CN108047975A - A kind of konjaku glucomannan sport plaster cloth and preparation method thereof - Google Patents
A kind of konjaku glucomannan sport plaster cloth and preparation method thereof Download PDFInfo
- Publication number
- CN108047975A CN108047975A CN201810006362.XA CN201810006362A CN108047975A CN 108047975 A CN108047975 A CN 108047975A CN 201810006362 A CN201810006362 A CN 201810006362A CN 108047975 A CN108047975 A CN 108047975A
- Authority
- CN
- China
- Prior art keywords
- konjaku glucomannan
- parts
- plaster cloth
- preparation
- sport plaster
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of konjaku glucomannan sport plaster cloths and preparation method thereof.The preparation method of konjaku glucomannan sport plaster cloth, the configuration including konjaku glucomannan glue mucus filter, prepare gluing elastic force cotton and assembling sport plaster cloth.A kind of konjaku glucomannan sport plaster cloth of the present invention is using konjaku glucomannan as primary raw material, emphasis utilizes antibiotic property and absorption of perspiration the two features, the function of sport plaster cloth uniqueness is assigned, konjaku glucomannan and auxiliary material used are substantially all biodegradable, meet the themes of the times of current environmental protection.The konjaku glucomannan sport plaster cloth of the present invention, all other sport plaster cloths are more excellent more on the market in the indexs such as absorption of perspiration, antibiotic property, antibiotic property, ring and cost of material, and konjaku glucomannan is at low cost, processing technology is simple, compared with similar sport plaster cloth, can become a new generation has the sport plaster cloth of the market competitiveness.
Description
Technical field
The present invention relates to a kind of sport plaster cloths and preparation method thereof, and in particular to a kind of konjaku glucomannan sport plaster cloth and
Its preparation method belongs to daily necessities field.
Background technology
Now, movement increasingly becomes an indispensable part in people's life, however existing during the motion
DOMS, blood circulation is not smooth and the problems such as joint is pulled still annoyings the people for having deep love for movement, particularly move
Top-notch players easily influence the physical training condition of later stage entirety and final training effect.Therefore, there have been to a certain extent can
Enough preventions and the sport plaster cloth for alleviating above-mentioned symptom, after sticking sport plaster cloth at injured muscles position, skin is led be subject to patch
It draws, increases the gap between subcutaneous tissue and muscle, so as to promote the blood circulation of tissue and lymphatic return, relieve pain,
Improve Xun Huan, mitigate oedema, also, it may also help in support and stablizes joint, posture correction, lifter motion ability.But now
The invention of sport plaster cloth is focused in the shape and bonding method of patch mostly, so, the selection of interlayer adhesive is also
Need further to be developed.Konjaku glucomannan not only has that elasticity is good, antibiotic property is good, absorption of perspiration is good, and viscosity is strong can to drop with biology
The features such as solution property, product inherent value can be greatly promoted to make sport plaster cloth as main adhesive raw material.In addition,
Production cost can be also largely reduced, therefore, is had great advantage compared with existing various sport plaster cloths in the market.
Number of patent application is a kind of 201220194259.0 patent " combination kinesiology tape "（The applying date：
2012.05.02）, a kind of combination kinesiology tape is which disclose, including at least 2 same types or differs type
Basis patch；The type of the basis patch includes promoting patch, water conservancy diversion patch, adjustment muscle patch and the patch that promotes blood circulation；It is described to carry
Rising patch includes X-shaped patch；The water conservancy diversion patch is selected from vertical bar shaped patch, Y shape patch or claw type patch；The adjustment muscle patch choosing
From vertical bar shaped patch or Y shape patch；The patch that promotes blood circulation includes claw type patch；Every basis patch includes elastic force
Cloth, barrier paper and the glue surface adhered the two together.But wherein adhesive material used in interbed is common glue surface, with konjaku Portugal
Sweet glycan is compared, and first, common glue surface does not have good biological degradability, and secondly, common glue surface is without antibiotic property, for a long time and flesh
Skin contact is likely to the discomfort for causing sporter.
