CN108003448A - A kind of degradation plastic packaging bag and preparation method thereof - Google Patents
A kind of degradation plastic packaging bag and preparation method thereof Download PDFInfo
- Publication number
- CN108003448A CN108003448A CN201711416632.6A CN201711416632A CN108003448A CN 108003448 A CN108003448 A CN 108003448A CN 201711416632 A CN201711416632 A CN 201711416632A CN 108003448 A CN108003448 A CN 108003448A
- Authority
- CN
- China
- Prior art keywords
- parts
- added
- degradation
- packaging bag
- plastic packaging
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of degradation plastic packaging bag, it is made of following raw material:20 30 parts of linear low density polyethylene resin, 10 20 parts of 3 hydroxybutyric acid, 3 hydroxyl pentanoate copolymer, 10 20 parts of polyvinyl alcohol, 10 15 parts of starch, 58 parts of polycaprolactone, 58 parts of cotton fibriia, 58 parts of chitosan, 20 40 parts of diatomite, 2 10 parts of Paris white, 15 parts of tributyl 2-acetylcitrate, 13 parts of polybutadiene rubber, 36 parts of degradation of promoter;The invention also discloses the preparation method of the plastic packaging bag, including prepare blend composition, melting extrusion granulation, hot-melt extruded Blown Film, bag making, cutting, heat-sealing, printing and etc..The raw material that the present invention uses is environment-protecting and non-poisonous harmless, and has good degradation effect, can reduce the influence to surrounding environment;The preparation method of the present invention is simple and convenient, with good economic efficiency to the of less demanding of mechanical equipment, low manufacture cost.
Description
Technical field
The invention belongs to plastic packaging bag preparing technical field, and in particular, to a kind of degradation plastic packaging bag and its
Preparation method.
Background technology
Plastic shopping bag is the necessity in daily life, it is well known that present consumer and market have all been formed to modeling
Expect the hard requirement of packaging bag consumption, and this consumption has become a kind of custom, and plastic packaging bag has incorporated everybody life
In work.
Plastic packaging bag is the high-molecular compound that is formed by addition polymerization or polycondensation polymerized using monomer as raw material, it
Generally it is made by the additive such as synthetic resin and filler, plasticizer, stabilizer, lubricant, colorant.In the daily life of people
In work, the application of plastic packaging bag is very extensive, but " white pollution " that waste plastic is brought is also increasingly severe.With people
Environmental consciousness enhancing, how to alleviate the topic that white pollution has been people's growing interest.Degradative plastics packaging bag is near
Emerging a kind of plastic products over year, its properties can meet requirement and with storage life performance it is constant
Characteristic, and the material of environmental sound can be degraded under natural environmental condition after.
At present, although occurring various degradative plastics packaging bags on the market, experiment shows:Most of degradeds
Plastic packaging bag starts thinning, weightless, intensity and declines after generally exposing 3 months in the environment, gradual splinter, if these
Fragment is embedded in rubbish or soil, then degradation effect unobvious.In addition, some adding ingredients in degradative plastics can change modeling
The increase of some characteristics of material, such as breathable moisture permeability, tensile strength are deteriorated, and are unfavorable for the popularization of degradative plastics packaging bag with answering
With.
The content of the invention
For the deficiencies in the prior art in above-mentioned background technology, the present invention provides a kind of degradation plastic packaging bag and its
Preparation method.
