CN108045003A - The high-strength grid cloth of light and thin type - Google Patents
The high-strength grid cloth of light and thin type Download PDFInfo
- Publication number
- CN108045003A CN108045003A CN201711047323.6A CN201711047323A CN108045003A CN 108045003 A CN108045003 A CN 108045003A CN 201711047323 A CN201711047323 A CN 201711047323A CN 108045003 A CN108045003 A CN 108045003A
- Authority
- CN
- China
- Prior art keywords
- yarn
- grid cloth
- light
- layer
- thin type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of high-strength grid cloth of light and thin type for having both stretch-resistance and frivolous property.A kind of high-strength grid cloth of light and thin type, including the base cloth layer formed by glass fiber yarn as warp thread and weft yarns, the glass fiber yarn is the reinforcement glass yarn for improving mixed liquor by dipping or coating；The warp thread and the density ratio of weft yarn are 1:1~3:1, equidistant arrangement between warp thread, equidistant arrangement between weft yarn；The weft yarn is equipped with tie up yarn of the spiral surrounding in weft yarn outer surface, and warp thread is connected by tying up yarn with weft yarn；The one side of base cloth layer is equipped with wearing layer, and the wearing layer is fluoropolymer type coating；The opposite side of base cloth layer is equipped with waterproof layer, and the waterproof layer is equipped with the polyvinyl chloride film of several pores for surface.Yarn density ratio configuration of the present invention is reasonable；Using ceramic fibre yarn as yarn is tied up, increase the bonding strength of yarn in grid cloth；Grid cloth has certain wearability and water proofing property.
Description
Technical field
The present invention relates to a kind of fabric, more particularly to a kind of high-strength grid cloth of light and thin type.
Background technology
Grid cloth is based on middle alkali or alkali-free glass fibre woven fabric, is formed through alkaline-resisting coating treatment.Grid cloth
Intensity is high, alkali resistance is good, and important structure function is played in heat-insulation system, mainly prevents the generation in crack.Since its is excellent
The performance of chemical substances pedantic scholar and the tensile strength through broadwise such as antiacid, alkali, the stress suffered by exterior wall heat-preserving system can be made
It is homodisperse, it is avoided that the collision due to outer impulse force, the deformation of the entire insulation construction caused by extruding, has insulating layer very high
Impact resistance intensity, and be easy to construction and quality control, play the role of in heat-insulation system " mild steel muscle ".Grid cloth is not only
As the increase material of wall, can more be widely used as outdoor advertising carrier.There is tall building wall in place involved by it
Advertising because the material property of grid cloth, more general common cloth is more solid and durable.But existing grid cloth production
Dead weight and limited stretch-resistance of the product due to itself are poor in the repellence to mastication forces, there is grid cloth to be torn hidden
Suffer from, influence security.
The content of the invention
It is an object of the invention to provide a kind of high-strength grid cloth of light and thin type for having both stretch-resistance and frivolous property, solve with
The problem of being proposed in upper background technology.
The technical solution adopted by the present invention to solve the technical problems is：
A kind of high-strength grid cloth of light and thin type, it is described including the base cloth layer formed by glass fiber yarn as warp thread and weft yarns
Glass fiber yarn be by dipping or coating improve mixed liquor reinforcement glass yarn, the improvement mixed liquor include it is following
The formula of weight percent：Water dispersible phenoxy resin 3.5 ~ 13.5, water dispersible phenolic resin 1.5 ~ 7.5, melamine
Formaldehyde resin 1.5 ~ 3.5, Ludox 0.5 ~ 4.5, epoxy silane coupling agent 0.4 ~ 1.5, lubricant 0.02 ~ 0.1, acetic acid 0.01 ~
0.1, water 69.3 ~ 92.57；The warp thread and the density ratio of weft yarn are 1:1~3:1, equidistant arrangement between warp thread, between weft yarn
Equidistant arrangement；The weft yarn is equipped with tie up yarn of the spiral surrounding in weft yarn outer surface, and warp thread is connected by tying up yarn with weft yarn；Base fabric
The one side of layer is equipped with wearing layer, and the wearing layer is fluoropolymer type coating；The opposite side of base cloth layer is equipped with waterproof layer, institute
The waterproof layer stated is equipped with the polyvinyl chloride film of several pores for surface.
