and then can realize and fix again.
In conclusion the present invention has the following advantages:Thickener, antifoaming agent are subjected to emulsification treatment in advance, improve it
Emulsifying effectiveness after his raw material addition so that the viscosity of ink obtains the promotion of high degree, so as to enhance the attached of ink
Put forth effort;Secondly, antifoaming agent can not only effectively remove the bubble in ink, can also strengthen intensity and hardness after ink setting, into
One step improves adhesive force.
Description of the drawings
Fig. 1 is the structural diagram of the present invention.
Fig. 2 is the enlarged drawing of A in Fig. 1.
Fig. 3 is the partial schematic diagram of the present invention.
Specific embodiment
In order to which those skilled in the art is made to be better understood from the present invention program, below in conjunction in the embodiment of the present invention
Attached drawing carries out the technical solution in the embodiment of the present invention clear, complete description.
Embodiment 1
A kind of ink includes the component of following parts by weight:20 parts of titanium dioxide, 20 parts of vinyl chloride-vinyl acetate resin, 10 parts of vanillic aldehyde, bay nitrogen
4 parts of ketone, 4 parts of hydrotalcite, 1 part of thickener, 2 parts of saturated polyester resin, 1 part of sulforicinoleic acid, 1 part of antifoaming agent;The thickening
Agent is the common thickener being directly commercially available on the market;The antifoaming agent includes the component based on following weight part ratio:Fluorite
10 parts, 2 parts of sodium carbonate, 3 parts of hydrophobic silica.
A kind of method for being used to prepare above-mentioned ink, includes the following steps:(1)Ionized water is removed, is stirred with dispersion machine
It mixes, is gradually added neutralizer while stirring, stir and ph values are tested by ph Meters after 5min, stop when pH value is 6.5
Stirring;(2)Thickener, antifoaming agent are added in into mixing plant, carry out emulsification treatment after stirring, controlled at 75 DEG C during emulsification,
A length of 10min during emulsification;(3)By titanium dioxide, vinyl chloride-vinyl acetate resin, vanillic aldehyde, azone, hydrotalcite, thickener part, saturated polyester
Resin part, sulforicinoleic acid add in mixing plant, finished product are obtained after mixing in 75 DEG C;The neutralizer is included by following
The component of weight part ratio meter:10 parts of aliphatic acid, 5 parts of polyethylene polyamine, 2 parts of oleic imidazolinone.
As shown in Figure 1, the mixing plant includes pedestal 1, contains liquid part 2 and stirring parts 3, the pedestal 1 is metallic plate,
The Sheng liquid part 2 is a metal drum;Holding division 21 is equipped on the outer wall of the Sheng liquid part 2, the holding division 21 is is located at Sheng liquid
One circle becket of 2 lower part of part, is equipped on the holding division 21 and fixes groove 211, the fixing groove 211 is by holding division
21 upper ends downwards concave shape into concave ring;A placed cavity 10 is equipped on the pedestal 1, the Sheng liquid part 2 is placed in institute
In the placed cavity 10 stated;Active open 101, the active open 101 and placed cavity are equipped on the side wall of the placed cavity 10
10 are connected, and fixing piece 11 is equipped on the pedestal 1, which is a metal derby;The fixing piece 11 is put with described
The flexible connection of 10 inner wall of chamber is put, 11 end of fixing piece is equipped with clamping part 110, the clamping part 110 and the fixing piece
11 is perpendicular, and the clamping part 110 can be caught in fixing in groove 211, so as to be fixed to containing liquid part;Described
The side wall of clamping part 110 is equipped with the recess portion 111 of arc, and 211 inner wall of fixing groove is equipped with arc protrusion 299, when
The clamping part 110 penetrate to fix groove 211 in when, the arc protrusion 299 be located at the arc-shaped depression portion 111 it
In.
Further, a driving mechanism 4 is equipped in the pedestal 1, which drives the holding division
110 are caught in holding division 111 described with driving in fixing groove 211 disengagement out of fixing groove 211;The driving mechanism 4
Including transmission parts 41 and with driving part 42;The transmission parts 41 include the first drive 411, transmission item 412 and second
Drive 413;Specifically, the end upper side wall in the fixing piece 11 is set for arc, on the side wall equipped with biting teeth, institute
It states the first drive 411 to be located in the cavity of pedestal 1, and first drive 411 is the gear with biting teeth, first transmission
Wheel 411 biting teeth be mutually engaged with the biting teeth on the fixing piece 11, therefore the first drive 411 rotate can drive fixing piece 11 into
Row rotation;The transmission item 412 is rack, and biting teeth is respectively equipped on the upper surface and lower face of the transmission item 412, described
Transmission item 412 is engaged with 41 phase of the first drive, and the transmission item 412 is located at the lower section of the first drive 41, and described second
Drive 413 is arranged on the lower section of transmission item 412, and is mutually engaged with the biting teeth on 412 lower face of the transmission item.
