CN108084604A - A kind of high abrasion sticking film for mobile phone - Google Patents
A kind of high abrasion sticking film for mobile phone Download PDFInfo
- Publication number
- CN108084604A CN108084604A CN201711426045.5A CN201711426045A CN108084604A CN 108084604 A CN108084604 A CN 108084604A CN 201711426045 A CN201711426045 A CN 201711426045A CN 108084604 A CN108084604 A CN 108084604A
- Authority
- CN
- China
- Prior art keywords
- parts
- mobile phone
- sticking film
- oxide
- high abrasion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of high abrasion sticking film for mobile phone, it is characterised in that including following mass parts than raw material：5 15 parts of polyvinyl chloride resin, 25 parts of triethylamine, 5 10 parts of salicylate, 24 parts of dimethicone, 58 parts of nano zine oxide, 6 11 parts of chlorinated paraffin, 47 parts of boron oxide, 36 parts of thallium oxide, 6 10 parts of polyethylene, 6 10 parts of ethylene glycol, 13 parts of lipoic acid, 14 parts of accelerant A CR, 5 10 parts of glycerine, 13 parts of film forming agent.By above-mentioned technical proposal, sticking film for mobile phone abrasion resistance of the invention is high, and service life is long.
Description
Technical field
The invention belongs to sticking film for mobile phone Material Field, more particularly to a kind of high abrasion sticking film for mobile phone.
Background technology
Sticking film for mobile phone is a kind of cold lamination film available for mounting handset surface, screen and other visible objects.According to
The principle of pad pasting mounting can be divided into：Gum pad pasting, electrostatic pad pasting etc., in fact sticking film for mobile phone be not limited only to mounting mobile phone, this
Outside can with mounting MP3, MP4, computer screen, mouse, speaker and it is any need to do the physical item protected, because its initially extensively use
In the beauty of mobile phone, therefore and gain the name " sticking film for mobile phone ", because that can be taken on an entirely new look by the mobile phone after sticking film for mobile phone mounting, bright
It is brilliant, can not only play the effect of old machine renovation, but also can with waterproof, prevent dust from entering keyboard, screen, play protection
Effect, therefore custom is called mobile phone cosmetic membrane, safeguard film for cellular phone to people again.Existing sticking film for mobile phone wearability is not high, key or
If person's nail scrapes accidentally, it is possible to crack or cut occurs, therefore the quality of existing Mobile phone film is in urgent need to be improved.
The content of the invention
It is an object of the invention to provide a kind of high sticking film for mobile phone of abrasion resistance, so as to suitable for practicality.
The object of the invention to solve the technical problems is realized using following technical scheme.According to proposed by the present invention
A kind of high abrasion sticking film for mobile phone, including following mass parts than raw material：5-15 parts of polyvinyl chloride resin, 2-5 parts of triethylamine, salicylate
5-10 parts, 2-4 parts of dimethicone, 5-8 parts of nano zine oxide, 6-11 parts of chlorinated paraffin, 4-7 parts of boron oxide, thallium oxide 3-6
Part, 6-10 parts of polyethylene, 6-10 parts of ethylene glycol, 1-3 parts of lipoic acid, 1-4 parts of accelerant A CR, 5-10 parts of glycerine, film forming agent 1-
3 parts.
Preferably, a kind of high abrasion sticking film for mobile phone include following mass parts than raw material：10 parts of polyvinyl chloride resin, three
3 parts of ethamine, 6 parts of salicylate, 3 parts of dimethicone, 6 parts of nano zine oxide, 8 parts of chlorinated paraffin, 5 parts of boron oxide, thallium oxide 4
Part, 8 parts of polyethylene, 8 parts of ethylene glycol, 2 parts of lipoic acid, 2 parts of accelerant A CR, 8 parts of glycerine, 2 parts of film forming agent.
By above-mentioned technical proposal, the present invention has stronger wearability, extends sticking film for mobile phone compared with prior art
Service life.
Above description is only the general introduction of technical solution of the present invention, in order to better understand the technological means of the present invention, and
It can be practiced according to the content of specification, and to allow the above and other objects, features and advantages of the present invention can be brighter
Aobvious understandable, special below to lift preferred embodiment, detailed description are as follows.
Specific embodiment
Further to illustrate the present invention to reach the technological means and effect that predetermined goal of the invention is taken, below in conjunction with
Preferred embodiment, to according to a kind of its specific embodiment of high abrasion sticking film for mobile phone proposed by the present invention, structure, feature and its work(
Effect is described in detail as after.
A kind of high abrasion sticking film for mobile phone, including following mass parts than raw material：5-15 parts of polyvinyl chloride resin, 2-5 parts of triethylamine,
5-10 parts of salicylate, 2-4 parts of dimethicone, 5-8 parts of nano zine oxide, 6-11 parts of chlorinated paraffin, 4-7 parts of boron oxide, oxygen
3-6 parts of thallium of change, 6-10 parts of polyethylene, 6-10 parts of ethylene glycol, 1-3 parts of lipoic acid, 1-4 parts of accelerant A CR, 5-10 parts of glycerine,
1-3 parts of film forming agent.
Embodiment one：A kind of high abrasion sticking film for mobile phone include following mass parts than raw material：10 parts of PVC resins,
3 parts of triethylamine, 6 parts of salicylate, 3 parts of dimethicone, 6 parts of nano zine oxide, 8 parts of chlorinated paraffin, 5 parts of boron oxide, oxidation
4 parts of thallium, 8 parts of polyethylene, 8 parts of ethylene glycol, 2 parts of lipoic acid, 2 parts of accelerant A CR, 8 parts of glycerine, 2 parts of film forming agent.
The above described is only a preferred embodiment of the present invention, any person skilled in the art is not departing from
In the range of technical solution of the present invention, technical spirit according to the invention is to any simple modification made for any of the above embodiments, equivalent
Variation and modification, in the range of still falling within technical solution of the present invention.
Claims (2)
1. a kind of high abrasion sticking film for mobile phone, it is characterised in that including following mass parts than raw material：5-15 parts of polyvinyl chloride resin, three second
2-5 parts of amine, 5-10 parts of salicylate, 2-4 parts of dimethicone, 5-8 parts of nano zine oxide, 6-11 parts of chlorinated paraffin, boron oxide
4-7 parts, 3-6 parts of thallium oxide, 6-10 parts of polyethylene, 6-10 parts of ethylene glycol, 1-3 parts of lipoic acid, 1-4 parts of accelerant A CR, glycerine
5-10 parts, 1-3 parts of film forming agent.
2. a kind of high abrasion sticking film for mobile phone as described in claim 1, it is characterised in that including following mass parts than raw material：
10 parts of polyvinyl chloride resin, 3 parts of triethylamine, 6 parts of salicylate, 3 parts of dimethicone, 6 parts of nano zine oxide, 8 parts of chlorinated paraffin, oxygen
Change 5 parts of boron, 4 parts of thallium oxide, 8 parts of polyethylene, 8 parts of ethylene glycol, 2 parts of lipoic acid, 2 parts of accelerant A CR, 8 parts of glycerine, film forming agent 2
Part.