CN108081776A - A kind of typography for improving Packaging Box antioxygenic property - Google Patents
A kind of typography for improving Packaging Box antioxygenic property Download PDFInfo
- Publication number
- CN108081776A CN108081776A CN201711216662.2A CN201711216662A CN108081776A CN 108081776 A CN108081776 A CN 108081776A CN 201711216662 A CN201711216662 A CN 201711216662A CN 108081776 A CN108081776 A CN 108081776A
- Authority
- CN
- China
- Prior art keywords
- parts
- packaging box
- carton
- processing
- antioxygenic property
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
A kind of typography for improving Packaging Box antioxygenic property, is related to the printing processing technique field of Packaging Box, and the present invention is easy to operation, easy making process is convenient, and the printing treatment of Packaging Box is carried out using scientific and effective technology, can effectively make the carton antioxygenic property after printing more preferable, anti-aging property is more preferable, the Packaging Box after processing, nontoxic, environment-friendly and green, anti-oxidantization performance is good, and printing effect is good, and printing fastness is high, not fugitive color, quality are high.
Description
Technical field
Printing processing technique field more particularly to a kind of raising Packaging Box inoxidizability the present invention relates to Packaging Box
The typography of energy.
Background technology
Packed in cases refers to product in the process of circulation, to protect product, facilitating accumulating, promotion sale, using carton
The packaging that body carries out product.Packed in cases is a kind of most widely used manner of packing.It is different from wooden-box package, woven bag
Packaging, cloth bag packaging, plastic casing packaging, packed in cases have draw materials it is easy, light-weight, easy printing, design shaping easily, into
The features such as this is cheap, is widely used for the marketing packing and transportation and packing of commodity.
The content of the invention
The technical problems to be solved by the invention are to provide a kind of typography for improving Packaging Box antioxygenic property.
The technical problems to be solved by the invention are realized using following technical scheme:
A kind of typography for improving Packaging Box antioxygenic property, which is characterized in that comprise the following steps that:
A, after the Packaging Box after machine-shaping being carried out unified collection, sprayed with thimerosal, carry out cleaning-sterilizing processing;
B, will treated Packaging Box, carry out high temperature steam treatment with the high-temperature steam of dressing liquid;
C, the Packaging Box that will be handled well in step b is put in refrigerating chamber and is freeze-dried;
D, step b and c are repeated 2-3 times;
E, by microwave treatment 10-15min under the carton that step d is handled well microwave frequency 2450MHz, power 600W;
F, the carton that step e is handled well is subjected to offset printing with offset press;
G, the carton for handling step f well sprays curing ink;
H, the carton printed step g carries out dry tack free processing, and carton is passed through in baking oven by when processing successively, is carried out
Baking is handled, and baking temperature is at 30-60 DEG C, and baking time control is in 10-20min;
I, step h dry tack frees treated Packaging Box is subjected to adhesive sticker brushing, processing is then dried again,
Temperature is controlled at 25-35 DEG C.
Further, the thimerosal of the step a is made of the raw material of following parts by weight:6-8 parts of alcohol, light-coloured vinegar 3-5
Part, 5-7 parts of salt, 1-2 parts of citric acid, 0.5-0.8 parts of sodium chlorate.
Further, the freezer temperature of the step c is -10 to -20 degree.
Further, the dressing liquid is made of the raw material of following parts by weight:3-5 parts of methylcellulose, water-soluble poly
5-8 parts of urethane, 2-4 parts of aluminum sulfate, 1-3 parts of polyvinyl alcohol, 2-4 parts of fluorine silicon resin.
Further, the ink of the step f is made of the raw material of following parts by weight:Alcohol-soluble resin 20-30 powder, face
6-10 parts of feed powder, 3-5 parts of titanium dioxide, 5-7 parts of propenyl, 6-8 parts of tributyl 2-acetylcitrate, 2-5 parts of activated carbon, curing agent 5-
7 parts, 3-5 parts of ethyl acetate, 6-8 parts of antistatic agent, 5-7 parts of vitamin C, -4 parts of vitamin E2,60-80 parts of deionized water.
