CN108084829A - A kind of internal combustion engine air modifying agent - Google Patents
A kind of internal combustion engine air modifying agent Download PDFInfo
- Publication number
- CN108084829A CN108084829A CN201711346201.7A CN201711346201A CN108084829A CN 108084829 A CN108084829 A CN 108084829A CN 201711346201 A CN201711346201 A CN 201711346201A CN 108084829 A CN108084829 A CN 108084829A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- oxide
- modifying agent
- air
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of internal combustion engine air modifying agent, belong to internal combustion engine art field, the air modifying agent by weight, including following components:1,100 1250 parts of acrylic plastics iron oxide red primer mixed solvent, 300 400 parts of solidfied material, 110 140 parts of modified polyolefin resin resist heavy 15 30 parts of agent, 6.5 9 parts of aerosil, 25 40 parts of superfine talcum powder, 37 parts of coupling agent;The present invention has activated the air of air-intake of combustion engine mouth, reduces the activation energy of burning needs, improves combustion velocity, can significantly improve the efficiency of combustion of fuel oil, reduces harmful exhaust;Such as the discharge of carbon monoxide, carbon dioxide, oxynitrides.
Description
Technical field
The invention belongs to technical field of internal combustion engines, more particularly to a kind of internal combustion engine air modifying agent.
Background technology
Due to gradually decreasing for petroleum resources, in order to reduce dependence of the internal combustion engine to petroleum based fuels increasingly in short supply, respectively
State has all carried out internal combustion engine and has used the research work of substitute fuel and put into effect many restrictive policies, with progressively substitute gasoline and
Diesel oil, such as natural gas fuel, methanol, ethyl alcohol, synthetic gasoline, combined diesel oil and dimethyl ether or using pure electric automobile
Deng in order to save petroleum resources, realizing the sustainable development of the mankind, the efficiency of combustion for improving internal combustion engine is imperative;People couple
The requirement for air quality of living is higher and higher, and it is similary imperative to reduce environmental pollution, wherein one of most important means are to reduce
The pollution level of pollution sources, the harmful exhaust of internal combustion engine discharge is one of air primary pollution source, therefore how to improve internal combustion engine
Efficiency of combustion, be greatly decreased harmful exhaust emissions need it is urgently to be resolved hurrily.
At present there are many kinds of method improve internal combustion engine efficiency of combustion, reduce the discharge of pernicious gas, as adiabatic engine,
Catalysis burning, oil emulsion, oxygen-enriched combusting, turbocharging, middle refrigeration technique and exhaust gas recycling, injection water, vapor, flue gas follow again
The methods of ring, bias combustion, pre-mixing combustion, pure oxygen burning, homogeneous charge compression and combustion, ozone burning.
The content of the invention
In view of the drawbacks described above of the prior art, it is empty that the technical problems to be solved by the invention are to provide a kind of internal combustion engine
Gas modifying agent.This air modifying agent with the air of air-intake of combustion engine mouth is mixed and effectively increases fuel combustion efficiency, and is subtracted
Waste emission amount is lacked.
To achieve the above object, the present invention provides provide a kind of internal combustion engine air modifying agent, the air modifying agent
By weight, including following components:1100-1250 parts of acrylic plastics iron oxide red primer mixed solvent, 300-400 parts of solidfied material,
110-140 parts of modified polyolefin resin, anti-heavy 15-30 parts of agent, 6.5-9 parts of aerosil, 25-40 parts of superfine talcum powder,
3-7 parts of coupling agent;
Include dimethylbenzene 250-320 according to weight meter in the acrylic plastics iron oxide red primer mixed solvent unit mass
Part, 430-480 parts of toluene, 120-150 parts of ethyl acetate, 120-150 parts of cyclohexanone, 170-200 parts of butyl acetate;
Include acrylic resin modified 180-230 parts according to weight meter in the solidfied material unit mass, function powder
110-130 parts, the first 30-45 parts of di-iron trioxide, 75-100 parts of ferroso-ferric oxide, 6-9 parts of zinc oxide, 10-15 parts of calcium carbonate;
The function powder by weight, including alundum (Al2O3) 10%-30%, organic germanium powder 0.1%-1.2%, Lan Bao
Mountain flour 0.1%-2%, albumen stone powder 1%-6%, seaweed carbon powder 1%-10%, nanometer elbaite powder 2%-15%, oxygen
Change magnesium 3%-10%, boron trioxide 5%-15%, nickel oxide powder 2%-15%, molybdenum oxide powder 1%-10%, the two or three oxidation two
Iron 3%-15%, sodium oxide molybdena 0.1%-3.5%, phosphorus pentoxide 0.1%-1.5%, kaolin 3%-10%, ceria
1%-12%, diatom ooze powder 2%-8%, calcium oxide 0.1%-2%, periclase 0.1%-2%, activated carbon 0.1%-5% are swollen
Moisten soil 2%-15%, cordierite powder 3%-10%, zircon flour 1%-10%, snake mountain flour 2%-15%, cobalt oxide powder 3%-
10%, Nd-Fe-B magnetic powder 0.1%-2%, AL2O3-SiO2- MgO-FeO ceramic powders 3%-10%, nano-titanium dioxide 3%-
10%.
