CN107988846A - A kind of Cypres and preparation method thereof - Google Patents
A kind of Cypres and preparation method thereof Download PDFInfo
- Publication number
- CN107988846A CN107988846A CN201711473766.1A CN201711473766A CN107988846A CN 107988846 A CN107988846 A CN 107988846A CN 201711473766 A CN201711473766 A CN 201711473766A CN 107988846 A CN107988846 A CN 107988846A
- Authority
- CN
- China
- Prior art keywords
- cypres
- parts
- water
- sodium
- sustained release
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of Cypres and preparation method thereof, and Cypres include following components by weight percentage:Bulk composition 20 40%, porous resin 5 15%, mould inhibitor 1 15%, sustained release agent 0.2 4%, auxiliary agent 0.5 2%, surplus are water.During preparation, bulk composition is added in reaction kettle, adds water, 5 15min are stirred with the rotating speed of 100 300r/min;Auxiliary agent is added into reaction kettle, 30 60min are stirred with the rotating speed of 200 400r/min;Sustained release agent is mixed into mould inhibitor, adds porous resin, is dissolved in water, obtains mixed solution;Mixed solution is added dropwise into reaction kettle, titrates 1 2h, and stir with the rotating speed of 800 1000r/min;After the completion of titration, keep rotating speed constant, continue to stir 1 2h, obtained Cypres energy long-acting barrier oxygen gas and water and bacterium, realize the purpose for extending effective period of food quality.
Description
Technical field
The present invention relates to pulp technology for making paper, more particularly to a kind of Cypres and preparation method thereof.
Background technology
Tin foil be it is a kind of be used to packing and storing the paper products of food, easy to reality during storing, transport and sell etc.
Now food is fresh-keeping, especially the fresh food such as fruits and vegetables, can be to avoid food because of external environments such as air, moisture using tin foil
The effect of factor and go bad, be conducive to extend the shelf life, therefore, those skilled in the art have been devoted to improve tin foil it is fresh-keeping
The research of fungistatic effect.
Tin foil is in preparation process, it will usually in its surface coating surface sizing agent.Existing Cypres are benzene
The new generation product of vinyl esters copolymerization, can effectively be combined with starch, assign starch coat good cross-link intensity
And water repelling property, and then paper is possessed good water repelling property.
But, on the one hand, at present on the research of Cypres mostly with improve paper water repelling property, ring Asia intensity and
Based in terms of deflection, a small number of researchs on fresh-keeping effect are usually to add antiseptic in existing Cypres, but
This mode fresh-keeping effect is limited, and is unfavorable for the long-term storage of food;On the other hand, the anti-mildew fresh-keeping of tin foil also main pin
Paper material is improved in itself.Therefore, how from the angle of Cypres to enable tin foil long-acting mould-proof fresh-keeping, prolong
The shelf-life of long food is those skilled in the art's technical problem urgently to be resolved hurrily.
The content of the invention
The present invention provides a kind of Cypres and preparation method thereof, can not make tin foil to solve existing Cypres
Possesses the technical problem of long-acting mould-proof fresh-keeping effect.
In a first aspect, the present invention provides a kind of Cypres, by weight percentage including following components:
Bulk composition 20%-40%;
Porous resin 5%-15%;
Mould inhibitor 1%-15%;
Sustained release agent 0.2%-4%;
Auxiliary agent 0.5%-2%;
Surplus is water.
Alternatively, the percentage by weight of each component is:
Bulk composition 40%;
Porous resin 15%;
Mould inhibitor 15%;
Sustained release agent 4%;
Auxiliary agent 2%;
Water 24%.
Alternatively, the bulk composition includes the component of following parts by weight:
30-40 parts of siloxanes;
4-6 parts of cationic monomer;
15-30 parts of acrylic ester monomer;
1-5 parts of cross-linking monomer;
75-78 parts of styrene;
15-30 parts of dispersant;
Concentration is 0.5-1.5 parts of the emulsifier aqueous solution of 25wt%;
Concentration is 0.5-1.5 parts of the initiator solution of 20wt%;
700-800 parts of deionized water.
