CN108071719A - The formula and its preparation process of a kind of braking sheet for automobile - Google Patents
The formula and its preparation process of a kind of braking sheet for automobile Download PDFInfo
- Publication number
- CN108071719A CN108071719A CN201711141248.XA CN201711141248A CN108071719A CN 108071719 A CN108071719 A CN 108071719A CN 201711141248 A CN201711141248 A CN 201711141248A CN 108071719 A CN108071719 A CN 108071719A
- Authority
- CN
- China
- Prior art keywords
- parts
- formula
- automobile
- braking sheet
- delanium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of formula of braking sheet for automobile, the formula of raw material by weight is as follows：14 parts 35 45 parts of ceramic fibre, 15 25 parts of epoxy resin, 15 25 parts of boron bakelite resin, 12 16 parts of copper fiber, 10 14 parts of polypropylene, 10 14 parts of calcium oxide, 10 14 parts of crystal whisker of hexa potassium titanate, 58 parts of Delanium, 58 parts of copper powder, 58 parts of glass dust, 58 parts of coke blacking, 14 parts of anti-aging agent, 14 parts of antioxidant, increasing of grinding agent.The present invention also provides a kind of preparation processes of braking sheet for automobile sheet.The present invention can mix various ingredients, so that the present invention carries braking sheet for automobile in the figuresome promotion of antifriction aspect of performance, its service life effectively enhanced meets the demand developed now.
Description
Technical field
The present invention relates to the formulas and its preparation of auto parts preparing technical field more particularly to a kind of braking sheet for automobile
Technique.
Background technology
Brake block is also brake rubber block.In the brake system of automobile, brake block is the breaking piece of most critical, all brakes
The quality of effect is all that brake block plays a decisive role, so the brake block for agreeing is people and the patron saint of automobile.
Brake block is generally made of steel plate, bonding thermal insulation layer and brake pad, and steel plate will come antirust, coating process by application
Ensure quality with SMT-4 furnace temperature tracker to detect the Temperature Distribution of coating process.Wherein thermal insulation layer is by adiabatic material
Material composition, it is therefore an objective to heat-insulated.Brake pad is made of friction material, adhesive, and when brake is compressed on brake disc or brake rim
Friction is generated, so as to achieve the purpose that vehicle deceleration brakes.Due to rubbing action, brake pad can gradually be worn, in general
The lower brake pad wear of cost must be faster.Brake block of the prior art after prolonged use, can all be worn, if
It can not occur in time, then there is security risk, for this purpose, formula and its preparation we have proposed a kind of braking sheet for automobile
Technique.
The content of the invention
The present invention proposes the formula and its preparation process of a kind of braking sheet for automobile, to solve to carry in above-mentioned background technology
The problem of going out.
The present invention proposes a kind of formula of braking sheet for automobile, and the formula of raw material by weight is as follows：Ceramic fibre 35-
45 parts, 15-25 parts of epoxy resin, 15-25 parts of boron bakelite resin, 12-16 parts of copper fiber, 10-14 parts of polypropylene, calcium oxide 10-
14 parts, it is 10-14 parts of crystal whisker of hexa potassium titanate, 5-8 parts of Delanium, 5-8 parts of copper powder, 5-8 parts of glass dust, 5-8 parts of coke blacking, anti-old
1-4 parts of agent, 1-4 parts of antioxidant increase 1-4 parts of grinding agent.
Preferably, ceramic fibre, epoxy resin, boron bakelite resin, the weight ratio of copper fiber are 38-42: 18-22: 18-22
∶13-15。
Preferably, polypropylene, calcium oxide, the weight ratio of crystal whisker of hexa potassium titanate are 11-13: 11-13: 11-13.
Preferably, Delanium, copper powder, glass dust, the weight ratio of coke blacking are 6-7: 6-7: 6-7: 6-7.
Preferably, anti-aging agent, antioxidant, the weight ratio of increasing grinding agent are 2-3: 2-3: 2-3.