The preparation method of the internal combustion engine air modifying agent is as follows:
By 250-320 parts of dimethylbenzene, 430-480 parts of toluene, 120-150 parts of ethyl acetate, 120-150 parts of cyclohexanone, second
170-200 parts of acid butyl ester is uniformly mixed standing and obtains acrylic plastics iron oxide red primer mixed solvent in two hours;By modified acroleic acid
180-230 parts of resin, 110-130 parts of function powder, the first 30-45 parts of di-iron trioxide, 75-100 parts of ferroso-ferric oxide, oxidation
6-9 parts of zinc, 10-15 parts of calcium carbonate, which is uniformly mixed, obtains solidfied material.
It will include alundum (Al2O3) 10%-30%, organic germanium powder 0.1%-1.2%, sapphire powder according to weight meter
0.1%-2%, albumen stone powder 1%-6%, seaweed carbon powder 1%-10%, nanometer elbaite powder 2%-15%, magnesia
3%-10%, boron trioxide 5%-15%, nickel oxide powder 2%-15%, molybdenum oxide powder 1%-10%, the second di-iron trioxide
3%-15%, sodium oxide molybdena 0.1%-3.5%, phosphorus pentoxide 0.1%-1.5%, kaolin 3%-10%, ceria 1%-
12%, diatom ooze powder 2%-8%, calcium oxide 0.1%-2%, periclase 0.1%-2%, activated carbon 0.1%-5%, bentonite
2%-15%, cordierite powder 3%-10%, zircon flour 1%-10%, snake mountain flour 2%-15%, cobalt oxide powder 3%-10%,
Nd-Fe-B magnetic powders 0.1%-2%, AL2O3-SiO2- MgO-FeO ceramic powders 3%-10%, nano-titanium dioxide 3%-10% etc.
Ingredient is mixed and is ground into powdery, when 800-1000 DEG C of temperature lower calcination 3 is small after be cooled to naturally room temperature stand 5-6 days after
It is ground into powdery and obtains function powder;
1100-1250 parts of acrylic plastics iron oxide red primer mixed solvent, 300-400 parts of solidfied material are added in the reactor,
Stand 3h;Then 110-140 parts of modified polyolefin resin is added in, 1.2- is reacted in anti-heavy 15-30 parts of agent at a temperature of 30-40 DEG C
1.8 it is small when;0-20 DEG C is adjusted the temperature to, adds 6.5-9 parts of aerosil, 25-40 parts of superfine talcum powder, coupling agent 3-
7 parts are continued to stir, and maintain 80-90 DEG C heat treatment 5-6 it is small when after filtering precipitation, impurity obtain air improvement solvent.
The present invention sprinkling that nebulizes at oil-burning machine air inlet is sufficiently mixed with air at air inlet, wherein air and air
Modifying agent ratio is 35:1-37:1, air has been activated by air modifying agent, has reduced the activation energy of burning needs, improves
Combustion velocity can significantly improve the efficiency of combustion of fuel oil, reduce harmful exhaust;Such as carbon monoxide, carbon dioxide, nitrogen
The discharge of oxygen compound.