The purpose of the present invention can be achieved through the following technical solutions:
A kind of degradation plastic packaging bag, is made of following raw material:Linear low density polyethylene resin 20-30
Part, 10-20 parts of 3-hydroxybutyrate -3- hydroxyl pentanoate copolymers, 10-20 parts of polyvinyl alcohol, 10-15 parts of starch, polycaprolactone 5-8
Part, 5-8 parts of cotton fibriia, 5-8 parts of chitosan, 20-40 parts of diatomite, 2-10 parts of Paris white, tributyl 2-acetylcitrate 1-5
Part, 1-3 parts of polybutadiene rubber, 3-6 parts of degradation of promoter;
The degradation plastic packaging bag is prepared by following steps:
(1) high mixer heating-up temperature is adjusted to 115-125 DEG C, rotating speed 450r/min, starch, cotton fibriia, shell are gathered
Sugar, diatomite, Paris white are added in high mixer, operate 10-15min;
(2) high mixer heating-up temperature is risen to 135-140 DEG C, rotating speed is adjusted to 500r/min, adds linear low density polyethylene
Olefine resin, 3-hydroxybutyrate -3- hydroxyl pentanoate copolymers, polyvinyl alcohol, polycaprolactone, are mixed 20-30min, then second
Acyl tributyl citrate, polybutadiene rubber, degradation of promoter are added thereto, and stir 15-20min, are closed high mixer, are cooled to
40-60 DEG C, obtain blend composition;
(3) blend composition is added into double screw extruder, is 160-170 DEG C, screw speed 300-500r/min bars in temperature
Melting extrusion is granulated under part, and master batch is made;
(4) master batch is added in Single screw extrusion inflation film manufacturing machine, blown film temperature is 145-170 DEG C, carries out hot-melt extruded blowing
Film forming, cooling, flanging, obtains material membrane;
(5) material membrane is added into Bag Making Machine, bag making, cutting, heat-sealing, printing, obtain degradation plastic packaging bag.
The starch is cornstarch, the one or more in soybean starch, starch from sweet potato, farina.
The degradation of promoter is by N- lauroyl glutamates, zinc dibenzyl dithiocarbamate, stearyl ethoxy
Imidazoline is 1 according to mass ratio:0.6-1:0.9-1.5 is mixed.
A kind of preparation method of degradation plastic packaging bag, includes the following steps:
(1) high mixer heating-up temperature is adjusted to 115-125 DEG C, rotating speed 450r/min, starch, cotton fibriia, shell are gathered
Sugar, diatomite, Paris white are added in high mixer, operate 10-15min;
(2) high mixer heating-up temperature is risen to 135-140 DEG C, rotating speed is adjusted to 500r/min, adds linear low density polyethylene
Olefine resin, 3-hydroxybutyrate -3- hydroxyl pentanoate copolymers, polyvinyl alcohol, polycaprolactone, are mixed 20-30min, then second
Acyl tributyl citrate, polybutadiene rubber, degradation of promoter are added thereto, and stir 15-20min, are closed high mixer, are cooled to
40-60 DEG C, obtain blend composition;
(3) blend composition is added into double screw extruder, is 160-170 DEG C, screw speed 300-500r/min bars in temperature
Melting extrusion is granulated under part, and master batch is made;
(4) master batch is added in Single screw extrusion inflation film manufacturing machine, blown film temperature is 145-170 DEG C, carries out hot-melt extruded blowing
Film forming, cooling, flanging, obtains material membrane;
(5) material membrane is added into Bag Making Machine, bag making, cutting, heat-sealing, printing, obtain degradation plastic packaging bag.
Beneficial effects of the present invention:
The present invention using linear low density polyethylene, 3-hydroxybutyrate -3- hydroxyl pentanoate copolymers, polyvinyl alcohol, gather oneself
Lactone is raw material, and 5 with the starch of scientific matching, chitosan, diatomite, Paris white, and raw material is environment-protecting and non-poisonous harmless, and has
There is good degradation effect, the influence to surrounding environment can be reduced;Meanwhile the present invention with the addition of suitable acetyl in the feed
Tributyl citrate, polybutadiene rubber, can ensure plastic packaging bag enough intensity and toughness;In the raw material of the present invention also
Comprising degradation of promoter, its add can reinforced polymeric article acceleration is presented in the presence of light and/or heat and/or moisture
Degradability;The preparation method of the present invention is simple and convenient, to the of less demanding of mechanical equipment, low manufacture cost, has good warp
Ji benefit.
