CN108035170A - A kind of Polyester fibre disperse dyes in low-temperature dyeing technique - Google Patents
A kind of Polyester fibre disperse dyes in low-temperature dyeing technique Download PDFInfo
- Publication number
- CN108035170A CN108035170A CN201711281951.0A CN201711281951A CN108035170A CN 108035170 A CN108035170 A CN 108035170A CN 201711281951 A CN201711281951 A CN 201711281951A CN 108035170 A CN108035170 A CN 108035170A
- Authority
- CN
- China
- Prior art keywords
- polyester fibre
- disperse dyes
- low
- temperature dyeing
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of Polyester fibre disperse dyes in low-temperature dyeing technique, in turn include the following steps:According to 1:8 10 bath raio into the water, sequentially adds acetic acid, low temperature dyeing assistant and disperse dyes;80 DEG C are warming up to, then to 95 100 DEG C, and keep 30 40min;It is cooled to 80 85 DEG C;It is cooled to 10 DEG C;40 45 DEG C are warming up in 5 10min again, and keeps 20 25min;Carry out reduction cleaning 23 times;Clean up, and dry again.The low temperature dyeing assistant is the emulsion containing organic ester.A kind of Polyester fibre disperse dyes in low-temperature dyeing technique according to the present invention, use containing organic esters such as fragrant cluster ester type compounds, optimize the techniques such as dyeing temperature so that on the basis of Polyester fibre low temperature color is met, may be such that the color fastness of dyeing and uniformity improve with obtaining.
Description
Technical field
The present invention relates to the staining technique field of Polyester fibre, especially a kind of Polyester fibre disperse dyes low temperature dye
Color technique.
Background technology
Polyester fiber is hydrophobic synthetic fibers, and the energy as cellulose or protein fibre is lacked in molecular structure
The active group combined with dyestuff.Polyester fiber crystallinity, the degree of orientation are high, and molecules align is closer, is only deposited in fiber
In the gap of very little.Routine to polyester fiber carry out water-bath dyeing when, in order to reach preferable coloring, it is necessary to using
More than more than 130 DEG C high temperature, to ensure that violent warm-up movement occurs for fiber macromolecular, enough momentary clearances are produced, allow dye
Material diffuses into fibrous inside;High temperature can also promote the dissolving and diffusion of dyestuff at the same time, be conducive to dye.To terylene high-temperature dyeing
Do not utilize it is energy-saving, in the existing low temperature dyeing technique to terylene there are color fastness it is not high, dyeing it is uneven the problems such as.
The content of the invention
The object of the present invention is to provide a kind of Polyester fibre disperse dyes in low-temperature dyeing technique, terylene is enabled to dissipate fibre
Dimension has high color fastness and even dyeing in dyeing.
In order to solve the above technical problems, the object of the present invention is achieved like this:
A kind of Polyester fibre disperse dyes in low-temperature dyeing technique according to the present invention, in turn includes the following steps:
Step(1), under the conditions of 50 DEG C, according to 1:Polyester fibre into the water, is sequentially added acetic acid, low by the bath raio of 8-10
Warm dyeing assistant and disperse dyes, and stir evenly, keep 15min;
Step(2), 80 DEG C are warming up within the 40-45min times, then 95-100 DEG C is warming up in 10-15min, and keep 30-
40min。
Step(3), add cold water and be cooled to 80-85 DEG C, and keep 10min;
Step(4), add cold water cooling, temperature lowering water is to 10 DEG C;40-45 DEG C is warming up in 5-10min again, and keeps 20-
25min;
Step(5), to step(4)Polyester fibre after processing carries out reduction cleaning 2-3 times;Cleaning to be carried out with clear water dry again
Only, and dry;
Step(1)In, the low temperature dyeing assistant is the emulsion containing organic ester.
As a further illustration of the above scheme, step(1)In, the addition of the acetic acid is to account for the amount of Polyester fibre
It is described scattered than being that to account for the weight ratio of Polyester fibre be 1-3% for the addition of 0.5-2.5%, the low temperature dyeing assistant
The weight ratio that the addition of dyestuff accounts for Polyester fibre is 1-5%.
As a further illustration of the above scheme, step(5)In, the technological parameter of the reduction cleaning is:Soaping agent 2g/
L, thiourea dioxide 2g/L, caustic soda 2g/L, bath raio 1:8-10,85-90 DEG C of temperature, time 10min.
As a further illustration of the above scheme, the soaping agent is paregal O or nonylphenol polyoxyethylene ether.
As a further illustration of the above scheme, organic ester contained in the low temperature dyeing assistant is to include but not
Be limited to dioctyl terephthalate, diethylene glycol dibenzoate, dimethyl terephthalate (DMT), ethyl benzoate, phenyl salicylate,
Fragrant cluster ester type compound including benzyl salicylate.
The beneficial effects of the invention are as follows:A kind of Polyester fibre disperse dyes in low-temperature dyeing technique according to the present invention,
Use containing organic esters such as fragrant cluster ester type compounds, optimized the techniques such as dyeing temperature so that meeting Polyester fibre
On the basis of low temperature color, it may be such that the color fastness of dyeing and uniformity improve with obtaining.
