CN108068416A - 玻璃纤维地板的制作方法 - Google Patents

玻璃纤维地板的制作方法 Download PDF

Info

Publication number
CN108068416A
CN108068416A CN201611041324.5A CN201611041324A CN108068416A CN 108068416 A CN108068416 A CN 108068416A CN 201611041324 A CN201611041324 A CN 201611041324A CN 108068416 A CN108068416 A CN 108068416A
Authority
CN
China
Prior art keywords
minute surface
thin plate
glass fiber
production method
floor provided
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201611041324.5A
Other languages
English (en)
Inventor
周冬生
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201611041324.5A priority Critical patent/CN108068416A/zh
Publication of CN108068416A publication Critical patent/CN108068416A/zh
Pending legal-status Critical Current

Abstract

本发明公开了玻璃纤维地板的制作方法，包括面板本体、热熔黏胶剂层、塑胶层和镜面薄板层。本发明由于采用镜面薄板，其平面光洁度好；强度大，不易弯曲变形；生产效率高，根据需要，本发明容易加工成具有各种图案。有利于健康和环保。

Description

玻璃纤维地板的制作方法
技术领域
本发明涉及人造装饰板领域，尤其属于一种具有镜面薄板的装饰板。
背景技术
目前的装饰材质主要应用与相框、相架，由于亚克力材质成本高，而且硬度大，加工过程容易开裂，所以目前基本上没有应用在家具、橱柜等室内装饰板上。
发明内容
本发明的目的是，为了克服现有技术的缺陷与不足，提供一种将镜面薄板粘贴在人造板表面的装饰板，使得该装饰板既具有镜面材质所具有的外观光亮、平整度好等装饰效果，同时也具有普通人造板所具有的容易成各种形状以满足室内家具、厨具及其它装饰的需要，并且装饰效果好，制造成本低。
本发明的目的可以通过采取以下技术方案达到：
一种玻璃纤维地板的制作方法，包括面板本体、塑胶层和镜面薄板层， 塑胶层和镜面薄板层涂胶贴合成一体，塑胶和镜面薄板一体通过热熔胶黏胶剂滚压成型。
作为本发明专利优选实施例，所述的镜面薄板的厚度为2-4mm；镜面薄板及塑胶层通过反应型PU热熔胶黏胶剂与面板本体在温度为100-200摄氏度，压力为4-9吨/平方米下进行滚压的；所述的面板本体为人造中密度板或高密度板。
与现有技术相比较，本发明具有以下优点：
（1）由于采用镜面薄板，其平面光洁度好，图案和花纹根据客户需要可随时调整；
（2）可以防水、防潮、防腐性能好；
（3）强度大，不易变形；
（4）生产效率高，根据需要，本发明容易加工成具有各种图案。
附图说明
图1是本发明结构示意图。
具体实施方式
本发明专利玻璃纤维地板的制作方法，包括面板本体1、PU热熔胶黏胶剂层2，塑胶层3和镜面薄板层4， 塑胶层3和镜面薄板层4采用冷贴涂胶技术贴合而成，镜面薄板层4和塑胶层3通过反应型PU热熔胶黏胶剂3与面板本体1滚压成型，面板本体1可以为人造中密度板或高密度板。
通过上述工艺制成的玻璃纤维地板的制作方法，由于采用镜面薄板，其平面光洁度好，亮丽如镜面，图案花纹根据客户需要可随时调整；可以防水、防潮、防腐性能好，同时也增加表面平整度；镜面板的强度大使得整个装饰板强度大，不易变形；可以取代普通装饰板应用在室内装饰、室内家具、橱柜等等，大大增加了镜面材质作为装饰板的应用范围；同时也省略了目前普通人造板需要二次装修，这样避免了二次装修所产生的污染，有利于健康和环保。
以上所揭露的仅为本发明的较佳实施例而已,当然不能以此来限定本发明之权利范围,因此依本发明申请专利范围所作的等同变化,仍属本发明所涵盖的范围。
以上所揭露的仅为本发明的较佳实施例而已,当然不能以此来限定本发明之权利范围,因此依本发明申请专利范围所作的等同变化,仍属本发明所涵盖的范围。

Claims (3)

1.一种玻璃纤维地板的制作方法，其特征在于：包括面板本体、塑胶层和镜面薄板层，塑胶层和镜面薄板层粘结贴合成一体，塑胶和镜面薄板一体通过热熔胶黏胶剂滚压成型。
2.如权力要求1所述的玻璃纤维地板的制作方法，其特征在于：所述的镜面薄板的厚度为2-4mm。
3.如权力要求1所述的玻璃纤维地板的制作方法的制造工艺，其特征在于：所述的面板本体为人造板。
CN201611041324.5A 2016-11-18 2016-11-18 玻璃纤维地板的制作方法 Pending CN108068416A (zh)