Preferably, the formula of raw material by weight is as follows：
38-42 parts of ceramic fibre, 18-22 parts of epoxy resin, 18-22 parts of boron bakelite resin, 13-15 parts of copper fiber, poly- third
11-13 parts of alkene, 11-13 parts of calcium oxide, 11-13 parts of crystal whisker of hexa potassium titanate, 6-7 parts of Delanium, 6-7 parts of copper powder, glass dust 6-7
Part, 6-7 parts of coke blacking, 2-3 parts of anti-aging agent, 2-3 parts of antioxidant increase 2-3 parts of grinding agent.
The present invention also provides a kind of preparation processes of braking sheet for automobile, include the following steps：
1), ceramic fibre, epoxy resin, boron bakelite resin and copper fiber are inserted in batch mixer in proportion, mixed
Expect 15-30min, then add Delanium, copper powder, glass dust and coke blacking again into batch mixer, after being thoroughly mixed,
It adds polypropylene, calcium oxide and crystal whisker of hexa potassium titanate thereto again, 10-20min is mixed again；
2), move it to again in smelting furnace, melting is carried out under conditions of 600-700 degrees Celsius, it, will after its thawing
Solution is filtered, and filters out impurity, interior thereto again to add anti-aging agent, antioxidant and increase grinding agent, and mixes 10-
14min forms mixed liquor, spare；
3) brake block die needed for, choosing, and after being cleared up, preheated under conditions of 100-120 degrees Celsius,
Then mixed liquor is poured into brake block die, it is hot under conditions of temperature is 150-160 degrees Celsius, pressure is 30-40MPa
It is molded, it after its shaping, is drawn off, and natural cooling, electrostatic spraying, mark, riveting and installation attachment are finally packed
Braking sheet for automobile is made.
Braking sheet for automobile provided by the invention, the content by selecting various ingredients and each component is different, can will be more
Kind of component is mixed, so that the present invention carries braking sheet for automobile in the figuresome promotion of antifriction aspect of performance, effectively
Its service life of enhancing, meets the demand developed now.
Specific embodiment
With reference to specific embodiment, the present invention will be further described.
Embodiment 1
The present invention proposes a kind of formula of braking sheet for automobile, and the formula of raw material by weight is as follows：Ceramic fibre 35
Part, 15 parts of epoxy resin, 15 parts of boron bakelite resin, 12 parts of copper fiber, 10 parts of polypropylene, 10 parts of calcium oxide, crystal whisker of hexa potassium titanate
10 parts, 5 parts of Delanium, 5 parts of copper powder, 5 parts of glass dust, 5 parts of coke blacking, 1 part of anti-aging agent, 1 part of antioxidant, increase 1 part of grinding agent.
The present invention also provides a kind of preparation processes of braking sheet for automobile, include the following steps：
1), ceramic fibre, epoxy resin, boron bakelite resin and copper fiber are inserted in batch mixer in proportion, mixed
Expect 15min, then add Delanium, copper powder, glass dust and coke blacking again into batch mixer, after being thoroughly mixed, then
It is secondary to add polypropylene, calcium oxide and crystal whisker of hexa potassium titanate thereto, 10min is mixed again；
2), move it to again in smelting furnace, melting is carried out under conditions of 600 degrees Celsius, after its thawing, by solution
It is filtered, filters out impurity, it is interior thereto again to add anti-aging agent, antioxidant and increase grinding agent, and 10min is mixed, shape
It is spare into mixed liquor；
3) brake block die needed for, choosing, and after being cleared up, preheated under conditions of 100 degrees Celsius, then
Mixed liquor is poured into brake block die, it is hot-forming under conditions of temperature is 150 degrees Celsius, pressure is 30MPa, treat it
It after shaping, is drawn off, and natural cooling, electrostatic spraying, mark, riveting and installation attachment are finally packed and automobile using are made
Brake block.
Embodiment 2
The present invention proposes a kind of formula of braking sheet for automobile, and the formula of raw material by weight is as follows：Ceramic fibre 38
Part, 18 parts of epoxy resin, 18 parts of boron bakelite resin, 13 parts of copper fiber, 11 parts of polypropylene, 11 parts of calcium oxide, crystal whisker of hexa potassium titanate
11 parts, 6 parts of Delanium, 6 parts of copper powder, 6 parts of glass dust, 6 parts of coke blacking, 2 parts of anti-aging agent, 2 parts of antioxidant, increase 2 parts of grinding agent.