Alternatively, the aperture of the porous resin is 1-10nm, granularity 100-200nm.
Alternatively, the mould inhibitor includes following components by weight percentage:
Calcium propionate 20%-45%;
Vitamine C sodium 40%-60%;
Other mould proof material 15%-40%.
Alternatively, other described mould proof materials include capsaicine, xanthoxlin, gingerol, catechin, citric acid, allicin,
Chitosan, sorbic acid, turmeric alcohol, cinnamomum camphora essential oil, Chinese medical extract, Meng ancestor bamboo extract, Hinokitiol and nisin
At least one of.
Alternatively, other described mould proof materials include sodium Diacetate, potassium sorbate/sodium, potassium citrate/sodium, ascorbic acid
At least one in sodium/potassium, sodium salicylate, sodium isoascorbate, Kathon CG, dodecyl alanine, Metagin/acetic acid, lysozyme
Kind.
Alternatively, the sustained release agent is bronopol.
Alternatively, the auxiliary agent is defoamer.
Second aspect, the present invention also provides a kind of Cypres preparation method, the described method comprises the following steps:
Bulk composition is added in reaction kettle, adds water to stir, 5-15min is stirred with the rotating speed of 100-300r/min;
Auxiliary agent is added into the reaction kettle, 30-60min is stirred with the rotating speed of 200-400r/min;
Sustained release agent is mixed into mould inhibitor, then adds porous resin, is dissolved in water, obtains mixed solution;
By the way of dropwise addition, the mixed solution is added dropwise into the reaction kettle, titration time 1-2h, and with 800-
The rotating speed of 1000r/min is stirred;
After the completion of titration, keep rotating speed constant, continue to discharge after stirring 1-2h, obtain the Cypres.
From above technical scheme, a kind of Cypres provided by the invention and preparation method thereof, the surface is applied
Jelly includes following components by weight percentage:Bulk composition 20%-40%, porous resin 5%-15%, mould inhibitor 1%-
15%th, sustained release agent 0.2%-4%, auxiliary agent 0.5%-2%, surplus are water.During preparation, bulk composition is added in reaction kettle, is added
Water stirs, and then adds auxiliary agent stirring, sustained release agent is mixed into mould inhibitor, then adds porous resin, is dissolved in water, is mixed
Solution is closed, then mixed solution is added drop-wise in reaction kettle, at this time, is filled with sustained release agent in the hole of porous resin, in sustained release agent
Mould inhibitor is wrapped up, reaches the effect slowly discharged.The Cypres of the present invention have good barrier, can not only obstruct oxygen
The factors such as gas and water, moreover it is possible to adverse effect of the bacterium to food is effectively obstructed, after tin foil sprays the Cypres of the present invention,
The suppression to food mould can be kept for a long time, realize the purpose for extending effective period of food quality.
Brief description of the drawings
Fig. 1 is a kind of flow chart of Cypres preparation method shown in the embodiment of the present invention.
Embodiment
In order to make those skilled in the art better understand the technical solutions in the application, below in conjunction with attached drawing, it is right
Technical solution in the embodiment of the present application is clearly and completely described.
Embodiment one
The present embodiment provides a kind of Cypres, by weight percentage including following components:It is bulk composition 20%, porous
Resin 5%, mould inhibitor 1%, sustained release agent 0.2%, auxiliary agent 0.5%, water 73.3%.
As shown in Figure 1, the embodiment of the present invention one also provides a kind of Cypres preparation method, include the following steps:
Step S101:Bulk composition is added in reaction kettle, adds water to stir, 5- is stirred with the rotating speed of 100-300r/min
15min;
Step S102:Auxiliary agent is added into the reaction kettle, 30-60min is stirred with the rotating speed of 200-400r/min;
Step S103:Sustained release agent is mixed into mould inhibitor, then adds porous resin, is dissolved in water, obtains mixed solution;
Step S104:By the way of dropwise addition, the mixed solution, titration time 1- are added dropwise into the reaction kettle
2h, and be stirred with the rotating speed of 800-1000r/min;
Step S105:After the completion of titration, keep rotating speed constant, continue to discharge after stirring 1-2h, obtain the top sizing
Agent.
