CN108102329A - 一种耐冲击的亚克力钻石及其制备方法 - Google Patents

一种耐冲击的亚克力钻石及其制备方法 Download PDF

Info

Publication number
CN108102329A
CN108102329A CN201711384078.8A CN201711384078A CN108102329A CN 108102329 A CN108102329 A CN 108102329A CN 201711384078 A CN201711384078 A CN 201711384078A CN 108102329 A CN108102329 A CN 108102329A
Authority
CN
China
Prior art keywords
compounding
antioxidant
impact
curing agent
diamond
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711384078.8A
Other languages
English (en)
Inventor
陈增辉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Cangnan County Tongpu Craft Gift Co
Original Assignee
Cangnan County Tongpu Craft Gift Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Cangnan County Tongpu Craft Gift Co filed Critical Cangnan County Tongpu Craft Gift Co
Priority to CN201711384078.8A priority Critical patent/CN108102329A/zh
Publication of CN108102329A publication Critical patent/CN108102329A/zh
Pending legal-status Critical Current

Abstract

一种耐冲击的亚克力钻石，按重量份计包括下述组分：磷酸酯8‑15％；消泡剂0.25‑1％；固化剂0.1‑0.5％；复配的抗氧剂0.1‑2％；玻璃纤维15％；亚克力树脂单体至100％；所述亚克力树脂单体由聚碳酸酯树脂与聚甲基丙烯酸甲酯的混合物构成，其中聚碳酸酯树脂与聚甲基丙烯酸甲酯的重量百分比为5：1‑5：2；所述的固化剂为有机过氧化物、偶氮化合物中的一种；所述的磷酸酯为间苯二酚四苯基二磷酸酯；所述的复配的抗氧剂为由质量百分比为50％的三亚磷酸与质量百分比为50％的四季戊四醇酯组成的混合物。

Description

一种耐冲击的亚克力钻石及其制备方法
技术领域
本发明涉具体涉及一种耐冲击的亚克力钻石及其制备方法。
背景技术
模压亚克力钻石通过将无机填料如氢氧化铝混入亚克力类树脂来制备，这种亚克力钻石具有各种优异的功能和性能，如外观、柔软的手感等，但是由于亚克力类树脂本身的特性使得产品的强度与耐热性存在一定的缺陷。
发明内容
为了解决上述问题，本发明提供了一种耐冲击的亚克力钻石：
一种耐冲击的亚克力钻石，按重量份计包括下述组分：
磷酸酯8-15％；
消泡剂0.25-1％；
固化剂0.1-0.5％；
复配的抗氧剂0.1-2％；
玻璃纤维15％；
亚克力树脂单体至100％；
所述亚克力树脂单体由聚碳酸酯树脂与聚甲基丙烯酸甲酯的混合物构成，其中聚碳酸酯树脂与聚甲基丙烯酸甲酯的重量百分比为5：1-5：2；所述的固化剂为有机过氧化物、偶氮化合物中的一种；所述的磷酸酯为间苯二酚四苯基二磷酸酯；所述的复配的抗氧剂为由质量百分比为50％的三亚磷酸与质量百分比为50％的四季戊四醇酯组成的混合物。
一种耐冲击的亚克力钻石的制备方法，步骤如下：捏合机中加入复配的抗氧剂、亚克力树脂单体、玻璃纤维、固化剂、消泡剂，将上述原料捏合获得透明的亚克力模塑料，将亚克力模塑料填充到模具中，在135℃、35MPa的压力下固化，制得亚克力钻石。
本发明具有如下有益效果：本产品大大提高了其韧性与强度，从而无论在外观还是在其性能上都更加接近真实的钻石，而且制作的工艺方法简单，非常适宜工业化生产。
具体实施方式
下面结合实施例对本发明进行进一步说明。
实施例1：一种耐冲击的亚克力钻石，按重量份计包括下述组分：
磷酸酯8％(间苯二酚四苯基二磷酸酯)；
消泡剂0.25％；
固化剂0.1％；
玻璃纤维15％；
复配的抗氧剂0.1％(三亚磷酸0.05％；四季戊四醇酯0.05％)。
亚克力树脂单体至100％(聚碳酸酯树脂：聚甲基丙烯酸甲酯为5:1.5)。
实施例2：一种耐冲击的亚克力钻石，按重量份计包括下述组分：
磷酸酯10％(间苯二酚四苯基二磷酸酯)；
消泡剂0.7％；
固化剂0.3％；
玻璃纤维15％；
复配的抗氧剂1％(三亚磷酸0.5％；四季戊四醇酯0.5％)。
亚克力树脂单体至100％(聚碳酸酯树脂：聚甲基丙烯酸甲酯为5:1.5)。
实施例3：一种耐冲击的亚克力钻石，按重量份计包括下述组分：
磷酸酯15％(间苯二酚四苯基二磷酸酯)；
消泡剂1％；
固化剂0.5％；
玻璃纤维15％；
复配的抗氧剂2％(三亚磷酸1％；四季戊四醇酯1％)；
亚克力树脂单体至100％(聚碳酸酯树脂：聚甲基丙烯酸甲酯为5:1.5)。
一种耐冲击的亚克力钻石的制备方法，步骤如下：捏合机中加入复配的抗氧剂、亚克力树脂单体、玻璃纤维、固化剂、消泡剂，将上述原料捏合获得透明的亚克力模塑料，将亚克力模塑料填充到模具中，在135℃、35MPa的压力下固化，制得亚克力钻石。
显然，本发明的上述实施例仅仅是为了说明本发明所作的举例，而并非对本发明的实施方式的限定。对于所属领域的普通技术人员来说，在上述说明的基础上还可以做出其他不同形式的变化或变动。这里无需也无法对所有的实施方式予以穷例。而这些属于本发明的实质精神所引申出的显而易见的变化或变动仍属于本发明的保护范围。

Claims (2)

1.一种耐冲击的亚克力钻石，其特征在于：按重量份计包括下述组分：
磷酸酯8-15％；
消泡剂0.25-1％；
固化剂0.1-0.5％；
复配的抗氧剂0.1-2％；
玻璃纤维15％；
亚克力树脂单体至100％；
所述亚克力树脂单体由聚碳酸酯树脂与聚甲基丙烯酸甲酯的混合物构成，其中聚碳酸酯树脂与聚甲基丙烯酸甲酯的重量百分比为5：1-5：2；所述的固化剂为有机过氧化物、偶氮化合物中的一种；所述的磷酸酯为间苯二酚四苯基二磷酸酯；所述的复配的抗氧剂为由质量百分比为50％的三亚磷酸与质量百分比为50％的四季戊四醇酯组成的混合物。
2.一种制备权利要求1所述的耐冲击的亚克力钻石的方法，其特征在于步骤如下：捏合机中加入复配的抗氧剂、亚克力树脂单体、玻璃纤维、固化剂、消泡剂，将上述原料捏合获得透明的亚克力模塑料，将亚克力模塑料填充到模具中，在135℃、35MPa的压力下固化，制得亚克力钻石。
CN201711384078.8A 2017-12-20 2017-12-20 一种耐冲击的亚克力钻石及其制备方法 Pending CN108102329A (zh)