Embodiment
Technical scheme is clearly and completely described below in conjunction with embodiment, it is clear that described reality
It is only part of the embodiment of the present invention to apply example, instead of all the embodiments.Based on the embodiments of the present invention, this area is general
All other embodiment that logical technical staff is obtained without creative efforts, belongs to what the present invention protected
Scope.
A kind of degradation plastic packaging bag, is made of following raw material:Linear low density polyethylene resin 20-30
Part, 10-20 parts of 3-hydroxybutyrate -3- hydroxyl pentanoate copolymers, 10-20 parts of polyvinyl alcohol, 10-15 parts of starch, polycaprolactone 5-8
Part, 5-8 parts of cotton fibriia, 5-8 parts of chitosan, 20-40 parts of diatomite, 2-10 parts of Paris white, tributyl 2-acetylcitrate 1-5
Part, 1-3 parts of polybutadiene rubber, 3-6 parts of degradation of promoter;
Starch is cornstarch, the one or more in soybean starch, starch from sweet potato, farina;Starch is a kind of
Renewable, degradable environment friendly material, raw material sources are extensive;
Degradation of promoter is by N- lauroyl glutamates, zinc dibenzyl dithiocarbamate, stearyl hydroxyethyl imidazole
Quinoline is 1 according to mass ratio:0.6-1:0.9-1.5 is mixed;The degradation of promoter can make polymer product in light and/or heat
And/or the degradability of acceleration is presented in the presence of moisture;
A kind of preparation method of degradation plastic packaging bag, includes the following steps:
(1) high mixer heating-up temperature is adjusted to 115-125 DEG C, rotating speed 450r/min, starch, cotton fibriia, shell are gathered
Sugar, diatomite, Paris white are added in high mixer, operate 10-15min;
(2) high mixer heating-up temperature is risen to 135-140 DEG C, rotating speed is adjusted to 500r/min, adds linear low density polyethylene
Olefine resin, 3-hydroxybutyrate -3- hydroxyl pentanoate copolymers, polyvinyl alcohol, polycaprolactone, are mixed 20-30min, then second
Acyl tributyl citrate, polybutadiene rubber, degradation of promoter are added thereto, and stir 15-20min, are closed high mixer, are cooled to
40-60 DEG C, obtain blend composition;
(3) blend composition is added into double screw extruder, is 160-170 DEG C, screw speed 300-500r/min bars in temperature
Melting extrusion is granulated under part, and master batch is made;
(4) master batch is added in Single screw extrusion inflation film manufacturing machine, blown film temperature is 145-170 DEG C, carries out hot-melt extruded blowing
Film forming, cooling, flanging, obtains material membrane;
(5) material membrane is added into Bag Making Machine, bag making, cutting, heat-sealing, printing, obtain degradation plastic packaging bag.
Embodiment 1
A kind of degradation plastic packaging bag, its preparation method are as follows:
(1) high mixer heating-up temperature is adjusted to 115 DEG C, rotating speed 450r/min, by 10 parts of cornstarch, cotton fibriia 5
Part, 5 parts of chitosan, 20 parts of diatomite, 2 parts of Paris white are added in high mixer, operate 10min;
(2) high mixer heating-up temperature is risen to 135 DEG C, rotating speed is adjusted to 500r/min, adds linear low density polyethylene tree
20 parts of fat, 10 parts of 3-hydroxybutyrate -3- hydroxyl pentanoate copolymers, 10 parts of polyvinyl alcohol, 5 parts of polycaprolactone, are mixed
20min, then 1 part of tributyl 2-acetylcitrate, 1 part of polybutadiene rubber, 3 parts of degradation of promoter are added thereto, stir
15min, closes high mixer, is cooled to 40 DEG C, obtains blend composition;
(3) blend composition is added into double screw extruder, is 160 DEG C, is melted under the conditions of screw speed 300r/min in temperature
Extruding pelletization, is made master batch;
(4) master batch being added in Single screw extrusion inflation film manufacturing machine, blown film temperature is 145 DEG C, carries out hot-melt extruded Blown Film,
Cooling, flanging, obtain material membrane;
(5) material membrane is added into Bag Making Machine, bag making, cutting, heat-sealing, printing, obtain degradation plastic packaging bag.