Embodiment
Participate in the election of the detailed description of the invention below for being preferable to carry out method and including embodiment this hair can be more easily understood
Bright content.Unless otherwise defined, all technologies used herein and scientific terminology have common with fields of the present invention
The normally understood identical implication of technical staff.
A kind of Polyester fibre disperse dyes in low-temperature dyeing technique according to the present invention, in turn includes the following steps:
Step(1), under the conditions of 50 DEG C, according to 1:Polyester fibre into the water, is sequentially added acetic acid, low by the bath raio of 8-10
Warm dyeing assistant and disperse dyes, and stir evenly, keep 15min.The addition of acetic acid is that the amount ratio for accounting for Polyester fibre is
0.5-2.5%, the addition of low temperature dyeing assistant are that to account for the weight ratio of Polyester fibre be 1-3%, and the addition of disperse dyes accounts for
The weight ratio of Polyester fibre is 1-5%.
Low temperature dyeing assistant is help dyeing system to reduce within dyeing preference temperature to 110 DEG C in dyeing and finishing industry one
A little small molecule auxiliary agents.Described low temperature dyeing assistant molecular formula one end carries hydrolyzable groups, and the other end is with certain length
Alkyl, therefore there are certain surfactant properties, and certain carrier effect can be played to dyestuff.Therefore in dyeing course
Middle addition low temperature dyeing assistant can effectively improve the dissolubility of dyestuff, suspension and dispersiveness in dye liquor, you can dyestuff is played
Solubilized dissolution assistant effect, and then beneficial to disperse dyes polyester fiber is adsorbed onto with molecular forms after the transfer of crystal bulky grain form
Surface.On the other hand, low temperature dyeing assistant molecule has the structure similar to terylene macromolecular repetitive unit, easily big with terylene
Molecule is combined.Thus low temperature dyeing assistant molecule is easily penetrated into inside polyester fiber in dyeing course, and then can be to fibre
Dimension plays plasticising Swelling Functions, thus is diffused into beneficial to the disperse dyes molecule of absorption inside polyester fiber.Above-mentioned two aspect
Factor plays the role of promoting dye at the same time, can obviously reduce the temperature needed for dyeing, under the action of appropriate low temperature dyeing assistant, dyeing
Temperature can usually be down to 100~108 DEG C, and dyeing installation conventional at present can relatively hold under not additional supercharging device
Change places and reach this temperature range.
Low temperature dyeing assistant is the emulsion containing organic ester in the present invention, organic ester contained therein be include but
It is not limited to dioctyl terephthalate, diethylene glycol dibenzoate, dimethyl terephthalate (DMT), ethyl benzoate, salicylic acid benzene
Fragrant cluster ester type compound including ester, benzyl salicylate.Used disperse dyes are low temperature disperse dyes.
Step(2), 80 DEG C are warming up within the 40-45min times, then 95-100 DEG C is warming up in 10-15min, and protect
Hold 30-40min.
Step(3), add cold water and be cooled to 80-85 DEG C, and keep 10min.
Step(4), add cold water cooling, be cooled to 10 DEG C;40-45 DEG C is warming up in 5-10min again, and keeps 20-
25min。
Step(5), to step(4)Polyester fibre after processing carries out reduction cleaning 2-3 times;Cleaned again with clear water
Totally, and dry.The technological parameter of reduction cleaning is:Soaping agent 2g/L, thiourea dioxide 2g/L, caustic soda 2g/L, bath raio 1:8-
10,85-90 DEG C of temperature, time 10min.Paregal O or nonylphenol polyoxyethylene ether may be selected in soaping agent.
Embodiment one
Under the conditions of 50 DEG C, according to 1:Polyester fibre into the water, is sequentially added acetic acid, low temperature dyeing assistant by 8 bath raio
And disperse dyes, and stir evenly, keep 15min.The addition of acetic acid is that to account for the amount ratio of Polyester fibre be 0.5%, low temperature dye
The addition of color auxiliary agent is that to account for the weight ratio of Polyester fibre be 13%, and the addition of disperse dyes accounts for the weight of Polyester fibre
Than for 1%.Used disperse dyes are disperse red FB 200% in the present embodiment.
80 DEG C are warming up within the 405min times, then 95 DEG C are warming up in 10min, and keeps 30min.Add cold water
80 DEG C are cooled to, and keeps 10min.
Cold water cooling is added, is cooled to 10 DEG C;40 DEG C are warming up in 5min again, and keeps 20min.
Reduction cleaning is carried out 2 times to the Polyester fibre after above-mentioned steps processing;Cleaned up, and dried with clear water again
It is dry.The technological parameter of reduction cleaning is:Soaping agent 2g/L, thiourea dioxide 2g/L, caustic soda 2g/L, bath raio 1:8,85 DEG C of temperature,
Time 10min.