Porous resin has very strong adsorption capacity, and sustained release agent is filled with its hole, mould inhibitor is wrapped up in sustained release agent, reaches
To the effect slowly discharged, the aperture of porous resin is 1-10nm, granularity 100-200nm.Test result indicates that porous resin
Aperture be 1-10nm, when granularity is 100-200nm, the bacteriostasis, preservation effect of Cypres is best, and action time more lengthens
Effect is lasting, can effectively extend the shelf-life of food.
Wherein, the bulk composition includes the component of following parts by weight:35 parts of siloxanes;5 parts of cationic monomer;Acrylic acid
20 parts of esters monomer;4 parts of cross-linking monomer;75 parts of styrene;20 parts of dispersant;Concentration is 1 part of the emulsifier aqueous solution of 25wt%;
Concentration is 1 part of the initiator solution of 20wt%;750 parts of deionized water.
The mould inhibitor includes following components by weight percentage:Calcium propionate 30%, vitamine C sodium 50%, other are mould proof
Material 20%.Other mould proof materials are potassium sorbate.
Calcium propionate is acid type food preservative, in acid condition, produces free propionic acid, has antibacterial action, its is antibacterial
Effect is influenced by environmental pH, and in pH value 5.0, the inhibitory action of mould is optimal, and bacteriostasis substantially reduces during pH value 6.0,
Minimal inhibitory concentration is 0.01%.To all kinds of moulds, gram-negative in acid medium (starch, containing protein and lipid phase)
Property bacillus or aerobic bacillus have stronger inhibitory action, can also suppress the generation of aflatoxins, and harmless to saccharomycete,
To person poultry harmless, have no toxic side effect.It is a kind of new, safe and efficient food of food, brewing, feed, Chinese medicine preparation aspects
Product and feed mould inhibitor.
Vitamine C sodium is typically used as the antioxidant of food, and blocking oxygen, protects food to go bad from oxidative damage,
And then be conducive to improve the shelf-life of food.
Potassium sorbate can effectively inhibit the activity of mould, saccharomycete and aerobic bacteria, moreover it is possible to prevent clostridium botulinum, Portugal
The harmful microbes such as grape coccus, salmonella are grown and breeding, and the effect of its supression development is more stronger than bactericidal effect, so as to reach
To the holding time of effectively extension food, and keep the flavor of original food.
The sustained release agent is bronopol, can control the rate of release of mould inhibitor, and the peak valley ripple of mould inhibitor is reduced or avoided
It is dynamic, so that mould inhibitor gently can constantly play effect, the suppression to food mould can be kept for a long time, realized and extended food
The purpose of product shelf-life.
The auxiliary agent is defoamer, also referred to as defomaing agent, is that surface tension is reduced in food or industry processes, is suppressed
Foam produces or eliminates the additive for having produced foam.Defoamer mainly has the fatty acid ester compounded thing of silicone emulsion, higher alcohols, gathers
Ethylene oxide polyoxypropylene pentaerythrite ether, polyoxyethylene polyoxy propyl alcohol amidogen ether, polypropylene glycerol aether and polyoxypropylene polyoxy second
7 kinds of alkene glycerin ether, dimethyl silicone polymer etc..
Compared with prior art, its bulk composition of Cypres provided in this embodiment has good water-resistance and ring
Compressive Strength, has very strong adsorption capacity by porous resin, sustained release agent is filled with its hole, is wrapped up in sustained release agent mould proof
Agent, mould inhibitor is except with good bacteria mildew-proof effect, also added the vitamine C sodium with strong anti-oxidation, therefore
Cypres provided in this embodiment have good barrier, can not only blocking oxygen, water, moreover it is possible to effectively barrier bacterium pair
The adverse effect of food, after tin foil sprays the Cypres of the present invention, can keep the suppression to food mould for a long time,
Realize the purpose for extending effective period of food quality.
