CN108117708A - A kind of heat-resistant anticorrosive rubber pad formula and preparation method thereof - Google Patents
A kind of heat-resistant anticorrosive rubber pad formula and preparation method thereof Download PDFInfo
- Publication number
- CN108117708A CN108117708A CN201711424110.0A CN201711424110A CN108117708A CN 108117708 A CN108117708 A CN 108117708A CN 201711424110 A CN201711424110 A CN 201711424110A CN 108117708 A CN108117708 A CN 108117708A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- heat
- resistant anticorrosive
- rubber pad
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to field of rubber technology, and in particular to a kind of heat-resistant anticorrosive rubber pad formula and preparation method thereof;A kind of heat-resistant anticorrosive rubber pad formula includes the formula of following components by weight percent:90~100 parts of fluorubber, 0~10 part of silicon rubber, 5~10 parts of magnesia, 5~10 parts of calcium hydroxide, 3~5 parts of processing aid, 30~50 parts of reinforcing agent, 2~4 parts of bisphenol AF, 5~8 parts of vinyl silicone oil, 0.5~1.5 part of benzyltriphenylphosphonium chloride BPP, vulcanizing agent are 25 0.2~1 part double;The vulcanizate of this rubber compounding has a permanent denaturation performance of good compression, and rubber is in process due to the use of in-lubricant, process not easy mold release in roll banding sulfidation;Vulcanize rubber simultaneously with good physical synthesis performance, the higher use formula of sexual valence is provided in the processing vulcanization of rubber slab.
Description
Technical field
The invention belongs to field of rubber technology, and in particular to a kind of heat-resistant anticorrosive rubber pad formula and preparation method thereof.
Background technology
With the development of national economy, rubber military project, it is civilian in purposes it is more and more extensive, performance requirement also by
Simple sealing is increased to high temperature resistant, media-resistant oil, anticorrosion, anti-aging, warping strength to wait requirement, and has on this basis deeper
The raising of level.For example the amount of present family car is stepping up, rubber and plastic sizing material is in purposes automobile sealed, on interior trim
More and more extensive, automobile high-performance, lightweight, high performance development trend also require rubber-plastics material to higher level direction
Development.Fluorubber is widely used in automobile hair as a kind of high heat resistance, hypotonicity energy and excellent medium-resistance
The positions such as motivation vehicle bridge, transmission seal.But Railway Project of the fluorubber as sealing article puzzlement user, 1 mixed refining process are relatively tired
It is difficult;Permanently denaturation is higher for the compression of 2 vulcanization rubber, directly results in product product height dimension when higher temperature uses for a long time
There is difference;The tearing strength of 3 vulcanization rubber standard samples is relatively low, directly results in product product when vulcanizing depanning and is easily torn
It splits.To improve the quality of product and increasing the service life of product, problem above is badly in need of solving.
The content of the invention
It is an object of the invention to provide a kind of heat-resistant anticorrosive rubber pad formulas and preparation method thereof.
The technical scheme is that:A kind of heat-resistant anticorrosive rubber pad formula includes the formula of following components by weight percent:
90~100 parts of fluorubber, 0~10 part of silicon rubber, 5~10 parts of magnesia, 5~10 parts of calcium hydroxide, processing aid 3
~5 parts, 30~50 parts of reinforcing agent, 2~4 parts of bisphenol AF, 5~8 parts of vinyl silicone oil, benzyltriphenylphosphonium chloride BPP 0.5~
1.5 parts, vulcanizing agent is 250.2~1 parts double.
Preferably fluorubber is Mooney viscosityFor 120~150;Fluorubber is divided into high Mooney viscosity and low Mooney
Viscosity, for making the fluorubber of rubber pad as du pont company's production in the present invention, the fluorubber of this Mooney section has higher
Intensity, while with silicon rubber and with can have preferable compression set.
Preferred processing aid palm wax, Rhein dissipate at least one of 54, and palm wax and Rhein dissipate 54 as inner pattern releasing agent applicable
The processing performance of rubber compound can not only be improved improves the release property of vulcanizate simultaneously so that vulcanizate has the good demoulding
Property
Preferred reinforcing agent is carbon black N990, ultra-fine barium sulfate, wollastonite are used in combination, carbon black N990 have grain diameter compared with
Greatly, it is preferable with fluorubber, silicon rubber Tuberculous;Wherein barium sulfate, wollastonite can not only reduce formula cost simultaneously it is inorganic
The addition of filler can assign the stronger media-resistant of rubber, antiseptic property.
The amount ratio of the bisphenol AF and benzyltriphenylphosphonium chloride BPP are 4:1.
A kind of processing method of heat-resistant anticorrosive rubber pad formula, the mixing of the rubber are divided into three steps:
A raw rubbers are plasticated, and fluorubber is plasticated 1~2 minute on a mill, during raw rubber of plasticating silicon rubber in batches
It plasticates in secondary addition open mill.
The mixing of b reinforcing agents and processing aid, operation oil is mixed uniform reinforcing agent, processing aid, operation oil two batches
It is secondary to add in the raw rubber plasticated, glue is repeatedly tapped rubber and turns in the process, mixing time is 1~2 minute;The glue being kneaded claims
For one section of rubber compound, then one section of rubber compound is carried out thin 5~10 times logical.
The thin one section of rubber compound having friendly relations of c adds in bisphenol AF, benzyltriphenylphosphonium chloride BPP and vulcanizing agent double 25.
