CN108017401A - A kind of energy-saving and environment-friendly fire-retardant antidetonation coating material - Google Patents
A kind of energy-saving and environment-friendly fire-retardant antidetonation coating material Download PDFInfo
- Publication number
- CN108017401A CN108017401A CN201711424781.7A CN201711424781A CN108017401A CN 108017401 A CN108017401 A CN 108017401A CN 201711424781 A CN201711424781 A CN 201711424781A CN 108017401 A CN108017401 A CN 108017401A
- Authority
- CN
- China
- Prior art keywords
- parts
- energy
- saving
- environment
- coating material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
It is disclosed by the invention to belong to coating material technical field; specially a kind of energy-saving and environment-friendly fire-retardant antidetonation coating material; the energy-saving and environment-friendly fire-retardant antidetonation coating material includes interior basic unit and external protection; the raw material of the interior basic unit include clay, quartz sand, dolomite, resin, thickener, foaming agent and water, and the clay, quartz sand, dolomite, resin, thickener, foaming agent, water are respectively according to quality proportion:70 75 parts of clay, 10 15 parts of quartz sand, 8 10 parts of dolomite, 57 parts of resin, 23 parts of thickener, 23 parts of foaming agent; remaining is water; the external protection is attached on the right side wall of interior basic unit; the external protection is asbestos stratum reticulare; the energy-saving and environment-friendly fire-retardant antidetonation coating material; the main material of use is natural material; energy conservation and environmental protection is preferable; greening degree is higher; by preferably aiding in added material to adding toughness in material; so that the toughness of material of coating is preferable, plasticity is higher, and anti seismic efficiency is preferable.
Description
Technical field
The present invention relates to coating material technical field, is specially a kind of energy-saving and environment-friendly fire-retardant antidetonation coating material.
Background technology
Kiln body, kiln car structural system, including shuttle kiln, tunnel oven, volume road kiln kiln ceiling structure system, kiln wall system,
It is hollow to enclose brick kiln car system etc..Refractory material used in the system conventional is mainly refractory brick, refractory brick include heavy brick and
Light-weight brick.Kiln is in stove operation process is burnt, and in addition to the thermal energy needed for green part to be supplied, also to supply kiln body, kiln car knot
Thermal energy needed for construction system.Since refractory brick is solid construction, and than great, substantial amounts of thermal energy is absorbed, energy loss is big.Separately
Outside, kiln in stove operation is burnt, it is necessary to be largely used to place or/and isolate the refractory kiln of green part.Since kiln furnitures are rapid wears
Part, will produce substantial amounts of kiln furnitures waste material.For existing kiln furnitures waste material without utility value, be only used as hollow ground fills out underbed, for this reason, I
Propose a kind of energy-saving and environment-friendly fire-retardant antidetonation coating material.
The content of the invention
It is an object of the invention to provide a kind of energy-saving and environment-friendly fire-retardant antidetonation coating material, to solve above-mentioned background technology
The existing kiln furnitures waste material of middle proposition is only used as the problem of filling out underbed of hollow ground without utility value.
To achieve the above object, the present invention provides following technical solution:A kind of energy-saving and environment-friendly fire-retardant antidetonation coating material,
The energy-saving and environment-friendly fire-retardant antidetonation coating material includes interior basic unit and external protection, the raw material of the interior basic unit include clay,
Quartz sand, dolomite, resin, thickener, foaming agent and water, the clay, quartz sand, dolomite, resin, thickener, foaming
Agent, water are respectively according to quality proportion:70-75 parts of clay, 10-15 parts of quartz sand, 8-10 parts of dolomite, 5-7 parts of resin, thickening
2-3 parts of agent, 2-3 parts of foaming agent, remaining is water, and the external protection is attached on the right side wall of interior basic unit, the external protection
For asbestos stratum reticulare.
Preferably, the raw material of the interior basic unit further include dispersant.