The beneficial effects of the invention are as follows:
The present invention has activated the air of air-intake of combustion engine mouth, reduces the activation energy of burning needs, improves combustion reaction
Speed can significantly improve the efficiency of combustion of fuel oil, reduce harmful exhaust;Such as carbon monoxide, carbon dioxide, oxynitrides
Discharge;
The present invention is apparent to the reduction of oil consumption;
The present invention by activating air, it can be achieved that reduce maximum outbreak pressure, reduce engine combustion noise, discharge and
Delivery temperature realizes lean burn, improves burning efficiency of internal combustion engine, improves performance driving economy and emission performance.
Specific embodiment
With reference to embodiment, the invention will be further described:
Solidfied material and function powder are prepared by the following in following embodiment;
By the dimethylbenzene of corresponding number, toluene, ethyl acetate, cyclohexanone, butyl acetate is uniformly mixed standing two hours must
To acrylic plastics iron oxide red primer mixed solvent;Will be acrylic resin modified, function powder, the first di-iron trioxide, four oxidations
Three-iron, zinc oxide, calcium carbonate are uniformly mixed to obtain solidfied material.
By the alundum (Al2O3) of corresponding weight, organic germanium powder, sapphire powder, albumen stone powder, seaweed carbon powder, nanometer lithium
Tourmaline powder, magnesia, boron trioxide nickel oxide powder, molybdenum oxide powder, the second di-iron trioxide, sodium oxide molybdena, phosphorus pentoxide are high
Ridge soil, ceria, diatom ooze powder, calcium oxide, periclase, activated carbon, bentonite, cordierite powder, zircon flour, serpentine
Powder, cobalt oxide powder, Nd-Fe-B magnetic powders, AL2O3-SiO2- MgO-FeO ceramic powders, nano-titanium dioxide are mixed and ground
Powdering, when 800-1000 DEG C of temperature lower calcination 3 is small after be cooled to naturally after room temperature stands 5-6 days and be ground into powdery and obtain function
Powder;
Embodiment 1
Air modifying agent by weight, including following components:1100 parts of acrylic plastics iron oxide red primer mixed solvent cures
300 parts of object, 110 parts of modified polyolefin resin resist heavy 15 parts of agent, 6.5 parts of aerosil, 25 parts of superfine talcum powder, coupling
3 parts of agent;In the present embodiment, resist the N-Methyl pyrrolidone solution that heavy agent is modified polyurea;In the present embodiment, coupling agent uses silicon
Alkane coupling agent;
Include 250 parts of dimethylbenzene, first according to weight meter in the acrylic plastics iron oxide red primer mixed solvent unit mass
430 parts of benzene, 120 parts of ethyl acetate, 120 parts of cyclohexanone, 170 parts of butyl acetate;
Include acrylic resin modified 180 parts according to weight meter in the solidfied material unit mass, 110 parts of function powder,
First 30 parts of di-iron trioxide, 75 parts of ferroso-ferric oxide, 6 parts of zinc oxide, 10 parts of calcium carbonate;
The function powder by weight, including alundum (Al2O3) 30%, organic germanium powder 0.1%, sapphire powder 0.1%,
Albumen stone powder 1%, seaweed carbon powder 1%, nanometer elbaite powder 2%, magnesia 3%, boron trioxide 5%, nickel oxide powder
2%, molybdenum oxide powder 1%, the second di-iron trioxide 3%, sodium oxide molybdena 0.1%, phosphorus pentoxide 0.1%, kaolin 3%, dioxy
Change cerium 1%, diatom ooze powder 2%, calcium oxide 0.1%, periclase 0.1%, activated carbon 0.1%, bentonite 2%, cordierite powder
8.2%, zircon flour 10%, snake mountain flour 2%, cobalt oxide powder 3%, Nd-Fe-B magnetic powders 0.1%, AL2O3-SiO2- MgO-FeO makes pottery
Porcelain powder 10%, nano-titanium dioxide 10%;
The preparation method of the internal combustion engine air modifying agent is as follows:
1100 parts of acrylic plastics iron oxide red primer mixed solvent, 300 parts of solidfied material are added in the reactor, stand 3h;So
110 parts of modified polyolefin resin, anti-heavy 15 parts of agent are added in afterwards when reaction 1.2-1.8 is small at a temperature of 30-40 DEG C;It adjusts the temperature to
0-20 DEG C, 6.5 parts of aerosil is added, 25 parts of superfine talcum powder, 3 parts of coupling agent continues to stir, and maintains 80-90 DEG C
Precipitation and contaminant filter are obtained into air improvement solvent after when heat treatment 5-6 is small.
