CN108102606A - A kind of composite floor board adhesive - Google Patents
A kind of composite floor board adhesive Download PDFInfo
- Publication number
- CN108102606A CN108102606A CN201711222811.6A CN201711222811A CN108102606A CN 108102606 A CN108102606 A CN 108102606A CN 201711222811 A CN201711222811 A CN 201711222811A CN 108102606 A CN108102606 A CN 108102606A
- Authority
- CN
- China
- Prior art keywords
- parts
- floor board
- composite floor
- adhesive
- board adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of composite floor board adhesives, in terms of parts by weight, are made of following component：90 110 parts of glue, 10 23 parts of flour, 10 15 parts of hydrochloric acid solution.The composite floor board adhesive is easy to use, small with the amount of crying, and heat-resisting resistance to ironing is good.
Description
Technical field：
The present invention relates to floor production fields, are especially a kind of composite floor board adhesive.
Background technology：
Composite floor board is to be peeled into veneer or by flitch slicing into veneer by juggle, then three formed with adhesive gluing
The board-like material of layer or multilayer usually uses odd-level veneer, and forms the orthogonal gluing of machine direction of adjacent layer veneer.
The adhesive used in plywood production, generally use is from preparing adhesive, and the homemade adhesive of institute is substantially
It is made of glue and some auxiliary materials.It is high using process specifications for traditional adhesive, and worker is not easy to grasp.This
Outside, traditional adhesive makes that glue consumption is big, internal stress is big, heat-resisting resistance to ironing is poor and the shortcomings of easy seep through.
The content of the invention：
The technical problem to be solved by the invention is to provide a kind of easy to use, small with the amount of crying, heat-resisting resistance to ironing is good
Composite floor board adhesive.
The technical solution of the present invention is to provide a kind of composite floor board adhesive, in terms of parts by weight, by following group
It is grouped into：90-110 parts of glue, 10-23 parts of flour, 10-15 parts of hydrochloric acid solution.
Preferably, in terms of parts by weight, it is made of following component：100 parts of glue, 18 parts of flour, 12 parts of hydrochloric acid solution.
Further, 1 part of fungicide, 0.5 part of antifoaming agent, 0.3 part of dispersant are further included.
The beneficial effects of the invention are as follows：Passing through adjustment of formula so that adhesive of the invention is easy to use, small with the amount of crying,
Heat-resisting resistance to ironing is good.
Specific embodiment：
The invention will be further described With reference to embodiment：
Embodiment one
A kind of composite floor board adhesive, in terms of parts by weight, is made of following component：100 parts of glue, 18 parts of flour,
12 parts of hydrochloric acid solution.Wherein, antifoaming agent is the high Airex902W of enlightening, and pH adjusting agent is the APM-95 of Tao Shi chemical industry, fungicide
For the TD182 of fine horse energy chemical industry, coalescents DPNB, wetting agent is the high Wet270 of enlightening, and dispersant is the high Dispers755W of enlightening.
Embodiment two
A kind of composite floor board adhesive, in terms of parts by weight, is made of following component：100 parts of glue, 18 parts of flour,
12 parts of hydrochloric acid solution, 0.5 part of antifoaming agent, 0.3 part of dispersant.The adhesive of the present invention is easy to use, small with the amount of crying, heat-resisting resistance to boiling hot
Performance is good.
Claims (3)
1. a kind of composite floor board adhesive, it is characterised in that：In terms of parts by weight, it is made of following component：Glue 90-110
Part, 10-23 parts of flour, 10-15 parts of hydrochloric acid solution.
2. composite floor board adhesive according to claim 1, it is characterised in that：In terms of parts by weight, by following component
Composition：100 parts of glue, 18 parts of flour, 12 parts of hydrochloric acid solution.
3. composite floor board adhesive according to claim 1, it is characterised in that：Further include 1 part of fungicide, antifoaming agent
0.5 part, 0.3 part of dispersant.