It should be noted that in following other embodiments, described in the preparation method and the present embodiment one of Cypres
Method is identical, with reference to the method for embodiment one, in addition, the identical part of Cypres component can phase between each embodiment
Mutual reference, hereafter repeats no more.
Embodiment two
The present embodiment provides a kind of Cypres, by weight percentage including following components:It is bulk composition 30%, porous
Resin 10%, mould inhibitor 8%, sustained release agent 2.1%, auxiliary agent 1.3%, water 48.6%.
Wherein, the bulk composition includes the component of following parts by weight:35 parts of siloxanes;5 parts of cationic monomer;Acrylic acid
20 parts of esters monomer;4 parts of cross-linking monomer;75 parts of styrene;20 parts of dispersant;Concentration is 1 part of the emulsifier aqueous solution of 25wt%;
Concentration is 1 part of the initiator solution of 20wt%;750 parts of deionized water.
The aperture of porous resin is 1-10nm, granularity 100-200nm.
The mould inhibitor includes following components by weight percentage:Calcium propionate 30%, vitamine C sodium 50%, other are mould proof
Material 20%.Other mould proof materials are potassium sorbate.
The sustained release agent is bronopol, and the auxiliary agent is defoamer.
Embodiment three
The present embodiment provides a kind of Cypres, by weight percentage including following components:It is bulk composition 40%, porous
Resin 15%, mould inhibitor 15%, sustained release agent 4%, auxiliary agent 2%, water 24%.
Wherein, the bulk composition includes the component of following parts by weight:35 parts of siloxanes;5 parts of cationic monomer;Acrylic acid
20 parts of esters monomer;4 parts of cross-linking monomer;75 parts of styrene;20 parts of dispersant;Concentration is 1 part of the emulsifier aqueous solution of 25wt%;
Concentration is 1 part of the initiator solution of 20wt%;750 parts of deionized water.
The aperture of porous resin is 1-10nm, granularity 100-200nm.
The mould inhibitor includes following components by weight percentage:Calcium propionate 30%, vitamine C sodium 50%, other are mould proof
Material 20%.Other mould proof materials are potassium sorbate.
The sustained release agent is bronopol, and the auxiliary agent is defoamer.
Cypres described in one~embodiment of embodiment three are coated on tin foil (the dosage of Cypres respectively
It is identical), obtain three kinds of tin foils are carried out to the test of sterilization fresh-keeping effect with existing common tin foil, respectively with four kinds of guarantors
Fresh paper packs apple, and the size shape of four kinds of tin foils is consistent, and four intact ripe apples degree, weight etc. are
It is consistent, and in (20 DEG C of temperature, relative humidity 60%) in completely the same test environment, then the result of the test obtained is such as
Shown in table 1 below:
Table 1
From the data result of table 1, has there is certain rotten, 20% apple table after 10 days in existing tin foil
Skin discoloration is oxidation and bacterial action as a result, it is because carrying out anaerobic respiration, apple after apple packing to produce slight alcohol smell
Saccharomycete is produced in fruit body, is a kind of ferment in saccharomycete, the carbohydrate in apple can be decomposed so that produce alcohol and
Carbon dioxide, shelf-life of the existing tin foil under the conditions of experimental enviroment are 10 days.And the embodiment of the present invention one, two and of embodiment
Embodiment three increases compared to existing tin foil, shelf-life, and the shelf-life is incremented by successively, this is because Cypres
Interior bulk composition, porous resin, mould inhibitor and sustained release agent is gradually incremented by, and mould inhibitor can be more efficient enduringly antibacterial and be killed
Bacterium, oxidation resistance and obstructing capacity action time longer result.Further, since potassium sorbate can effectively suppress saccharomycete
Activity, therefore in the test process of one~embodiment of embodiment three apple do not have substantially produce alcohol smell.Embodiment three corresponds to
Shelf-lifves of Cypres can reach 20 days, for existing wrapping paper, substantially increase the shelf-life of food, its
Fresh-keeping effect is more efficient and lasting.