Further, the raw material composition of the preferably following parts by weight of the ink of above-mentioned steps f:25 powder of alcohol-soluble resin, face
8 parts of feed powder, 4 parts of titanium dioxide, 6 parts of propenyl, 7 parts of tributyl 2-acetylcitrate, 4 parts of activated carbon, 6 parts of curing agent, ethyl acetate 4
Part, 7 parts of antistatic agent, 6 parts of vitamin C, 3 parts of vitamin E, 70 parts of deionized water.
The processing method of ink in above-mentioned steps f, is realized by following step:
1) alcohol-soluble resin, propenyl, tributyl 2-acetylcitrate, ethyl acetate are previously added in heating kettle, opened
It heats and stirs to molten condition, it is spare;
2) pigment powder, titanium dioxide, activated carbon, curing agent, antistatic agent are carried out heating stirring with deionized water to mix, is added
Hot temperature is 60-70 degree;
3) material of step 1) and handling well 2) is mixed, adds in vitamin C and vitamin E, be put into blender into
Row stirring, mixing speed 800-1000r/min;
4) mixture for handling step 3) well adds in ball mill and carries out ball milling, is milled to fineness less than 0.1mm.
The typography of Packaging Box antioxygenic property is improved in the present invention, is handled first using disinfectant cleaning-sterilizing,
Effectively the dust impurity of carton surface can be removed, avoid the subsequent printing processing of impurity effect of carton surface, and
Steam treatment first is carried out to carton with dressing liquid before printing, the papery that can make carton is soft scattered, increases gap, sufficiently
Dressing liquid is absorbed, also makes subsequently print ink and is better in coloration, household freezer is placed into and is freeze-dried, can determine the carton after disperseing
Type, and high-temperature steam and freezing step are repeated, the anti-oxidantization performance of carton is strengthened, then microwave treatment is carried out to carton,
Increase the electrostatic of carton surface, increase the adhesive force of subsequent ink, and the first processing of steam cold air drying again, paper can be increased
The toughness of case improves the easy damaged performance of carton.
Present invention has the advantages that:The present invention is easy to operation, and easy making process is convenient, using scientific and effective technique skill
Art carries out the printing treatment of Packaging Box, can effectively make that the carton antioxygenic property after printing is more preferable, and anti-aging property is more
Good, the Packaging Box after processing is nontoxic, environment-friendly and green, and anti-oxidantization performance is good, and printing effect is good, and printing fastness is high,
Not fugitive color, quality are high.
Specific embodiment
In order to be easy to understand the technical means, the creative features, the aims and the efficiencies achieved by the present invention, tie below
The example for closing specific embodiment is described in further details the present invention.
Embodiment one
A kind of typography for improving Packaging Box antioxygenic property, which is characterized in that comprise the following steps that:
A, after the Packaging Box after machine-shaping being carried out unified collection, sprayed with thimerosal, carry out cleaning-sterilizing processing;
B, will treated Packaging Box, carry out high temperature steam treatment with the high-temperature steam of dressing liquid;
C, the Packaging Box that will be handled well in step b is put in refrigerating chamber and is freeze-dried;
D, step b and c are repeated 2 times;
E, by microwave treatment 10min under the carton that step d is handled well microwave frequency 2450MHz, power 600W;
F, the carton that step e is handled well is subjected to offset printing with offset press;
G, the carton for handling step f well sprays curing ink;
H, the carton printed step g carries out dry tack free processing, and carton is passed through in baking oven by when processing successively, is carried out
Baking is handled, and baking temperature is at 30 DEG C, and baking time control is in 10min;
I, step h dry tack frees treated Packaging Box is subjected to adhesive sticker brushing, processing is then dried again,
Temperature is controlled at 25 DEG C.
Further, the thimerosal of the step a is made of the raw material of following parts by weight:6 parts of alcohol, 3 parts of light-coloured vinegar, salt
5 parts, 1 part of citric acid, 0.5 part of sodium chlorate.
Further, the freezer temperature of the step c is -10 degree.
Further, the dressing liquid is made of the raw material of following parts by weight:3 parts of methylcellulose, water-soluble poly ammonia
5 parts of ester, 2 parts of aluminum sulfate, 1 part of polyvinyl alcohol, 2 parts of fluorine silicon resin.
Further, the ink of the step f is made of the raw material of following parts by weight:20 powder of alcohol-soluble resin, pigment
6 parts of powder, 3 parts of titanium dioxide, 5 parts of propenyl, 6 parts of tributyl 2-acetylcitrate, 2 parts of activated carbon, 5 parts of curing agent, ethyl acetate 3
Part, 6 parts of antistatic agent, 5 parts of vitamin C, vitamin E2 part, 60 parts of deionized water.