Embodiment 2
Air modifying agent by weight, including following components:1250 parts of acrylic plastics iron oxide red primer mixed solvent cures
400 parts of object, 140 parts of modified polyolefin resin resist heavy 30 parts of agent, 9 parts of aerosil, 40 parts of superfine talcum powder, coupling agent 7
Part;In the present embodiment, resist the N-Methyl pyrrolidone solution that heavy agent is modified polyurea;In the present embodiment, coupling agent uses silane
Coupling agent;
Include 320 parts of dimethylbenzene, first according to weight meter in the acrylic plastics iron oxide red primer mixed solvent unit mass
480 parts of benzene, 150 parts of ethyl acetate, 150 parts of cyclohexanone, 200 parts of butyl acetate;
Include acrylic resin modified 230 parts according to weight meter in the solidfied material unit mass, 130 parts of function powder,
First 45 parts of di-iron trioxide, 100 parts of ferroso-ferric oxide, 9 parts of zinc oxide, 15 parts of calcium carbonate.
The function powder by weight, including alundum (Al2O3) 30%, organic germanium powder 0.1%, sapphire powder 0.1%,
Albumen stone powder 1%, seaweed carbon powder 1%, nanometer elbaite powder 2%, magnesia 3%, boron trioxide 5%, nickel oxide powder
2%, molybdenum oxide powder 1%, the second di-iron trioxide 3%, sodium oxide molybdena 0.1%, phosphorus pentoxide 0.1%, kaolin 3%, dioxy
Change cerium 1%, diatom ooze powder 2%, calcium oxide 0.1%, periclase 0.1%, activated carbon 0.1%, bentonite 2%, cordierite powder
8.2%, zircon flour 10%, snake mountain flour 2%, cobalt oxide powder 3%, Nd-Fe-B magnetic powders 0.1%, AL2O3-SiO2- MgO-FeO makes pottery
Porcelain powder 10%, nano-titanium dioxide 10%;
The preparation method of the internal combustion engine air modifying agent is as follows:
1250 parts of acrylic plastics iron oxide red primer mixed solvent, 400 parts of solidfied material are added in the reactor, stand 3h;So
140 parts of modified polyolefin resin, anti-heavy 30 parts of agent are added in afterwards when reaction 1.2-1.8 is small at a temperature of 30-40 DEG C;It adjusts the temperature to
0-20 DEG C, 9 parts of aerosil is added, 40 parts of superfine talcum powder, 7 parts of coupling agent continues to stir, and maintains 80-90 DEG C of heat
Precipitation and contaminant filter are obtained into air improvement solvent after when processing 5-6 is small.
Embodiment 3
Air modifying agent by weight, including following components:1200 parts of acrylic plastics iron oxide red primer mixed solvent cures
350 parts of object, 130 parts of modified polyolefin resin resist heavy 23 parts of agent, 8 parts of aerosil, 35 parts of superfine talcum powder, coupling agent 5
Part;In the present embodiment, resist the N-Methyl pyrrolidone solution that heavy agent is modified polyurea;In the present embodiment, coupling agent uses silane
Coupling agent;
Include 280 parts of dimethylbenzene, first according to weight meter in the acrylic plastics iron oxide red primer mixed solvent unit mass
450 parts of benzene, 130 parts of ethyl acetate, 130 parts of cyclohexanone, 180 parts of butyl acetate;
Include acrylic resin modified 200 parts according to weight meter in the solidfied material unit mass, 120 parts of function powder,
First 35 parts of di-iron trioxide, 90 parts of ferroso-ferric oxide, 8 parts of zinc oxide, 12 parts of calcium carbonate.
