CN108129126A - A kind of high strength fiberboard - Google Patents
A kind of high strength fiberboard Download PDFInfo
- Publication number
- CN108129126A CN108129126A CN201711326603.0A CN201711326603A CN108129126A CN 108129126 A CN108129126 A CN 108129126A CN 201711326603 A CN201711326603 A CN 201711326603A CN 108129126 A CN108129126 A CN 108129126A
- Authority
- CN
- China
- Prior art keywords
- parts
- high strength
- raw material
- fibred
- dolomite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of high strength fiberboards, are made of following raw material according to parts by weight：46 parts of 20 60 parts of wood-fibred, 20 60 parts of bamboo fibre, 20 40 parts of hydrotalcite, 9 12 parts of silicon-aluminum sol, 10 20 parts of pre-polymerization resin, 8 12 parts of delustering agent, 10 20 parts of stearic acid, 68 parts of dolomite, 56 parts of swelling agent, 5 10 parts of potassium feldspar and boric acid.A kind of high strength fiberboard intensity of the present invention is high, has good compressive resistance and low heat conductivity, has good heat insulation effect, while fiber is uniform, and durability is strong, reduces the energy and raw material loss, improves production efficiency.
Description
Technical field
The present invention relates to wooden boards field, specifically a kind of high strength fiberboard.
Background technology
As the improvement of people's living standards, house ornamentation decoration has become a kind of necessity.At present, fitment material for family development is fast
In terms of speed, especially interior decoration and decoration, need to consume a large amount of fitment material for family.Interior fitment material for family is broadly divided into pure at present
Inorganic plate, timber, organic board, textile material, composite board, since timber trick easy to moisture absorption, perishable, easy is damaged by worms and is steeped
The defects of easy to crack after water, application scenario are restricted, and flame-retardant fibre board has certain intensity and hardness, Resistance to wind Erosion
By force, it has stable high-temperature performance, compressive resistance is high under the condition of high temperature, is commonly used for the heat-barrier material of high-temperature service.
Invention content
The purpose of the present invention is to provide a kind of high strength fiberboards, solve above-mentioned technological deficiency.
To achieve the above object, the present invention provides following technical solution：
A kind of high strength fiberboard, is made of following raw material according to parts by weight：20-60 parts of wood-fibred, 20-60 parts of bamboo fibre, water
20-40 parts of talcum, 9-12 parts of silicon-aluminum sol, 10-20 parts of pre-polymerization resin, 8-12 parts of delustering agent, 10-20 parts of stearic acid, dolomite
4-6 parts of 6-8 parts, 5-6 parts of swelling agent, 5-10 parts of potassium feldspar and boric acid.
A kind of above-mentioned high strength fiberboard, is made of following raw material according to parts by weight：20-58 parts of wood-fibred, bamboo fibre 20-
58 parts, 20-38 parts of hydrotalcite, 9-11 parts of silicon-aluminum sol, 10-18 parts of pre-polymerization resin, 8-11 parts of delustering agent, 10-18 parts of stearic acid,
4-5 parts of 6-7 parts of dolomite, 5-6 parts of swelling agent, 5-8 parts of potassium feldspar and boric acid.
A kind of above-mentioned high strength fiberboard, is made of following raw material according to parts by weight：40 parts of wood-fibred, 40 parts of bamboo fibre,
30 parts of hydrotalcite, 11 parts of silicon-aluminum sol, 15 parts of pre-polymerization resin, 10 parts of delustering agent, 15 parts of stearic acid, 7 parts of dolomite, swelling agent 6
5 parts of part, 8 parts of potassium feldspar and boric acid.
Compared with prior art, the beneficial effects of the invention are as follows：
A kind of high strength fiberboard intensity of the present invention is high, has good compressive resistance and low heat conductivity, has good heat preservation
Effect, while fiber is uniform, durability is strong, reduces the energy and raw material loss, improves production efficiency.
Specific embodiment
The technical solution of this patent is described in more detail With reference to embodiment.
Embodiment 1
A kind of high strength fiberboard, is made of following raw material according to parts by weight：20 parts of wood-fibred, 20 parts of bamboo fibre, hydrotalcite 20
Part, 9 parts of silicon-aluminum sol, 10 parts of pre-polymerization resin, 8 parts of delustering agent, 10 parts of stearic acid, 6 parts of dolomite, 5 parts of swelling agent, potassium feldspar 5
4 parts of part and boric acid.
Embodiment 2
A kind of high strength fiberboard, is made of following raw material according to parts by weight：60 parts of wood-fibred, 60 parts of bamboo fibre, hydrotalcite 40
Part, 12 parts of silicon-aluminum sol, 20 parts of pre-polymerization resin, 12 parts of delustering agent, 20 parts of stearic acid, 8 parts of dolomite, 6 parts of swelling agent, potassium feldspar
10 parts and 6 parts of boric acid.
Embodiment 3
A kind of high strength fiberboard, is made of following raw material according to parts by weight：40 parts of wood-fibred, 40 parts of bamboo fibre, hydrotalcite 30
Part, 11 parts of silicon-aluminum sol, 15 parts of pre-polymerization resin, 10 parts of delustering agent, 15 parts of stearic acid, 7 parts of dolomite, 6 parts of swelling agent, potassium feldspar
8 parts and 5 parts of boric acid.
A kind of high strength fiberboard intensity of the present invention is high, has good compressive resistance and low heat conductivity, has good
Heat insulation effect, while fiber is uniform, durability is strong, reduces the energy and raw material loss, improves production efficiency.
The better embodiment of this patent is explained in detail above, but this patent is not limited to above-mentioned embodiment party
Formula, can also be under the premise of this patent objective not be departed from the knowledge that one skilled in the relevant art has
It makes a variety of changes.
Claims (3)
1. a kind of high strength fiberboard, which is characterized in that be made of following raw material according to parts by weight：20-60 parts of wood-fibred, bamboo are fine
20-60 parts of dimension, 20-40 parts of hydrotalcite, 9-12 parts of silicon-aluminum sol, 10-20 parts of pre-polymerization resin, 8-12 parts of delustering agent, stearic acid 10-
4-6 parts of 20 parts, 6-8 parts of dolomite, 5-6 parts of swelling agent, 5-10 parts of potassium feldspar and boric acid.
2. a kind of high strength fiberboard according to claim 1, which is characterized in that be made of following raw material according to parts by weight：
20-58 parts of wood-fibred, 20-58 parts of bamboo fibre, 20-38 parts of hydrotalcite, 9-11 parts of silicon-aluminum sol, 10-18 parts of pre-polymerization resin, delustring
4-5 parts of 8-11 parts of agent, 10-18 parts of stearic acid, 6-7 parts of dolomite, 5-6 parts of swelling agent, 5-8 parts of potassium feldspar and boric acid.
3. a kind of high strength fiberboard according to claim 1, which is characterized in that be made of following raw material according to parts by weight：
40 parts of wood-fibred, 40 parts of bamboo fibre, 30 parts of hydrotalcite, 11 parts of silicon-aluminum sol, 15 parts of pre-polymerization resin, 10 parts of delustering agent, stearic acid
5 parts of 15 parts, 7 parts of dolomite, 6 parts of swelling agent, 8 parts of potassium feldspar and boric acid.