CN108030592A - One kind easily tears medical proof fabric - Google Patents
One kind easily tears medical proof fabric Download PDFInfo
- Publication number
- CN108030592A CN108030592A CN201711348654.3A CN201711348654A CN108030592A CN 108030592 A CN108030592 A CN 108030592A CN 201711348654 A CN201711348654 A CN 201711348654A CN 108030592 A CN108030592 A CN 108030592A
- Authority
- CN
- China
- Prior art keywords
- parts
- proof fabric
- medical proof
- agent
- rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention discloses one kind and easily tears medical proof fabric, using non-woven fabrics as base material, first by non-woven fabrics bleaching, by the roller mangle of the starching machine equipped with modification liquid, carries out cylinder preliminary drying, then is dried by drying tunnel, obtains modification nonwoven cloth;Then rubber cement is prepared, radish filiform or flake is made in sheet natural rubber block with rubber mixing machine, then it is dipped in the mixed liquor of gasoline and toluene and is fully swollen, glyceryl tristearate and coumarone indene resin are added, stirs evenly, adds various auxiliary agents, it can obtain the pressure-sensitive rubber cement of rubber-type, finally pressure-sensitive rubber cement is coated onto in modified base fabric with coating machine, the processing such as winding is then dried, you can finished product;What the present invention made easily tears medical proof fabric, is not only easy to tear off, patient will not produce feeling of pain when tearing, and after long-time adheres to, still with good skin adherence, it will not be separated automatically with skin, it ensure that the adhesive plaster can play fixation, play its due effect.
Description
Technical field
The present invention relates to a kind of medical proof fabric, more particularly to one kind easily tears medical proof fabric.
Background technology
Adhesive plaster is a kind of sticking plastic products adhesive plaster, and common adhesive plaster includes medical proof fabric, insulating tape etc., its
Middle medical proof fabric has good permeability, and nontoxic nonirritant, and Nature comparison is gentle, has good viscosity, is usually used in
Fixed injection needle, wrapping etc.;But when existing medical proof fabric is taken off from adult, it often can all experience and " tear for a moment
The pain split ", if so this adhesive plaster is taken off from the tender and lovely skin of baby, it is likely that skin can be damaged, it is also possible to can cause
When medical complaint and dispute event, certain negative effect is caused to medical institutions.
In the prior art, there is also the adhesive plaster being much easy to tear off, in Application No. CN201510781909.X
A kind of novel medical proof fabric of state's patent, such adhesive plaster good permeability is environmentally protective, and is easy to tear off after being attached on human body,
Some feeling of pains will not be produced to human body.
But with time change, viscosity has significantly to be reduced existing easily openable medical proof fabric, waits until certain time
Afterwards, since adhesive plaster viscosity is too small, it can be separated with human body automatically, can not just play fixation, it is often necessary to repeatedly paste,
It is cumbersome and time consuming, or even influence treatment results.
The content of the invention
In view of the deficiencies of the prior art, the present invention intends to provide one kind easily to tear medical proof fabric, the medical adhesive
After cloth is pasted on human body, it is easy to tear, and keep stronger viscosity in a long time, will not mutually be taken off with human body automatically
From.
To achieve the above object, the present invention provides following technical solution:One kind easily tears medical proof fabric, including following weight
Part composition:
Non-woven fabrics:90 parts;
Carbon black:2 parts;
Magnesia:2 parts;
Coupling agent:3 parts;
Crosslinking agent:5 parts;
Emulsifying agent:1 part;
Solubilizer:1 part;
Antiseptic:3 parts;
Plasticizer:2 parts;
Waterproofing agent:1 part;
Antioxidant:2 parts;
Stabilizer:5 parts;
Modified working solution:10-30 parts;
The stabilizer is double [3- (triethoxysilane) propyl group] amine, magnesium stearate, lauryl sodium sulfate, bay Asia
The mixture of amino disodium beclomethasone and phosphorous acid three (2- ethylhexyls) ester, its mass ratio are 3:1:2:2:2;
The modified working solution includes following weight parts material composition:
Acrylate copolymer emulsion:15 parts;
Tert-pentyl alcohol bismuth:2 parts;
N, N- dibutyl -1,3- propane diamine:3 parts;
Sodium cellulose glycolate:1 part;
Zinc oxide:2 parts;
Water:50 parts.
The coupling agent is 3-aminopropyltriethoxysilane.
The crosslinking agent is cumyl peroxide.
The emulsifying agent is two (2- ethylhexyls) amine.
The solubilizer is ethoxylated dodecyl alcohol and the mixture of ethylene oxide, its mass ratio is 1:1.
The antiseptic is the mixture of glycerin monostearate, potassium sorbate and povidone iodine, its mass ratio is 2:1:
2。
The plasticizer is o-phthalic acid dibutyl ester.
The waterproofing agent is (3,3,3- trifluoro propyls) trimethoxy silane.
