CN107987582A - A kind of automotive paints preparation method - Google Patents
A kind of automotive paints preparation method Download PDFInfo
- Publication number
- CN107987582A CN107987582A CN201711371908.3A CN201711371908A CN107987582A CN 107987582 A CN107987582 A CN 107987582A CN 201711371908 A CN201711371908 A CN 201711371908A CN 107987582 A CN107987582 A CN 107987582A
- Authority
- CN
- China
- Prior art keywords
- parts
- automotive paints
- drier
- butanol
- acrylonitrile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of automotive paints preparation method, it is characterized in that, including varnish, acrylonitrile, talcum powder, pigment, binding agent, drier, phosphoric acid, butanol, oil, methyl methacrylate and aluminium powder slurries, the above material is by weight ratio, 19 20 parts of varnish, 40 45 parts of acrylonitrile, 57 parts of talcum powder, 10 14 parts of pigment, 56 parts of binding agent, 45 parts of drier, 56 parts of water methyl methacrylate, 78 parts of aluminium powder slurries, 2 36 parts of phosphatase 11,15 27 parts of butanol, 1 22 parts of oil.Stannous chloride, zirconium oxide and polyvinyl alcohol are further included in the paint.A kind of automotive paints that the present invention obtains and preparation method thereof, easy to make, wear-resisting, good corrosion resistance is beautiful, not easily to fall off, can produce on a large scale, and manufactures of low cost, the car shell of automobile can be more effectively protected, using feeling more relieved.
Description
Technical field
The present invention relates to paint technology field, more particularly to a kind of automotive paints preparation method.
Background technology
Car paint is the aesthetic measure that secondly can also increase car primarily to protect car body not to be corroded, automobile coating and
Other paint are different, since automobile itself is expensive, the experience and tempering of experience spring, summer, autumn and winter throughout the year in addition, to the performance of automobile coating
It is required that high, automobile coating will not only accomplish that paint film has good mechanical performance, richness is good, gloss is high, also accomplish to adhere to
Power is good, hardness is high, scratch resistance capability is strong, while more to possess fabulous weatherability, scratch resistance wearability, gloss continuation, and excellent
The performances such as good resistance to gasoline, ethanol-tolerant, acidproof, alkaline-resisting, salt spray resistance, but the universal manufacturing process of automotive paints now is non-
Often trouble, and wear-resisting and corrosion resistance is not fine, usually can cause to fall paint or depainting, it is necessary to which car owner more changes oil often
Paint, it is very troublesome.
The content of the invention
In consideration of it, the present invention provides a kind of automotive paints preparation method, it is characterised in that including varnish, acrylonitrile,
Talcum powder, pigment, binding agent, drier, phosphoric acid, butanol, oil, methyl methacrylate and aluminium powder slurries, it is described more than
Material is 19-20 parts of varnish, 40-45 parts of acrylonitrile, 5-7 parts of talcum powder, 10-14 parts of pigment, binding agent by weight ratio
5-6 parts, 4-5 parts of drier, 5-6 parts of water methyl methacrylate, 7-8 parts of aluminium powder slurries, 2-36 parts of phosphatase 11, butanol 15-27
Part, 1-22 parts of oil.
The present invention is further described, stannous chloride, zirconium oxide and polyvinyl alcohol are further included in the paint.
Using above-mentioned technical proposal, have the advantages that:
A kind of automotive paints that the present invention obtains and preparation method thereof, easy to make, wear-resisting, good corrosion resistance are beautiful, no
It is easy to fall off, it can produce on a large scale, and manufacture of low cost, the car shell of automobile can be more effectively protected, using feeling more relieved.
Embodiment
Embodiment one:
A kind of automotive paints preparation method, it is characterised in that including varnish, acrylonitrile, talcum powder, pigment, binding agent,
Drier, phosphoric acid, butanol, oil, methyl methacrylate and aluminium powder slurries, the above material is varnish by weight ratio
19-20 parts, 40-45 parts of acrylonitrile, 5-7 parts of talcum powder, 10-14 parts of pigment, 5-6 parts of binding agent, 4-5 parts of drier,
5-6 parts of water methyl methacrylate, 7-8 parts of aluminium powder slurries, 2-36 parts of phosphatase 11,15-27 parts of butanol, 1-22 parts of oil.
Stannous chloride, zirconium oxide and polyvinyl alcohol are further included in the paint.
A kind of automotive paints that the present invention obtains and preparation method thereof, easy to make, wear-resisting, good corrosion resistance are beautiful
See, is not easily to fall off, can produce on a large scale, and manufacture is of low cost, the car shell of automobile can be more effectively protected, using more
Trust.
The basic principle and main feature of the present invention is the foregoing described, It should be understood by those skilled in the art that of the invention
It is not restricted to the described embodiments, the above embodiments and description only illustrate the principle of the present invention, is not departing from
On the premise of spirit and scope of the invention, various changes and modifications of the present invention are possible, these changes and improvements both fall within requirement
In the scope of the invention of protection, invent claimed scope and be defined by the appending claims and its equivalent thereof.
Claims (2)
- A kind of 1. automotive paints preparation method, it is characterised in that including varnish, acrylonitrile, talcum powder, pigment, binding agent, Drier, phosphoric acid, butanol, oil, methyl methacrylate and aluminium powder slurries, the above material is varnish by weight ratio 19-20 parts, 40-45 parts of acrylonitrile, 5-7 parts of talcum powder, 10-14 parts of pigment, 5-6 parts of binding agent, 4-5 parts of drier, 5-6 parts of water methyl methacrylate, 7-8 parts of aluminium powder slurries, 2-36 parts of phosphatase 11,15-27 parts of butanol, 1-22 parts of oil.
- 2. a kind of automotive paints preparation method according to claim 1, it is characterised in that further include chlorination in the paint Stannous, zirconium oxide and polyvinyl alcohol.