A kind of patent of invention " ventilative comfort type sport plaster cloth " of Application No. 201510149213.5（The applying date：
2015.04.01）, a kind of ventilative comfort type sport plaster cloth of the disclosure of the invention is plastic including the thick stretch fabric of chevron and environment-friendly type
Property adhesive scribbles dotted environment-friendly type plasticity adhesive on the thick stretch fabric of chevron, and main raw material(s) is EVA resin, auxiliary
It is made with tackifier, viscosity modifier and antioxidant.EVA resin is ethylene-vinyl acetate copolymer, is generally used for making injection
And foaming product, the 65% of total quantity consumed is accounted for, it is immature for making the technical recipe of adhesive.Furthermore though EVA resin has
Certain air permeability but be not as good as KGM effects, and without antibiotic property, and the resin is in the production process using acetylene method technique
Route, and this method production cost is higher, thus causes to greatly improve by the sport plaster cloth cost that raw material make of EVA.
Under the historical background to increase severely in high quality sports products demand, requirement of the people to sport plaster cloth is from preferably easypro
Appropriateness, elasticity are risen to in preferable antibiotic property, the level of absorption of perspiration, existing such as cotton material or EVA resin
The sport plaster cloth of material cannot meet consumer demand, in addition, from production cost angle, konjak portuguese gansu polyose
Sugar possesses very strong advantage, and in this context, a kind of sport plaster cloth of konjaku glucomannan just comes into being.
The content of the invention
The object of the present invention is to provide it is a kind of be different from conventional motion patch there is the degradable of antibiotic property and absorption of perspiration
Sport plaster cloth and preparation method thereof.The present invention utilizes its water imbibition, film forming, water conservation using konjaku glucomannan as primary raw material
Property, biodegradability are simultaneously aided with other synergist（Rosin resin, terpene resin, polyvinyl alcohol, microwax and phosphite ester）
The novel sports patch that antibiotic property is good, absorption of perspiration is good, drawing elasticity is good and environmental-protecting performance is high is made.
The preparation method of the konjaku glucomannan sport plaster cloth of the present invention, the configuration including konjaku glucomannan glue mucus,
Filtering, dry and gluing, assembling sport plaster cloth, it is characterised in that preparation process is as follows：
（1）The preparation of konjaku glucomannan glue mucus：It is prepared by mass parts, takes 0.12-0.15 parts of rosin resin, polyvinyl alcohol
0.12-0.16 parts of 0.35-0.45 parts, 0.03-0.06 parts of microwax, 0.04-0.12 parts of terpene resin and phosphite ester, in
It under conditions of 1500r/min, 85-95 DEG C, sequentially adds in 94-100 parts of water, after stirring 6-7h, with the NaOH tune of 1mol/L
Save pH to 7-11；1-2 parts of konjaku glucomannan is added, 4-5h is stirred under conditions of 1500r/min, 85-95 DEG C, obtains konjaku
Glucomannan glue mucus, it is spare；
The konjaku glucomannan, rosin resin, terpene resin, polyvinyl alcohol, microwax and phosphite ester are food-grade.
（2）Filtering：By step（1）The konjaku glucomannan glue mucus prepared pour into the filter screen of a diameter of 1mm into
Row filtering, the liquid after filtering is konjaku glucomannan adhesive；
（3）Prepare gluing elastic force cotton：Selection JYP-045 hot melt adhesive glue melting boxes prepare gluing elastic force cotton, and hot melt adhesive is set to melt
Glue box temperature degree is 110-130 DEG C, and preheats 30min, then by step（2）1 part of konjaku glucomannan adhesive, elastic force cotton
4 parts, konjaku glucomannan adhesive is coated on elastic force cotton by JYP-045 hot melt adhesive glue melting box, obtains gluing elastic cotton
Cloth；
（4）Assemble sport plaster cloth：Take step（3）Gluing elastic force cotton, the close paper of the patch last layer back of the body, then pass it through cutting and receive
Volume, is made konjaku glucomannan sport plaster cloth.
