CN108002556A - A kind of formula of the outer chilled water system scaling factor of elimination - Google Patents
A kind of formula of the outer chilled water system scaling factor of elimination Download PDFInfo
- Publication number
- CN108002556A CN108002556A CN201711334119.2A CN201711334119A CN108002556A CN 108002556 A CN108002556 A CN 108002556A CN 201711334119 A CN201711334119 A CN 201711334119A CN 108002556 A CN108002556 A CN 108002556A
- Authority
- CN
- China
- Prior art keywords
- formula
- chilled water
- water system
- scaling factor
- elimination
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of formula of chilled water system scaling factor outside elimination, which is suitable for the outer chilled water system of valve cooling system, is a kind of green, nontoxic, efficient compound prescription, there is good scale inhibition, inhibition, bactericidal property.The formula is made of di-bromonitrilopropiona,ide, imidazoline bi-quaternary ammonium salt class, poly-aspartate, the bipolymer of Epoxysuccinic acid maleic acid, sodium gluconate.Medicament in formula is green medicament, and environment is not polluted, and cheap, scale inhibitor bactericidal effect is good, can be effectively improved the corrosion and scaling problem of outer chilled water system.
Description
Technical field
The invention belongs to technical field of direct current power transmission, and in particular to a kind of formula of the outer chilled water system scaling factor of elimination.
Background technology
Since direct current transportation has the characteristics that power transmission distance is remote, power transmission capacity is big, control is flexible, direct current transportation is ensured
Safety and stability development be electric utility progress vital task.In DC transmission system, converter valve is DC transmission system
In one of most crucial equipment, and water cooling system is then the important component of current conversion station.Valve water-cooling system is by interior cooling system
System is formed with outer cooling system, and internal cooling system directly cools down converter valve, and outer chilled water system is then to inner cold water medium
Cooled down, be finally reached the purpose of cooling converter valve.
Outer chilled water system is mainly made of cooling tower, spray circuit and equalizing reservoir.Since outer cold water water quality is poor, and
In the circulation loop, water and air contact can bring the impurity in air and mushroom material in shower water into, when being mixed with impurity
Current return buffering pond after, buffer pond in impurity constantly accumulate, so as to cause outer cold water water quality not up to standard.When outer cold water
When water quality is not up to standard in system, the problems such as outer chilled water system corrosion and scaling and microbial growth can be caused, and influence heat exchange effect
Rate so that inner cold water is in overtemperature state, jeopardizes the stable operation of converter valve.In order to ensure the safe operation of converter valve, we
The water treatment agent with sterilization scale inhibitor effect must be added in cooling circuit.
At present, water treatment agent species used in circulation is various, but generally existing dosage is big, and price is high, effect
Rate is low, and not the features such as easily biological-degradable, and most medicament only has a certain effect in scale inhibition or inhibition or sterilization,
Function is single.Therefore, water treatment agent will be towards green, and efficiently, multiple-effect type direction is developed.
The content of the invention
The present invention provides a kind of formula of the outer chilled water system scaling factor of elimination, has at a low price, and efficiently, green is environmentally friendly
Feature, integrates inhibition, scale inhibition, sterilization.
Technical scheme:
The formula of the outer chilled water system scaling factor of a kind of elimination, it is characterised in that component is as follows, by mass percentage:10%~
20% di-bromonitrilopropiona,ide, 5% ~ 10% imidazoline bi-quaternary ammonium salt class, 15% ~ 20% poly-aspartate, 20% ~ 30%
The bipolymer of Epoxysuccinic acid-maleic acid, 15% ~ 25% sodium gluconate, remaining component are water.
In preferred embodiments of the present invention, imidazoline double seasons of the formula of the outer chilled water system scaling factor of the elimination
Its hydrophobic group carbon number of ammonium salt class is more than 16.
In preferred embodiments of the present invention, the average molecular matter of the bipolymer of the Epoxysuccinic acid-maleic acid
Amount is 600 ~ 1000.
During the formula of chilled water system scaling factor is raw materials used outside the elimination, di-bromonitrilopropiona,ide is with resistance
The fungicide of dirty corrosion inhibition.
During the formula of chilled water system scaling factor is raw materials used outside the elimination, poly-aspartate, Epoxysuccinic acid-horse
Carry out sour bipolymer and mainly play scale effect.