Institute can be enhanced by improving the mixture of the phenoxy resin in mixed liquor, melamine resin and phenolic resin
The tensile strength of the glass fiber yarn of coating, phenoxy resin mixing melamine resin therein answer glass fibre
It closes pull resistance and is significantly improved effect；Phenolic resin therein not only provides mechanical strength, and it is special also to provide bonding for a part
Property；Ludox therein is dispersion liquid of the nano level silica dioxide granule in water or in solvent, the titanium dioxide in Ludox
Silicon contains substantial amounts of water and hydroxyl, and Ludox eventually forms fine and close and harder film with moisture evaporation, colloid molecules increase,
Cohesive force is strong and high temperature resistant；In view of the outdoor advertising carrier application environment of the high-strength grid cloth of the light and thin type, what weft yarn was born
The external force that external force is born compared with warp thread is high, so the density of weft yarn is set above warp thread, the side for improving grid cloth anti-tear is pulled
Ability, and tie up yarn and play the role of assistant reinforcement degree of being connected firmly；In view of other situations of wall thermal insulating application, in base cloth layer
Outside sets wearing layer and waterproof layer, increases the wearability and water proofing property of grid cloth.
Preferably, the wearing layer is the coating composition for including fluoropolymer, adhesive and inorganic filler particle.
Inorganic filler particle is not soluble in water, and Knoop hardness is higher, its coating composition formed is made to have preferable anti-scratch power and resistance to
Long property.
Preferably, the warp thread is the glass fiber yarn of line density 400tex ~ 2400tex.
Preferably, the weft yarn is the glass fiber yarn of line density 1200tex ~ 4800tex.
Preferably, described ties up the ceramic fibre yarn that yarn is line density 1150tex ~ 2600tex.Ceramic fibre has
The advantages that light-weight, high temperature resistant, although ceramic fibre is more crisp in itself, silk is also shorter, and spinnability is poor, glutinous by addition
Glue can make ceramic fibre yarn by the methods of core, increase wire enhancing of glass fiber, reach higher intensity, ceramics
Silvalin can increase the bonding strength of warp thread and weft yarn as yarn is tied up, and improve tear resistance, and because its light-weight spy
Point will not be significantly increased the weight of grid cloth, can also increase the heat-resisting quantity, thermal insulation and anti-flammability of grid cloth.
The beneficial effects of the invention are as follows：
The high-strength grid cloth of light and thin type of the present invention, using the reinforcement glass yarn of tensile strength bigger as warp thread and weft yarns
The base cloth layer formed, yarn density ratio configuration are reasonable；Using ceramic fibre yarn as yarn is tied up, increase the company of yarn in grid cloth
Connect intensity；Grid cloth has both frivolous property while with higher-strength, and set outside base cloth layer appropriate wearing layer and
Waterproof layer makes grid cloth have certain wearability and water proofing property.
Description of the drawings
Fig. 1 is the main structure diagram of the present invention；
Fig. 2 is the layer structure schematic diagram of the present invention.
In figure：1st, warp thread, 2, weft yarn, 3, base cloth layer, 4, tie up yarn, 5, wearing layer, 6, waterproof layer.
Specific embodiment
Below by specific embodiment, and with reference to attached drawing, technical scheme is described in further detail.It should
Work as understanding, implementation of the invention is not limited to the following examples, the accommodation in any form done to the present invention and/or
Change falls within the scope of the present invention.