The antioxidant is N-N'- diphenyl-p-phenylenediamines and the mixture of 4- tert-butyl catechols, its mass ratio is
1:2。
A kind of preparation method for easily tearing medical proof fabric:
The first step:The processing of cloth material, non-woven fabrics progress bleaching is bleached cloth, then poured into modified working solution first
In the stock tank of starching machine, control and roll point pressure for 3500~4500 kilograms, above-mentioned bleach cloth is passed through with 8~18 meters of speed per minute
Roller mangle, pick-up rate is 60~80%, then by 90~110 ° of preliminary dryings of cylinder about half a minute, through tenter expanding to open width
Width, enters drying tunnel, and by drying tunnel at 170~195 DEG C, drying time is about 1-5 minutes, that is, obtains the modification nonwoven as base fabric
Cloth;
Second step, prepares rubber cement, and 20-50 parts of sheets are given birth to natural rubber block is rolled into radish filiform or thin slice through rubber mixing machine
Shape, is dipped in 30-80 parts of mass ratioes as 2:It is abundant that swelling is allowed in 1 gasoline and the mixed liquor of toluene, obtains raw rubber swelling thing, so
The 3-5 parts of glyceryl tristearates as softening agent are added afterwards, add 5-20 parts of coumarone indene resins, stir 5-20min, then
Sequentially add carbon black, magnesia, coupling agent, crosslinking agent, emulsifying agent, solubilizer, antiseptic, plasticizer, waterproofing agent, antioxidant and
Stabilizer, continues to stir 30-60min, so as to obtain rubber pressure-sensitive adhesive slurry;
3rd step, rubber cement coating, the rubber cement obtained in second step is placed in the rubber cement groove before coating machine painting drum,
It is 0.1~0.25mm to control cylinder gap, makes base fabric slowly by roller, through drying, winding, cut-out finished product.
Beneficial effects of the present invention:One kind easily tear medical proof fabric, using non-woven fabrics as base material, first by non-woven fabrics into
Row bleaching is bleached cloth, and is then allowed and is bleached cloth by the roller mangle equipped with the starching machine for being modified working solution, then carries out cylinder
Preliminary drying, is then dried by drying tunnel, you can obtains modification nonwoven cloth;Then rubber cement is prepared, the life with rubber mixing machine sheet
Natural rubber block be made that radish is Filamentous or flake, be then dipped in the mixed liquor of gasoline and toluene, the matter of gasoline and toluene
Measure as 2:1, the mixing liquid energy being configured so that makes raw rubber sufficiently be swollen, and after swelling completely, adds three glycerol stearates
Ester is as softening agent and coumarone indene resin as tackifier, and coumarone indene resin is except playing tackifying effect, moreover it is possible to plays plasticizing, soft
Change the effect with reinforcement, first stir certain time, add various auxiliary agents, you can obtain the pressure-sensitive rubber cement of rubber-type, finally use
Pressure-sensitive rubber cement is coated onto in modified base fabric by coating machine, and the thickness of coating is 0.1-0.25mm, and the processing such as winding is then dried,
It can be prepared by finished product;What the present invention made easily tears medical proof fabric, is not only easy to tear off, and patient will not produce feeling of pain when tearing,
And after adhesion when 3 is small, still with good skin adherence, it will not be separated, ensure that with skin automatically
The adhesive plaster can play fixation, play its due effect.
One of innovative point as the present invention, carries out the bleached non-woven fabrics that obtains and is handled with modification liquid, modified working solution is with water
For solvent, by adding acrylic emulsion, tert-pentyl alcohol bismuth, N, N- dibutyl -1,3- propane diamine, sodium cellulose glycolate and oxidation
Zinc these types material, can carry out good modification so that final system under the collective effect of these types of material to non-woven fabrics
Easily tear medical proof fabric and be easy to tear off, patient will not be made to produce feeling of pain, more skin will not be caused to damage;Another innovation
Point is that stabilizer have selected double [3- (triethoxysilane) propyl group] amine, magnesium stearate, lauryl sodium sulfate, bay imino groups
Disodium beclomethasone and phosphorous acid three (2- ethylhexyls) ester this 5 kinds of materials;These materials it is mutually coordinated under, ensure that and easily tear
Medical proof fabric has preferable viscosity, and viscosity change with time it is smaller, even if after when adhesion 3 is small on the skin, viscosity
It is still relatively strong, good fixation can be played.
Antiseptic have selected glycerin monostearate, potassium sorbate and povidone iodine this 3 kinds of materials, in this 3 kinds of materials
Under collective effect, obtained easily tearing medical adhesive tape has good antibacterial property, reduces the possibility to patient's secondary injury, more
It is safe and healthy;It has selected N-N'- diphenyl-p-phenylenediamines and 4- tert-butyl catechols this 2 kinds of materials on antioxidant, this 2 kinds
Under the collective effect of material, good anti-aging effect can be played, it is easy to aging to ensure that the present invention does not allow, can be placed for a long time,
Easy to produce, transport and storage.