Embodiment 2
A kind of degradation plastic packaging bag, its preparation method are as follows:
(1) high mixer heating-up temperature is adjusted to 120 DEG C, rotating speed 450r/min, by 12 parts of soybean starch, cotton fibriia 7
Part, 6 parts of chitosan, 30 parts of diatomite, 6 parts of Paris white are added in high mixer, operate 12min;
(2) high mixer heating-up temperature is risen to 138 DEG C, rotating speed is adjusted to 500r/min, adds linear low density polyethylene tree
25 parts of fat, 15 parts of 3-hydroxybutyrate -3- hydroxyl pentanoate copolymers, 15 parts of polyvinyl alcohol, 6 parts of polycaprolactone, are mixed
25min, then 3 parts of tributyl 2-acetylcitrate, 2 parts of polybutadiene rubber, 5 parts of degradation of promoter are added thereto, stir
18min, closes high mixer, is cooled to 50 DEG C, obtains blend composition;
(3) blend composition is added into double screw extruder, is 165 DEG C, is melted under the conditions of screw speed 400r/min in temperature
Extruding pelletization, is made master batch;
(4) master batch being added in Single screw extrusion inflation film manufacturing machine, blown film temperature is 155 DEG C, carries out hot-melt extruded Blown Film,
Cooling, flanging, obtain material membrane;
(5) material membrane is added into Bag Making Machine, bag making, cutting, heat-sealing, printing, obtain degradation plastic packaging bag.
Embodiment 3
A kind of degradation plastic packaging bag, its preparation method are as follows:
(1) high mixer heating-up temperature is adjusted to 125 DEG C, rotating speed 450r/min, by 15 parts of starch from sweet potato, cotton fibriia 8
Part, 8 parts of chitosan, 40 parts of diatomite, 10 parts of Paris white are added in high mixer, operate 15min;
(2) high mixer heating-up temperature is risen to 140 DEG C, rotating speed is adjusted to 500r/min, adds linear low density polyethylene tree
30 parts of fat, 20 parts of 3-hydroxybutyrate -3- hydroxyl pentanoate copolymers, 20 parts of polyvinyl alcohol, 8 parts of polycaprolactone, are mixed
30min, then 5 parts of tributyl 2-acetylcitrate, 3 parts of polybutadiene rubber, 6 parts of degradation of promoter are added thereto, stir
20min, closes high mixer, is cooled to 60 DEG C, obtains blend composition;
(3) blend composition is added into double screw extruder, is 170 DEG C, is melted under the conditions of screw speed 500r/min in temperature
Extruding pelletization, is made master batch;
(4) master batch being added in Single screw extrusion inflation film manufacturing machine, blown film temperature is 170 DEG C, carries out hot-melt extruded Blown Film,
Cooling, flanging, obtain material membrane;
(5) material membrane is added into Bag Making Machine, bag making, cutting, heat-sealing, printing, obtain degradation plastic packaging bag.
Present invention disclosed above preferred embodiment is only intended to help and illustrates the present invention.Preferred embodiment is not detailed
All details are described, are not limited the invention to the specific embodiments described.Obviously, according to the content of this specification,
It can make many modifications and variations.This specification is chosen and specifically describes these embodiments, is in order to preferably explain the present invention
Principle and practical application so that skilled artisan can be best understood by and utilize the present invention.The present invention is only
Limited by claims and its four corner and equivalent.
