CN107963732A - A kind of preparation method of recirculated cooling water corrosion inhibiting and descaling agent - Google Patents
A kind of preparation method of recirculated cooling water corrosion inhibiting and descaling agent Download PDFInfo
- Publication number
- CN107963732A CN107963732A CN201711470782.5A CN201711470782A CN107963732A CN 107963732 A CN107963732 A CN 107963732A CN 201711470782 A CN201711470782 A CN 201711470782A CN 107963732 A CN107963732 A CN 107963732A
- Authority
- CN
- China
- Prior art keywords
- cooling water
- magnetic field
- ultrasonic wave
- recirculated cooling
- corrosion inhibiting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
A kind of preparation method of recirculated cooling water corrosion inhibiting and descaling agent of the present invention, including step:The each component of corrresponding quality percentage is stirred 30min by S100 at normal temperatures and pressures, is uniformly mixed, is obtained mixture;And mixture is placed in the reaction kettle equipped with ultrasonic wave and ultrastrong magnetic field by S200, by being condensed into dope under the synergistic effect in ultrasonic wave and magnetic field, the recirculated cooling water corrosion inhibiting and descaling agent is made, wherein, the power of the ultrasonic wave is 50w, and the intensity of ultrastrong magnetic field is 20T.Made recirculated cooling water corrosion inhibiting and descaling agent has the mobility for improving sludge, strengthens scale-inhibiting properties.
Description
The present invention is divisional application, and former number of patent application is CN201511007496.6, and the applying date is on December 18th, 2015, specially
The artificial Ningbo high and new technology industrial development zone Xia Yuan Science and Technology Ltd.s of economic rights.
Technical field
The present invention relates to a kind of water treatment field, is a kind of corrosion inhibiting and descaling agent suitable for recirculated cooling water specifically
And preparation method thereof.
Background technology
With the fast development of society, the ratio that industrial water consumption accounts for national water consumption is increasing year by year, and water resource is serious
Shortage.At present, not only pollution environment is arranged outside a large amount of municipal sewages in China and also wastes recycling resource, carries out municipal sewage warp
It is one of effective means for alleviating water scarcity problem to be used for recirculated cooling water after biochemical treatment.Most recirculating cooling water system
Requirement to water quality is not very harsh, and for municipal sewage after secondary biochemical treatment, water quality is relatively simple, and with being back to, circulation is cold
But the great potential of water and wide application prospect.But equipment list usually occurs in recirculating cooling water system operational process
Face fouling and the phenomenon of corrosion, influence its normal operation, industrial production can be not only influenced when serious even makes whole system
Paralysis.
Contain substantial amounts of inorganic ions (such as Ca in municipal sewage2+、Mg2+、SO4 2-、Cl-) and a small amount of organic matter, especially
Ca2+、Mg2+、SO4 2-And Cl-Under concentration several times and hot conditions, it is easy to cause in recirculating cooling water system equipment surface shape
Into mineral scale, and the high salinity under the conditions of concentration can make the etching problem of system more serious.
The effective means that corrosion inhibiting and descaling agent is control system corrosion and fouling is added in recirculated cooling water.Study at present
Compare typically poly-aspartate in green inorganic agent, such as disclosed in the patent of invention of Publication No. CN101412568B
One kind utilizes poly-aspartate, aminotrimethylenephosphonic acid, hydrolyzed maleic anhydride, acrylic acid and 2- acrylamide -2- methyl-props
A kind of circulating water antisludging agent prepared by sulfonic acid copolymer, polyacrylic acid and water, its have it is safe and reliable, be easy to configuration, user
Just the features such as, but poly-aspartate propylhomoserin higher price, and the general difficulty of corrosion and scale inhibition performance of itself reaches very high water
It is flat, and it can be only achieved preferable scale inhibition effect mainly by with phosphorous salt compound use.
On the other hand, reusing sewage is in recirculated cooling water, and particularly high salt, the waste water of high conductivity are in concentration process
In its there is corrosion factor more stronger than industrial water, original corrosion-mitigation scale-inhibition agent prescription can not be applicable in, exploitation be based on city
Newly formula is to solve urban sewage recycling in the key technology of cooling water problems to the corrosion inhibiting and descaling agent of biochemical sewage effluent quality.
The content of the invention
It is a primary object of the present invention to provide a kind of preparation method of recirculated cooling water corrosion inhibiting and descaling agent, it is suitable for work
Industry recirculating cooling water system and high concentration multiple, the recycling of perishable water quality, to realize high-salt wastewater in recirculated cooling water
In reach the effect of anticorrosion, good antiscale property, low emission.
To achieve the above objectives, the technical solution adopted by the present invention is:A kind of recirculated cooling water corrosion inhibiting and descaling agent is by poly- third
Acrylamide, sodium gluconate, aminotrimethylene phosphoric acid, ammonium molybdate, cyclohexylamine, surfactant, plant extracts, preservative
And water composition, wherein, the plant extracts is made of gallic acid, chlorogenic acid, nutgall tannin and Ellagitannins.
An embodiment according to the present invention, the mass percent of the recirculated cooling water corrosion inhibiting and descaling agent constitutive material are:
20%~30% polyacrylamide, 5%~15% sodium gluconate, 10%~18% aminotrimethylene phosphoric acid, 2%~6%
Ammonium molybdate, 8~15% cyclohexylamine, 20%~35% plant extracts, 0.5%~5% surfactant and 1%~5% are anti-
Rotten agent, remaining is deionized water.
An embodiment according to the present invention, the preservative are selected from zinc sulfate, 1,3- dibutyl benzotriazole and hexafluoro
The one or more of phosphoric acid Diacetone Acrylamide.