Example IV
The present embodiment provides a kind of Cypres, by weight percentage including following components:It is bulk composition 40%, porous
Resin 15%, mould inhibitor 15%, sustained release agent 4%, auxiliary agent 2%, water 24%.
Wherein, the bulk composition includes the component of following parts by weight:35 parts of siloxanes;5 parts of cationic monomer;Acrylic acid
20 parts of esters monomer;4 parts of cross-linking monomer;75 parts of styrene;20 parts of dispersant;Concentration is 1 part of the emulsifier aqueous solution of 25wt%;
Concentration is 1 part of the initiator solution of 20wt%;750 parts of deionized water.
The aperture of porous resin is 1-10nm, granularity 100-200nm.
The mould inhibitor includes following components by weight percentage:Calcium propionate 30%, vitamine C sodium 50%, other are mould proof
Material 20%.Other mould proof materials include sodium Diacetate, sodium sorbate, potassium citrate/sodium, sodium ascorbate/potassium, salicylic acid
At least one of sodium, sodium isoascorbate, Kathon CG, dodecyl alanine, Metagin/acetic acid, lysozyme.
Sodium Diacetate plays antibacterial action mainly by the molecular state acetic acid of decomposition, it has bacterium and mould good suppression energy
Power.
Sodium sorbate is a kind of food additives, has the anti-microbial property that security is good, antiseptic property is efficient and higher,
There is inhibitory action to bacterium, mould, saccharomycete, particularly anti-mold effect is good, is widely used in food, beverage, cosmetics
With medicine etc..
Potassium citrate is used as buffer, chelating agent, stabilizer, antioxidant, emulsifying agent, flavor enhancement in the food industry
Deng.Available for milk and milk products, jelly, jam, meat, canned hydrogel dessert, the guarantor of the food such as the emulsification of cheese, citrus
It is fresh.
Sodium citrate non-toxic and safe, have pH regulation performances and good stability, therefore can be used for food industry.Lemon
Sour sodium is used as food additives, has the call, and is mainly used as flavor enhancement, buffer, emulsifying agent, swelling agent, stabilizer and prevents
Rotten agent etc..
Sodium ascorbate is mainly used as the antioxidant of food.
Sodium isoascorbate, also known as sodium iso-vc, D-araboascorbic acid sodium, erythorbic acid sodium are a kind of food fresh keepings, help color,
Antioxygen, preservative.
Kathon CG aqueous solution appearance is light amber transparency liquid, and smell is gentle, (20/4) 1.19 viscosity (23) of relative density
5.0mpa.s, solidification point -18-21.5, pH3.5-5.0, it is soluble easily in water, low-carbon alcohols and ethylene glycol.Optimal use pH value 4-8,
pH>Stability declines when 8, stores at room temperature 1 year, and 50 DEG C of storage half a year, activity decline is seldom, and high temperature storage activity declines, it
Emulsifying agent, protein compatibility that can be with anion, cation, nonionic and various ionics, have efficient, nontoxic, antibacterial kill
The advantages of bacterium is extensive, lasting effect is long, and water can be dissolved in, it is easy to use, it can be directly added into.
Lysozyme is also known as muramidase or N-acetylmuramide lycanohydrlase, is that one kind can hydrolyze glutinous polysaccharide in pathogenic bacteria
Alkaline enzyme.Mainly by destroying the β between the -acetylmuramic acid in cell membrane and n-acetylglucosamine-Isosorbide-5-Nitrae glycosidic bond,
The insoluble glutinous polysaccharide of cell membrane is resolved into soluble glycopeptide, cause cell wall rupture content to escape and make bacterolysis.It is molten
Bacterium enzyme can also with negatively charged virus protein directly in conjunction with, with DNA, RNA, apoprotein formed double salt, make virally inactivated.
Therefore, which has the effect such as antibacterial, anti-inflammatory, antiviral.
