CN108017919A - A kind of preparation method of plastic stalk special material for tube - Google Patents
A kind of preparation method of plastic stalk special material for tube Download PDFInfo
- Publication number
- CN108017919A CN108017919A CN201711121005.XA CN201711121005A CN108017919A CN 108017919 A CN108017919 A CN 108017919A CN 201711121005 A CN201711121005 A CN 201711121005A CN 108017919 A CN108017919 A CN 108017919A
- Authority
- CN
- China
- Prior art keywords
- stalk
- plastic
- door
- section bar
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of preparation method of plastic stalk special material for tube, its main feature is that after stalk is smashed, straw powder and the surface grafting polymerization of modified primitive are realized by way of Reaction extrusion in double screw extruder, make modified straw powder that there is thermoplasticity, then by can the straw powder of thermoplastic processing be uniformly mixed with polyvinyl chloride, processing aid, filler, and extruding pelletization, up to plastic stalk special material for tube.By adjusting the ratio and processing technology of each component, the special material for tube of different straw contents can be obtained.The PP Pipe Compound has the advantages that extensive, cheap, sustainable, the easy thermoplastic shaping of raw material sources, nontoxic, available for preparing various types of pipe parts.
Description
Technical field
The present invention relates to a kind of preparation method of plastic stalk door-window section bar PP Pipe Compound, belong to the system of functional high molecule material
It is standby with modified field.
Background technology
In architectural exterior-protecting construction, although door and window system occupied area is small, because its heat insulation property is relatively poor, pass through
The heat of door and window loss is very big, accounts for the 40%~50% of building enclosure component total energy consumption.Therefore, door and window material and design are shadows
One of principal element of building energy consumption is rung, is the important research direction in building energy conservation problem., should by research and development for many years
The research staff in field is in the selection of energy saving door and window structure design and door and window critical material, the sunshading technology of energy saving door and window and door and window
Energy consumption analogue technique etc. achieve notable achievement.Wherein, frame material is the important composition portion in door-window section bar system
Point, its projected area accounts for the 15%~20% of whole door-window opening area, selection and the direct shadow of assembly method of frame material
The performances such as the durable, insulation during the leakproofness of sound door and window and door and window use, and the properties of glass system are produced
Considerable influence.Therefore, the heat transfer of frame material is reduced, reduces the heat convection in frame gap, is to improve door and window heat insulating ability
The effective ways of energy.
On the other hand, with the strengthening of people's awareness of environmental protection, recycled using waste and old material and comprehensive utilization of resources is core
The circular-type economy development model of the heart has increasingly become the main trend of development of world economy.Devoting Major Efforts To Developing resource circulation utilization skill
Art, will exert far reaching influence the national economic development and environment sustainable development.In recent years, waste plastic and reproducible is utilized
Wood fiber prepares wood plastic composite and gradually causes government and the attention of related researcher.
At present, people are mostly directly to burn in wood fibre renewable using stalk, so as to cause significantly
Secondary hazards, be mainly shown as：1st, serious atmosphere pollution is caused, is detrimental to health.During crop straw burning, dioxy in air
The concentration for changing sulphur is 2 times usually, and nitrogen dioxide, the concentration of pellet are 4 times usually.When pellet is dense
Degree is when reaching a certain level, and the part for containing mucous membrane to the eyes, nose and throat of people stimulates larger, gently then causes cough, chest
It is vexed, shed tears, bronchitis may be caused when serious.2nd, fire is triggered.Easily ignite during crop straw burning the inflammable of surrounding
Thing, causes " baked wheaten cake is operated " may both endanger other people life securities, it is also possible to cause serious economic loss.3rd, road is influenced to hand over
Logical and aviation safety.The smog that crop straw burning is formed, causes air On The Deterioration of Visibility Over, directly affects civil aviaton, railway, highway
Normal operation, easily trigger traffic accident.Other Land use systems in relation to stalk, such as straw power generation, using biogas gas,
Straw feed, stalk base wood plastic composite materials etc., there is respective insoluble defect, and the utilization rate of stalk on the whole
It is relatively low, added value is not notable.Therefore, other high added values are explored, stalk user's rule of high usage is imperative.And
Its main raw material(s) of plastic stalk door-window section bar PP Pipe Compound of the present invention is stalk and all kinds of wood fibres, is derived from a wealth of sources,
It is cheap, it is nontoxic natural macromolecular, it is poisonous to add lead salt stabilizer etc. in the process for preparing door-window section bar
Harmful substance, will not damage environment and production, user of service.With respect to other materials, such as aluminium section bar, stalk material
Thermal conductivity is low, and specific heat capacity is big, can effectively reduce the loss of heat, show good heat-insulating property.In addition, plastic stalk door and window
Straw content is higher in section bar PP Pipe Compound, can be effectively increased the usage amount of stalk, thus to environmental protection, increase farmers' income,
Reduce CO2 emission, reduction environmental and safety problems because of caused by straw burning are respectively provided with significant effect.
