CN108103851A - A kind of superpower 3D textures wallpaper and preparation method thereof - Google Patents
A kind of superpower 3D textures wallpaper and preparation method thereof Download PDFInfo
- Publication number
- CN108103851A CN108103851A CN201810044409.1A CN201810044409A CN108103851A CN 108103851 A CN108103851 A CN 108103851A CN 201810044409 A CN201810044409 A CN 201810044409A CN 108103851 A CN108103851 A CN 108103851A
- Authority
- CN
- China
- Prior art keywords
- superpower
- wallpaper
- pvc
- printing
- textures
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of superpower 3D textures wallpapers, including printing layer among bottom wallpaper base, PVC, printing layer is coated in bottom wallpaper base among PVC, further includes the superpower 3D texture layers of top layer, and the superpower 3D texture layers of the top layer are arranged on the top of printing layer among PVC.Invention additionally discloses a kind of superpower 3D textures wallpapers and preparation method thereof, and printing layer among PVC is applied to by coating and printing in wallpaper base, by baking oven in 180 240 DEG C of drying；The slurry that superpower 3D effect can be formed after reaction is coated among PVC by gravure printing wheel and cylinder print wheel in printing layer again, then baking oven is sent to by the wallpaper printing assembly line that speed is 50M/min, and disclosure satisfy that personal needs and wallpaper with superpower 3D grain effects up to a kind of after being dried controlled at 80 ~ 200 DEG C.
Description
Technical field
The invention belongs to field of papermaking, are related to a kind of wallpaper, specifically a kind of superpower 3D textures wallpaper and its preparation
Method.
Background technology
With the high speed development of social economy, the material and cultural life quality of people is also constantly being promoted, and wall is used
Ornament materials on also have continuous pursuit --- from lime, apply expect wallpaper, then again development wall paint.It is above-mentioned in difference
The used various wall decoration materials of epoch institute have its advantage, but all there is the scarce of personalized and artistry difference simultaneously
It falls into, i.e., can not meet everyone individual demand, can only be the wallpaper for having what kind in the market, which type of is just used
Wallpaper.
As domestic living conditions constantly improve, requirement of the people for inner wall decoration also increasingly improves, beautiful pursuing
While, it is also desirable to interior wall wallpaper material can embody certain Individualized Pursuit, and superpower 3D textures wallpaper then both can be used for interior
Wall is decorated, and the wallpaper of different 3D grained profiles can be also customized according to client's specific requirements, can be by art up, personalized and practicability
It combines together, obtains the pro-gaze of more and more people.
The content of the invention
For above-mentioned technical problem of the prior art, the present invention provides a kind of superpower 3D textures wallpaper and its preparation sides
Method, this superpower 3D textures wallpaper and preparation method thereof will solve the bad skill of wallpaper stereoscopic effect of the prior art
Art problem.
The present invention provides a kind of superpower 3D textures wallpapers, are layer structure, including print among bottom wallpaper base, PVC
Brush layer, PVC centres printing layer are coated in bottom wallpaper base, further include the superpower 3D texture layers of top layer, the top layer is superpower
3D texture layers are arranged on the top of printing layer among the PVC；
The superpower 3D texture layers of the top layer are to turn golden foamed slurry by 3D to be coated on by gravure printing wheel and cylinder print wheel
In the printing layer of PVC centres and dry；
The bottom wallpaper base is body paper, non-woven paper or pure paper.
Further, the superpower 3D texture layers of the top layer are made of 3D turns of golden foamed slurries, are calculated in mass ratio, 3D
Turn dioctyl phthalate of the Gold conductor by 20-25%, the potassium Zn-Ca series stabilization agent of 0.6-1%, the titanium dioxide of 1-3%, 1-2%'s
SP401 foaming agents, the 68EX resin-oatmeals of the P457 of the BF210 of 0.6-1%, 20-25%, 15-20%, the talcum powder composition of 30-40%.
Further, the preparation method that the 3D turns golden foamed slurry is to weigh each raw material according to mass percent, will
Dioctyl phthalate, efficient stabilization agent, titanium dioxide, foaming agent, BF210 are mixed, and stir 3 ~ 10min；Then add in
P457,68EX resin-oatmeal and talcum powder continue 10 ~ 20min of stirring, and mixing speed turns/hour for 400-600, and it is equal to be allowed to mixing
Even, temperature is controlled within 30 DEG C；It is used after 20 ~ 30h of storage, two is carried out at 150 ° DEG C and 200 DEG C respectively during use
It is secondary to foam up to superpower 3D textures wallpaper.