Further, the driving part 42 includes actuator 422 and driving item 421, and the actuator 422 is one
Cylinder, the driving item 421 all carries the rack of the biting teeth for both ends, and actuator 422 and the driving item 421 are being put
Put in chamber 10 is the biting teeth on the driving item 421 and the biting teeth on second drive 413 by being obliquely installed under
It is mutually engaged, the driving item 421 is driven to move by actuator 422, so as to which second drive 413 be driven to rotate.
Support element 5 is equipped in the placed cavity 10, which is a metallic support, which is equipped with movable cavity
51, the interlude of the transmission item 412 is set in the activity cavity 51;Specifically, the transmission item 412 is equipped with activity
Portion 418, the movable part 418 do not have one section of biting teeth to be intermediate, which is located in the movable cavity 51, transmission
The left and right sweeping action in movable cavity 51 of item 412, the first limiting section 511 and the second limiting section 512 limit the transmission
412 activity of item.
Further, multiple through-holes 419 are equipped on the movable part 418, ball 420, institute are equipped in the through-hole 419
The lower face for stating the first limiting section 511 and the second limiting section 512 is recessed upwards, forms sliding slot 513, the sliding slot 513 and ball 41
It is in contact, so as to reduce frictional force during transmission 412 sweeping action of item.
Further, the stirring parts 3 include bull stick 31 and agitating paddle 32, which is connected with motor, in motor
Driving under rotated, bull stick 31 be a metallic rod, the agitating paddle 32 be two panels metal paddle, set on the agitating paddle 32
There are multiple spoilers 33, which includes flow-disturbing convex ribs 331, adds between two adjacent flow-disturbing convex ribs 331 by one
Strong part 332 is connected, which is metallic plate.
When in use, actuator 422 is so that driving item 421 carries out downward activity so that the second drive 413 turns clockwise
It is dynamic, when the second rotating wheel 413 rotates clockwise, transmission item 412 is driven to turn to middle part towards the middle section of placed cavity 10
Dynamic, in rotation process, rotation strip 412 drives 411 counterclockwise movement of the first drive, so as to which the first drive 411 is with solid
Determine part 11 to move, fixing piece 11 is disengaged from holding division 21;It is only the movement shape of right part in the present embodiment in the above process
State, each first drive 411, the second drive 413 and the driving rack 412 of the present embodiment left part and the fortune of right part
Dynamic direction is opposite.
Embodiment 2
A kind of ink includes the component of following parts by weight:30 parts of titanium dioxide, 30 parts of vinyl chloride-vinyl acetate resin, 12 parts of vanillic aldehyde, bay nitrogen
6 parts of ketone, 6 parts of hydrotalcite, 3 parts of thickener, 3 parts of saturated polyester resin, 2 parts of sulforicinoleic acid, 2 parts of antifoaming agent;The thickening
Agent is the common thickener being directly commercially available on the market;The antifoaming agent includes the component based on following weight part ratio:Fluorite
15 parts, 6 parts of sodium carbonate, 5 parts of hydrophobic silica.
A kind of method for being used to prepare above-mentioned ink, includes the following steps:(1)Ionized water is removed, is stirred with dispersion machine
It mixes, is gradually added neutralizer while stirring, stir and ph values are tested by ph Meters after 10min, stop when pH value is 7.5
Stirring;(2)Thickener, antifoaming agent are added in into mixing plant, carry out emulsification treatment after stirring, controlled at 80 DEG C during emulsification,
A length of 15min during emulsification;(3)By titanium dioxide, vinyl chloride-vinyl acetate resin, vanillic aldehyde, azone, hydrotalcite, thickener part, saturated polyester
Resin part, sulforicinoleic acid add in mixing plant, finished product are obtained after mixing in 85 DEG C;The neutralizer is included by following
The component of weight part ratio meter:15 parts of aliphatic acid, 8 parts of polyethylene polyamine, 3 parts of oleic imidazolinone.
Mixing plant in the present embodiment is identical with the structure in embodiment 1, repeats no more.
Embodiment 3
A kind of ink includes the component of following parts by weight:30 parts of titanium dioxide, 20 parts of vinyl chloride-vinyl acetate resin, 10 parts of vanillic aldehyde, bay nitrogen
6 parts of ketone, 6 parts of hydrotalcite, 3 parts of thickener, 2 parts of saturated polyester resin, 1 part of sulforicinoleic acid, 1 part of antifoaming agent;The thickening
Agent is the common thickener being directly commercially available on the market;The antifoaming agent includes the component based on following weight part ratio:Fluorite
10 parts, 2 parts of sodium carbonate, 3 parts of hydrophobic silica.