Embodiment five
The present embodiment provides a kind of Cypres, by weight percentage including following components:It is bulk composition 40%, porous
Resin 15%, mould inhibitor 15%, sustained release agent 4%, auxiliary agent 2%, water 24%.
Wherein, the bulk composition includes the component of following parts by weight:35 parts of siloxanes;5 parts of cationic monomer;Acrylic acid
20 parts of esters monomer;4 parts of cross-linking monomer;75 parts of styrene;20 parts of dispersant;Concentration is 1 part of the emulsifier aqueous solution of 25wt%;
Concentration is 1 part of the initiator solution of 20wt%;750 parts of deionized water.
The aperture of porous resin is 1-10nm, granularity 100-200nm.
The mould inhibitor includes following components by weight percentage:Calcium propionate 30%, vitamine C sodium 50%, other are mould proof
Material 20%.Other mould proof materials are Natural anti-mildew material extract, including capsaicine, xanthoxlin, gingerol, catechin, lemon
Lemon acid, allicin, chitosan, sorbic acid, turmeric alcohol, cinnamomum camphora essential oil, Chinese medical extract, Meng ancestor bamboo extract, Hinokitiol and
At least one of nisin.
The sustained release agent is bronopol, and the auxiliary agent is defoamer.
Capsaicine, xanthoxlin, gingerol, catechin, cinnamomum camphora essential oil, Chinese medical extract, Hinokitiol, Meng's ancestor's bamboo extract tool
There is good sterilizing, food preservative can be used as.
The chelation of citric acid and the characteristic of adjusting pH value make it to increase antioxidant during food processing, storage
Performance, inhibitory enzyme activity, extend effective period of food quality.
Allicin is most fast to the sterilization speed of Cryptococcus neoformans, and killing effect is best, and allicin can not only kill germ, and
And can relatively efficiently it kill including moulds such as aspergillus flavus, aspergillus niger, aspergillus fumigatus.The anti-mildew effect of allicin is that mould can be destroyed
Coloured glaze base enzyme function, hinder the metabolism of mould.
Chitosan is easy to dissolve in weakly acidic solvent, it is worth pointing out that containing amino (NH2 in dissolved solution
+), these amino are inhibited bacteria by combining negative electron.Chitosan inhibits bacteria activity, makes it in medicine, weaving and food
The fields such as product have a wide range of applications.
Sorbic acid has higher anti-microbial property, presses down mycostatic growth and breeding, by suppressing the dehydrogenation in microbial body
Enzyme system, reaches the growth for suppressing microorganism and plays antisepsis, have suppression to make to mould, saccharomycete and many aerobic organisms
With.
Turmeric alcohol has the antimycotic and antioxidation of strength, the fungus and mildew resistance available for food.
Nisin (Nisin), also known as nisin, are a kind of peptide materials that streptococcus lactis produces,
It is made of 34 amino acid residues, molecular weight is about 3500Da.Nisin can effectively suppress to cause being permitted for food spoilage
More gram-positive bacteriums, such as lactobacillus, leukonid, micrococcus, staphylococcus, Listeria, particularly to producing gemma
Bacterium such as bacillus, clostridium have very strong inhibitory action.Since nisin can inhibit.After edible
Amino acid is hydrolyzed into quickly under physiological pH condition and α-chymotrypsin protein enzyme effect of human body, will not be changed in human body intestinal canal just
Normal flora and the generation resistance problem that such as other antibiotic occur, more cross tolerance will not occur with other antibiotic, be
A kind of efficient, nontoxic, safe, without side-effects antiseptics for natural food.
Compared to embodiment three and example IV, the present embodiment adds Natural anti-mildew material extract in mould inhibitor,
Make mould inhibitor outer with good bacteria mildew-proof effect, moreover it is possible to ensure that the fungus-resistant material of Cypres release will not be right
Food produces harm or adverse effect, uses more safety and environmental protection.
