CN108081715A - A kind of durable type filtrate base fabric and preparation method thereof - Google Patents

A kind of durable type filtrate base fabric and preparation method thereof Download PDF

Info

Publication number
CN108081715A
CN108081715A CN201711481364.6A CN201711481364A CN108081715A CN 108081715 A CN108081715 A CN 108081715A CN 201711481364 A CN201711481364 A CN 201711481364A CN 108081715 A CN108081715 A CN 108081715A
Authority
CN
China
Prior art keywords
winding
yarn
warp
weft
base fabric
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711481364.6A
Other languages
Chinese (zh)
Inventor
邱学春
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201711481364.6A priority Critical patent/CN108081715A/en
Publication of CN108081715A publication Critical patent/CN108081715A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of durable type filtrate base fabrics, including warp and weft, the warp and weft are made of the winding of aramid yarn, long glass fiber reinforced PP yarns, carbon fibre composite yarn and the first rubber yarn, the warp and weft and junction be equipped with winding tie, the winding knot includes winding line, and the winding is tied equipped with rubber layer.Warp and weft of the present invention are by winding line winding in twisted shape, and form winding knot, improve tensile resistence and intensity, winding is tied equipped with rubber layer, rubber layer can increase the tensile resistance and intensity of filtrate base fabric, and it avoids being stained with spot at winding knot and being difficult to clear up, it influences to use next time, and rubber layer is equipped with honeycomb hole, honeycomb hole can draw more antiseptics, make the more durable more antibacterial of filtrate base fabric, entire base fabric tensile resistance and intensity are higher, and antibacterial resistance to corrosion is higher, it is more durable, using rear easy to clean, do not stay spot.