Embodiment
Embodiment 1:It is a kind of easily to tear medical proof fabric, including following parts by weight composition:
Non-woven fabrics:90 parts;
Carbon black:2 parts;
Magnesia:2 parts;
Coupling agent:3 parts;
Crosslinking agent:5 parts;
Emulsifying agent:1 part;
Solubilizer:1 part;
Antiseptic:3 parts;
Plasticizer:2 parts;
Waterproofing agent:1 part;
Antioxidant:2 parts;
Stabilizer:5 parts;
Modified working solution:10-30 parts;
The stabilizer is double [3- (triethoxysilane) propyl group] amine, magnesium stearate, lauryl sodium sulfate, bay Asia
The mixture of amino disodium beclomethasone and phosphorous acid three (2- ethylhexyls) ester, its mass ratio are 3:1:2:2:2;
The modified working solution includes following weight parts material composition:
Acrylate copolymer emulsion:15 parts;
Tert-pentyl alcohol bismuth:2 parts;
N, N- dibutyl -1,3- propane diamine:3 parts;
Sodium cellulose glycolate:1 part;
Zinc oxide:2 parts;
Water:50 parts.
The coupling agent is 3-aminopropyltriethoxysilane.
The crosslinking agent is cumyl peroxide.
The emulsifying agent is two (2- ethylhexyls) amine.
The solubilizer is ethoxylated dodecyl alcohol and the mixture of ethylene oxide, its mass ratio is 1:1.
The antiseptic is the mixture of glycerin monostearate, potassium sorbate and povidone iodine, its mass ratio is 2:1:
2。
The plasticizer is o-phthalic acid dibutyl ester.
The waterproofing agent is (3,3,3- trifluoro propyls) trimethoxy silane.
The antioxidant is N-N'- diphenyl-p-phenylenediamines and the mixture of 4- tert-butyl catechols, its mass ratio is
1:2。
A kind of preparation method for easily tearing medical proof fabric:
The first step:The processing of cloth material, non-woven fabrics progress bleaching is bleached cloth, then poured into modified working solution first
In the stock tank of starching machine, control and roll point pressure for 3500~4500 kilograms, above-mentioned bleach cloth is passed through with 8~18 meters of speed per minute
Roller mangle, pick-up rate is 60~80%, then by 90~110 ° of preliminary dryings of cylinder about half a minute, through tenter expanding to open width
Width, enters drying tunnel, and by drying tunnel at 170~195 DEG C, drying time is about 1-5 minutes, that is, obtains the modification nonwoven as base fabric
Cloth;
Second step, prepares rubber cement, and 20-50 parts of sheets are given birth to natural rubber block is rolled into radish filiform or thin slice through rubber mixing machine
Shape, is dipped in 30-80 parts of mass ratioes as 2:It is abundant that swelling is allowed in 1 gasoline and the mixed liquor of toluene, obtains raw rubber swelling thing, so
The 3-5 parts of glyceryl tristearates as softening agent are added afterwards, add 5-20 parts of coumarone indene resins, stir 5-20min, then
Sequentially add carbon black, magnesia, coupling agent, crosslinking agent, emulsifying agent, solubilizer, antiseptic, plasticizer, waterproofing agent, antioxidant and
Stabilizer, continues to stir 30-60min, so as to obtain rubber pressure-sensitive adhesive slurry;
3rd step, rubber cement coating, the rubber cement obtained in second step is placed in the rubber cement groove before coating machine painting drum,
It is 0.1~0.25mm to control cylinder gap, makes base fabric slowly by roller, through drying, winding, cut-out finished product.
Comparative example 1:It is a kind of easily to tear medical proof fabric, including following parts by weight composition:
It is a kind of easily to tear medical proof fabric, including following parts by weight composition:
Non-woven fabrics:90 parts;
Carbon black:2 parts;
Magnesia:2 parts;
Coupling agent:3 parts;
Crosslinking agent:5 parts;
Emulsifying agent:1 part;
Solubilizer:1 part;
Antiseptic:3 parts;
Plasticizer:2 parts;
Waterproofing agent:1 part;
Antioxidant:2 parts;
Stabilizer:5 parts;
Modified working solution:10-30 parts;
The stabilizer is magnesium stearate, three (2- of lauryl sodium sulfate, bay iminodipropionate and phosphorous acid
Ethylhexyl) ester mixture, its mass ratio be 1:2:2:2;
The modified working solution includes following weight parts material composition:
Acrylate copolymer emulsion:15 parts;
Tert-pentyl alcohol bismuth:2 parts;
N, N- dibutyl -1,3- propane diamine:3 parts;
Sodium cellulose glycolate:1 part;
Zinc oxide:2 parts;
Water:50 parts.
The coupling agent is 3-aminopropyltriethoxysilane.
The crosslinking agent is cumyl peroxide.
The emulsifying agent is two (2- ethylhexyls) amine.