Advantages of the present invention and usefulness：A kind of konjaku glucomannan sport plaster cloth of the present invention is with konjaku glucomannan
For primary raw material, on the characteristics such as water imbibition, film forming, water-retaining property and the biodegradability that it has, emphasis utilizes anti-
Bacterium property and absorption of perspiration the two features assign the function of sport plaster cloth uniqueness.And konjaku glucomannan and auxiliary material used are basic
It is all biodegradable, meet the themes of the times of current environmental protection.In addition, in modern production, due to konjaku glucomannan cost
It is low, processing technology is simple, compared with similar sport plaster cloth, have the market competitiveness.
Auxiliary material rosin resin is used as adhesive in daily chemical industry used in the present invention, for increasing viscosity, changing glue
Stick holds viscosity, its addition can increase the viscosity of patch, prevents from dropping when using；Polyvinyl alcohol is important industrial chemicals,
It is a kind of extremely safe macromolecule organic, nontoxic to human body, without side-effects, has good biocompatibility, energy and flesh
Skin intimate contact is used as auxiliary adhesive, can enhance the effect of rosin resin in the present invention；Microwax is on the make used as viscous
Spend conditioning agent；Terpene resin is some thermoplastic block copolymers, has good inoxidizability, compatibility and dissolubility, it
Addition can effectively mitigate the oxidation of patch intermediate adhesive；Phosphite ester is auxiliary antioxidant, and good processing stability.
Konjaku glucomannan sport plaster cloth obtained is done into following performance test：
（1）Water imbibition
By konjaku glucomannan sport plaster cloth and ordinary movement patch（Common adhesives, resin adhesive）It is placed in clear water, makees
Water absorption rate compares within 10 minutes.
（2）Antibiotic property
Examination bacterium is supplied with reference to the standard selection of QB/T 2591-2003.
（3）Biological degradability
Konjaku glucomannan sport plaster cloth and ordinary movement patch are buried 30 days, tested using soil burying.
As shown in table 1, the konjaku glucomannan sport plaster cloth properties by the test present invention are excellent, and index is equal
More than commercially available ordinary movement patch, alternative existing sport plaster cloth.
The konjaku glucomannan sport plaster cloth of 1 present invention of table with having sport plaster cloth correlated performance test comparison on the market
As a result
By above-mentioned test comparison, konjaku glucomannan sport plaster cloth of the invention, in absorption of perspiration, antibiotic property, antibiotic property, ring
With all other sport plaster cloths are more excellent more on the market in the indexs such as cost of material, sport plaster cloth of new generation can be become.
Specific embodiment
The present invention is described in further detail with reference to specific embodiment.
Embodiment 1, a kind of preparation method of konjaku glucomannan sport plaster cloth, comprise the following steps：
（1）The configuration of konjaku glucomannan glue mucus：Prepared by mass parts, take 0.12 part of rosin resin, 0.35 part of polyvinyl alcohol,
0.12 part of 0.03 part of microwax, 0.04 part of terpene resin and phosphite ester under conditions of 1500r/min, 85 DEG C, add successively
Enter in 99 parts of water, after stirring 6h, pH to 8 is adjusted with the NaOH of 1mol/L；1 part of konjaku glucomannan is added, in 1500r/
Min stirs 4h under conditions of 85 DEG C, obtains konjaku glucomannan glue mucus, spare；
（2）Filtering：By step（1）The glue mucus of preparation are poured into the filter screen of a diameter of 1mm and are filtered, the liquid after filtering
As konjaku glucomannan adhesive；
（3）Prepare gluing elastic force cotton：Selection JYP-045 hot melt adhesive glue melting boxes prepare gluing elastic force cotton, set glue box temperature degree
For 110 DEG C, and 30min is preheated, then by step（2）1 part of konjaku glucomannan adhesive, 4 parts of elastic force cotton, pass through JYP-
Konjaku glucomannan adhesive is coated on elastic force cotton by 045 hot melt adhesive glue melting box, obtains gluing elastic force cotton；
（4）Assemble sport plaster cloth：Take step（3）Gluing elastic force cotton, the close paper of the patch last layer back of the body, then pass it through cutting and receive
Volume, is made a kind of new konjaku glucomannan sport plaster cloth.