The present invention also provides a kind of preparation methods of superpower 3D textures wallpaper, include the following steps：
（1）, first printing layer among PVC is applied to by coating and printing in wallpaper base, controlled at 180-240 DEG C into
Row drying；
（2）, the 3D prepared turned into golden foamed slurries be uniformly mixed；
（3）, by gravure printing wheel and cylinder print wheel, by step（2）The 3D of gained turns golden foamed slurry and is coated among PVC
In printing layer, baking oven is then sent to by the wallpaper printing assembly line that speed is 40 ~ 60M/min, and controlled at 150
DEG C carry out first time foaming, the wallpaper printing assembly line after foaming, which continues to be fed into 200 DEG C of baking oven, to carry out second and foam, drying
Afterwards up to a kind of superpower 3D textures wallpaper.
Specifically, the bottom wallpaper base is 90-160g/M2, printing layer and the superpower 3D textures of top layer among PVC
Layer is 10-50g/M2。
Specifically, the potassium Zn-Ca series stabilization agent is potassium zinc organic synthesis body, purchased from Shanghai Kun Rui Chemical Co., Ltd.s；
SP401 foaming agents are modified azodicarbonamide, purchased from Jiangsu Suo Pu（Group）Co., Ltd；BF210 is PVC white hair infusions,
Purchased from outstanding letter（Shanghai）Share control takeover Co., Ltd；P457 is polyvinyl chloride resin powder, purchased from Henan Qing Ai Industrial Co., Ltd.s；
68EX resin-oatmeals are modified PVC resin powder, and the beautiful plasticizing Co., Ltd that converges is won purchased from Ningbo.
3D is turned technology for gold and is applied to wallpaper field by the present invention, obtains a kind of superpower 3D textures wallpaper, described is superpower
3D texture layers are turning technology for gold textured pattern arbitrarily needed for engraving using local, have the characteristics that three-dimensional sense by force, good hand touch.
The present invention is compared with prior art, and technological progress is significant.A kind of superpower 3D of the present invention locally turns golden line
Manage wallpaper, due to superpower 3D locally turn to employ in golden texture layer can high-foaming at high temperature homogenate, make to produce superpower
3D texture wallpapers have the characteristics that three-dimensional sense is strong, good hand touch, rich artistry, meet personal needs and with practical well
Property.
Description of the drawings
Fig. 1 is a kind of structure diagram of superpower 3D textures wallpaper, wherein：1st, wallpaper base；2nd, printing layer among PVC,
3rd, superpower 3D texture layers.
Specific embodiment
By way of example and in conjunction with the accompanying drawings, the present invention is described in further detail, but is not limited to the present invention
Scope.
Embodiment 1
A kind of superpower 3D textures wallpaper is layer structure, and structure diagram is as shown in Figure 1, by bottom wallpaper base 1 and PVC
Intermediate printing layer 2 and the superpower 3D texture layers 3 of top layer form, and printing layer 2 is coated in bottom wallpaper base 1 among PVC, bottom wall
Paper substrate 1 is 90~100g/M2Body paper, printing layer 2 and the superpower 3D texture layers 3 of top layer are 40g/M among PVC2；
The superpower 3D texture layers 3 turn golden foamed slurry for 3D, calculate in mass ratio, turn the adjacent benzene two of Gold conductor 23% by 3D
Formic acid dioctyl ester, 0.66% potassium Zn-Ca series stabilization agent, 1.65% titanium dioxide, 1.3%SP401 foaming agents, 0.66%BF210,23%
P457,16.28%68EX resin-oatmeal, 33% talcum powder composition.Its preparation method is by dioctyl phthalate, efficiently stabilizes
Agent, titanium dioxide, foaming agent, BF210 are mixed, and stir 5min；Then P457,68EX resin-oatmeal and talcum powder are added in, is continued
15min is stirred, mixing speed turns/hour for 400-600, is allowed to uniformly mixed, and temperature is controlled within 30 DEG C；After storage for 24 hours
It uses, second time of foaming is carried out at 150 ° DEG C and 200 DEG C up to superpower 3D textures wallpaper respectively during use.Then led to
It crosses gravure printing wheel and cylinder print wheel is coated among PVC in printing layer 2 and dries；
A kind of production method of above-mentioned superpower 3D textures wallpaper, step are as follows：
（1）, first printing layer 2 among PVC is applied to by coating and printing in wallpaper base 1, coating quality 40g/M2, control
Temperature processed is dried for 180-240 DEG C；
（2）, will have the function of that high-foaming 3D turns to obtain superpower 3D after gold homogenate is mixed with a small amount of tap water to turn Gold conductor；
（3）, by gravure printing wheel and cylinder print wheel, by step（2）The superpower 3D of gained turns gold homogenate and is coated among PVC
In printing layer 2, coating speed 50M/min, coating quality 40g/M2, it is then the wallpaper printing of 50M/min by speed
Assembly line is sent to baking oven, and controlled at 150 DEG C of progress first time foaming, the wallpaper printing assembly line after foaming continues
It is sent into 200 DEG C of baking oven and carries out second of foaming, up to a kind of superpower 3D texture wallpapers of three-dimensional sense after drying.