Embodiment six
The present embodiment provides a kind of Cypres, by weight percentage including following components:It is bulk composition 40%, porous
Resin 15%, mould inhibitor 15%, sustained release agent 4%, auxiliary agent 2%, water 24%.
Wherein, the bulk composition includes the component of following parts by weight:35 parts of siloxanes;5 parts of cationic monomer;Acrylic acid
20 parts of esters monomer;4 parts of cross-linking monomer;75 parts of styrene;20 parts of dispersant;Concentration is 1 part of the emulsifier aqueous solution of 25wt%;
Concentration is 1 part of the initiator solution of 20wt%;750 parts of deionized water.
The aperture of porous resin is 1-10nm, granularity 100-200nm.
The mould inhibitor includes following components by weight percentage:Calcium propionate 45%, vitamine C sodium 40%, other are mould proof
Material 15%.Other mould proof materials are Natural anti-mildew material extract, including capsaicine, xanthoxlin, gingerol, catechin, lemon
Lemon acid, allicin, chitosan, sorbic acid, turmeric alcohol, cinnamomum camphora essential oil, Chinese medical extract, Meng ancestor bamboo extract, Hinokitiol and
At least one of nisin.
The sustained release agent is bronopol, and the auxiliary agent is defoamer.
Embodiment seven
The present embodiment provides a kind of Cypres, by weight percentage including following components:It is bulk composition 40%, porous
Resin 15%, mould inhibitor 15%, sustained release agent 4%, auxiliary agent 2%, water 24%.
Wherein, the bulk composition includes the component of following parts by weight:35 parts of siloxanes;5 parts of cationic monomer;Acrylic acid
20 parts of esters monomer;4 parts of cross-linking monomer;75 parts of styrene;20 parts of dispersant;Concentration is 1 part of the emulsifier aqueous solution of 25wt%;
Concentration is 1 part of the initiator solution of 20wt%;750 parts of deionized water.
The aperture of porous resin is 1-10nm, granularity 100-200nm.
The mould inhibitor includes following components by weight percentage:Calcium propionate 20%, vitamine C sodium 40%, other are mould proof
Material 40%.Other mould proof materials are Natural anti-mildew material extract, including capsaicine, xanthoxlin, gingerol, catechin, lemon
Lemon acid, allicin, chitosan, sorbic acid, turmeric alcohol, cinnamomum camphora essential oil, Chinese medical extract, Meng ancestor bamboo extract, Hinokitiol and
At least one of nisin.
The sustained release agent is bronopol, and the auxiliary agent is defoamer.
Embodiment six reduces the percentage by weight of vitamine C sodium compared to embodiment five, opposite to improve calcium propionate
Percentage by weight, therefore increase the effect of fungus and mildew resistance, oxidation resistance is opposite to be weakened;In embodiment seven, other are mould proof
The content highest of material, reaches 40%, since other mould proof materials may include a variety of different mould inhibitors, can inhibit more
The activity of multiple types bacterium, so that mould proof, the antibacterial and fresh-keeping effect of surfactant is further improved, so that suitable for more
Food categories it is fresh-keeping, extend the shelf-life of food.
From above technical scheme, a kind of Cypres provided by the invention and preparation method thereof, the surface is applied
Jelly includes following components by weight percentage:Bulk composition 20%-40%, porous resin 5%-15%, mould inhibitor 1%-
15%th, sustained release agent 0.2%-4%, auxiliary agent 0.5%-2%, surplus are water.During preparation, bulk composition is added in reaction kettle, is added
Water stirs, and then adds auxiliary agent stirring, sustained release agent is mixed into mould inhibitor, then adds porous resin, is dissolved in water, is mixed
Solution is closed, then mixed solution is added drop-wise in reaction kettle, at this time, is filled with sustained release agent in the hole of porous resin, in sustained release agent
Mould inhibitor is wrapped up, reaches the effect slowly discharged.The Cypres of the present invention have good barrier, can not only obstruct oxygen
The factors such as gas and water, moreover it is possible to adverse effect of the bacterium to food is effectively obstructed, after tin foil sprays the Cypres of the present invention,
The suppression to food mould can be kept for a long time, realize the purpose for extending effective period of food quality.
