CN108102609A - A kind of permanent seal cooling glass antidimmer - Google Patents
A kind of permanent seal cooling glass antidimmer Download PDFInfo
- Publication number
- CN108102609A CN108102609A CN201711282675.XA CN201711282675A CN108102609A CN 108102609 A CN108102609 A CN 108102609A CN 201711282675 A CN201711282675 A CN 201711282675A CN 108102609 A CN108102609 A CN 108102609A
- Authority
- CN
- China
- Prior art keywords
- parts
- juice
- potato
- permanent seal
- seal cooling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of permanent seal cooling glass antidimmers, belong to antifog technical field.The present invention mixes potato with water, squeezes the juice to get potato juice；Fruit with water is mixed, is squeezed the juice to get fruit juice；By potato juice, fruit juice, plasticizer and anti-regenerating agent ultrasonic mixing, microwave is to get modification potato juice；By chitosan liquid, polyvinyl alcohol liquid, nano-titanium dioxide, essential oil, modification potato juice, ethanol solution, lemon juice, silane coupling agent is placed in batch mixer, high-speed stirred obtains mixed slurry, and then mixed slurry is placed in froth in vacuum machine, bubble removing is vacuumized to get permanent seal cooling glass antidimmer.Antifoggant provided by the invention has excellent anti-fog performance, and can play long-acting antifog effect.
Description
Technical field
The invention discloses a kind of permanent seal cooling glass antidimmers, belong to antifog technical field.
Background technology
When using glass or other transparent bases, often there is the temperature difference in both sides, and the moisture content in air can be in glass or base
Mist formation is agglomerated on material, such as the too low possibly even frosting of temperature, so as to significantly reduce the light transmittance of glass or base material, influences sight.
This phenomenon often appears in windshield, house door glass, eyeglass etc., makes troubles to daily life,
Especially in vehicle running environment, driver is frequently encountered windscreen fogging on the early spring, autumn, winter and rainy day,
Condensation phenomenon causes security risk to the trip of vehicle, deals with improperly and easily causes the accident.Automobile window glass fogging be by
In automobile window glass surface temperature than relatively low, the saturated vapour pressure of moisture is less than the saturated vapour pressure of ambient enviroment, so
Steam will pool droplet on the surface of automobile window glass and form condensation phenomenon.Fogging makes windscreen become mould
Paste, light transmittance is extremely low, and driver is prevented easily to trigger traffic accident from ambient enviroment is clearly viewed.Therefore, automobile window glass
Antifog and demisting is that each driver is concerned about and eager issue to be resolved.In this regard, scholar has studied many anti-fogging measures, wherein
Most common method is exactly antifoggant.At present, the preparation method of glass antidimmer mainly has the surfactant method thin with macromolecule
Embrane method.Most surfaces active agent formulation antifoggant mainly by reducing contact angle of the glass surface to water, makes the water of glass surface
Pearl drawout and filming, ensure base material transparency achieve the purpose that it is antifog.Such antifoggant main component has surface-active
Agent, solvent, dispersant etc..Since its is simple for process, simple operation is subjected to the pro-gaze of scholar.However, glass in the market is prevented
Mist product, but all there is prepare when need heating, to production equipment requirement it is high the shortcomings that, especially in the presence of anti-fog effect not
Endurable shortcoming.In order to solve this problem, each side is finding various countermeasures.It common are small molecule surface-active
Dosage form, polymer electrolyte antifoggant and titanium dioxide type antifoggant etc., but the effect or unsatisfactory obtained.
Therefore, the shortcomings that traditional glass antifoggant is antifog ineffective and durability is poor how is improved, it is comprehensive to obtain higher
The glass antidimmer of performance is closed, is that it is promoted and applied to broader field, meets that industrial production demand is urgently to be resolved hurrily to ask
Topic.
The content of the invention
The present invention solves the technical problem of：It is antifog ineffective and durability is poor for traditional glass antifoggant
Shortcoming provides a kind of permanent seal cooling glass antidimmer.
In order to solve the above-mentioned technical problem, the technical solution adopted in the present invention is：
A kind of permanent seal cooling glass antidimmer, is made of the raw material of following parts by weight：20~30 parts of chitosan liquid, 20~30 parts
Polyvinyl alcohol liquid, 10~20 parts of nano-titanium dioxides, 10~20 parts of essential oils, 8~10 parts of modification potato juices, 10~20 parts of second
Alcoholic solution, 10~20 portions of lemon juices, 5~8 parts of silane coupling agents；
The preparation process of the modification potato juice is：It counts in parts by weight, by 20~30 parts of potato juices, 20~30 parts
Fruit juice, 3~4 parts of plasticizer and 3~4 parts of anti-regenerating agent ultrasonic mixings, microwave treatment is to get modification potato juice.