Description

A kind of durable type filtrate base fabric and preparation method thereof
Technical field
The present invention relates to filtrate base fabric preparation field, more particularly to a kind of durable type filtrate base fabric and preparation method thereof.
Background technology
Filtrate base fabric is frequently used for the uses such as dedusting, filtering, needs good filtering function in use and resists Tensile strength, is easily deformed and short-life filtrate base fabric can cause using upper many inconvenience, it is necessary to often replace, increase Labour and cost, existing filtrate base fabric wear no resistance, and antibacterial ability is not strong, and stretch-proof and intensity are all relatively low, make With short life, for a long time using easily generation deformation, and easily sheltering evil people and countenance evil practices in gap, cloth gap also can gradually increase.
Therefore, it is necessary to solve the above problems to invent a kind of durable type filtrate base fabric and preparation method thereof.
The content of the invention
It is an object of the invention to provide a kind of durable type filtrate base fabric and preparation method thereof, to solve above-mentioned background technology The problem of middle proposition.
To achieve the above object, the present invention provides following technical solution：A kind of durable type filtrate base fabric, including warp and latitude Line, the warp and weft are by aramid yarn, long glass fiber reinforced PP yarns, carbon fibre composite yarn and the first rubber yarn Line winding be made, the warp and weft and junction be equipped with winding tie, it is described winding knot includes wind line, it is described winding tie Rubber layer is equipped with, the rubber layer is equipped with honeycomb hole, antibiotic layer is equipped with outside the rubber layer, warp and weft.
Preferably, the winding line is wound in warp and weft.
Preferably, the aramid yarn, long glass fiber reinforced PP yarns, carbon fibre composite yarn and the first rubber yarn Winding sets and is wound in twisted shape.
Preferably, the winding line includes laterally winding line and longitudinally wound line, and the winding line is by nanometer boron fibre yarn Line and the winding of the second rubber yarn are made.
Preferably, the antibiotic layer is made of nano silver antimicrobials.
A kind of durable type filtrate base fabric and preparation method thereof, its preparation method is：
a）Material prepares：Aramid yarn, long glass fiber reinforced PP yarns, carbon fibre composite yarn and the first rubber yarn is accurate It gets ready；
b）Make warp and weft：It is in twisted shape by aramid yarn, long glass fiber reinforced PP yarns and carbon fibre composite yarn It is wrapped in outside the first rubber yarn and warp and weft is made；
c）Make winding line：Winding line is made in nanometer boron fibre yarn and the winding of the second rubber yarn；
d）Winding：Warp and weft are arranged in a crossed manner, and by Boards wall end, laterally winding line is wrapped in outside weft Portion will be wrapped in longitudinally wound line outside warp, when running into the junction of warp and weft, laterally wind line and longitudinally wound line The S-shaped place of being intertwined and connected forms winding knot respectively；
e）Dispensing：Rubber material is heated to liquid condition, top and bottom are tied to winding and carry out dispensing formation rubber layer；
f）Make antibiotic layer：Manufactured filtrate base fabric is immersed in nano silver antimicrobials, is stained at this time in honeycomb hole very much Nano silver antimicrobials, the filtrate base fabric after final impregnating are made by rolling and stoving process；
g）Non-woven fabrics bonding agent will be sprayed in manufactured finished product filtrate base fabric, carry out lamination coating, facilitate and taken off according to required thickness Open use.
The technique effect and advantage of the present invention：Warp and weft are by aramid yarn, long glass fiber reinforced PP yarns, carbon fiber Twisted shape is made in composite material yarn and the winding of the first rubber yarn, improves tensile resistence and intensity, carbon fibre composite yarn Line can high temperature resistant, rub resistance, conduction, heat conduction and corrosion-resistant, long glass fiber reinforced PP yarns enhance the intensity of base fabric, rubber yarn Enhance the intensity and toughness of warp and weft；And warp and weft are in twisted shape by winding line winding, and form winding knot, Winding line is made of nanometer boron fibre yarn and the winding of the second rubber yarn, be conducive to that nanometer boron fibre yarn is light but intensity Greatly, the second rubber yarn toughness is stronger and corrosion-resistant；Winding is tied equipped with rubber layer, and rubber layer can increase the anti-of filtrate base fabric Tensile property and intensity, and avoid being stained with spot at winding knot and being difficult to clear up, influence next use；And rubber layer is equipped with Honeycomb hole, honeycomb hole can draw more antiseptics, make the more durable more antibacterial of filtrate base fabric, entire base fabric stretch-proof energy Power and intensity are higher, and antibacterial resistance to corrosion is higher, more durable.
Description of the drawings
Fig. 1 is the overall structure diagram of the present invention.
Fig. 2 is the rubber layer structure diagram of the present invention.
Fig. 3 is the warp structure diagram of the present invention.
Fig. 4 is the winding cable architecture schematic diagram of the present invention.
In figure：1 warp, 2 wefts, 3 aramid yarns, 4 long glass fiber reinforced PP yarns, 5 carbon fibre composite yarns, 6 One rubber yarn, 7 winding knots, 8 winding lines, 81 laterally wind line, 82 longitudinally wound line, 9 rubber layers, 10 honeycomb holes, 11 antibacterials Layer, 12 nanometers of boron fibre yarns, 13 second rubber yarns.
Specific embodiment
Below in conjunction with the attached drawing in the embodiment of the present invention, the technical solution in the embodiment of the present invention is carried out clear, complete Site preparation describes, it is clear that described embodiment is only part of the embodiment of the present invention, instead of all the embodiments.It is based on Embodiment in the present invention, those of ordinary skill in the art are obtained every other without making creative work Embodiment belongs to the scope of protection of the invention.
The present invention provides a kind of durable type filtrate base fabrics as shown in Figs 1-4, including warp 1 and weft 2, the warp 1 and weft 2 twined by aramid yarn 3, long glass fiber reinforced PP yarns 4,5 and first rubber yarn 6 of carbon fibre composite yarn It turns to, carbon fibre composite yarn 5 being capable of high temperature resistant, rub resistance, conduction, heat conduction and corrosion-resistant, the warp 1 and weft 2 and junction be equipped with winding knot 7, it is described winding knot 7 include winding line 8, it is described winding knot 7 be equipped with rubber layer 9, rubber layer 9 can increase the tensile resistance and intensity of filtrate base fabric, and avoid being stained with spot at winding knot 7 and being difficult to clear up, under the influence of Secondary use, the rubber layer 9 are equipped with honeycomb hole 10, and honeycomb hole 10 can draw more antiseptics, make filtrate base fabric more Durable more antibacterial is equipped with antibiotic layer 11 outside the rubber layer 9, warp 1 and weft 2.
The winding line 8 is wound on warp 1 and weft 2, is conducive to reinforce base fabric, the aramid yarn 3, long glass Fibre enhancing PP yarns 4, the winding of 5 and first rubber yarn 6 of carbon fibre composite yarn set and are wound in twisted shape, are conducive to Increasing the intensity and tensile resistence of warp 1 and weft 2, the winding line 8 includes laterally winding line 81 and longitudinally wound line 82, The winding line 8 is made of nanometer boron fibre yarn 12 and the winding of the second rubber yarn 13, is conducive to a nanometer boron fibre yarn 12 Light but intensity is big, 13 toughness of the second rubber yarn is stronger and corrosion-resistant, and the antibiotic layer 11 is made of nano silver antimicrobials, Be conducive to enhance the anti-microbial property of filtrate base fabric, more durable, its preparation method is：
a）Material prepares：By aramid yarn 3, long glass fiber reinforced PP yarns 4,5 and first rubber yarn of carbon fibre composite yarn Line 6 is ready to；
b）Make warp 1 and weft 2：By aramid yarn 3, long glass fiber reinforced PP yarns 4 and carbon fibre composite yarn 5 in fiber crops Warp 1 and weft 2 is made in flower-shaped be wrapped in outside the first rubber yarn 6, enhances the intensity and toughness of warp 1 and weft 2；
c）Make winding line 8：Winding line 8, enhancing winding is made in nanometer boron fibre yarn 12 and the winding of the second rubber yarn 13 The intensity and toughness of line 8；
d）Winding：Warp 1 and weft 2 is arranged in a crossed manner, and by Boards wall end, laterally winding line 81 is wrapped in latitude It outside line 2, will be wrapped in longitudinally wound line 82 outside warp 1, and when running into the junction of warp 1 and weft 2, laterally wind line 81 With longitudinally wound line 82, the S-shaped place of being intertwined and connected forms winding knot 7 respectively；
e）Dispensing：Rubber material is heated to liquid condition, carrying out dispensing to 7 top and bottom of winding knot forms rubber layer 9, rubber Glue-line 9 can increase the tensile resistance and intensity of filtrate base fabric, and avoid being stained with spot at winding knot 7 and being difficult to clear up, shadow It rings and uses next time；
f）Make antibiotic layer 11：Manufactured filtrate base fabric is immersed in nano silver antimicrobials, is stained with very in honeycomb hole 10 at this time More nano silver antimicrobials, the filtrate base fabric after final impregnating are made by rolling and stoving process, can enhance filtrate base fabric Anti-microbial property, it is more durable；
g）Non-woven fabrics bonding agent will be sprayed in manufactured finished product filtrate base fabric, carry out lamination coating, facilitate and taken off according to required thickness Open use.
Finally it should be noted that：The foregoing is only a preferred embodiment of the present invention, is not intended to limit the invention, Although the present invention is described in detail with reference to the foregoing embodiments, for those skilled in the art, still may be used To modify to the technical solution recorded in foregoing embodiments or carry out equivalent substitution to which part technical characteristic, Within the spirit and principles of the invention, any modifications, equivalent replacements and improvements are made should be included in the present invention's Within protection domain.