Embodiment：
The high-strength grid cloth of a kind of light and thin type as depicted in figs. 1 and 2, including being interweaved by glass fiber yarn as warp thread 1 and weft yarn 2
The base cloth layer 3 formed, glass fiber yarn are the reinforcement glass yarn for improving mixed liquor by coating, and improvement mixed liquor includes following
The formula of weight percent：Water dispersible phenoxy resin 3.5 ~ 13.5, water dispersible phenolic resin 1.5 ~ 7.5, melamine
Formaldehyde resin 1.5 ~ 3.5, Ludox 0.5 ~ 4.5, epoxy silane coupling agent 0.4 ~ 1.5, lubricant 0.02 ~ 0.1, acetic acid 0.01 ~
0.1, water 69.3 ~ 92.57.
Institute can be enhanced by improving the mixture of the phenoxy resin in mixed liquor, melamine resin and phenolic resin
The tensile strength of the glass fiber yarn of coating, phenoxy resin mixing melamine resin therein answer glass fibre
It closes pull resistance and is significantly improved effect；Phenolic resin therein not only provides mechanical strength, and it is special also to provide bonding for a part
Property；Ludox therein is dispersion liquid of the nano level silica dioxide granule in water or in solvent, the titanium dioxide in Ludox
Silicon contains substantial amounts of water and hydroxyl, and Ludox eventually forms fine and close and harder film with moisture evaporation, colloid molecules increase,
Cohesive force is strong and high temperature resistant.
Warp thread is the glass fiber yarn of line density 2400tex, and weft yarn is the glass fiber yarn of line density 4800tex.Warp thread
Density ratio with weft yarn is 3:1, equidistant arrangement between warp thread, equidistant arrangement between weft yarn.Weft yarn is equipped with spiral surrounding in weft yarn
Yarn 4 is tied up in outer surface, and warp thread is connected by tying up yarn with weft yarn.Tie up the ceramic fibre yarn that yarn is line density 1150tex.It is ceramic fine
Dimension has many advantages, such as light-weight, high temperature resistant, although ceramic fibre is more crisp in itself, silk is also shorter, and spinnability is poor, passes through
Addition viscose can make ceramic fibre yarn by the methods of core, increase wire enhancing of glass fiber, reach higher strong
Degree, ceramic fiber yarn can increase the bonding strength of warp thread and weft yarn as yarn is tied up, and improve tear resistance, and because its weight
The characteristics of light, will not be significantly increased the weight of grid cloth, can also increase the heat-resisting quantity of grid cloth, thermal insulation and fire-retardant
Property.
The one side of base cloth layer is equipped with wearing layer 5, and wearing layer is fluoropolymer type coating, and specifically, wearing layer is bag
The coating composition of fluoropolymer, adhesive and inorganic filler particle.Inorganic filler particle is not soluble in water, Knoop hardness compared with
Height makes its coating composition formed have preferable anti-scratch power and durability.Inorganic filler particle is selected in the present embodiment
For zirconium carbide ceramics particle and the mixture of alumina particle, the wherein granularity of zirconium carbide ceramics particle is 80 ~ 120 microns, oxygen
The granularity for changing aluminium is 4 ~ 10 microns.
The opposite side of base cloth layer is equipped with waterproof layer 6, and waterproof layer is equipped with the polyvinyl chloride film of several pores for surface.It examines
Consider the outdoor advertising carrier application environment of the high-strength grid cloth of the light and thin type, the external force that weft yarn is born is compared with the external force that warp thread is born
Height so the density of weft yarn is set above warp thread, improves the side tear resistance of grid cloth, and tie up yarn play auxiliary plus
The effect of strong ties firmness.In view of other situations of practical application, wearing layer and waterproof layer outside base cloth layer are set, increased
Add the wearability and water proofing property of grid cloth.
The test data of the high-strength grid cloth of light and thin type of the present embodiment is shown in Table 1.