Embodiment two
Under the conditions of 50 DEG C, according to 1:Polyester fibre into the water, is sequentially added acetic acid, low temperature dyeing assistant by 9 bath raio
And disperse dyes, and stir evenly, keep 15min.The addition of acetic acid is that to account for the amount ratio of Polyester fibre be 1.5%, low temperature dye
The addition of color auxiliary agent is that to account for the weight ratio of Polyester fibre be 2%, and the addition of disperse dyes accounts for the weight ratio of Polyester fibre
For 3%.Used disperse dyes are Disperse Blue 2BLN 200% in the present embodiment.
80 DEG C are warming up within the 40min times, then 100 DEG C are warming up in 15min, and keeps 40min.Add cold water
85 DEG C are cooled to, and keeps 10min.
Cold water cooling is added, is cooled to 10 DEG C;45 DEG C are warming up in 10min again, and keeps 25min.
Reduction cleaning is carried out 3 times to the Polyester fibre after above-mentioned steps processing;Cleaned up, and dried with clear water again
It is dry.The technological parameter of reduction cleaning is:Soaping agent 2g/L, thiourea dioxide 2g/L, caustic soda 2g/L, bath raio 1:10, temperature 90
DEG C, time 10min.
Embodiment three
Under the conditions of 50 DEG C, according to 1:Polyester fibre into the water, is sequentially added acetic acid, low temperature dyeing assistant by 10 bath raio
And disperse dyes, and stir evenly, keep 15min.The addition of acetic acid is that to account for the amount ratio of Polyester fibre be 2.5%, low temperature dye
The addition of color auxiliary agent is that to account for the weight ratio of Polyester fibre be 3%, and the addition of disperse dyes accounts for the weight ratio of Polyester fibre
For 5%.Used disperse dyes are disperse yellow E-3G 200% in the present embodiment.
80 DEG C are warming up within the 42min times, then 98 DEG C are warming up in 12min, and keeps 35min.Add cold water
80 DEG C are cooled to, and keeps 10min.
Cold water cooling is added, is cooled to 10 DEG C;40 DEG C are warming up in 6in again, and keeps 20-25min.
Reduction cleaning is carried out 3 times to the Polyester fibre after above-mentioned steps processing;Cleaned up, and dried with clear water again
It is dry.The technological parameter of reduction cleaning is:Soaping agent 2g/L, thiourea dioxide 2g/L, caustic soda 2g/L, bath raio 1:8,90 DEG C of temperature,
Time 10min.
Preferred embodiment of the invention described in detail above.It should be appreciated that those of ordinary skill in the art without
Need creative work to conceive according to the present invention and make many modifications and variations.Therefore, all technologies in the art
Personnel are available by logical analysis, reasoning, or a limited experiment on the basis of existing technology under this invention's idea
Technical solution, all should be in the protection domain being defined in the patent claims.
Claims (5)
1. a kind of Polyester fibre disperse dyes in low-temperature dyeing technique, it is characterised in that in turn include the following steps:
Step(1), under the conditions of 50 DEG C, according to 1:Polyester fibre into the water, is sequentially added acetic acid, low by the bath raio of 8-10
Warm dyeing assistant and disperse dyes, and stir evenly, keep 15min;
Step(2), 80 DEG C are warming up within the 40-45min times, then 95-100 DEG C is warming up in 10-15min, and keep 30-
40min;
Step(3), add cold water and be cooled to 80-85 DEG C, and keep 10min;
Step(4), add cold water cooling, be cooled to 10 DEG C;40-45 DEG C is warming up in 5-10min again, and keeps 20-
25min;
Step(5), to step(4)Polyester fibre after processing carries out reduction cleaning 2-3 times;Cleaning to be carried out with clear water dry again
Only, and dry;
Step(1)In, the low temperature dyeing assistant is the emulsion containing organic ester.
2. Polyester fibre disperse dyes in low-temperature dyeing technique as claimed in claim 1, it is characterised in that step(1)In, institute
The addition for stating acetic acid is that to account for the amount ratio of Polyester fibre be 0.5-2.5%, and the addition of the low temperature dyeing assistant is washed to account for
The weight ratio of synthetic fibre staple in bulk is 1-3%, and the weight ratio that the additions of the disperse dyes accounts for Polyester fibre is 1-5%.
3. Polyester fibre disperse dyes in low-temperature dyeing technique as claimed in claim 1, it is characterised in that step(5)In, institute
The technological parameter for stating reduction cleaning is:Soaping agent 2g/L, thiourea dioxide 2g/L, caustic soda 2g/L, bath raio 1:8-10, temperature 85-
90 DEG C, time 10min.
4. Polyester fibre disperse dyes in low-temperature dyeing technique as claimed in claim 3, it is characterised in that the soaping agent is
Paregal O or nonylphenol polyoxyethylene ether.
5. Polyester fibre disperse dyes in low-temperature dyeing technique as claimed in claim 1, it is characterised in that the low temperature dye
Contained organic ester is to include but not limited to dioctyl terephthalate, diethylene glycol dibenzoate, to benzene two in color auxiliary agent
Fragrant cluster ester type compound including formic acid dimethyl ester, ethyl benzoate, phenyl salicylate, benzyl salicylate.