The preparation process of the chitosan liquid is：By chitosan and acetic acid solution in mass ratio 1：50~1：100 heating are stirred
Mixing is mixed, ultrasound degassing is to get chitosan liquid.
The preparation process of the polyvinyl alcohol liquid is：By polyvinyl alcohol and water in mass ratio 1：50~1：100 mixing swellings
Afterwards, heating stirring dissolving is to get polyvinyl alcohol liquid.
The essential oil is rose ethereal oil, any one in jasmine essential oil or tea tree ethereal oil.
The silane coupling agent is silane resin acceptor kh-550, in silane coupling agent KH-560 or Silane coupling reagent KH-570
Any one.
The potato juice is by potato and water in mass ratio 1：10~1：20 mixing squeeze the juice to obtain.
The fruit juice is by fruit and water in mass ratio 1：10~1：20 mixing squeeze the juice to obtain；The fruit is apple
Any one in fruit, pears or peach.
The plasticizer is di-n-octyl phthalate, BBP(Butyl Benzyl Phthalate, di-sec-octyl phthalate or
Any one in diisobutyl phthalate.
The anti-regenerating agent is sodium chloride, any one in sodium sulphate or stearic acid acyl lactylate.
The beneficial effects of the invention are as follows：
The potato juice that the present invention is modified by adding fruit juice, firstly, since heteroglycan molecular backbone in fruit juice
On there are hydrophobic grouping, and the end of the chain is hydrophilic radical, can the spontaneous surface orientation in glass adsorb, hydrophilic radical is presented and is directed toward water
Phase, hydrophobic group deviate from water phase, and film superficial water molecule is by hydrophobic grouping and reduces the interaction between hydrone, so as to reduce water
Surface tension so that level is layered on system surface, forms transparent moisture film, plays good anti-fog performance, secondly as Ma Ling
Not strong with reference to power between potato juice membrane molecule, surface molecular disperses unevenness, gap easily occurs, and film thickness is not high, and adhesion is poor,
By adding in fruit juice, the heteroglycan in fruit juice is with the crosslinking of potato juice molecular association intermolecular hydrogen bonding in netted knot
Structure, on the one hand, compensate for the hole of film so that the consistency and hardness of system are improved, and effectively hydrone are prevented to enter, drop
The moisture absorption ratio of low system, on the other hand, heteroglycan are crosslinked with potato juice molecular association intermolecular hydrogen bonding, form three dimensional network
Network interts crosslinking on the basis of chitosan and the three-dimensional network of polyvinyl alcohol formation, enhances the crosslink density of system, further carry
The consistency and hardness of high system so as to enhance the endurance quality of film, play long-acting antifog effect, further, since heteroglycan
Contain great amount of hydroxy group so that hydroxyl quantity increases in system so that film enhances with glass surface combination power, further enhances film
Endurance quality plays long-acting antifog effect.