The processing method of ink in above-mentioned steps f, is realized by following step:
1) alcohol-soluble resin, propenyl, tributyl 2-acetylcitrate, ethyl acetate are previously added in heating kettle, opened
It heats and stirs to molten condition, it is spare;
2) pigment powder, titanium dioxide, activated carbon, curing agent, antistatic agent are carried out heating stirring with deionized water to mix, is added
Hot temperature is 60 degree;
3) material of step 1) and handling well 2) is mixed, adds in vitamin C and vitamin E, be put into blender into
Row stirring, mixing speed 800r/min;
4) mixture for handling step 3) well adds in ball mill and carries out ball milling, is milled to fineness less than 0.1mm.
Embodiment two
A kind of typography for improving Packaging Box antioxygenic property, which is characterized in that comprise the following steps that:
A, after the Packaging Box after machine-shaping being carried out unified collection, sprayed with thimerosal, carry out cleaning-sterilizing processing;
B, will treated Packaging Box, carry out high temperature steam treatment with the high-temperature steam of dressing liquid;
C, the Packaging Box that will be handled well in step b is put in refrigerating chamber and is freeze-dried;
D, step b and c are repeated 3 times;
E, by microwave treatment 15min under the carton that step d is handled well microwave frequency 2450MHz, power 600W;
F, the carton that step e is handled well is subjected to offset printing with offset press;
G, the carton for handling step f well sprays curing ink;
H, the carton printed step g carries out dry tack free processing, and carton is passed through in baking oven by when processing successively, is carried out
Baking is handled, and baking temperature is at 60 DEG C, and baking time control is in 20min;
I, step h dry tack frees treated Packaging Box is subjected to adhesive sticker brushing, processing is then dried again,
Temperature is controlled at 35 DEG C.
Further, the thimerosal of the step a is made of the raw material of following parts by weight:8 parts of alcohol, 5 parts of light-coloured vinegar, salt
7 parts, 2 parts of citric acid, 0.8 part of sodium chlorate.
Further, the freezer temperature of the step c is -20 degree.
Further, the dressing liquid is made of the raw material of following parts by weight:5 parts of methylcellulose, water-soluble poly ammonia
8 parts of ester, 4 parts of aluminum sulfate, 3 parts of polyvinyl alcohol, 4 parts of fluorine silicon resin.
Further, the ink of the step f is made of the raw material of following parts by weight:30 powder of alcohol-soluble resin, pigment
10 parts of powder, 5 parts of titanium dioxide, 7 parts of propenyl, 8 parts of tributyl 2-acetylcitrate, 5 parts of activated carbon, 7 parts of curing agent, ethyl acetate 5
Part, 8 parts of antistatic agent, 7 parts of vitamin C, 4 parts of vitamin E, 80 parts of deionized water.
The processing method of ink in above-mentioned steps f, is realized by following step:
1) alcohol-soluble resin, propenyl, tributyl 2-acetylcitrate, ethyl acetate are previously added in heating kettle, opened
It heats and stirs to molten condition, it is spare;
2) pigment powder, titanium dioxide, activated carbon, curing agent, antistatic agent are carried out heating stirring with deionized water to mix, is added
Hot temperature is 70 degree;
3) material of step 1) and handling well 2) is mixed, adds in vitamin C and vitamin E, be put into blender into
Row stirring, mixing speed 1000r/min;
4) mixture for handling step 3) well adds in ball mill and carries out ball milling, is milled to fineness less than 0.1mm.
Embodiment three
A kind of typography for improving Packaging Box antioxygenic property, which is characterized in that comprise the following steps that:
A, after the Packaging Box after machine-shaping being carried out unified collection, sprayed with thimerosal, carry out cleaning-sterilizing processing;
B, will treated Packaging Box, carry out high temperature steam treatment with the high-temperature steam of dressing liquid;
C, the Packaging Box that will be handled well in step b is put in refrigerating chamber and is freeze-dried;
D, step b and c are repeated 3 times;
E, by microwave treatment 13min under the carton that step d is handled well microwave frequency 2450MHz, power 600W;
F, the carton that step e is handled well is subjected to offset printing with offset press;
G, the carton for handling step f well sprays curing ink;
H, the carton printed step g carries out dry tack free processing, and carton is passed through in baking oven by when processing successively, is carried out
Baking is handled, and baking temperature is at 50 DEG C, and baking time control is in 15min;
I, step h dry tack frees treated Packaging Box is subjected to adhesive sticker brushing, processing is then dried again,
Temperature is controlled at 30 DEG C.