During the formula of chilled water system scaling factor is raw materials used outside the elimination, imidazoline bi-quaternary ammonium salt class, glucose
Sour sodium mainly plays corrosion inhibition.
During the formula of the outer chilled water system scaling factor of the elimination is raw materials used, imidazoline bi-quaternary ammonium salt class to copper, iron,
Aluminium is respectively provided with corrosion inhibition.
The formula of the outer chilled water system scaling factor of heretofore described elimination has the characteristics that:
Di-bromonitrilopropiona,ide in the present invention has the characteristics of sterilizing time is short, and sterilizing rate is high, and the duration is long.
Sodium gluconate in the present invention has excellent chelating ability, to Fe3+Chelating ability it is especially prominent, its energy
Metal surface is covered in formation complex protective films such as the calcium ion in solution, iron ions.
Formula of the present invention, its applicable pH scope are 8-9.
Formula of the present invention, its concentration in outer cold water are 30 ~ 90mg/L.
Formulation green environmental protection of the present invention, nontoxic, high performance cheap.
Embodiment
The present invention is intended to further illustrate with reference to embodiments, is not intended to limit the present invention.
In the embodiment of the present invention, comparative example, scale-inhibiting properties test uses《National Standard of the People's Republic of China GBT/
16632-2008, the measure of water treatment agent scale-inhibiting properties --- tosca method》.Corrosion inhibition tests reference《The Chinese people
Republic's national standard GB/T/18175-2000, the measure of water treatment agent corrosion inhibition --- rotary hanging plate method》.Test piece uses carbon
Steel test piece, specification are 50mm × 25mm × 2mm, temperature 45 C, take out and weigh after rotating speed 80r/min, rotation test 72h.Sterilization
Rate test uses heterotrophic plate counts method.
The concentration of formula used in test solution is 35mg/L in the embodiment of the present invention, comparative example.
Embodiment 1
Di-bromonitrilopropiona,ide 10%, imidazoline bi-quaternary ammonium salt class 5%, poly-aspartate 15%, Epoxysuccinic acid-maleic acid
Bipolymer 20%, sodium gluconate 15%, remaining component are water, pH 8.5.The testing result that the present embodiment obtains is shown in Table 1.
Embodiment 2
Di-bromonitrilopropiona,ide 15%, imidazoline bi-quaternary ammonium salt class 10%, poly-aspartate 20%, Epoxysuccinic acid-maleic acid
Bipolymer 25%, sodium gluconate 20%, remaining component are water, pH 8.5.The testing result that the present embodiment obtains is shown in Table 1.
Comparative example 1
Comparative example 1 is that the blank for being not added with above-mentioned formula simulates etchant solution.The testing result that this comparative example obtains is shown in Table 1.
Comparative example 2-3
Comparative example 2-3 be used for measure according in embodiment 1 each component ratio prepare formula under different pH scale inhibitor
Effect;
Preparation formula is carried out according to each component ratio in embodiment 1, unlike, the pH of the etchant solution residing for comparative example 2,3
Value is respectively 8,9, and the testing result that this comparative example obtains is shown in Table 1.
Comparative example 4-5
Comparative example 4-5 be used for measure according in embodiment 2 each component ratio prepare formula under different pH scale inhibitor
Effect;
Preparation formula is carried out according to each component ratio in embodiment 2, unlike, the pH of the etchant solution residing for comparative example 4,5
Value is respectively 8,9, and the testing result that this comparative example obtains is shown in Table 1
1 formulation efficacy table of table
Claims (3)
1. the formula of the outer chilled water system scaling factor of a kind of elimination, it is characterised in that component is as follows, by mass percentage:10%~
20% di-bromonitrilopropiona,ide, 5% ~ 10% imidazoline bi-quaternary ammonium salt class, 15% ~ 20% poly-aspartate, 20% ~ 30%
The bipolymer of Epoxysuccinic acid-maleic acid, 15% ~ 25% sodium gluconate, remaining component are water.
2. the formula of the outer chilled water system scaling factor of elimination according to claim 1, it is characterised in that the epoxy amber
The relative molecular mass of the bipolymer of amber acid-maleic acid is 600 ~ 1000.
3. the formula of outer chilled water system scaling factor is eliminated according to claim 1, it is characterised in that the pH scopes being applicable in
For 8 ~ 9.