At present, there is not yet can thermoplastic processing stalk material relevant report.Therefore, plastic stalk door-window section bar PP Pipe Compound
Exploitation with using for reduce energy consumption, advocate environment harmony, realize that the sustainable development of material has important practical significance.
The content of the invention
A kind of plastic stalk door-window section bar PP Pipe Compound proposed the purpose of the present invention is the deficiency for current material
Preparation method, its main feature is that after stalk is smashed, the surface grafting polymerization of stalk is realized by Reaction extrusion, is made modified
Straw powder has excellent thermoplasticity, is then uniformly mixed with high fluidity vinyl chloride copolymer, processing aid, filler etc., squeezes
Go out granulation and obtain plastic stalk door-window section bar PP Pipe Compound.
The present invention relates to a kind of preparation method of plastic stalk door-window section bar PP Pipe Compound, comprise the following steps：
（1）Recycling all kinds of stalks and crush, the straw powder size after smashing is 40~200 mesh, and in strong base solution at activation
When reason 10~20 is small, then filter, with deionized water rinsing powder, until the pH value of filtrate collects activated processing close to 7
Straw powder material, is dried, and its water content is less than 0.1%；
（2）By the straw powder after activation process, functional monomer, initiator and dispersant in mass ratio 100:10~20:0.5~
2:1~10 is uniformly mixed in homogenizer, is then reacted in double screw extruder under the conditions of 100~140 DEG C
Property extrusion, up to the stalk dry mash of graft modification；
（3）By above-mentioned stalk dry mash, high fluidity vinyl chloride copolymer, processing aid and filler in mass ratio 100:10~
30:1~10:0~20 in homogenizer be uniformly mixed, by gained batch mixing in dual-screw pelletizer in 140~180 DEG C into
Row extruding pelletization, up to plastic stalk door-window section bar PP Pipe Compound.
The step（1）In, the stalk is Wheat Straw, rice straw, maize straw, cotton stalk, bagasse, bamboo
At least one of powder, wood powder, cavings, coconut husk, soybean skin, peanut shell.
The step（1）In, the strong base solution is potassium hydroxide (KOH), sodium hydroxide (NaOH), lithium hydroxide
(LiOH) one kind in aqueous solution, its mass percent are more than or equal to 10wt.%.
The step（2）In, the functional monomer is methacrylic acid, acrylic acid, maleic anhydride, acetic anhydride, propionic acid
In acid anhydride, succinic anhydride, benzoyl oxide, methyl acrylate, ethyl acrylate, n-butyl acrylate, isobutyl acrylate at least
It is a kind of.
The step（2）In, the initiator for diphenyl peroxide first is pungent, peroxysuccinic acid, peroxide of glutaric acid,
Di-tert-butyl peroxide, peroxidized t-butyl perbenzoate, tert-butyl hydroperoxide pivalate, benzoyl peroxide, peroxidating
One kind in lauroyl.
The step（2）In, the dispersant is polyvinyl alcohol, hydroxymethyl cellulose, hydroxypropyl cellulose, carboxylated fiber
At least one of element, carboxycellulose sodium, gelatin, sodium alginate, polyvinylpyrrolidone.
The step（3）In, the high fluidity vinyl chloride copolymer is the ethylene vinyl chloride that the degree of polymerization is 200~1000
Copolymer, propylene vinyl chloride copolymer, acrylic acid vinyl chloride copolymer, vinyl acetate-chloroethylene copolymer thing, styrene vinyl chloride
At least one of copolymer, acrylate vinyl chloride copolymer, acrylonitrile vinyl chloride copolymer.
The step（3）In, the processing aid is repefral, dibutyl phthalate, adjacent benzene two
Formic acid dioctyl ester, citrate, Tissuemat E, oxidized polyethylene wax, hydroxyl Tissuemat E, calcium zinc stabilizer, light stabilizer, chlorine
Change at least one of polyethylene, anti-impact type ACR, nitrile rubber, phosphate, phosphite ester.
The step（3）In, the filler is titanium dioxide, calcium carbonate, silica, kaolin, talcum powder, mica
At least one of powder, diatomite, silicates mineral matter.
The present invention has the following advantages：
（1）Plastic stalk door-window section bar PP Pipe Compound prepared by the present invention has raw material（All kinds of stalks）Derive from a wealth of sources, price
Cheap, sustainable feature, can partly substitute existing plastic-steel, aluminum alloy doors and windows；
（2）Plastic stalk door-window section bar PP Pipe Compound prepared by the present invention has nontoxic, hygienic, degradable, environmentally protective spy
The main component of point, wherein stalk is the nontoxic natural macromolecular such as lignin, cellulose, hemicellulose, security and
Degradability is excellent；
（3）The processing performance of plastic stalk door-window section bar PP Pipe Compound is good, overcomes natural timber poor durability, Yi Chao, perishable, easy
The shortcomings of moth, door and window prepared therefrom have excellent anti-flammability and heat-insulating property, and light, service life length.
