CN108103775A - 一种无纺布用柔软剂 - Google Patents

一种无纺布用柔软剂 Download PDF

Info

Publication number
CN108103775A
CN108103775A CN201711233691.XA CN201711233691A CN108103775A CN 108103775 A CN108103775 A CN 108103775A CN 201711233691 A CN201711233691 A CN 201711233691A CN 108103775 A CN108103775 A CN 108103775A
Authority
CN
China
Prior art keywords
parts
sodium
softening agent
woven fabrics
octamethylcyclotetrasiloxanes
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711233691.XA
Other languages
English (en)
Inventor
芦茂庆
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI HONGYUAN NONWOVEN FABRIC Co Ltd
Original Assignee
ANHUI HONGYUAN NONWOVEN FABRIC Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI HONGYUAN NONWOVEN FABRIC Co Ltd filed Critical ANHUI HONGYUAN NONWOVEN FABRIC Co Ltd
Priority to CN201711233691.XA priority Critical patent/CN108103775A/zh
Publication of CN108103775A publication Critical patent/CN108103775A/zh
Pending legal-status Critical Current

Abstract

一种无纺布用柔软剂，包括以下重量份数原料：8～10份苯甲酸钠，11～16份八甲基四硅氧烷，7～9份硬脂酸钠，3～5份羟基丙基甲基纤维素，8～12份聚乙烯醇，2～4份碳酸钠，1～2份油酸钠，3～5份三聚磷酸钠，5～9份十二烷基硫酸钠，6～8份二甲基二硅氧烷，1～3份偶联剂，0.5～1.2份氢氧化钠，10～14份聚乙氧基化脂肪醇，11～14份抗坏血酸，10～12份柠檬酸及40～50份去离子水。本发明的有益效果为：（1）该柔软剂为非离子型柔软剂，其柔软效果好，且该柔软剂对环境的污染小，对人体无危害，更加的环保；（2）使用该柔软剂的无纺布能够保持有良好的弹性及耐磨性。

Description

一种无纺布用柔软剂
技术领域
本发明涉及无纺布生产领域，具体涉及一种无纺布用柔软剂。
背景技术
柔软剂是一类能改变纤维的静、动摩擦系数的化学物质。当改变静摩擦系数时，手感触摸有平滑感，易于在纤维或织物上移动；当改变动摩擦系数时，纤维与纤维之间的微细结构易于相互移动，也就是纤维或者织物易于变形。二者的综合感觉就是柔软。柔软剂按离子性来分有阳离子型、非离子型、阴离子型和两性季铵盐型四种。
现有大部分柔软剂效果差，同时对环境危害也大。
发明内容
本发明的目的是为了克服现有技术中的不足，提供一种无纺布用柔软剂。
为解决上述技术问题，本发明的技术方案为：
一种无纺布用柔软剂，包括以下重量份数原料：8～10份苯甲酸钠，11～16份八甲基四硅氧烷，7～9份硬脂酸钠，3～5份羟基丙基甲基纤维素，8～12份聚乙烯醇，2～4份碳酸钠，1～2份油酸钠，3～5份三聚磷酸钠，5～9份十二烷基硫酸钠，6～8份二甲基二硅氧烷，1～3份偶联剂，0.5～1.2份氢氧化钠，10～14份聚乙氧基化脂肪醇，11～14份抗坏血酸，10～12份柠檬酸及40～50份去离子水。
进一步的，包括以下重量份数原料：8份苯甲酸钠，11份八甲基四硅氧烷，7份硬脂酸钠，3份羟基丙基甲基纤维素，8份聚乙烯醇，2碳酸钠，1份油酸钠，3份三聚磷酸钠，5份十二烷基硫酸钠，6份二甲基二硅氧烷，1份偶联剂，0.5份氢氧化钠，10份聚乙氧基化脂肪醇，11份抗坏血酸，10份柠檬酸及40份去离子水。
进一步的，包括以下重量份数原料： 10份苯甲酸钠， 16份八甲基四硅氧烷， 9份硬脂酸钠， 5份羟基丙基甲基纤维素， 12份聚乙烯醇， 4份碳酸钠， 2份油酸钠， 5份三聚磷酸钠， 9份十二烷基硫酸钠， 8份二甲基二硅氧烷， 3份偶联剂， 1.2份氢氧化钠， 14份聚乙氧基化脂肪醇， 14份抗坏血酸， 12份柠檬酸及50份去离子水。
进一步的，包括以下重量份数原料：9份苯甲酸钠，14份八甲基四硅氧烷，8份硬脂酸钠，4份羟基丙基甲基纤维素，10份聚乙烯醇，3碳酸钠，1.5份油酸钠，4份三聚磷酸钠，7份十二烷基硫酸钠，7份二甲基二硅氧烷，2份偶联剂，0.8份氢氧化钠，12份聚乙氧基化脂肪醇，13份抗坏血酸，11份柠檬酸及45份去离子水。
本发明的有益效果为：（1）该柔软剂为非离子型柔软剂，其柔软效果好，且该柔软剂对环境的污染小，对人体无危害，更加的环保；（2）使用该柔软剂的无纺布能够保持有良好的弹性及耐磨性。
具体实施方式
为使对本发明的结构特征及所达成的功效有更进一步的了解与认识，用以较佳的实施例配合详细的说明，说明如下：
实施例1
一种无纺布用柔软剂，包括以下重量份数原料：8份苯甲酸钠，11份八甲基四硅氧烷，7份硬脂酸钠，3份羟基丙基甲基纤维素，8份聚乙烯醇，2碳酸钠，1份油酸钠，3份三聚磷酸钠，5份十二烷基硫酸钠，6份二甲基二硅氧烷，1份偶联剂，0.5份氢氧化钠，10份聚乙氧基化脂肪醇，11份抗坏血酸，10份柠檬酸及40份去离子水。
实施例2
一种无纺布用柔软剂，包括以下重量份数原料： 10份苯甲酸钠， 16份八甲基四硅氧烷， 9份硬脂酸钠， 5份羟基丙基甲基纤维素， 12份聚乙烯醇， 4份碳酸钠， 2份油酸钠， 5份三聚磷酸钠， 9份十二烷基硫酸钠， 8份二甲基二硅氧烷， 3份偶联剂， 1.2份氢氧化钠，14份聚乙氧基化脂肪醇， 14份抗坏血酸， 12份柠檬酸及50份去离子水。
实施例3
一种无纺布用柔软剂，包括以下重量份数原料：9份苯甲酸钠，14份八甲基四硅氧烷，8份硬脂酸钠，4份羟基丙基甲基纤维素，10份聚乙烯醇，3碳酸钠，1.5份油酸钠，4份三聚磷酸钠，7份十二烷基硫酸钠，7份二甲基二硅氧烷，2份偶联剂，0.8份氢氧化钠，12份聚乙氧基化脂肪醇，13份抗坏血酸，11份柠檬酸及45份去离子水。
本发明的有益效果为：（1）该柔软剂为非离子型柔软剂，其柔软效果好，且该柔软剂对环境的污染小，对人体无危害，更加的环保；（2）使用该柔软剂的无纺布能够保持有良好的弹性及耐磨性。
以上显示和描述了本发明的基本原理、主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是本发明的原理，在不脱离本发明精神和范围的前提下本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明的范围内。本发明要求的保护范围由所附的权利要求书及其等同物界定。