Further, the thimerosal of the step a is made of the raw material of following parts by weight:7 parts of alcohol, 4 parts of light-coloured vinegar, salt
6 parts, 1.5 parts of citric acid, 0.7 part of sodium chlorate.
Further, the freezer temperature of the step c is -15 degree.
Further, the dressing liquid is made of the raw material of following parts by weight:4 parts of methylcellulose, water-soluble poly ammonia
7 parts of ester, 3 parts of aluminum sulfate, 2 parts of polyvinyl alcohol, 3 parts of fluorine silicon resin.
Further, the raw material composition of the preferably following parts by weight of the ink of above-mentioned steps f:25 powder of alcohol-soluble resin, face
8 parts of feed powder, 4 parts of titanium dioxide, 6 parts of propenyl, 7 parts of tributyl 2-acetylcitrate, 4 parts of activated carbon, 6 parts of curing agent, ethyl acetate 4
Part, 7 parts of antistatic agent, 6 parts of vitamin C, 3 parts of vitamin E, 70 parts of deionized water.
The processing method of ink in above-mentioned steps f, is realized by following step:
1) alcohol-soluble resin, propenyl, tributyl 2-acetylcitrate, ethyl acetate are previously added in heating kettle, opened
It heats and stirs to molten condition, it is spare;
2) pigment powder, titanium dioxide, activated carbon, curing agent, antistatic agent are carried out heating stirring with deionized water to mix, is added
Hot temperature is 65 degree;
3) material of step 1) and handling well 2) is mixed, adds in vitamin C and vitamin E, be put into blender into
Row stirring, mixing speed 900r/min;
4) mixture for handling step 3) well adds in ball mill and carries out ball milling, is milled to fineness less than 0.1mm.
Following table is the Packaging Box examining report after present invention printing:
The performance indicator for ink prepared by the present invention and existing high-grade ink compares below:
The basic principles, main features and the advantages of the invention have been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (4)
1. a kind of typography for improving Packaging Box antioxygenic property, which is characterized in that comprise the following steps that:
A, after the Packaging Box after machine-shaping being carried out unified collection, sprayed with thimerosal, carry out cleaning-sterilizing processing;
B, will treated Packaging Box, carry out high temperature steam treatment with the high-temperature steam of dressing liquid;
C, the Packaging Box that will be handled well in step b is put in refrigerating chamber and is freeze-dried;
D, step b and c are repeated 2-3 times;
E, by microwave treatment 10-15min under the carton that step d is handled well microwave frequency 2450MHz, power 600W;
F, the carton that step e is handled well is subjected to offset printing with offset press;
G, the carton for handling step f well sprays curing ink;
H, the carton printed step g carries out dry tack free processing, and carton is passed through in baking oven by when processing successively, is toasted
Processing, baking temperature is at 30-60 DEG C, and baking time control is in 10-20min;
I, step h dry tack frees treated Packaging Box is subjected to adhesive sticker brushing, processing, temperature is then dried again
Control is at 25-35 DEG C.
2. the typography according to claim 1 for improving Packaging Box antioxygenic property, it is characterised in that:The step
The thimerosal of a is made of the raw material of following parts by weight:6-8 parts of alcohol, 3-5 parts of light-coloured vinegar, 5-7 parts of salt, 1-2 parts of citric acid, chlorine
Sour sodium 0.5-0.8 parts.
3. the typography according to claim 1 for improving Packaging Box antioxygenic property, it is characterised in that:The step
The freezer temperature of c is -10 to -20 degree.
4. the typography according to claim 1 for improving Packaging Box antioxygenic property, it is characterised in that:The arrangement
Liquid is made of the raw material of following parts by weight:3-5 parts of methylcellulose, 5-8 parts of soluble polyurethane, 2-4 parts of aluminum sulfate, poly- second
1-3 parts of enol, 2-4 parts of fluorine silicon resin.