Brief description of the drawings
Influence of Fig. 1 initiator concentrations to modified straw powder grafting rate.
Influence of Fig. 2 corn straw modifications content to Mechanical Properties of Products.
Specific embodiment
The present invention is specifically described below by specific embodiment, it is necessary to which indicated herein is the present embodiment
For the invention will be further described, it is impossible to be interpreted as limiting the scope of the invention, the knack people in the field
Member can make the present invention according to the content of foregoing invention the modifications and adaptations of some unsubstantialities.
Embodiment 1
Maize straw is recycled, is crushed, the corn stalk pellets size after smashing is 40 mesh.Weigh the corn stalk of 40 mesh
2000 g of powder, puts into 20 L reaction kettles, the sodium hydrate aqueous solution 6L of 15wt.% is added into reaction kettle, when immersion 10 is small.
Then filter, and with deionized water rinsing powder, until the pH value of filtrate is approximately equal to 7, collect the straw powder after activated processing
Material, is dried, and its water content is less than 0.1%.
1000 g of drying corn stalk powder after activation, 100 g of methacrylic acid, mistake are sequentially added in homogenizer
5 g of Benzoyl Oxide, 10 g of polyvinyl alcohol, are uniformly mixed, and the material of mixing is carried out reactivity in double screw extruder squeezes
Go out, processing temperature is 100 DEG C, up to the maize straw dry mash of graft modification.
Above-mentioned 1000 g of maize straw dry mash is sequentially added in homogenizer, the ethene chlorine that the degree of polymerization is 200
100 g of ethylene copolymer, 10 g of processing aid（Wherein 7 g of repefral, 0.5 g of Tissuemat E, calcium zinc stabilizer
0.5 g, 1 g of nitrile rubber, 1 g of light stabilizer）, titanium dioxide 50g, be uniformly mixed, by gained batch mixing in double screw extruder
Middle carry out extruding pelletization, processing temperature are 140 DEG C, and gained pellet is plastic maize straw door-window section bar PP Pipe Compound.
Embodiment 2
Poplar material is recycled, is crushed, the Poplar Powder size after smashing is 100 mesh.2000 g of Poplar Powder of 100 mesh is weighed,
Put into 20 L reaction kettles, the sodium hydrate aqueous solution 6L of 10wt.% is added into reaction kettle, when immersion 15 is small.Then filter,
And with deionized water rinsing powder, until the pH value of filtrate is approximately equal to 7, the straw powder material after activated processing is collected, is done
It is dry, its water content is less than 0.1%.
1000 g of drying Poplar Powder, 150 g of maleic anhydride, benzoyl peroxide after activation are sequentially added in homogenizer
12 g of t-butyl formate, 60 g of hydroxymethyl cellulose, are uniformly mixed, the material of mixing are reacted in double screw extruder
Property extrusion, processing temperature be 120 DEG C, up to the poplar dry mash of graft modification.
Above-mentioned 1000 g of poplar dry mash is sequentially added in homogenizer, the propylene vinyl chloride that the degree of polymerization is 600
200 g of copolymer, 60 g of processing aid（Wherein 42 g of dibutyl phthalate, 3 g of oxidized polyethylene wax, calcium zinc stabilizer 3
G, 6 g of anti-impact ACR, 6 g of light stabilizer）, silica 1 20g, be uniformly mixed, by gained batch mixing in double screw extruder into
Row extruding pelletization, processing temperature are 160 DEG C, and gained pellet is plastic Poplar Powder door-window section bar PP Pipe Compound.
Embodiment 3
Cotton stalk is recycled, is crushed, the cotton stalk particle size after smashing is 200 mesh.Weigh the cotton straw of 200 mesh
2000 g of bar powder, puts into 20 L reaction kettles, and the potassium hydroxide aqueous solution 6L of 20wt.% is added into reaction kettle, and immersion 20 is small
When.Then filter, and with deionized water rinsing powder, until the pH value of filtrate is approximately equal to 7, collect the stalk after activated processing
Powder, is dried, and its water content is less than 0.1%.
1000 g of dried cotton straw powder, 200 g of benzoyl oxide, peroxide after activation are sequentially added in homogenizer
Change 20 g of lauroyl, 100 g of carboxycellulose sodium, be uniformly mixed, the material of mixing is reacted in double screw extruder
Property extrusion, processing temperature be 140 DEG C, up to the cotton stalk dry mash of graft modification.