Claims (4)

1.一种无纺布用柔软剂，其特征在于：包括以下重量份数原料：8～10份苯甲酸钠，11～16份八甲基四硅氧烷，7～9份硬脂酸钠，3～5份羟基丙基甲基纤维素，8～12份聚乙烯醇，2～4份碳酸钠，1～2份油酸钠，3～5份三聚磷酸钠，5～9份十二烷基硫酸钠，6～8份二甲基二硅氧烷，1～3份偶联剂，0.5～1.2份氢氧化钠，10～14份聚乙氧基化脂肪醇，11～14份抗坏血酸，10～12份柠檬酸及40～50份去离子水。
2.根据权利要求1所述的一种无纺布用柔软剂，其特征在于：包括以下重量份数原料：8份苯甲酸钠，11份八甲基四硅氧烷，7份硬脂酸钠，3份羟基丙基甲基纤维素，8份聚乙烯醇，2碳酸钠，1份油酸钠，3份三聚磷酸钠，5份十二烷基硫酸钠，6份二甲基二硅氧烷，1份偶联剂，0.5份氢氧化钠，10份聚乙氧基化脂肪醇，11份抗坏血酸，10份柠檬酸及40份去离子水。
3.根据权利要求1所述的一种无纺布用柔软剂，其特征在于：包括以下重量份数原料：10份苯甲酸钠， 16份八甲基四硅氧烷， 9份硬脂酸钠， 5份羟基丙基甲基纤维素， 12份聚乙烯醇， 4份碳酸钠， 2份油酸钠， 5份三聚磷酸钠， 9份十二烷基硫酸钠， 8份二甲基二硅氧烷， 3份偶联剂， 1.2份氢氧化钠， 14份聚乙氧基化脂肪醇， 14份抗坏血酸， 12份柠檬酸及50份去离子水。
4.根据权利要求1所述的一种无纺布用柔软剂，其特征在于：包括以下重量份数原料：9份苯甲酸钠，14份八甲基四硅氧烷，8份硬脂酸钠，4份羟基丙基甲基纤维素，10份聚乙烯醇，3碳酸钠，1.5份油酸钠，4份三聚磷酸钠，7份十二烷基硫酸钠，7份二甲基二硅氧烷，2份偶联剂，0.8份氢氧化钠，12份聚乙氧基化脂肪醇，13份抗坏血酸，11份柠檬酸及45份去离子水。
CN201711233691.XA 2017-11-30 2017-11-30 一种无纺布用柔软剂 Pending CN108103775A (zh)