Specific embodiment
By potato and water in mass ratio 1：10~1：20 are placed in juice extractor, squeeze the juice to get potato juice；By fruit
With water in mass ratio 1：10~1：20 are placed in juice extractor, squeeze the juice to get fruit juice；It counts in parts by weight, by 20~30 parts
Potato juice, 20~30 fruits juices, 3~4 parts of plasticizer and 3~4 parts of anti-regenerating agents are placed in No. 1 beaker, and by No. 1
Beaker is placed in ultrasonic disperse instrument, in supersonic frequency under the conditions of 55~75kHz, 20~30min of ultrasonic disperse obtains dispersion liquid,
Then dispersion liquid is placed in micro-wave oven, in frequency under the conditions of 1500~2000MHz, 20~30min of microwave is to get modified horse
Bell potato juice；By the acetic acid solution in mass ratio 1 that chitosan and mass fraction are 0.6~1.0%：50~1：100 are placed in No. 2 burnings
In cups, and No. 2 beakers are placed in digital display and are tested the speed in constant temperature blender with magnetic force, in temperature be 90~100 DEG C, rotating speed for 500~
Under the conditions of 600r/min, heating stirring mixes 30~50min, obtains mixed liquor, then mixed liquor is placed in ultrasonic disperse instrument, Yu Chao
Under the conditions of acoustic frequency is 55~75kHz, 20~30min is to get chitosan liquid for ultrasound degassing, by polyvinyl alcohol and water in mass ratio
1：50~1：100 add in No. 3 beakers, after being stirred 20~30min with glass bar, stand 3~4h of swelling, then No. 3 are burnt
Cup moves into digital display and tests the speed constant temperature blender with magnetic force, in temperature be 95~100 DEG C, under the conditions of rotating speed is 400~500r/min, heating
40~50min of stirring and dissolving is to get polyvinyl alcohol liquid；It counts in parts by weight, by 20~30 parts of chitosan liquid, 20~30 parts of poly- second
Enol liquid, 10~20 parts of nano-titanium dioxides, 10~20 parts of essential oils, 8~10 parts of modification potato juices, 10~20 parts of quality point
Number is 70~80% ethanol solution, 10~20 portions of lemon juices, and 5~8 parts of silane coupling agents are placed in batch mixer, in rotating speed be 1000
Under the conditions of~1200r/min, 30~50min of high-speed stirred obtains mixed slurry, and mixed slurry then is placed in froth in vacuum machine
In, 30~40min of bubble removing is vacuumized to get permanent seal cooling glass antidimmer.The essential oil be rose ethereal oil, jasmine anthosin
Oil or tea tree ethereal oil in any one.The silane coupling agent be silane resin acceptor kh-550, silane coupling agent KH-560 or
Any one in Silane coupling reagent KH-570.The fruit is apple, any one in pears or peach.The plasticizer is neighbour
In phthalic acid di-n-octyl, BBP(Butyl Benzyl Phthalate, di-sec-octyl phthalate or diisobutyl phthalate
Any one.The anti-regenerating agent is sodium chloride, any one in sodium sulphate or stearic acid acyl lactylate.
Example 1
By potato and water in mass ratio 1：20 are placed in juice extractor, squeeze the juice to get potato juice；Fruit and water are pressed into quality
Than 1：20 are placed in juice extractor, squeeze the juice to get fruit juice；It counts in parts by weight, by 30 parts of potato juices, 30 fruits slurry
Juice, 4 parts of plasticizer and 4 parts of anti-regenerating agents are placed in No. 1 beaker, and No. 1 beaker is placed in ultrasonic disperse instrument, in supersonic frequency
Under the conditions of 75kHz, ultrasonic disperse 30min obtains dispersion liquid, then dispersion liquid is placed in micro-wave oven, in frequency be 2000MHz
Under the conditions of, microwave 30min is to get modification potato juice；Chitosan and mass fraction are pressed into quality for 1.0% acetic acid solution
Than 1：100 are placed in No. 2 beakers, and No. 2 beakers are placed in digital display and are tested the speed in constant temperature blender with magnetic force, are 100 DEG C in temperature, turn
Speed is under the conditions of 600r/min, heating stirring mixing 50min obtains mixed liquor, then mixed liquor is placed in ultrasonic disperse instrument, Yu Chao
Under the conditions of acoustic frequency is 75kHz, 30min is to get chitosan liquid for ultrasound degassing, by polyvinyl alcohol and water in mass ratio 1：100 add
Enter in No. 3 beakers, after being stirred 30min with glass bar, stand swelling 4h, then No. 3 beakers are moved into digital displays and are tested the speed constant temperature magnetic
Power blender is 100 DEG C in temperature, and under the conditions of rotating speed is 500r/min, heating stirring dissolves 50min to get polyvinyl alcohol liquid；
It counts in parts by weight, by 30 parts of chitosan liquid, 30 parts of polyvinyl alcohol liquid, 20 parts of nano-titanium dioxides, 20 parts of essential oils, 10 parts of modifications
Potato juice, 20 parts of mass fractions are 80% ethanol solution, 20 portions of lemon juices, and 8 parts of silane coupling agents are placed in batch mixer, in
Under the conditions of rotating speed is 1200r/min, high-speed stirred 50min obtains mixed slurry, and mixed slurry then is placed in froth in vacuum machine
In, bubble removing 40min is vacuumized to get permanent seal cooling glass antidimmer.The essential oil is rose ethereal oil.It is described silane coupled
Agent is silane resin acceptor kh-550.The fruit is apple.The plasticizer is di-n-octyl phthalate.The anti-retrogradation
Agent is sodium chloride.