The present invention also provides a kind of preparation processes of braking sheet for automobile, include the following steps：
1), ceramic fibre, epoxy resin, boron bakelite resin and copper fiber are inserted in batch mixer in proportion, mixed
Expect 20min, then add Delanium, copper powder, glass dust and coke blacking again into batch mixer, after being thoroughly mixed, then
It is secondary to add polypropylene, calcium oxide and crystal whisker of hexa potassium titanate thereto, 13min is mixed again；
2), move it to again in smelting furnace, melting is carried out under conditions of 630 degrees Celsius, after its thawing, by solution
It is filtered, filters out impurity, it is interior thereto again to add anti-aging agent, antioxidant and increase grinding agent, and 12min is mixed, shape
It is spare into mixed liquor；
3) brake block die needed for, choosing, and after being cleared up, preheated under conditions of 105 degrees Celsius, then
Mixed liquor is poured into brake block die, it is hot-forming under conditions of temperature is 154 degrees Celsius, pressure is 33MPa, treat it
It after shaping, is drawn off, and natural cooling, electrostatic spraying, mark, riveting and installation attachment are finally packed and automobile using are made
Brake block.
Embodiment 3
The present invention proposes a kind of formula of braking sheet for automobile, and the formula of raw material by weight is as follows：Ceramic fibre 42
Part, 22 parts of epoxy resin, 22 parts of boron bakelite resin, 15 parts of copper fiber, 13 parts of polypropylene, 13 parts of calcium oxide, crystal whisker of hexa potassium titanate
13 parts, 7 parts of Delanium, 7 parts of copper powder, 7 parts of glass dust, 7 parts of coke blacking, 3 parts of anti-aging agent, 3 parts of antioxidant, increase 3 parts of grinding agent.
The present invention also provides a kind of preparation processes of braking sheet for automobile, include the following steps：
1), ceramic fibre, epoxy resin, boron bakelite resin and copper fiber are inserted in batch mixer in proportion, mixed
Expect 25min, then add Delanium, copper powder, glass dust and coke blacking again into batch mixer, after being thoroughly mixed, then
It is secondary to add polypropylene, calcium oxide and crystal whisker of hexa potassium titanate thereto, 16min is mixed again；
2), move it to again in smelting furnace, melting is carried out under conditions of 670 degrees Celsius, after its thawing, by solution
It is filtered, filters out impurity, it is interior thereto again to add anti-aging agent, antioxidant and increase grinding agent, and 13min is mixed, shape
It is spare into mixed liquor；
3) brake block die needed for, choosing, and after being cleared up, preheated under conditions of 115 degrees Celsius, then
Mixed liquor is poured into brake block die, it is hot-forming under conditions of temperature is 157 degrees Celsius, pressure is 37MPa, treat it
It after shaping, is drawn off, and natural cooling, electrostatic spraying, mark, riveting and installation attachment are finally packed and automobile using are made
Brake block.
Embodiment 4
The present invention proposes a kind of formula of braking sheet for automobile, and the formula of raw material by weight is as follows：Ceramic fibre 45
Part, 25 parts of epoxy resin, 25 parts of boron bakelite resin, 16 parts of copper fiber, 14 parts of polypropylene, 14 parts of calcium oxide, crystal whisker of hexa potassium titanate
14 parts, 8 parts of Delanium, 8 parts of copper powder, 8 parts of glass dust, 8 parts of coke blacking, 4 parts of anti-aging agent, 4 parts of antioxidant, increase 4 parts of grinding agent.