The function powder by weight, including alundum (Al2O3) 10%, organic germanium powder 1.2%, sapphire powder 2%, egg
Albarium end 6%, seaweed carbon powder 3.8%, nanometer elbaite powder 2%, magnesia 3%, boron trioxide 5%, nickel oxide powder
2%, molybdenum oxide powder 10%, the second di-iron trioxide 3%, sodium oxide molybdena 3.5%, phosphorus pentoxide 1.5%, kaolin 3%, dioxy
Change cerium 1%, diatom ooze powder 8%, calcium oxide 2%, periclase 2%, activated carbon 5%, bentonite 2%, cordierite powder 10%, zirconium
Mountain flour 1%, snake mountain flour 2%, cobalt oxide powder 3%, Nd-Fe-B magnetic powders 2%, AL2O3-SiO2- MgO-FeO ceramic powders 3%,
Nano-titanium dioxide 3%;
The preparation method of the internal combustion engine air modifying agent is as follows:
1200 parts of acrylic plastics iron oxide red primer mixed solvent, 350 parts of solidfied material are added in the reactor, stand 3h;So
130 parts of modified polyolefin resin, anti-heavy 23 parts of agent are added in afterwards when reaction 1.2-1.8 is small at a temperature of 30-40 DEG C;It adjusts the temperature to
0-20 DEG C, 8 parts of aerosil is added, 35 parts of superfine talcum powder, 5 parts of coupling agent continues to stir, and maintains 80-90 DEG C of heat
Precipitation and contaminant filter are obtained into air improvement solvent after when processing 5-6 is small.
12 horsepowers of single cylinder diesel is used in the present embodiment, starts diesel engine under normal conditions, passes through electric eddy current dynamometer
Measure the rotating speed of internal combustion engine, torque and it is 30 seconds every in oil consumption, the probe of gas tester is extend into exhaust pipe,
Carbon monoxide, nitric oxide in reading exhaust gas, the concentration of nitrogen dioxide;After the completion of test, sprayed in air inlet pipe entrance side empty
Gas modifying agent ratio, air and air modifying agent ratio are 36:1, it retests and records related data;
It is to spray the front and rear rate of fuel consumption variation that the air modifying agent in embodiment 1-3 measures respectively as shown in table 1 to table 3
Table from table 1 to table 3, in the range of the effective power of diesel engine, sprays the rate of fuel consumption after air modifying agent and is substantially reduced;
Table 1 sprays front and rear oil changes table
(air modifying agent in sprinkling embodiment 1)
Table 2 sprays front and rear oil changes table
(air modifying agent in sprinkling embodiment 2)
Table 3 sprays front and rear oil changes table
(air modifying agent in sprinkling embodiment 3)
It is to spray an oxygen in the front and rear exhaust gas that the air modifying agent in embodiment 1-3 measures respectively as shown in table 4 to table 6
Change carbon content table, from table 1 to table 3, in the range of the effective power of diesel engine, spray one oxygen of tail gas after air modifying agent
Changing carbon emission amount significantly reduces;
Table 4 sprays carbon monoxide content table in front and rear exhaust gas
(air modifying agent in sprinkling embodiment 1)
Table 5 sprays front and rear carbon monoxide content table
(air modifying agent in sprinkling embodiment 2)
Table 6 sprays front and rear carbon monoxide content table
(air modifying agent in sprinkling embodiment 3)
It is to spray dioxy in the front and rear exhaust gas that the air modifying agent in embodiment 1-3 measures respectively as shown in table 7 to table 9
Change nitrogen content table, from table 1 to table 3, in the range of the effective power of diesel engine, the nitrogen dioxide content in tail gas is with work(
Rate increase first becomes larger to become smaller afterwards, compared to the nitrogen dioxide content before sprinkling, sprays the tail gas nitrogen dioxide row after air modifying agent
High-volume reduced always in each testing time point;
Table 7 sprays nitrogen dioxide content table in front and rear exhaust gas
(air modifying agent in sprinkling embodiment 1)
Table 8 sprays nitrogen dioxide content table in front and rear exhaust gas
(air modifying agent in sprinkling embodiment 2)