Example 2
By potato and water in mass ratio 1：20 are placed in juice extractor, squeeze the juice to get potato juice；Fruit and water are pressed into quality
Than 1：20 are placed in juice extractor, squeeze the juice to get fruit juice；It counts in parts by weight, by 30 parts of potato juices, 30 fruits slurry
Juice, 4 parts of plasticizer and 4 parts of anti-regenerating agents are placed in No. 1 beaker, and No. 1 beaker is placed in ultrasonic disperse instrument, in supersonic frequency
Under the conditions of 75kHz, ultrasonic disperse 30min obtains dispersion liquid, then dispersion liquid is placed in micro-wave oven, in frequency be 2000MHz
Under the conditions of, microwave 30min is to get modification potato juice；Chitosan and mass fraction are pressed into quality for 1.0% acetic acid solution
Than 1：100 are placed in No. 2 beakers, and No. 2 beakers are placed in digital display and are tested the speed in constant temperature blender with magnetic force, are 100 DEG C in temperature, turn
Speed is under the conditions of 600r/min, heating stirring mixing 50min obtains mixed liquor, then mixed liquor is placed in ultrasonic disperse instrument, Yu Chao
Under the conditions of acoustic frequency is 75kHz, 30min is to get chitosan liquid for ultrasound degassing, by polyvinyl alcohol and water in mass ratio 1：100 add
Enter in No. 3 beakers, after being stirred 30min with glass bar, stand swelling 4h, then No. 3 beakers are moved into digital displays and are tested the speed constant temperature magnetic
Power blender is 100 DEG C in temperature, and under the conditions of rotating speed is 500r/min, heating stirring dissolves 50min to get polyvinyl alcohol liquid；
It counts in parts by weight, by 30 parts of chitosan liquid, 30 parts of polyvinyl alcohol liquid, 20 parts of essential oils, 10 parts of modification potato juices, 20 parts of matter
Amount fraction is 80% ethanol solution, and 20 portions of lemon juices, 8 parts of silane coupling agents are placed in batch mixer, in rotating speed be 1200r/min items
Under part, high-speed stirred 50min obtains mixed slurry, and then mixed slurry is placed in froth in vacuum machine, vacuumizes bubble removing
40min is to get permanent seal cooling glass antidimmer.The essential oil is rose ethereal oil.The silane coupling agent is silane coupling agent KH-
550.The fruit is apple.The plasticizer is di-n-octyl phthalate.The anti-regenerating agent is sodium chloride.
Example 3
By potato and water in mass ratio 1：20 are placed in juice extractor, squeeze the juice to get potato juice；Fruit and water are pressed into quality
Than 1：20 are placed in juice extractor, squeeze the juice to get fruit juice；It counts in parts by weight, by 30 parts of potato juices, 30 fruits slurry
Juice, 4 parts of plasticizer and 4 parts of anti-regenerating agents are placed in No. 1 beaker, and No. 1 beaker is placed in ultrasonic disperse instrument, in supersonic frequency
Under the conditions of 75kHz, ultrasonic disperse 30min obtains dispersion liquid, then dispersion liquid is placed in micro-wave oven, in frequency be 2000MHz
Under the conditions of, microwave 30min is to get modification potato juice；Chitosan and mass fraction are pressed into quality for 1.0% acetic acid solution
Than 1：100 are placed in No. 2 beakers, and No. 2 beakers are placed in digital display and are tested the speed in constant temperature blender with magnetic force, are 100 DEG C in temperature, turn
Speed is under the conditions of 600r/min, heating stirring mixing 50min obtains mixed liquor, then mixed liquor is placed in ultrasonic disperse instrument, Yu Chao
Under the conditions of acoustic frequency is 75kHz, 30min is to get chitosan liquid for ultrasound degassing, by polyvinyl alcohol and water in mass ratio 1：100 add
Enter in No. 3 beakers, after being stirred 30min with glass bar, stand swelling 4h, then No. 3 beakers are moved into digital displays and are tested the speed constant temperature magnetic
Power blender is 100 DEG C in temperature, and under the conditions of rotating speed is 500r/min, heating stirring dissolves 50min to get polyvinyl alcohol liquid；
It counts in parts by weight, by 30 parts of chitosan liquid, 30 parts of polyvinyl alcohol liquid, 20 parts of nano-titanium dioxides, 10 parts of modification potato slurries
Juice, 20 parts of mass fractions are 80% ethanol solution, 20 portions of lemon juices, and 8 parts of silane coupling agents are placed in batch mixer, are in rotating speed
Under the conditions of 1200r/min, high-speed stirred 50min obtains mixed slurry, and then mixed slurry is placed in froth in vacuum machine, takes out true
Sky removes bubble removing 40min to get permanent seal cooling glass antidimmer.The silane coupling agent is silane resin acceptor kh-550.The water
Fruit is apple.The plasticizer is di-n-octyl phthalate.The anti-regenerating agent is sodium chloride.