Beneficial effects of the present invention are:The vulcanizate of this rubber compounding has the permanent denaturation performance of good compression, rubber
In process due to the use of in-lubricant, process not easy mold release in roll banding sulfidation;Vulcanize rubber tool simultaneously
There is good physical synthesis performance, the higher use formula of sexual valence is provided in the processing vulcanization of rubber slab.
Specific embodiment
Embodiment one
A kind of heat-resistant anticorrosive rubber pad formula includes the formula of following components by weight percent:
90 parts of fluorubber, 10 parts of silicon rubber, 6 parts of magnesia, 10 parts of calcium hydroxide, 2 parts of palm wax, Rhein dissipates 541 parts, charcoal
It is N99020 parts black, 8 parts of ultra-fine barium sulfate, 12 parts of wollastonite, 2 parts of bisphenol AF, 5 parts of vinyl silicone oil, benzyltriphenylphosphonium chloride
0.5 part of BPP, vulcanizing agent are 250.6 parts double.
Embodiment two
A kind of heat-resistant anticorrosive rubber pad formula includes the formula of following components by weight percent:
95 parts of fluorubber, 5 parts of silicon rubber, 6 parts of magnesia, 10 parts of calcium hydroxide, 2 parts of palm wax, Rhein dissipates 542 parts, charcoal
It is N99025 parts black, 5 parts of ultra-fine barium sulfate, 10 parts of wollastonite, 2 parts of bisphenol AF, 5 parts of vinyl silicone oil, benzyltriphenylphosphonium chloride
0.5 part of BPP, vulcanizing agent are 250.6 parts double.
Embodiment three
According to the formula that embodiment one, the formula of embodiment two carry out, mixing step is:
A raw rubbers are plasticated, and fluorubber is plasticated 1~2 minute on a mill, during raw rubber of plasticating silicon rubber in batches
Plasticate in secondary addition open mill, open mill plasticate raw rubber when first to preheat roller temperature to 60 DEG C, roller temperature is to 135 during plasticating
DEG C when to lead to cooling water and cool down.
B reinforcing agents and processing aid, operation oil mixing first reinforcing agent carbon black N990, ultra-fine barium sulfate, wollastonite,
Palm wax, Rhein dissipate 54 and are uniformly mixed, and then in two batches in secondary addition rubber compound, are kneaded the oily ethylene of an operation during charging
Base silicone oil is added in rubber compound, repeatedly taps rubber and turn in the process glue, and mixing time is 1~2 minute;The glue being kneaded is known as
Then one section of rubber compound carries out one section of rubber compound thin 5~10 times logical.
The thin one section of rubber compound having friendly relations of c adds in bisphenol AF, benzyltriphenylphosphonium chloride BPP and vulcanizing agent double 25, adds in sulphur
Roller temperature is set as 90 DEG C during agent, and more than 110 DEG C when will lead to cooling water.
D is rubber mixed by stopping glue standard and park to carry out preforming compound blank afterwards for 24 hours and vulcanize, and conditions of vulcanization is 180 DEG C of *
300s。
Embodiment one, the performance of the vulcanizate of embodiment two being kneaded according to embodiment three are shown in Table one.
Hardness (shore A) | Intensity (MPa) | Elongation at break (%) | 200 DEG C of * 70h of compression set | |
Embodiment one | 68 | 11.2 | 240 | 40 |
Embodiment two | 70 | 14 | 220 | 35 |
Claims (6)
1. a kind of heat-resistant anticorrosive rubber pad formula, it is characterised in that:Include the formula of following components by weight percent:
90~100 parts of fluorubber, 0~10 part of silicon rubber, 5~10 parts of magnesia, 5~10 parts of calcium hydroxide, processing aid 3~5
Part, 30~50 parts of reinforcing agent, 2~4 parts of bisphenol AF, 5~8 parts of vinyl silicone oil, benzyltriphenylphosphonium chloride BPP 0.5~
1.5 parts, vulcanizing agent is 25 0.2~1 part double.
2. a kind of heat-resistant anticorrosive rubber pad formula according to claim 1, it is characterised in that:The fluorubber glues for Mooney
DegreeFor 120~150.
3. a kind of heat-resistant anticorrosive rubber pad formula according to claim 1, it is characterised in that:The processing aid palm
Wax, Rhein dissipate at least one of 54.
4. a kind of heat-resistant anticorrosive rubber pad formula according to claim 1, it is characterised in that:The reinforcing agent is carbon black
N990, ultra-fine barium sulfate, wollastonite are used in combination.
5. a kind of heat-resistant anticorrosive rubber pad formula according to claim 1, it is characterised in that:The bisphenol AF and benzyl three
The amount ratio of tetraphenylphosphonium chloride phosphorus BPP is 4:1.
6. a kind of processing method of heat-resistant anticorrosive rubber pad formula according to claims 1 to 5, it is characterised in that:It is described
The mixing of rubber is divided into three steps:
A raw rubbers are plasticated, and fluorubber is plasticated 1~2 minute on a mill, during raw rubber of plasticating silicon rubber in batches
It adds in open mill and plasticates;
The mixing of b reinforcing agents and processing aid, operation oil is mixed uniform reinforcing agent, processing aid, operation two batch of oil
It adds in the raw rubber plasticated, repeatedly taps rubber and turn in the process glue, mixing time is 1~2 minute;The glue being kneaded is known as
Then one section of rubber compound carries out one section of rubber compound thin 5~10 times logical;
The thin one section of rubber compound having friendly relations of c adds in bisphenol AF, benzyltriphenylphosphonium chloride BPP and vulcanizing agent double 25.