Preferably, the dispersant is triethyl group hexyl phosphoric acid dispersant, and triethyl group hexyl phosphoric acid dispersant is according to matter
Measure 2-2.5 parts of the raw material of interior basic unit shared by accounting.
Preferably, the particle outside diameter of the dolomite is the dolomite particles less than 1.2cm-2.2cm.
Preferably, be bonded by bonding agent between the external protection and interior basic unit, the bonding agent is hot-setting adhesive.
Preferably, the external protection includes two groups of asbestos gauges and micarex filled layer, and asbestos gauge described in two groups is coated on
The both sides of micarex filled layer.
Compared with prior art, the beneficial effects of the invention are as follows:The energy-saving and environment-friendly fire-retardant antidetonation coating material, use
Main material is natural material, and energy conservation and environmental protection is preferable, and greening degree is higher, by preferably aiding in adding toughness in material
Added material so that the toughness of material of coating is preferable, and plasticity is higher, and anti seismic efficiency is preferable.
Brief description of the drawings
Fig. 1 is schematic structural view of the invention;
Fig. 2 is the compares figure of three groups of embodiments of the invention.
In figure:Basic unit, 2 external protections in 1.
Embodiment
Below in conjunction with the attached drawing in the embodiment of the present invention, the technical solution in the embodiment of the present invention is carried out clear, complete
Site preparation describes, it is clear that described embodiment is only part of the embodiment of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, those of ordinary skill in the art are obtained every other without making creative work
Embodiment, belongs to the scope of protection of the invention.
Referring to Fig. 1, the present invention provides a kind of technical solution:A kind of energy-saving and environment-friendly fire-retardant antidetonation coating material, the section
Fire-retardant antidetonation coating material that can be environmentally friendly includes interior basic unit 1 and external protection 2, and the raw material of interior basic unit 1 include clay, quartz
Sand, dolomite, resin, thickener, foaming agent and water, clay, quartz sand, dolomite, resin, thickener, foaming agent, water according to
Quality proportion is respectively:70-75 parts of clay, 10-15 parts of quartz sand, 8-10 parts of dolomite, 5-7 parts of resin, 2-3 parts of thickener,
2-3 parts of foaming agent, remaining is water, and external protection 2 is attached on the right side wall of interior basic unit 1, and external protection 2 is asbestos stratum reticulare.
Wherein, the raw material of interior basic unit 1 further include dispersant, and dispersant is triethyl group hexyl phosphoric acid dispersant, and three second
For base hexyl phosphoric acid dispersant according to 2-2.5 parts of the raw material of interior basic unit 1 shared by quality accounting, the particle outside diameter of dolomite is small
Be bonded by bonding agent between the dolomite particles of 1.2cm-2.2cm, external protection 2 and interior basic unit 1, bonding agent is thermosetting
Glue, external protection 2 include two groups of asbestos gauges and micarex filled layer, and two groups of asbestos gauges are coated on the both sides of micarex filled layer.
Hereinafter the different-effect (being illustrated in figure 2 statistical chart) that brings of control different proportion is carried out with three groups of embodiments:
Embodiment one
A kind of energy-saving and environment-friendly fire-retardant antidetonation coating material, the energy-saving and environment-friendly fire-retardant antidetonation coating material include interior basic unit
1 and external protection 2, the raw material of interior basic unit 1 include clay, quartz sand, dolomite, resin, thickener, foaming agent and water, stick
Soil, quartz sand, dolomite, resin, thickener, foaming agent, water are respectively according to quality proportion:70 parts of clay, 10 parts of quartz sand,
8 parts of dolomite, 7 parts of resin, 3 parts of thickener, 3 parts of foaming agent, remaining is water, and external protection 2 is attached to the right side wall of interior basic unit 1
On, external protection 2 is asbestos stratum reticulare.