Table 9 sprays nitrogen dioxide content table in front and rear exhaust gas
(air modifying agent in sprinkling embodiment 3)
As shown in table 10 to table 12, sprayed one in the front and rear exhaust gas that the air modifying agent in embodiment 1-3 measures respectively
Content of nitrogen oxide table, from table 1 to table 3, in the range of the effective power of diesel engine, content of nitric oxide in tail gas with
Power increases and increases, and compared to the content of nitric oxide before sprinkling, sprays the tail gas nitric oxide discharge capacity after air modifying agent
It is reduced always in each testing time point;
Table 10 sprays content of nitric oxide table in front and rear exhaust gas
(air modifying agent in sprinkling embodiment 1)
Table 11 sprays content of nitric oxide table in front and rear exhaust gas
(air modifying agent in sprinkling embodiment 2)
Table 12 sprays content of nitric oxide table in front and rear exhaust gas
(air modifying agent in sprinkling embodiment 3)
As shown in table 1 to table 12, the internal combustion engine being prepared using the method for embodiment 1-3 is activated with air modifying agent
The air of air-intake of combustion engine mouth reduces the activation energy of burning needs, improves combustion velocity, can significantly improve fuel oil
Efficiency of combustion, oil consumption reduces about 3%-9%;Harmful exhaust is reduced, such as carbon monoxide reduces about 1%-3%, two
Nitrogen oxide reduces about 2%-7%, nitric oxide reduces about 8%-15%;It is most produced shockingly by activating air, it can be achieved that reducing
Pressure is sent out, reduces combustion noise, discharge and the delivery temperature of engine, realizes lean burn, burning efficiency of internal combustion engine is improved, carries
High performance driving economy and emission performance.
The preferred embodiment of the present invention described in detail above.It should be appreciated that those of ordinary skill in the art without
Creative work is needed according to the present invention can to conceive and makes many modifications and variations.Therefore, all technologies in the art
Personnel are available by logical analysis, reasoning, or a limited experiment on the basis of existing technology under this invention's idea
Technical solution, all should be in the protection domain being defined in the patent claims.
Claims (1)
1. a kind of internal combustion engine air modifying agent, it is characterised in that:The air modifying agent by weight, including following components:
1100-1250 parts of acrylic plastics iron oxide red primer mixed solvent, 300-400 parts of solidfied material, modified polyolefin resin 110-140
Part, resist heavy 15-30 parts of agent, 6.5-9 parts of aerosil, 25-40 parts of superfine talcum powder, 3-7 parts of coupling agent;
Include 250-320 parts of dimethylbenzene, first according to weight meter in the acrylic plastics iron oxide red primer mixed solvent unit mass
430-480 parts of benzene, 120-150 parts of ethyl acetate, 120-150 parts of cyclohexanone, 170-200 parts of butyl acetate;
Include acrylic resin modified 180-230 parts according to weight meter in the solidfied material unit mass, function powder 110-130
Part, the first 30-45 parts of di-iron trioxide, 75-100 parts of ferroso-ferric oxide, 6-9 parts of zinc oxide, 10-15 parts of calcium carbonate;
The function powder by weight, including alundum (Al2O3) 10%-30%, organic germanium powder 0.1%-1.2%, sapphire powder
0.1%-2%, albumen stone powder 1%-6%, seaweed carbon powder 1%-10%, nanometer elbaite powder 2%-15%, magnesia
3%-10%, boron trioxide 5%-15%, nickel oxide powder 2%-15%, molybdenum oxide powder 1%-10%, the second di-iron trioxide
3%-15%, sodium oxide molybdena 0.1%-3.5%, phosphorus pentoxide 0.1%-1.5%, kaolin 3%-10%, ceria 1%-
12%, diatom ooze powder 2%-8%, calcium oxide 0.1%-2%, periclase 0.1%-2%, activated carbon 0.1%-5%, bentonite
2%-15%, cordierite powder 3%-10%, zircon flour 1%-10%, snake mountain flour 2%-15%, cobalt oxide powder 3%-10%,
Nd-Fe-B magnetic powders 0.1%-2%, AL2O3-SiO2- MgO-FeO ceramic powders 3%-10%, nano-titanium dioxide 3%-10%.