The solubilizer is ethoxylated dodecyl alcohol and the mixture of ethylene oxide, its mass ratio is 1:1.
The antiseptic is the mixture of glycerin monostearate, potassium sorbate and povidone iodine, its mass ratio is 2:1:
2。
The plasticizer is o-phthalic acid dibutyl ester.
The waterproofing agent is (3,3,3- trifluoro propyls) trimethoxy silane.
The antioxidant is N-N'- diphenyl-p-phenylenediamines and the mixture of 4- tert-butyl catechols, its mass ratio is
1:2。
A kind of preparation method for easily tearing medical proof fabric:
The first step:The processing of cloth material, non-woven fabrics progress bleaching is bleached cloth, then poured into modified working solution first
In the stock tank of starching machine, control and roll point pressure for 3500~4500 kilograms, above-mentioned bleach cloth is passed through with 8~18 meters of speed per minute
Roller mangle, pick-up rate is 60~80%, then by 90~110 ° of preliminary dryings of cylinder about half a minute, through tenter expanding to open width
Width, enters drying tunnel, and by drying tunnel at 170~195 DEG C, drying time is about 1-5 minutes, that is, obtains the modification nonwoven as base fabric
Cloth;
Second step, prepares rubber cement, and 20-50 parts of sheets are given birth to natural rubber block is rolled into radish filiform or thin slice through rubber mixing machine
Shape, is dipped in 30-80 parts of mass ratioes as 2:It is abundant that swelling is allowed in 1 gasoline and the mixed liquor of toluene, obtains raw rubber swelling thing, so
The 3-5 parts of glyceryl tristearates as softening agent are added afterwards, add 5-20 parts of coumarone indene resins, stir 5-20min, then
Sequentially add carbon black, magnesia, coupling agent, crosslinking agent, emulsifying agent, solubilizer, antiseptic, plasticizer, waterproofing agent, antioxidant and
Stabilizer, continues to stir 30-60min, so as to obtain rubber pressure-sensitive adhesive slurry;
3rd step, rubber cement coating, the rubber cement obtained in second step is placed in the rubber cement groove before coating machine painting drum,
It is 0.1~0.25mm to control cylinder gap, makes base fabric slowly by roller, through drying, winding, cut-out finished product.
Comparative example 2:It is a kind of easily to tear medical proof fabric, including following parts by weight composition:
Non-woven fabrics:90 parts;
Carbon black:2 parts;
Magnesia:2 parts;
Coupling agent:3 parts;
Crosslinking agent:5 parts;
Emulsifying agent:1 part;
Solubilizer:1 part;
Antiseptic:3 parts;
Plasticizer:2 parts;
Waterproofing agent:1 part;
Antioxidant:2 parts;
Stabilizer:5 parts;
Modified working solution:10-30 parts;
The stabilizer is double [3- (triethoxysilane) propyl group] amine, bay iminodipropionate and phosphorous acid three
The mixture of (2- ethylhexyls) ester, its mass ratio are 3:2:2;
The modified working solution includes following weight parts material composition:
Acrylate copolymer emulsion:15 parts;
Tert-pentyl alcohol bismuth:2 parts;
N, N- dibutyl -1,3- propane diamine:3 parts;
Sodium cellulose glycolate:1 part;
Zinc oxide:2 parts;
Water:50 parts.
The coupling agent is 3-aminopropyltriethoxysilane.
The crosslinking agent is cumyl peroxide.
The emulsifying agent is two (2- ethylhexyls) amine.
The solubilizer is ethoxylated dodecyl alcohol and the mixture of ethylene oxide, its mass ratio is 1:1.
The antiseptic is the mixture of glycerin monostearate, potassium sorbate and povidone iodine, its mass ratio is 2:1:
2。
The plasticizer is o-phthalic acid dibutyl ester.
The waterproofing agent is (3,3,3- trifluoro propyls) trimethoxy silane.
The antioxidant is N-N'- diphenyl-p-phenylenediamines and the mixture of 4- tert-butyl catechols, its mass ratio is
1:2。
A kind of preparation method for easily tearing medical proof fabric:
The first step:The processing of cloth material, non-woven fabrics progress bleaching is bleached cloth, then poured into modified working solution first
In the stock tank of starching machine, control and roll point pressure for 3500~4500 kilograms, above-mentioned bleach cloth is passed through with 8~18 meters of speed per minute
Roller mangle, pick-up rate is 60~80%, then by 90~110 ° of preliminary dryings of cylinder about half a minute, through tenter expanding to open width
Width, enters drying tunnel, and by drying tunnel at 170~195 DEG C, drying time is about 1-5 minutes, that is, obtains the modification nonwoven as base fabric
Cloth;
Second step, prepares rubber cement, and 20-50 parts of sheets are given birth to natural rubber block is rolled into radish filiform or thin slice through rubber mixing machine
Shape, is dipped in 30-80 parts of mass ratioes as 2:It is abundant that swelling is allowed in 1 gasoline and the mixed liquor of toluene, obtains raw rubber swelling thing, so
The 3-5 parts of glyceryl tristearates as softening agent are added afterwards, add 5-20 parts of coumarone indene resins, stir 5-20min, then
Sequentially add carbon black, magnesia, coupling agent, crosslinking agent, emulsifying agent, solubilizer, antiseptic, plasticizer, waterproofing agent, antioxidant and
Stabilizer, continues to stir 30-60min, so as to obtain rubber pressure-sensitive adhesive slurry;
3rd step, rubber cement coating, the rubber cement obtained in second step is placed in the rubber cement groove before coating machine painting drum,
It is 0.1~0.25mm to control cylinder gap, makes base fabric slowly by roller, through drying, winding, cut-out finished product.