Claims (4)
1. a kind of degradation plastic packaging bag, it is characterised in that be made of following raw material:Linear low density polyethylene tree
20-30 parts of fat, 10-20 parts of 3-hydroxybutyrate -3- hydroxyl pentanoate copolymers, 10-20 parts of polyvinyl alcohol, 10-15 parts of starch, gather oneself
5-8 parts of lactone, 5-8 parts of cotton fibriia, 5-8 parts of chitosan, 20-40 parts of diatomite, 2-10 parts of Paris white, acetyl tributyl citrate three
1-5 parts of butyl ester, 1-3 parts of polybutadiene rubber, 3-6 parts of degradation of promoter;
The degradation plastic packaging bag is prepared by following steps:
(1) high mixer heating-up temperature is adjusted to 115-125 DEG C, rotating speed 450r/min, by starch, cotton fibriia, chitosan, silicon
Diatomaceous earth, Paris white are added in high mixer, operate 10-15min;
(2) high mixer heating-up temperature is risen to 135-140 DEG C, rotating speed is adjusted to 500r/min, adds linear low density polyethylene tree
Fat, 3-hydroxybutyrate -3- hydroxyl pentanoate copolymers, polyvinyl alcohol, polycaprolactone, are mixed 20-30min, then acetyl lemon
Lemon acid tributyl, polybutadiene rubber, degradation of promoter are added thereto, and stir 15-20min, are closed high mixer, are cooled to 40-
60 DEG C, obtain blend composition;
(3) blend composition is added into double screw extruder, is 160-170 DEG C, under the conditions of screw speed 300-500r/min in temperature
Melting extrusion is granulated, and master batch is made;
(4) master batch being added in Single screw extrusion inflation film manufacturing machine, blown film temperature is 145-170 DEG C, carries out hot-melt extruded Blown Film,
Cooling, flanging, obtain material membrane;
(5) material membrane is added into Bag Making Machine, bag making, cutting, heat-sealing, printing, obtain degradation plastic packaging bag.
A kind of 2. degradation plastic packaging bag according to claim 1, it is characterised in that the starch for cornstarch,
One or more in soybean starch, starch from sweet potato, farina.
3. a kind of degradation plastic packaging bag according to claim 1, it is characterised in that the degradation of promoter is by the N- months
Osmanthus acyl glutamic acid, zinc dibenzyl dithiocarbamate, imidazoline-based stearyl hydroxyethyl are 1 according to mass ratio:0.6-1:
0.9-1.5 is mixed.
4. the preparation method of a kind of degradation plastic packaging bag according to claim 1, it is characterised in that including following step
Suddenly:
(1) high mixer heating-up temperature is adjusted to 115-125 DEG C, rotating speed 450r/min, by starch, cotton fibriia, chitosan, silicon
Diatomaceous earth, Paris white are added in high mixer, operate 10-15min;
(2) high mixer heating-up temperature is risen to 135-140 DEG C, rotating speed is adjusted to 500r/min, adds linear low density polyethylene tree
Fat, 3-hydroxybutyrate -3- hydroxyl pentanoate copolymers, polyvinyl alcohol, polycaprolactone, are mixed 20-30min, then acetyl lemon
Lemon acid tributyl, polybutadiene rubber, degradation of promoter are added thereto, and stir 15-20min, are closed high mixer, are cooled to 40-
60 DEG C, obtain blend composition;
(3) blend composition is added into double screw extruder, is 160-170 DEG C, under the conditions of screw speed 300-500r/min in temperature
Melting extrusion is granulated, and master batch is made;
(4) master batch being added in Single screw extrusion inflation film manufacturing machine, blown film temperature is 145-170 DEG C, carries out hot-melt extruded Blown Film,
Cooling, flanging, obtain material membrane;
(5) material membrane is added into Bag Making Machine, bag making, cutting, heat-sealing, printing, obtain degradation plastic packaging bag.