The present invention also provides a kind of preparation processes of braking sheet for automobile, include the following steps：
1), ceramic fibre, epoxy resin, boron bakelite resin and copper fiber are inserted in batch mixer in proportion, mixed
Expect 30min, then add Delanium, copper powder, glass dust and coke blacking again into batch mixer, after being thoroughly mixed, then
It is secondary to add polypropylene, calcium oxide and crystal whisker of hexa potassium titanate thereto, 20min is mixed again；
2), move it to again in smelting furnace, melting is carried out under conditions of 700 degrees Celsius, after its thawing, by solution
It is filtered, filters out impurity, it is interior thereto again to add anti-aging agent, antioxidant and increase grinding agent, and 14min is mixed, shape
It is spare into mixed liquor；
3) brake block die needed for, choosing, and after being cleared up, preheated under conditions of 120 degrees Celsius, then
Mixed liquor is poured into brake block die, it is hot-forming under conditions of temperature is 160 degrees Celsius, pressure is 40MPa, treat it
It after shaping, is drawn off, and natural cooling, electrostatic spraying, mark, riveting and installation attachment are finally packed and automobile using are made
Brake block.
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto,
Any one skilled in the art in the technical scope disclosed by the present invention, technique according to the invention scheme and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (7)
1. a kind of formula of braking sheet for automobile, which is characterized in that the formula of its raw material by weight is as follows：Ceramic fibre 35-45
Part, 15-25 parts of epoxy resin, 15-25 parts of boron bakelite resin, 12-16 parts of copper fiber, 10-14 parts of polypropylene, calcium oxide 10-14
Part, 10-14 parts of crystal whisker of hexa potassium titanate, 5-8 parts of Delanium, 5-8 parts of copper powder, 5-8 parts of glass dust, 5-8 parts of coke blacking, anti-aging agent
1-4 parts, 1-4 parts of antioxidant, increase 1-4 parts of grinding agent.
2. the formula of braking sheet for automobile according to claim 1, which is characterized in that ceramic fibre, epoxy resin, boron phenol
Urea formaldehyde, the weight ratio of copper fiber are 38-42: 18-22: 18-22: 13-15.
3. the formula of braking sheet for automobile according to claim 1, which is characterized in that polypropylene, calcium oxide, potassium hexatitanate
The weight ratio of whisker is 11-13: 11-13: 11-13.
4. the formula of braking sheet for automobile according to claim 1, which is characterized in that Delanium, copper powder, glass dust,
The weight ratio of coke blacking is 6-7: 6-7: 6-7: 6-7.
5. the formula of braking sheet for automobile according to claim 1, which is characterized in that anti-aging agent, antioxidant increase grinding agent
Weight ratio be 2-3: 2-3: 2-3.
6. the formula of the braking sheet for automobile according to claim 2-5, which is characterized in that the formula of its raw material by weight is such as
Under：
38-42 parts of ceramic fibre, 18-22 parts of epoxy resin, 18-22 parts of boron bakelite resin, 13-15 parts of copper fiber, polypropylene 11-
13 parts, it is 11-13 parts of calcium oxide, 11-13 parts of crystal whisker of hexa potassium titanate, 6-7 parts of Delanium, 6-7 parts of copper powder, 6-7 parts of glass dust, burnt
2-3 parts 6-7 parts of powdered carbon, 2-3 parts of anti-aging agent, 2-3 parts of antioxidant, increasing of grinding agent.
7. a kind of preparation process of braking sheet for automobile according to claim 1, which is characterized in that include the following steps：
1), ceramic fibre, epoxy resin, boron bakelite resin and copper fiber are inserted in batch mixer in proportion, carry out batch mixing 15-
Then 30min adds Delanium, copper powder, glass dust and coke blacking again into batch mixer, after being thoroughly mixed, again
Polypropylene, calcium oxide and crystal whisker of hexa potassium titanate are added thereto, and 10-20min is mixed again；
2), move it to again in smelting furnace, melting is carried out under conditions of 600-700 degrees Celsius, after its thawing, by solution
It is filtered, filters out impurity, it is interior thereto again to add anti-aging agent, antioxidant and increase grinding agent, and 10-14min is mixed,
Mixed liquor is formed, it is spare；
3) brake block die needed for, choosing, and after being cleared up, preheated under conditions of 100-120 degrees Celsius, then
Mixed liquor is poured into brake block die, is hot pressed under conditions of temperature is 150-160 degrees Celsius, pressure is 30-40MPa
Type after its shaping, is drawn off, and natural cooling, electrostatic spraying, mark, riveting and installation attachment, and finally packaging is made
Braking sheet for automobile.