Comparative example 3:It is a kind of easily to tear medical proof fabric, including following parts by weight composition:
Non-woven fabrics:90 parts;
Carbon black:2 parts;
Magnesia:2 parts;
Coupling agent:3 parts;
Crosslinking agent:5 parts;
Emulsifying agent:1 part;
Solubilizer:1 part;
Antiseptic:3 parts;
Plasticizer:2 parts;
Waterproofing agent:1 part;
Antioxidant:2 parts;
Stabilizer:5 parts;
Modified working solution:10-30 parts;
The stabilizer is the mixing of double [3- (triethoxysilane) propyl group] amine, magnesium stearate, lauryl sodium sulfate
Thing, its mass ratio are 3:1:2;
The modified working solution includes following weight parts material composition:
Acrylate copolymer emulsion:15 parts;
Tert-pentyl alcohol bismuth:2 parts;
N, N- dibutyl -1,3- propane diamine:3 parts;
Sodium cellulose glycolate:1 part;
Zinc oxide:2 parts;
Water:50 parts.
The coupling agent is 3-aminopropyltriethoxysilane.
The crosslinking agent is cumyl peroxide.
The emulsifying agent is two (2- ethylhexyls) amine.
The solubilizer is ethoxylated dodecyl alcohol and the mixture of ethylene oxide, its mass ratio is 1:1.
The antiseptic is the mixture of glycerin monostearate, potassium sorbate and povidone iodine, its mass ratio is 2:1:
2。
The plasticizer is o-phthalic acid dibutyl ester.
The waterproofing agent is (3,3,3- trifluoro propyls) trimethoxy silane.
The antioxidant is N-N'- diphenyl-p-phenylenediamines and the mixture of 4- tert-butyl catechols, its mass ratio is
1:2。
A kind of preparation method for easily tearing medical proof fabric:
The first step:The processing of cloth material, non-woven fabrics progress bleaching is bleached cloth, then poured into modified working solution first
In the stock tank of starching machine, control and roll point pressure for 3500~4500 kilograms, above-mentioned bleach cloth is passed through with 8~18 meters of speed per minute
Roller mangle, pick-up rate is 60~80%, then by 90~110 ° of preliminary dryings of cylinder about half a minute, through tenter expanding to open width
Width, enters drying tunnel, and by drying tunnel at 170~195 DEG C, drying time is about 1-5 minutes, that is, obtains the modification nonwoven as base fabric
Cloth;
Second step, prepares rubber cement, and 20-50 parts of sheets are given birth to natural rubber block is rolled into radish filiform or thin slice through rubber mixing machine
Shape, is dipped in 30-80 parts of mass ratioes as 2:It is abundant that swelling is allowed in 1 gasoline and the mixed liquor of toluene, obtains raw rubber swelling thing, so
The 3-5 parts of glyceryl tristearates as softening agent are added afterwards, add 5-20 parts of coumarone indene resins, stir 5-20min, then
Sequentially add carbon black, magnesia, coupling agent, crosslinking agent, emulsifying agent, solubilizer, antiseptic, plasticizer, waterproofing agent, antioxidant and
Stabilizer, continues to stir 30-60min, so as to obtain rubber pressure-sensitive adhesive slurry;
3rd step, rubber cement coating, the rubber cement obtained in second step is placed in the rubber cement groove before coating machine painting drum,
It is 0.1~0.25mm to control cylinder gap, makes base fabric slowly by roller, through drying, winding, cut-out finished product.
Comparative example 4:It is a kind of easily to tear medical proof fabric, including following parts by weight composition:
Non-woven fabrics:90 parts;
Carbon black:2 parts;
Magnesia:2 parts;
Coupling agent:3 parts;
Crosslinking agent:5 parts;
Emulsifying agent:1 part;
Solubilizer:1 part;
Antiseptic:3 parts;
Plasticizer:2 parts;
Waterproofing agent:1 part;
Antioxidant:2 parts;
Stabilizer:5 parts;
Modified working solution:10-30 parts;
The stabilizer is double [3- (triethoxysilane) propyl group] amine, magnesium stearate, lauryl sodium sulfate, bay Asia
The mixture of amino disodium beclomethasone and phosphorous acid three (2- ethylhexyls) ester, its mass ratio are 3:1:2:2:2;
The modified working solution includes following weight parts material composition:
Acrylate copolymer emulsion:15 parts;
N, N- dibutyl -1,3- propane diamine:3 parts;
Zinc oxide:2 parts;
Water:50 parts.