Above-mentioned 1000 g of cotton stalk dry mash is sequentially added in homogenizer, the styrene that the degree of polymerization is 1000
300 g of vinyl chloride copolymer, 100 g of processing aid（Wherein 70 g of citrate, 5 g of hydroxyl Tissuemat E, calcium zinc stabilizer 5
G, 10 g of nitrile rubber, 10 g of phosphite ester）, calcium carbonate 200g, be uniformly mixed, by gained batch mixing in double screw extruder into
Row extruding pelletization, processing temperature are 180 DEG C, and gained pellet is plastic cotton stalk door-window section bar PP Pipe Compound.
Claims (10)
- A kind of 1. preparation method of plastic stalk door-window section bar PP Pipe Compound, its main feature is that the preparation of the stalk door-window section bar PP Pipe Compound Comprise the following steps：（1）Recycling all kinds of stalks and crush, the straw powder size after smashing is 40~200 mesh, and in strong base solution at activation When reason 10~20 is small, then filter, with deionized water rinsing powder, until the pH value of filtrate collects activated processing close to 7 Straw powder material, is dried, and its water content is less than 0.1%；（2）By the straw powder after activation process, functional monomer, initiator and dispersant in mass ratio 100:10~20:0.5~ 2:1~10 is uniformly mixed in homogenizer, is then reacted in double screw extruder under the conditions of 100~140 DEG C Property extrusion, up to the stalk dry mash of graft modification；（3）By above-mentioned stalk dry mash, high fluidity vinyl chloride copolymer, processing aid and filler in mass ratio 100:10~ 30:1~10:0~20 in homogenizer be uniformly mixed, by gained batch mixing in dual-screw pelletizer in 140~180 DEG C into Row extruding pelletization, up to plastic stalk door-window section bar PP Pipe Compound.
- 2. a kind of preparation method of plastic stalk door-window section bar PP Pipe Compound as described in claim 1, it is characterised in that stalk is wheat In stalk, rice straw, maize straw, cotton stalk, bagasse, bamboo powder, wood powder, cavings, coconut husk, soybean skin, peanut shell It is at least one.
- 3. a kind of preparation method of plastic stalk special material for tube as described in claim 1, it is characterised in that strong base solution is hydrogen One kind in potassium oxide (KOH), sodium hydroxide (NaOH), lithium hydroxide (LiOH) aqueous solution, its mass percent are more than or equal to 10wt.%。
- A kind of 4. preparation method of plastic stalk door-window section bar PP Pipe Compound as described in claim 1, it is characterised in that feature list Body is methacrylic acid, acrylic acid, maleic anhydride, acetic anhydride, propionic andydride, succinic anhydride, benzoyl oxide, methyl acrylate, third At least one of olefin(e) acid ethyl ester, n-butyl acrylate, isobutyl acrylate.
- 5. a kind of preparation method of plastic stalk door-window section bar PP Pipe Compound as described in claim 1, it is characterised in that initiator is Diphenyl peroxide first is pungent, peroxysuccinic acid, peroxide of glutaric acid, di-tert-butyl peroxide, the tertiary fourth of perbenzoic acid One kind in ester, tert-butyl hydroperoxide pivalate, benzoyl peroxide, lauroyl peroxide.
- 6. a kind of preparation method of plastic stalk door-window section bar PP Pipe Compound as described in claim 1, it is characterised in that dispersant is Polyvinyl alcohol, hydroxymethyl cellulose, hydroxypropyl cellulose, carboxycellulose, carboxycellulose sodium, gelatin, sodium alginate, poly- second At least one of vinyl pyrrolidone.
- A kind of 7. preparation method of plastic stalk door-window section bar PP Pipe Compound as described in claim 1, it is characterised in that high fluidity Vinyl chloride copolymer be the degree of polymerization be 200~1000 ethylene vinylchloride copolymer, propylene vinyl chloride copolymer, acrylic acid chloroethene Alkene copolymer, vinyl acetate-chloroethylene copolymer thing, styrene vinyl chloride copolymer, acrylate vinyl chloride copolymer, acrylonitrile At least one of vinyl chloride copolymer.
- A kind of 8. preparation method of plastic stalk door-window section bar PP Pipe Compound as described in claim 1, it is characterised in that processing aid It is poly- for repefral, dibutyl phthalate, dioctyl phthalate, citrate, Tissuemat E, oxidation Ethylene waxes, hydroxyl Tissuemat E, calcium zinc stabilizer, light stabilizer, haloflex, anti-impact type ACR, nitrile rubber, phosphate, At least one of phosphite ester.
- A kind of 9. preparation method of plastic stalk door-window section bar PP Pipe Compound as described in claim 1, it is characterised in that filler two At least one in titanium oxide, calcium carbonate, silica, kaolin, talcum powder, mica powder, diatomite, silicates mineral matter Kind.
- 10. the plastic door-window section bar PP Pipe Compound of stalk is made as described in claim 1.