A kind of method for being used to prepare above-mentioned ink, includes the following steps:(1)Ionized water is removed, is stirred with dispersion machine
It mixes, is gradually added neutralizer while stirring, stir and ph values are tested by ph Meters after 10min, stop when pH value is 7.5
Stirring;(2)Thickener, antifoaming agent are added in into mixing plant, carry out emulsification treatment after stirring, controlled at 75 DEG C during emulsification,
A length of 15min during emulsification;(3)By titanium dioxide, vinyl chloride-vinyl acetate resin, vanillic aldehyde, azone, hydrotalcite, thickener part, saturated polyester
Resin part, sulforicinoleic acid add in mixing plant, finished product are obtained after mixing in 75 DEG C;The neutralizer is included by following
The component of weight part ratio meter:10 parts of aliphatic acid, 5 parts of polyethylene polyamine, 2 parts of oleic imidazolinone.
Mixing plant in the present embodiment is identical with the structure in embodiment 1, repeats no more.
Obviously, described embodiment is only the part of the embodiment of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, those of ordinary skill in the art are obtained every other without making creative work
Embodiment should all belong to the scope of protection of the invention.
Claims (10)
1. a kind of ink of high adhesion force, it is characterised in that:Include the component of following parts by weight:20-30 parts of titanium dioxide, chlorine vinegar
20-30 parts of resin, 10-12 parts of vanillic aldehyde, 4-6 parts of azone, 4-6 parts of hydrotalcite, 1-3 parts of thickener, saturated polyester resin
2-3 parts, 1-2 parts of sulforicinoleic acid, 1-2 parts of antifoaming agent.
2. the ink of high adhesion force according to claim 1, it is characterised in that:The antifoaming agent is included by following parts by weight
Than the component of meter:10-15 parts of fluorite, 2-6 parts of sodium carbonate, 3-5 parts of hydrophobic silica.
3. a kind of preparation method for being used to prepare any one of the claims 1-2 ink, it is characterised in that:Including with
Lower step:
Ionized water is removed, is stirred with dispersion machine, is gradually added neutralizer while stirring, ph values are tested after stirring 5-10min
Stop stirring when 6.5-7.5;
Thickener, antifoaming agent are added in into mixing plant, carry out emulsification treatment after stirring, controlled at 75-80 DEG C during emulsification, breast
A length of 10-15min during change;
By titanium dioxide, vinyl chloride-vinyl acetate resin, vanillic aldehyde, azone, hydrotalcite, thickener part, saturated polyester resin part, sulfonation castor-oil plant
Oleic acid adds in mixing plant, and finished product is obtained after mixing in 75-85 DEG C.
4. the preparation method of ink according to claim 1, it is characterised in that:The neutralizer is included by following parts by weight
Than the component of meter:10-15 parts of aliphatic acid, 5-8 parts of polyethylene polyamine, 2-3 parts of oleic imidazolinone.
5. the preparation method of ink according to claim 3, it is characterised in that:The mixing plant includes pedestal(1), contain
Liquid part(2)And contain liquid part with described(2)Matched stirring parts(3);The Sheng liquid part(2)Outer wall is equipped with holding division(21),
The pedestal(1)It is equipped with and the holding division(21)Matched fixing piece(11);The pedestal(1)It is equipped with to drive
The fixing piece(11)Up and down driving mechanism(4).
6. the preparation method of ink according to claim 5, it is characterised in that:The pedestal(1)It is equipped with a placed cavity
(10), the driving mechanism(4)Set on the placed cavity(10)It is interior;The driving mechanism(4)Including transmission parts(41)With with institute
State transmission parts(41)Matched driving part(42).
7. the preparation method of ink according to claim 6, it is characterised in that:The transmission parts(411)Including with institute
State fixing piece(11)Matched first drive(41)And first drive(41)Matched transmission item(412)And
With being driven item(412)Matched second drive(413).
8. the preparation method of ink according to claim 7, it is characterised in that:The driving part(42)Including driving item
(421)With with the driving item(421)Matched actuator(422);The driving item(421)With second drive
(413)It matches.
9. the preparation method of ink according to claim 8, it is characterised in that:The placed cavity(10)Inside it is equipped with a support
Part(5), the support element(5)On set movable cavity(51), the transmission item(412)Set on the activity cavity(51)It is interior.
10. the preparation method of ink according to claim 5, it is characterised in that:The activity cavity(51)In inner wall phase
Extend to form the first limiting section(511), the activity cavity(51)Bottom upwardly extends to form the second limiting section(512);It is described
It is driven item(412)Set on the first limiting section(511)With the second limiting section(512)Between.