The coupling agent is 3-aminopropyltriethoxysilane.
The crosslinking agent is cumyl peroxide.
The emulsifying agent is two (2- ethylhexyls) amine.
The solubilizer is ethoxylated dodecyl alcohol and the mixture of ethylene oxide, its mass ratio is 1:1.
The antiseptic is the mixture of glycerin monostearate, potassium sorbate and povidone iodine, its mass ratio is 2:1:
2。
The plasticizer is o-phthalic acid dibutyl ester.
The waterproofing agent is (3,3,3- trifluoro propyls) trimethoxy silane.
The antioxidant is N-N'- diphenyl-p-phenylenediamines and the mixture of 4- tert-butyl catechols, its mass ratio is
1:2。
A kind of preparation method for easily tearing medical proof fabric:
The first step:The processing of cloth material, non-woven fabrics progress bleaching is bleached cloth, then poured into modified working solution first
In the stock tank of starching machine, control and roll point pressure for 3500~4500 kilograms, above-mentioned bleach cloth is passed through with 8~18 meters of speed per minute
Roller mangle, pick-up rate is 60~80%, then by 90~110 ° of preliminary dryings of cylinder about half a minute, through tenter expanding to open width
Width, enters drying tunnel, and by drying tunnel at 170~195 DEG C, drying time is about 1-5 minutes, that is, obtains the modification nonwoven as base fabric
Cloth;
Second step, prepares rubber cement, and 20-50 parts of sheets are given birth to natural rubber block is rolled into radish filiform or thin slice through rubber mixing machine
Shape, is dipped in 30-80 parts of mass ratioes as 2:It is abundant that swelling is allowed in 1 gasoline and the mixed liquor of toluene, obtains raw rubber swelling thing, so
The 3-5 parts of glyceryl tristearates as softening agent are added afterwards, add 5-20 parts of coumarone indene resins, stir 5-20min, then
Sequentially add carbon black, magnesia, coupling agent, crosslinking agent, emulsifying agent, solubilizer, antiseptic, plasticizer, waterproofing agent, antioxidant and
Stabilizer, continues to stir 30-60min, so as to obtain rubber pressure-sensitive adhesive slurry;
3rd step, rubber cement coating, the rubber cement obtained in second step is placed in the rubber cement groove before coating machine painting drum,
It is 0.1~0.25mm to control cylinder gap, makes base fabric slowly by roller, through drying, winding, cut-out finished product.
Comparative example 5:It is a kind of easily to tear medical proof fabric, including following parts by weight composition:
Non-woven fabrics:90 parts;
Carbon black:2 parts;
Magnesia:2 parts;
Coupling agent:3 parts;
Crosslinking agent:5 parts;
Emulsifying agent:1 part;
Solubilizer:1 part;
Antiseptic:3 parts;
Plasticizer:2 parts;
Waterproofing agent:1 part;
Antioxidant:2 parts;
Stabilizer:5 parts;
Modified working solution:10-30 parts;
The stabilizer is double [3- (triethoxysilane) propyl group] amine, magnesium stearate, lauryl sodium sulfate, bay Asia
The mixture of amino disodium beclomethasone and phosphorous acid three (2- ethylhexyls) ester, its mass ratio are 3:1:2:2:2;
The modified working solution includes following weight parts material composition:
Acrylate copolymer emulsion:15 parts;
Tert-pentyl alcohol bismuth:2 parts;
Sodium cellulose glycolate:1 part;
Water:50 parts.
The coupling agent is 3-aminopropyltriethoxysilane.
The crosslinking agent is cumyl peroxide.
The emulsifying agent is two (2- ethylhexyls) amine.
The solubilizer is ethoxylated dodecyl alcohol and the mixture of ethylene oxide, its mass ratio is 1:1.
The antiseptic is the mixture of glycerin monostearate, potassium sorbate and povidone iodine, its mass ratio is 2:1:
2。
The plasticizer is o-phthalic acid dibutyl ester.
The waterproofing agent is (3,3,3- trifluoro propyls) trimethoxy silane.