The high-strength grid cloth test data table of table 1- light and thin types
| Test event | Unit | Test index | Test result |
| Mesh centre-to-centre spacing | mm | 4*4 | 4*4 |
| Warp-wise ultimate strength | N/50mm | ≥1250 | 1550 |
| Broadwise ultimate strength | N/50mm | ≥1250 | 1450 |
| Elongation at break（Broadwise） | % | ≤5 | 3.2 |
| Plastic-coated amount | g/m2 | ≥20 | 25.5 |
The base cloth layer that the present embodiment is formed using the reinforcement glass yarn of tensile strength bigger as warp thread and weft yarns, yarn
Density ratio configuration is reasonable；Using ceramic fibre yarn as yarn is tied up, increase the bonding strength of yarn in grid cloth；Grid cloth is having
Frivolous property is had both while having higher-strength, and appropriate wearing layer and waterproof layer are set outside base cloth layer, has grid cloth
There are certain wearability and water proofing property.
Embodiment described above is a kind of preferable scheme of the present invention, and not the present invention is made in any form
Limitation also has other variants and remodeling on the premise of without departing from the technical solution recorded in claim.
Claims (9)
1. a kind of high-strength grid cloth of light and thin type, including by glass fiber yarn as warp thread（1）And weft yarn（2）The base fabric being interwoven
Layer（3）, it is characterised in that：The glass fiber yarn is to pass through dipping or coating to improve the reinforcement glass yarn of mixed liquor, institute
The improvement mixed liquor stated includes the formula of following weight percent：Water dispersible phenoxy resin 3.5 ~ 13.5, water dispersible phenol
Urea formaldehyde 1.5 ~ 7.5, melamine resin 1.5 ~ 3.5, Ludox 0.5 ~ 4.5, epoxy silane coupling agent 0.4 ~ 1.5, profit
Lubrication prescription 0.02 ~ 0.1, acetic acid 0.01 ~ 0.1, water 69.3 ~ 92.57；The warp thread and the density ratio of weft yarn are 1:1~3:1, warp thread
Between equidistant arrangement, equidistant arrangement between weft yarn；The weft yarn ties up yarn equipped with spiral surrounding in weft yarn outer surface（4）, warp
Yarn is connected by tying up yarn with weft yarn；The one side of base cloth layer is equipped with wearing layer（5）, the wearing layer is fluoropolymers painting
Layer；The opposite side of base cloth layer is equipped with waterproof layer（6）, the waterproof layer is polyvinyl chloride film of the surface equipped with several pores
Layer.
2. the high-strength grid cloth of light and thin type according to claim 1, it is characterised in that：The wearing layer is bag fluoropolymer
The coating composition of object, adhesive and inorganic filler particle.
3. the high-strength grid cloth of light and thin type according to claim 1 or 2, it is characterised in that：The warp thread is line density
The glass fiber yarn of 400tex ~ 2400tex.
4. the high-strength grid cloth of light and thin type according to claim 1 or 2, it is characterised in that：The weft yarn is line density
The glass fiber yarn of 1200tex ~ 4800tex.
5. the high-strength grid cloth of light and thin type according to claim 3, it is characterised in that：The weft yarn is line density
The glass fiber yarn of 1200tex ~ 4800tex.
6. the high-strength grid cloth of light and thin type according to claim 1 or 2, it is characterised in that：Described ties up yarn as line density
The ceramic fibre yarn of 1150tex ~ 2600tex.
7. the high-strength grid cloth of light and thin type according to claim 3, it is characterised in that：Described ties up yarn as line density
The ceramic fibre yarn of 1150tex ~ 2600tex.
8. the high-strength grid cloth of light and thin type according to claim 4, it is characterised in that：Described ties up yarn as line density
The ceramic fibre yarn of 1150tex ~ 2600tex.
9. the high-strength grid cloth of light and thin type according to claim 5, it is characterised in that：Described ties up yarn as line density
The ceramic fibre yarn of 1150tex ~ 2600tex.