Embodiment 2, a kind of preparation method of konjaku glucomannan sport plaster cloth, comprise the following steps：
（1）The configuration of konjaku glucomannan glue mucus：Prepared by mass parts, take 0.13 part of rosin resin, 0.40 part of polyvinyl alcohol,
0.13 part of 0.05 part of microwax, 0.08 part of terpene resin and phosphite ester under conditions of 1500r/min, 90 DEG C, add successively
Enter in 98 parts of water, after stirring 6.5h, pH to 9 is adjusted with the NaOH of 1mol/L；1.5 parts of konjaku glucomannan is added, in
1500r/min stirs 4.5h under conditions of 90 DEG C, obtains konjaku glucomannan glue mucus, spare；
（2）Filtering：By step（1）The konjaku glucomannan glue mucus of preparation, which are poured into the filter screen of a diameter of 1mm, to be filtered,
Liquid after filtering is konjaku glucomannan adhesive；
（3）Prepare gluing elastic force cotton：Selection JYP-045 hot melt adhesive glue melting boxes prepare gluing elastic force cotton, and hot melt adhesive is set to melt
Glue box temperature degree is 120 DEG C, and preheats 30min, then by step（2）1 part of konjaku glucomannan adhesive, 4 parts of elastic force cotton,
Konjaku glucomannan adhesive is coated on elastic force cotton by JYP-045 hot melt adhesive glue melting box, obtains gluing elastic force cotton；
（4）Assemble sport plaster cloth：Take step（3）Gluing elastic force cotton, the close paper of the patch last layer back of the body, then pass it through cutting and receive
Volume, is made a kind of new konjaku glucomannan sport plaster cloth.
Embodiment 3, a kind of preparation method of konjaku glucomannan sport plaster cloth, comprise the following steps：
（1）The configuration of konjaku glucomannan glue mucus：Prepared by mass parts, take 0.15 part of rosin resin, 0.45 part of polyvinyl alcohol,
0.16 part of 0.06 part of microwax, 0.12 part of terpene resin and phosphite ester under conditions of 1500r/min, 95 DEG C, add successively
Enter in 96 parts of water, after stirring 7h, pH to 10 is adjusted with the NaOH of 1mol/L；2 parts of konjaku glucomannan is added, in 1500r/
Min stirs 5h under conditions of 95 DEG C, obtains konjaku glucomannan glue mucus, spare；
（2）Filtering：By step（1）The glue mucus of preparation are poured into the filter screen of a diameter of 1mm and are filtered, the liquid after filtering
As konjaku glucomannan adhesive；
（3）Prepare gluing elastic force cotton：Selection JYP-045 hot melt adhesive glue melting boxes prepare gluing elastic force cotton, set glue box temperature degree
For 125 DEG C, and 30min is preheated, then by step（2）1 part of konjaku glucomannan adhesive, 4 parts of elastic force cotton passes through JYP-
Konjaku glucomannan adhesive is coated on elastic force cotton by 045 hot melt adhesive glue melting box, obtains gluing elastic force cotton；
（4）Assemble sport plaster cloth：Take step（3）Gluing elastic force cotton, the close paper of the patch last layer back of the body, then pass it through cutting and receive
Volume, is made a kind of new konjaku glucomannan sport plaster cloth.
The foregoing is merely presently preferred embodiments of the present invention, all equivalent changes done according to scope of the present invention patent with
Modification should all belong to the covering scope of the present invention.