Example 4
By potato and water in mass ratio 1：20 are placed in juice extractor, squeeze the juice to get potato juice；By chitosan and quality point
Number is 1.0% acetic acid solution in mass ratio 1：100 are placed in No. 2 beakers, and No. 2 beakers are placed in digital display and are tested the speed constant temperature magnetic force
It it is 100 DEG C in temperature, under the conditions of rotating speed is 600r/min, heating stirring mixing 50min obtains mixed liquor, then will be mixed in blender
It closes liquid to be placed in ultrasonic disperse instrument, in supersonic frequency under the conditions of 75kHz, ultrasound degassing 30min, will be poly- to get chitosan liquid
Vinyl alcohol and water in mass ratio 1：100 add in No. 3 beakers, after being stirred 30min with glass bar, stand swelling 4h, then by 3
Number beaker moves into digital display and tests the speed constant temperature blender with magnetic force, in temperature be 100 DEG C, under the conditions of rotating speed is 500r/min, heating stirring
50min is dissolved to get polyvinyl alcohol liquid；It counts in parts by weight, by 30 parts of chitosan liquid, 30 parts of polyvinyl alcohol liquid, 20 parts of nanometers
Titanium dioxide, 20 parts of essential oils, 10 parts of potato juices, 20 parts of mass fractions are 80% ethanol solution, 20 portions of lemon juices, 8 parts of silane
Coupling agent is placed in batch mixer, then will be mixed in rotating speed under the conditions of 1200r/min, high-speed stirred 50min obtains mixed slurry
It closes slurry to be placed in froth in vacuum machine, vacuumizes bubble removing 40min to get permanent seal cooling glass antidimmer.The essential oil is rose
Rare flower essential oil.The silane coupling agent is silane resin acceptor kh-550.The fruit is apple.The plasticizer is O-phthalic
Sour di-n-octyl.The anti-regenerating agent is sodium chloride.
Example 5
By potato and water in mass ratio 1：20 are placed in juice extractor, squeeze the juice to get potato juice；Fruit and water are pressed into quality
Than 1：20 are placed in juice extractor, squeeze the juice to get fruit juice；It counts in parts by weight, by 30 parts of potato juices, 30 fruits slurry
Juice, 4 parts of plasticizer and 4 parts of anti-regenerating agents are placed in No. 1 beaker, and No. 1 beaker is placed in ultrasonic disperse instrument, in supersonic frequency
Under the conditions of 75kHz, ultrasonic disperse 30min obtains dispersion liquid, then dispersion liquid is placed in micro-wave oven, in frequency be 2000MHz
Under the conditions of, microwave 30min is to get modification potato juice；Chitosan and mass fraction are pressed into quality for 1.0% acetic acid solution
Than 1：100 are placed in No. 2 beakers, and No. 2 beakers are placed in digital display and are tested the speed in constant temperature blender with magnetic force, are 100 DEG C in temperature, turn
Speed is under the conditions of 600r/min, heating stirring mixing 50min obtains mixed liquor, then mixed liquor is placed in ultrasonic disperse instrument, Yu Chao
Under the conditions of acoustic frequency is 75kHz, 30min is to get chitosan liquid for ultrasound degassing, by polyvinyl alcohol and water in mass ratio 1：100 add
Enter in No. 3 beakers, after being stirred 30min with glass bar, stand swelling 4h, then No. 3 beakers are moved into digital displays and are tested the speed constant temperature magnetic
Power blender is 100 DEG C in temperature, and under the conditions of rotating speed is 500r/min, heating stirring dissolves 50min to get polyvinyl alcohol liquid；
It counts in parts by weight, by 30 parts of chitosan liquid, 30 parts of polyvinyl alcohol liquid, 20 parts of nano-titanium dioxides, 20 parts of essential oils, 10 parts of modifications
Potato juice, 20 parts of mass fractions are 80% ethanol solution, and 8 parts of silane coupling agents are placed in batch mixer, in rotating speed be 1200r/
Under the conditions of min, high-speed stirred 50min obtains mixed slurry, and then mixed slurry is placed in froth in vacuum machine, vacuumizes removal
Bubble 40min is to get permanent seal cooling glass antidimmer.The essential oil is rose ethereal oil.The silane coupling agent is silane coupled
Agent KH-550.The fruit is apple.The plasticizer is di-n-octyl phthalate.The anti-regenerating agent is sodium chloride.