The superpower 3D textures wallpaper of above-mentioned gained is had the characteristics that strong three-dimensional sense, good hand touch, artistic effect are splendid.
The above is only the citing of embodiments of the present invention, it is noted that for those skilled in the art
For, without departing from the technical principles of the invention, several improvement and modification, these improvements and modifications can also be made
It should be regarded as protection scope of the present invention.
Claims (4)
1. a kind of superpower 3D textures wallpaper is layer structure, including printing layer among bottom wallpaper base, PVC, printed among PVC
Brush layer is coated in bottom wallpaper base, it is characterised in that：Further include the superpower 3D texture layers of top layer, the superpower 3D lines of the top layer
Reason layer is arranged on the top of printing layer among the PVC；
The superpower 3D texture layers of the top layer are to turn golden foamed slurry by 3D to be coated on by gravure printing wheel and cylinder print wheel
In the printing layer of PVC centres and dry；
The bottom wallpaper base is body paper, non-woven paper or pure paper.
2. a kind of superpower 3D textures wallpaper as described in claim 1, it is characterised in that：The superpower 3D texture layers of the top layer by
3D turns golden foamed slurry composition, calculates in mass ratio, 3D turns dioctyl phthalate of the Gold conductor by 20-25%, 0.6-1%
Potassium Zn-Ca series stabilization agent, the titanium dioxide of 1-3%, the SP401 foaming agents of 1-2%, the P457 of the BF210 of 0.6-1%, 20-25%,
The 68EX resin-oatmeals of 15-20%, the talcum powder composition of 30-40%.
3. a kind of superpower 3D textures wallpaper as claimed in claim 2, it is characterised in that：The 3D turns the system of golden foamed slurry
Preparation Method is to weigh each raw material according to mass percent, by dioctyl phthalate, efficient stabilization agent, titanium dioxide, foaming
Agent, BF210 are mixed, and stir 3 ~ 10min；Then P457,68EX resin-oatmeal and talcum powder are added in, continue stirring 10 ~
20min, mixing speed turn/hour for 400-600, are allowed to uniformly mixed, and temperature is controlled within 30 DEG C；Make after 20 ~ 30h of storage
With use carries out second time of foaming up to superpower 3D textures wallpaper at 150 ° DEG C and 200 DEG C respectively in the process.
4. the preparation method of a kind of superpower 3D textures wallpaper described in claim 1, it is characterised in that include the following steps：
（1）, first printing layer among PVC is applied to by coating and printing in wallpaper base, controlled at 180-240 DEG C into
Row drying；
（2）, the 3D prepared turned into golden foamed slurries be uniformly mixed；
（3）, by gravure printing wheel and cylinder print wheel, by step（2）The 3D of gained turns golden foamed slurry and is coated among PVC
In printing layer, baking oven is then sent to by the wallpaper printing assembly line that speed is 40 ~ 60M/min, and controlled at 150
DEG C carry out first time foaming, the wallpaper printing assembly line after foaming, which continues to be fed into 200 DEG C of baking oven, to carry out second and foam, drying
Afterwards up to a kind of superpower 3D textures wallpaper.