Claims (6)

1. a kind of durable type filtrate base fabric, including warp（1）And weft（2）, it is characterised in that：The warp（1）And weft（2） By aramid yarn（3）, long glass fiber reinforced PP yarns（4）, carbon fibre composite yarn（5）With the first rubber yarn（6）It twines It turns to, the warp（1）And weft（2）And junction be equipped with winding tie（7）, the winding knot（7）Including winding line （8）, the winding knot（7）It is equipped with rubber layer（9）, the rubber layer（9）It is equipped with honeycomb hole（10）, the rubber layer（9）、 Warp（1）And weft（2）Outside is equipped with antibiotic layer（11）.
2. a kind of durable type filtrate base fabric according to claim 1, it is characterised in that：The winding line（8）Winding is set In warp（1）And weft（2）On.
3. a kind of durable type filtrate base fabric according to claim 1, it is characterised in that：The aramid yarn（3）, roving glass fiber Enhance PP yarns（4）, carbon fibre composite yarn（5）With the first rubber yarn（6）Winding sets and is wound in twisted shape.
4. a kind of durable type filtrate base fabric according to claim 1, it is characterised in that：The winding line（8）Including transverse direction Wind line（81）With longitudinally wound line（82）, the winding line（8）By nanometer boron fibre yarn（12）With the second rubber yarn （13）Winding is made.
5. a kind of durable type filtrate base fabric according to claim 1, it is characterised in that：The antibiotic layer（11）By nano silver Antiseptic is made.
6. a kind of preparation method of durable type filtrate base fabric according to claim 1-5, it is characterised in that：Its preparation method For：
a）Material prepares：By aramid yarn（3）, long glass fiber reinforced PP yarns（4）, carbon fibre composite yarn（5）With first Rubber yarn（6）It is ready to；
b）Make warp（1）And weft（2）：By aramid yarn（3）, long glass fiber reinforced PP yarns（4）And carbon fibre composite Yarn（5）The first rubber yarn is wrapped in twisted shape（6）Warp is made in outside（1）And weft（2）；
c）Make winding line（8）：By nanometer boron fibre yarn（12）With the second rubber yarn（13）Winding line is made in winding（8）；
d）Winding：By warp（1）And weft（2）It is arranged in a crossed manner, and by Boards wall end, will laterally wind line（81）It twines It is wound on weft（2）Outside, will be longitudinally wound line（82）It is wrapped in warp（1）Outside runs into warp（1）And weft（2）Connection During place, line is laterally wound（81）With longitudinally wound line（82）The S-shaped place of being intertwined and connected forms winding knot respectively（7）；
e）Dispensing：Rubber material is heated to liquid condition, winding is tied（7）Top and bottom carry out dispensing and form rubber layer （9）；
f）Make antibiotic layer（11）：Manufactured filtrate base fabric is immersed in nano silver antimicrobials, at this time honeycomb hole（10）It is interior viscous There are many nano silver antimicrobials, the filtrate base fabric after final impregnating is made by rolling and stoving process；
g）Non-woven fabrics bonding agent will be sprayed in manufactured finished product filtrate base fabric, carry out lamination coating, facilitate and taken off according to required thickness Open use.
CN201711481364.6A 2017-12-29 2017-12-29 A kind of durable type filtrate base fabric and preparation method thereof Pending CN108081715A (en)