The antioxidant is N-N'- diphenyl-p-phenylenediamines and the mixture of 4- tert-butyl catechols, its mass ratio is
1:2。
A kind of preparation method for easily tearing medical proof fabric:
The first step:The processing of cloth material, non-woven fabrics progress bleaching is bleached cloth, then poured into modified working solution first
In the stock tank of starching machine, control and roll point pressure for 3500~4500 kilograms, above-mentioned bleach cloth is passed through with 8~18 meters of speed per minute
Roller mangle, pick-up rate is 60~80%, then by 90~110 ° of preliminary dryings of cylinder about half a minute, through tenter expanding to open width
Width, enters drying tunnel, and by drying tunnel at 170~195 DEG C, drying time is about 1-5 minutes, that is, obtains the modification nonwoven as base fabric
Cloth;
Second step, prepares rubber cement, and 20-50 parts of sheets are given birth to natural rubber block is rolled into radish filiform or thin slice through rubber mixing machine
Shape, is dipped in 30-80 parts of mass ratioes as 2:It is abundant that swelling is allowed in 1 gasoline and the mixed liquor of toluene, obtains raw rubber swelling thing, so
The 3-5 parts of glyceryl tristearates as softening agent are added afterwards, add 5-20 parts of coumarone indene resins, stir 5-20min, then
Sequentially add carbon black, magnesia, coupling agent, crosslinking agent, emulsifying agent, solubilizer, antiseptic, plasticizer, waterproofing agent, antioxidant and
Stabilizer, continues to stir 30-60min, so as to obtain rubber pressure-sensitive adhesive slurry;
3rd step, rubber cement coating, the rubber cement obtained in second step is placed in the rubber cement groove before coating machine painting drum,
It is 0.1~0.25mm to control cylinder gap, makes base fabric slowly by roller, through drying, winding, cut-out finished product.
Comparative example 6:The medical proof fabric produced by Qingdao Hai Shi Hai Nuo medical supplies Co., Ltd.
Comparative example 7:A kind of novel medical proof fabric prepared by the Chinese patent according to Application No. CN201510781909.X.
Sample made from embodiment 1 and comparative example 1-7 is cut into wide 15mm, the adhesive tape of long 40mm sizes adheres to volunteer
Inner forearm skin surface on.From adhesion 3 it is small when after, evaluation skin adherence, peel off when pain situation.
180 ° of peel strength tests:It will implement 1 and comparative example 1-7 and respective samples be made by GB2792-81 standards, use
LANGUANG electron detachments testing machine measures.
The present invention's easily tears medical proof fabric, using non-woven fabrics as base material, first obtains non-woven fabrics progress bleaching
To bleaching cloth, then allow and bleach cloth by the roller mangle equipped with the starching machine for being modified working solution, then carry out cylinder preliminary drying, then pass through
Drying tunnel is dried, you can obtains modification nonwoven cloth;Then rubber cement is prepared, the natural rubber block system with rubber mixing machine the life of sheet
It is Filamentous or laminar into radish, then it is dipped in the mixed liquor of gasoline and toluene, the quality of gasoline and toluene is 2:1, so match somebody with somebody
The mixing liquid energy put makes raw rubber sufficiently be swollen, swelling completely after, add glyceryl tristearate as softening agent with
Coumarone indene resin is as tackifier, and coumarone indene resin is except playing tackifying effect, moreover it is possible to plays the work of plasticizing, softening and reinforcement
With first stirring certain time, add various auxiliary agents, you can the pressure-sensitive rubber cement of rubber-type is obtained, finally will be pressure-sensitive with coating machine
Rubber cement is coated onto in modified base fabric, and the thickness of coating is 0.1-0.25mm, the processing such as winding is then dried, you can be made into
Product;What the present invention made easily tears medical proof fabric, is not only easy to tear off, and patient will not produce feeling of pain when tearing, and by 3
After the adhesion of hour, still with good skin adherence, it will not be separated automatically with skin, ensure that the adhesive plaster can play
Fixation, plays its due effect.
One of innovative point as the present invention, carries out the bleached non-woven fabrics that obtains and is handled with modification liquid, modified working solution is with water
For solvent, by adding acrylic emulsion, tert-pentyl alcohol bismuth, N, N- dibutyl -1,3- propane diamine, sodium cellulose glycolate and oxidation
Zinc these types material, can carry out good modification so that final system under the collective effect of these types of material to non-woven fabrics
Easily tear medical proof fabric and be easy to tear off, patient will not be made to produce feeling of pain, more skin will not be caused to damage;Another innovation
Point is that stabilizer have selected double [3- (triethoxysilane) propyl group] amine, magnesium stearate, lauryl sodium sulfate, bay imino groups
Disodium beclomethasone and phosphorous acid three (2- ethylhexyls) ester this 5 kinds of materials;These materials it is mutually coordinated under, ensure that and easily tear
Medical proof fabric has preferable viscosity, and viscosity change with time it is smaller, even if after when adhesion 3 is small on the skin, viscosity
It is still relatively strong, good fixation can be played.
Antiseptic have selected glycerin monostearate, potassium sorbate and povidone iodine this 3 kinds of materials, in this 3 kinds of materials
Under collective effect, obtained easily tearing medical proof fabric has good antibacterial property, reduces the possibility to patient's secondary injury, more
It is safe and healthy;It has selected N-N'- diphenyl-p-phenylenediamines and 4- tert-butyl catechols this 2 kinds of materials on antioxidant, this 2 kinds
Under the collective effect of material, good anti-aging effect can be played, it is easy to aging to ensure that the present invention does not allow, can be placed for a long time,
Easy to produce, transport and storage.