The preparation method of each Cypres described in two~embodiment of the embodiment of the present application seven, can refer in embodiment one
Description and explanation, identical part can be cross-referenced between each embodiment.
Those skilled in the art will readily occur to the present invention its after considering specification and putting into practice invention disclosed herein
Its embodiment.This application is intended to cover the present invention any variations, uses, or adaptations, these modifications, purposes or
Person's adaptive change follows the general principle of the present invention and including undocumented common knowledge in the art of the invention
Or conventional techniques.Description and embodiments are considered only as exemplary, and true scope and spirit of the invention are by appended
Claim is pointed out.
It should be appreciated that the invention is not limited in the precision architecture for being described above and being shown in the drawings, and
And various modifications and changes may be made without departing from the scope thereof.The scope of the present invention is only limited by appended claim.
Claims (10)
1. a kind of Cypres, it is characterised in that by weight percentage including following components:
Bulk composition 20%-40%;
Porous resin 5%-15%;
Mould inhibitor 1%-15%;
Sustained release agent 0.2%-4%;
Auxiliary agent 0.5%-2%;
Surplus is water.
2. Cypres according to claim 1, it is characterised in that the percentage by weight of each component is:
Bulk composition 40%;
Porous resin 15%;
Mould inhibitor 15%;
Sustained release agent 4%;
Auxiliary agent 2%;
Water 24%.
3. Cypres according to claim 1, it is characterised in that the bulk composition includes the group of following parts by weight
Point:
30-40 parts of siloxanes;
4-6 parts of cationic monomer;
15-30 parts of acrylic ester monomer;
1-5 parts of cross-linking monomer;
75-78 parts of styrene;
15-30 parts of dispersant;
Concentration is 0.5-1.5 parts of the emulsifier aqueous solution of 25wt%;
Concentration is 0.5-1.5 parts of the initiator solution of 20wt%;
700-800 parts of deionized water.
4. Cypres according to claim 1, it is characterised in that the aperture of the porous resin is 1-10nm, grain
Spend for 100-200nm.
5. Cypres according to claim 1, it is characterised in that the mould inhibitor includes following by weight percentage
Component:
Calcium propionate 20%-45%;
Vitamine C sodium 40%-60%;
Other mould proof material 15%-40%.
6. Cypres according to claim 5, it is characterised in that other described mould proof materials include capsaicine, flower
Green pepper element, gingerol, catechin, citric acid, allicin, chitosan, sorbic acid, turmeric alcohol, cinnamomum camphora essential oil, Chinese medical extract,
At least one of Meng ancestor bamboo extract, Hinokitiol and nisin.
7. Cypres according to claim 5, it is characterised in that other described mould proof materials include sodium Diacetate,
Potassium sorbate/sodium, potassium citrate/sodium, sodium ascorbate/potassium, sodium salicylate, sodium isoascorbate, Kathon CG, the third ammonia of dodecyl
At least one of acid, Metagin/acetic acid, lysozyme.
8. Cypres according to claim 1, it is characterised in that the sustained release agent is bronopol.
9. Cypres according to claim 1, it is characterised in that the auxiliary agent is defoamer.
10. a kind of Cypres preparation method, it is used to prepare such as claim 1-9 any one of them Cypres, its
It is characterized in that, the described method includes:
Bulk composition is added in reaction kettle, adds water to stir, 5-15min is stirred with the rotating speed of 100-300r/min;
Auxiliary agent is added into the reaction kettle, 30-60min is stirred with the rotating speed of 200-400r/min;
Sustained release agent is mixed into mould inhibitor, then adds porous resin, is dissolved in water, obtains mixed solution;
By the way of dropwise addition, the mixed solution is added dropwise into the reaction kettle, titration time 1-2h, and with 800-
The rotating speed of 1000r/min is stirred;
After the completion of titration, keep rotating speed constant, continue to discharge after stirring 1-2h, obtain the Cypres.