Comparative example：The glass antidimmer of Shanghai Chemical Engineering Technology Co., Ltd production.
The permanent seal cooling glass antidimmer of 1 to 5 gained of example and comparative example product are subjected to performance detection, specific detection method
It is as follows：
1. anti-fog effect：It takes（6×6）cm2Several pieces of plate glass cleans drying.Test specimen antifoggant is leached with clean sponge, is wiped
It is applied on the glass of drying and print is made.After antifoggant naturally dry, with the 1d of JY-82 types contact angle instrument measurement print
Contact angle θ1, 14d contact angles θ2And 28d contact angles θ3；When contact angle is below 10 degree, there is anti-fog effect；
Specific testing result is as shown in table 1：
Table 1
From 1 testing result of table, permanent seal cooling glass antidimmer prepared by technical solution of the present invention has excellent anti-fog performance
The characteristics of, and long-acting antifog effect can be played, it has broad prospects in the development of the antifog industry of glass.
Claims (9)
1. a kind of permanent seal cooling glass antidimmer, it is characterised in that：It is made of the raw material of following parts by weight：20~30 parts of shells gather
Liquid glucose, 20~30 parts of polyvinyl alcohol liquid, 10~20 parts of nano-titanium dioxides, 10~20 parts of essential oils, 8~10 parts of modification potato slurries
Juice, 10~20 parts of ethanol solutions, 10~20 portions of lemon juices, 5~8 parts of silane coupling agents；
The preparation process of the modification potato juice is：It counts in parts by weight, by 20~30 parts of potato juices, 20~30 parts
Fruit juice, 3~4 parts of plasticizer and 3~4 parts of anti-regenerating agent ultrasonic mixings, microwave treatment is to get modification potato juice.
2. a kind of permanent seal cooling glass antidimmer according to claim 1, it is characterised in that：The preparation process of the chitosan liquid
For：By chitosan and acetic acid solution in mass ratio 1：50~1：100 heating stirrings mix, and ultrasound degassing is to get chitosan liquid.
3. a kind of permanent seal cooling glass antidimmer according to claim 1, it is characterised in that：The preparation of the polyvinyl alcohol liquid
Cheng Wei：By polyvinyl alcohol and water in mass ratio 1：50~1：After 100 mixing swellings, heating stirring is dissolved to get polyvinyl alcohol liquid.
4. a kind of permanent seal cooling glass antidimmer according to claim 1, it is characterised in that：The essential oil is rose ethereal oil,
Any one in jasmine essential oil or tea tree ethereal oil.
5. a kind of permanent seal cooling glass antidimmer according to claim 1, it is characterised in that：The silane coupling agent is even for silane
Join agent KH-550, any one in silane coupling agent KH-560 or Silane coupling reagent KH-570.
6. a kind of permanent seal cooling glass antidimmer according to claim 1, it is characterised in that：The potato juice is by Ma Ling
Potato and water in mass ratio 1：10~1：20 mixing squeeze the juice to obtain.
7. a kind of permanent seal cooling glass antidimmer according to claim 1, it is characterised in that：The fruit juice be by fruit with
Water in mass ratio 1：10~1：20 mixing squeeze the juice to obtain；The fruit is apple, any one in pears or peach.
8. a kind of permanent seal cooling glass antidimmer according to claim 1, it is characterised in that：The plasticizer is phthalic acid
Any one in di-n-octyl, BBP(Butyl Benzyl Phthalate, di-sec-octyl phthalate or diisobutyl phthalate.
9. a kind of permanent seal cooling glass antidimmer according to claim 1, it is characterised in that：The anti-regenerating agent is sodium chloride,
Any one in sodium sulphate or stearic acid acyl lactylate.