Claims (5)
1. a kind of preparation method of konjaku glucomannan sport plaster cloth, it is characterised in that preparation process is as follows：
（1）The preparation of konjaku glucomannan glue mucus：It is prepared by mass parts, takes 0.12-0.15 parts of rosin resin, polyvinyl alcohol
0.12-0.16 parts of 0.35-0.45 parts, 0.03-0.06 parts of microwax, 0.04-0.12 parts of terpene resin and phosphite ester, in
It under conditions of 1500r/min, 85-95 DEG C, sequentially adds in 94-100 parts of water, after stirring 6-7h, with the NaOH tune of 1mol/L
Save pH to 7-11；1-2 parts of konjaku glucomannan is added, 4-5h is stirred under conditions of 1500r/min, 85-95 DEG C, obtains konjaku
Glucomannan glue mucus, it is spare；
（2）Filtering：By step（1）The konjaku glucomannan glue mucus prepared are poured into the filter screen of a diameter of 1mm and carried out
Filter, the liquid after filtering is konjaku glucomannan adhesive；
（3）Prepare gluing elastic force cotton：Selection hot melt adhesive glue melting box prepares gluing elastic force cotton, sets hot melt adhesive glue melting box
Temperature is 110-130 DEG C, and preheats 30min, then by step（2）1 part of konjaku glucomannan adhesive, 4 parts of elastic force cotton,
Konjaku glucomannan adhesive is coated on elastic force cotton by JYP-045 hot melt adhesive glue melting box, obtains gluing elastic force cotton；
（4）Assemble sport plaster cloth：Take step（3）Gluing elastic force cotton, the close paper of the patch last layer back of the body, then pass it through cutting and receive
Volume, is made konjaku glucomannan sport plaster cloth.
A kind of 2. preparation method of konjaku glucomannan sport plaster cloth according to claim 1, it is characterised in that the evil spirit
The preparation of taro Glucomannan glue mucus：Take 0.12 part of rosin resin, 0.35 part of polyvinyl alcohol, 0.03 part of microwax, terpene resin
0.04 part and 0.12 part of phosphite ester, under conditions of 1500r/min, 85 DEG C, sequentially add in 99 parts of water, after stirring 6h, use
The NaOH of 1mol/L adjusts pH to 8；1 part of konjaku glucomannan is added, 4h is stirred under conditions of 1500r/min, 85 DEG C,
Obtain konjaku glucomannan glue mucus.
A kind of 3. preparation method of konjaku glucomannan sport plaster cloth according to claim 1, it is characterised in that the evil spirit
The preparation of taro Glucomannan glue mucus：Take 0.13 part of rosin resin, 0.40 part of polyvinyl alcohol, 0.05 part of microwax, terpene resin
0.08 part and 0.13 part of phosphite ester, under conditions of 1500r/min, 90 DEG C, sequentially add in 98 parts of water, after stirring 6.5h,
PH to 9 is adjusted with the NaOH of 1mol/L；1.5 parts of konjaku glucomannan is added, is stirred under conditions of 1500r/min, 90 DEG C
4.5h obtains konjaku glucomannan glue mucus.
A kind of 4. preparation method of konjaku glucomannan sport plaster cloth according to claim 1, it is characterised in that the evil spirit
The preparation of taro Glucomannan glue mucus：Take 0.15 part of rosin resin, 0.45 part of polyvinyl alcohol, 0.06 part of microwax, terpene resin
0.12 part and 0.16 part of phosphite ester, under conditions of 1500r/min, 95 DEG C, sequentially add in 96 parts of water, after stirring 7h, use
The NaOH of 1mol/L adjusts pH to 10；2 parts of konjaku glucomannan is added, 5h is stirred under conditions of 1500r/min, 95 DEG C,
Obtain konjaku glucomannan glue mucus.
5. the konjaku glucomannan sport plaster cloth prepared as the either method described in claim 1-4.