The above is only the preferred embodiment of the present invention, and protection scope of the present invention is not limited merely to above-mentioned implementation
Example, all technical solutions belonged under thinking of the present invention belong to protection scope of the present invention.It should be pointed out that for the art
Those of ordinary skill for, some improvements and modifications without departing from the principles of the present invention, these improvements and modifications
It should be regarded as protection scope of the present invention.
Claims (10)
1. one kind easily tears medical proof fabric, it is characterised in that:Formed including following parts by weight:
Non-woven fabrics:90 parts;
Carbon black:2 parts;
Magnesia:2 parts;
Coupling agent:3 parts;
Crosslinking agent:5 parts;
Emulsifying agent:1 part;
Solubilizer:1 part;
Antiseptic:3 parts;
Plasticizer:2 parts;
Waterproofing agent:1 part;
Antioxidant:2 parts;
Stabilizer:5 parts;
Modified working solution:10-30 parts;
The stabilizer is double [3- (triethoxysilane) propyl group] amine, magnesium stearate, lauryl sodium sulfate, bay imino group
The mixture of disodium beclomethasone and phosphorous acid three (2- ethylhexyls) ester, its mass ratio are 3:1:2:2:2;
The modified working solution includes following weight parts material composition:
Acrylate copolymer emulsion:15 parts;
Tert-pentyl alcohol bismuth:2 parts;
N, N- dibutyl -1,3- propane diamine:3 parts;
Sodium cellulose glycolate:1 part;
Zinc oxide:2 parts;
Water:50 parts.
2. one kind according to claim 1 easily tears medical proof fabric, it is characterised in that:The coupling agent is 3- aminopropyls three
Ethoxysilane.
3. one kind according to claim 2 easily tears medical proof fabric, it is characterised in that:The crosslinking agent is peroxidating diisopropyl
Benzene.
4. one kind according to claim 3 easily tears medical proof fabric, it is characterised in that:The emulsifying agent is two (2- ethyl hexyls
Base) amine.
5. one kind according to claim 4 easily tears medical proof fabric, it is characterised in that:The solubilizer is laruyl alcohol polyoxy second
The mixture of alkene ether and ethylene oxide, its mass ratio are 1:1.
6. one kind according to claim 5 easily tears medical proof fabric, it is characterised in that:The antiseptic is glycerol monostearate
The mixture of ester, potassium sorbate and povidone iodine, its mass ratio are 2:1:2.
7. one kind according to claim 6 easily tears medical proof fabric, it is characterised in that:The plasticizer is phthalic acid two
Pungent fat.
8. one kind according to claim 7 easily tears medical proof fabric, it is characterised in that:The waterproofing agent is (3,3,3- trifluoros
Propyl group) trimethoxy silane.
9. one kind according to claim 8 easily tears medical proof fabric, it is characterised in that:The antioxidant for N-N'- diphenyl-
The mixture of p-phenylenediamine and 4- tert-butyl catechols, its mass ratio are 1:2.
A kind of 10. preparation method for easily tearing medical proof fabric according to claim 1 to 9, it is characterised in that:
The first step:The processing of cloth material, non-woven fabrics progress bleaching is bleached cloth, modified working solution then is poured into starching first
In the stock tank of machine, control and roll point pressure for 3500~4500 kilograms, above-mentioned bleach cloth is passed through roller with 8~18 meters of speed per minute
Mangle, pick-up rate is 60~80%, wide to open width through tenter expanding then by 90~110 ° of preliminary dryings of cylinder about half a minute,
Enter drying tunnel, by drying tunnel at 170~195 DEG C, drying time is about 1-5 minutes, that is, obtains the modification nonwoven cloth as base fabric;
Second step, prepares rubber cement, and 20-50 parts of sheets are given birth to natural rubber block is rolled into radish filiform or flake, leaching through rubber mixing machine
In 30-80 parts of mass ratioes be 2:It is abundant that swelling is allowed in 1 gasoline and the mixed liquor of toluene, obtains raw rubber swelling thing, Ran Houjia
Enter the 3-5 parts of glyceryl tristearates as softening agent, add 5-20 parts of coumarone indene resins, stir 5-20min, then successively
Add carbon black, magnesia, coupling agent, crosslinking agent, emulsifying agent, solubilizer, antiseptic, plasticizer, waterproofing agent, antioxidant and stabilization
Agent, continues to stir 30-60min, so as to obtain rubber pressure-sensitive adhesive slurry;
3rd step, rubber cement coating, the rubber cement obtained in second step is placed in the rubber cement groove before coating machine painting drum, is controlled
Cylinder gap is 0.1~0.25mm, makes base fabric slowly by roller, through drying, winding, cut-out finished product.