Embodiment two
A kind of energy-saving and environment-friendly fire-retardant antidetonation coating material, the energy-saving and environment-friendly fire-retardant antidetonation coating material include interior basic unit
1 and external protection 2, the raw material of interior basic unit 1 include clay, quartz sand, dolomite, resin, thickener, foaming agent and water, stick
Soil, quartz sand, dolomite, resin, thickener, foaming agent, water are respectively according to quality proportion:72.5 parts of clay, quartz sand
12.5 parts, 9 parts of dolomite, 6 parts of resin, 2.5 parts of thickener, 2.5 parts of foaming agent, remaining is water, and external protection 2 is attached to interior base
On the right side wall of layer 1, external protection 2 is asbestos stratum reticulare.
Embodiment three
A kind of energy-saving and environment-friendly fire-retardant antidetonation coating material, the energy-saving and environment-friendly fire-retardant antidetonation coating material include interior basic unit
1 and external protection 2, the raw material of interior basic unit 1 include clay, quartz sand, dolomite, resin, thickener, foaming agent and water, stick
Soil, quartz sand, dolomite, resin, thickener, foaming agent, water are respectively according to quality proportion:75 parts of clay, 15 parts of quartz sand,
10 parts of dolomite, 5 parts of resin, 2 parts of thickener, 2 parts of foaming agent, remaining is water, and external protection 2 is attached to the right side of interior basic unit 1
On wall, external protection 2 is asbestos stratum reticulare.
It is according to the product performance that three groups of embodiments are drawn above:Embodiment one:Finished product is excessively flexible, and intensity is relatively low,
It is easily deformed;Embodiment two:Product intensity and toughness are moderate;Embodiment three:Product intensity is larger, and when use easily occurs crisp
Split.
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
Understanding without departing from the principles and spirit of the present invention can carry out these embodiments a variety of changes, modification, replace
And modification, the scope of the present invention is defined by the appended.
Claims (6)
- A kind of 1. energy-saving and environment-friendly fire-retardant antidetonation coating material, it is characterised in that:The energy-saving and environment-friendly fire-retardant antidetonation coating material Including interior basic unit (1) and external protection (2), the raw material of the interior basic unit (1) include clay, quartz sand, dolomite, resin, Thickener, foaming agent and water, the clay, quartz sand, dolomite, resin, thickener, foaming agent, water are according to quality proportion point It is not:70-75 parts of clay, 10-15 parts of quartz sand, 8-10 parts of dolomite, 5-7 parts of resin, 2-3 parts of thickener, foaming agent 2-3 Part, remaining is water, and the external protection (2) is attached on the right side wall of interior basic unit (1), and the external protection (2) is asbestos gauge Layer.
- 2. the energy-saving and environment-friendly fire-retardant antidetonation coating material of one kind according to claim 1, it is characterised in that:The interior basic unit (1) raw material further include dispersant.
- 3. the energy-saving and environment-friendly fire-retardant antidetonation coating material of one kind according to claim 2, it is characterised in that:The dispersant For triethyl group hexyl phosphoric acid dispersant, and triethyl group hexyl phosphoric acid dispersant is according to the former material of interior basic unit (1) shared by quality accounting 2-2.5 parts of material.
- 4. the energy-saving and environment-friendly fire-retardant antidetonation coating material of one kind according to claim 1, it is characterised in that:The dolomite Particle outside diameter be dolomite particles less than 1.2cm-2.2cm.
- 5. the energy-saving and environment-friendly fire-retardant antidetonation coating material of one kind according to claim 1, it is characterised in that:The outer protection Be bonded by bonding agent between layer (2) and interior basic unit (1), the bonding agent is hot-setting adhesive.
- 6. the energy-saving and environment-friendly fire-retardant antidetonation coating material of one kind according to claim 1, it is characterised in that:The outer protection Layer (2) includes two groups of asbestos gauges and micarex filled layer, and asbestos gauge described in two groups is coated on the both sides of micarex filled layer.