CN107965621A - HDPE is molded push pipe - Google Patents
HDPE is molded push pipe Download PDFInfo
- Publication number
- CN107965621A CN107965621A CN201711069347.1A CN201711069347A CN107965621A CN 107965621 A CN107965621 A CN 107965621A CN 201711069347 A CN201711069347 A CN 201711069347A CN 107965621 A CN107965621 A CN 107965621A
- Authority
- CN
- China
- Prior art keywords
- push pipe
- hdpe
- layer
- outer layer
- pigment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of push pipe, disclose a kind of HDPE shapings push pipe, it includes push pipe body, push pipe body includes internal layer, sandwich layer and the outer layer set from inside to outside, internal layer is identical with the material component of outer layer, mixed by 98.35% HDPE and 1.65% pigment, sandwich layer is mixed by 83% HDPE, 6% inorganic mineral and 11% thermoplastic elastomer (TPE).There is high ring rigidity by push pipe made from above-mentioned formula, the characteristics such as the inner wall coefficient of sliding friction is small, while there is damping, sound insulation.
Description
Technical field
The present invention relates to a kind of push pipe, more particularly to a kind of HDPE shaping push pipes.
Background technology
High density polyethylene (HDPE), English name are " High Density Polyethylene ", referred to as " HDPE ". HDPE
It is that a kind of crystallinity is high, nonpolar thermoplastic resin.The milky appearance of ortho states HDPE, in meagre section in a certain degree
It is translucent.PE has a characteristics of excellent resistance to most of lives and chemicals for industrial use, the non-hygroscopic and waterproof that has had
It is vapor permeability, available for packaging applicationss.HDPE has good electrical property, and particularly dielectric strength is high, is readily applicable to it
Electric wire.In there is fabulous impact resistance to high molecular weight grades, room temperature in addition under -40F low temperatures it is such.
HDPE pipes are traditional steel tubing, the regeneration product of polyvinyl chloride drinking-water pipe, its due to as hydraulic pressure solenoid,
Tensile strength height must is fulfilled for, high pressure, rigidity is high, the characteristic such as dimensional stability height during processing and forming, existing HDPE pipes
Performance, which still has, to have greater room for improvement.
The content of the invention
The present invention for the problem of performance existing for HDPE pipes has much room for improvement in the prior art, there is provided a kind of HDPE into
Type push pipe.
In order to solve the above-mentioned technical problem, the present invention is addressed by following technical proposals:
HDPE is molded push pipe, including push pipe body, it is characterised in that internal layer that push pipe body includes setting from inside to outside,
The material component of sandwich layer and outer layer, internal layer and outer layer is identical, is mixed by 98.35% HDPE and 1.65% pigment,
Sandwich layer is mixed by 83% HDPE, 6% inorganic mineral and 11% thermoplastic elastomer (TPE), it is ensured that push pipe epipodium is firm
Degree, the inner wall coefficient of sliding friction is small, while has effects that damping, sound insulation, is effectively improved the performance of HDPE shaping push pipes.
Preferably, push pipe body is formed and protected up to 55 through chromium plating process, Rockwell hardness by internal layer, sandwich layer and outer layer
Shield, and die face caustic dip, and in the hard steel mould through oil spraying or siliceous spray uniform fusion co-extrusion and formed, ensure stream
Body resistance is small, makes ectonexine and sandwich layer uniform fusion, and technique is simple, reliable in quality, equipment damage are small.
Preferably, the pigment includes 0.5% yellow uitramarine, 0.1% red pigment, 1% blue pigment with
And 0.05% charcoal blacks.
Be 0.4-0.6mm preferably, internal layer is identical with the wall thickness of outer layer, the wall thickness of sandwich layer for 1.9-2.4mm and
The density of sandwich layer is 1.2-1.8g/cm3。
The present invention has significant technique effect as a result of above technical scheme:
The present invention is designed to the easily molded push pipes of HDPE using this kind formula so that mixed material is easy into conventional processing temperature
Type, and improve the characteristics such as the ring stiffness of push pipe, high temperature resistant, proof to external pressure, product structure, sandwich layer fill process are optimized, has and subtracts
Shake, sound insulation effect so that product has more core competitiveness.
Embodiment
Embodiment 1
HDPE is molded push pipe, including push pipe body, and push pipe body includes internal layer, sandwich layer and the outer layer set from inside to outside,
Internal layer is identical with the material component of outer layer, is mixed by 98.35% HDPE and 1.65% pigment, sandwich layer is by 83%
HDPE, 6% inorganic mineral and 11% thermoplastic elastomer (TPE) mix, and sandwich layer uses inorganic mineral, PE and thermoplastic elastomehc
Property body tertiary blending viscoelastic material composition, reduce cost;Optimize the formula of HDPE material, it is ensured that high ring rigidity,
The inner wall coefficient of sliding friction is small, while has effects that damping, sound insulation.
Push pipe body by internal layer, sandwich layer and outer layer through chromium plating process and die face caustic dip, and through oil spraying or
Uniform fusion co-extrusion in the hard steel mould of siliceous spray and formed.Using the hard firm mould through chromium plating process, Rockwell hardness up to 55,
Protection, while die face caustic dip, and oil spraying or siliceous spray are formed, ensures that fluid resistance is small, makes ectonexine and sandwich layer
Uniform fusion, technique is simple, reliable in quality, equipment damage are small.
Pigment includes 0.5% yellow uitramarine in the present embodiment, 0.1% red pigment, 1% blue pigment and
0.05% charcoal blacks.I.e. in the present embodiment internal layer and outer layer by 98.35% HDPE and 0.5% yellow uitramarine, 0.1%
Red pigment, 1% blue pigment and 0.05% charcoal blacks be uniformly mixed.
The internal layer of HDPE shapings push pipe is identical with the wall thickness of outer layer in the present embodiment, is 0.5mm, the wall thickness of sandwich layer is
2.2mm, the density of sandwich layer is 1.5g/cm3。
The HDPE prepared in the present embodiment by above-mentioned formula, which is molded push pipe, has that easily molded, ring stiffness is high, proof to external pressure
Etc. advantage, in environmental protection, machine-shaping and recyclable economy etc., by scientific and technical innovation, improve product competitiveness, certainty into
For very promising building material, which has reached domestic top standard.
Embodiment 2
With embodiment 1, except that the wall thickness of internal layer and outer layer is 0.4mm, the wall thickness of sandwich layer is 1.9mm, sandwich layer
Density be 1.2g/cm3。
Embodiment 3
With embodiment 1, except that the wall thickness of internal layer and outer layer is 0.6mm, the wall thickness of sandwich layer is 2.4mm, sandwich layer
Density be 1.8g/cm3。
In short, the foregoing is merely presently preferred embodiments of the present invention, all equalizations made according to scope of the present invention patent
Change and modification, should all belong to the covering scope of patent of the present invention.
Claims (4)
1.HDPE is molded push pipe, including push pipe body, it is characterised in that push pipe body includes internal layer, the core set from inside to outside
Layer and outer layer, internal layer is identical with the material component of outer layer, is mixed by 98.35% HDPE and 1.65% pigment, core
Layer is mixed by 83% HDPE, 6% inorganic mineral and 11% thermoplastic elastomer (TPE).
2. HDPE according to claim 1 is molded push pipe, it is characterised in that:Push pipe body is existed by internal layer, sandwich layer and outer layer
Through chromium plating process and die face caustic dip, and uniform fusion co-extrusion and shape in the hard steel mould through oil spraying or siliceous spray
Into.
3. HDPE according to claim 1 is molded push pipe, it is characterised in that:The pigment includes 0.5% yellow uitramarine,
0.1% red pigment, 1% blue pigment and 0.05% charcoal blacks.
4. HDPE according to claim 1 is molded push pipe, it is characterised in that:Internal layer is identical with the wall thickness of outer layer, is
0.4-0.6mm, the wall thickness of sandwich layer is 1.9-2.4mm and the density of sandwich layer is 1.2-1.8g/cm3。