An embodiment according to the present invention, component in plant extracts using mass percent as:20%~40% does not eat
Sub- acid, 10%~25% chlorogenic acid, 15%~35% nutgall tannin, 20%~30% Ellagitannins.
An embodiment according to the present invention, the surfactant is in neopelex and polyethylene glycol
It is one or two kinds of.
A kind of preparation method of recirculated cooling water corrosion inhibiting and descaling agent, it includes step:
The each component of corrresponding quality percentage is stirred 30min by S100 at normal temperatures and pressures, is uniformly mixed, is obtained mixture;
And
Mixture is placed in the reaction kettle equipped with ultrasonic wave and ultrastrong magnetic field by S200, passes through the collaboration in ultrasonic wave and magnetic field
Dope is condensed under effect, the recirculated cooling water corrosion inhibiting and descaling agent is made.
An embodiment according to the present invention, the power of the ultrasonic wave in the step S200 are 20w~100w, ultrastrong magnetic field
Intensity be 10T~20T.
An embodiment according to the present invention, the power of the ultrasonic wave is 50w, and the intensity of ultrastrong magnetic field is 20T.
Beneficial effects of the present invention are:
1st, on the one hand polyacrylamide, sodium gluconate and aminotrimethylene phosphoric acid can and be circulated by acting synergistically
The incrustation scale reaction generated in water makes it gradually decompose, and on the other hand can strengthen and the calcium in recirculated water, magnesium plasma
Chelation simultaneously has distortion of lattice performance, so as to improve the mobility of sludge, strengthens scale-inhibiting properties;
2nd, the collective effect of ammonium molybdate and cyclohexylamine can not only be with Cl-Occur in metallic surface passivating film fault location " competing
Strive absorption ", the anti-Cl of enhancing passivating film-The corrosion of chloride under the performance of spot corrosion, particularly hot conditions, and can remove and follow
Sour gas in ring water, suppresses it and corrodes in pipe-line system;
3rd, the gallic acid in plant extracts, chlorogenic acid, nutgall tannin and Ellagitannins component are able to assist anti-
Rotten agent quick adsorption forms one layer of very thin film in metal surface, protects the metal from hazardous medium in air and water, particularly
High concentration Cl-Corrosion so that strengthen corrosion mitigating effect;On the other hand it can be with cooperative reinforcing to Ca in water2+、Mg2+Deng inorganic ions
Chelating ability, and then strengthen scale inhibition effect.
Embodiment
It is described below for disclosing the present invention so that those skilled in the art can realize the present invention.It is excellent in being described below
Embodiment is selected to be only used as illustrating, it may occur to persons skilled in the art that other obvious modifications.
A kind of recirculated cooling water corrosion inhibiting and descaling agent is by polyacrylamide, sodium gluconate, aminotrimethylene phosphoric acid, molybdic acid
Ammonium, cyclohexylamine, surfactant, plant extracts, preservative and water composition, wherein, the plant extracts by gallic acid,
Chlorogenic acid, nutgall tannin and Ellagitannins composition.
Wherein, the polyacrylamide in the recirculated cooling water corrosion inhibiting and descaling agent, sodium gluconate and amino trimethylene first
On the one hand base phosphoric acid can make it gradually decompose by acting synergistically with the incrustation scale reaction generated in recirculated water, on the other hand
Can strengthen with the calcium in recirculated water, magnesium plasma chelation and there is distortion of lattice performance, so as to improve the stream of sludge
Dynamic property, strengthens scale-inhibiting properties.
Wherein, the collective effect of ammonium molybdate and cyclohexylamine can not only be with Cl-Occur in metallic surface passivating film fault location
" competitive Adsorption ", the anti-Cl of enhancing passivating film-The corrosion of chloride under the performance of spot corrosion, particularly hot conditions, and can take off
Except the sour gas in recirculated water, suppress it and corrode in pipe-line system.
Wherein, the gallic acid in plant extracts, chlorogenic acid, nutgall tannin and Ellagitannins component are assisted
Preservative quick adsorption forms one layer of very thin film in metal surface, protects the metal from hazardous medium in air and water, especially
It is high concentration Cl-Corrosion so that strengthen corrosion mitigating effect;On the other hand it can be with cooperative reinforcing to Ca in water2+、Mg2+Etc. it is inorganic from
The chelating ability of son, and then strengthen scale inhibition effect.
The preservative is selected from the one of zinc sulfate, 1,3- dibutyl benzotriazole and hexafluorophosphoric acid Diacetone Acrylamide
Kind is a variety of.
Wherein, 1,3- dibutyl benzotriazole, zinc sulfate and hexafluorophosphoric acid Diacetone Acrylamide are able in carbon respectively
The surface of steel, copper and stainless steel forms one layer of fine and close protective film, effectively completely cuts off carbon steel, copper or the surface of stainless steel and oxygen connects
Touch, corrosion mitigating effect is good, effectively prevents in recirculating cooling water system and highly enriched processing procedure to carbon steel, copper and stainless steel
Corrosion.
The mass percent of the recirculated cooling water corrosion inhibiting and descaling agent constitutive material is:20%~30% polyacrylamide,
5%~15% sodium gluconate, 10%~18% aminotrimethylene phosphoric acid, 2%~6% ammonium molybdate, 8~15% cyclohexylamine,
20%~35% plant extracts, 0.5%~5% surfactant and 1%~5% preservative, remaining is deionized water.
Wherein, the component in plant extracts using mass percent as:Gallic acid 20%~40%, chlorogenic acid 10%~
25%th, nutgall tannin 15%~35%, Ellagitannins 20%~30%.
The surfactant is selected from one or both of neopelex and polyethylene glycol.
A kind of preparation method of recirculated cooling water corrosion inhibiting and descaling agent, it includes step:
The each component of corrresponding quality percentage is stirred 30min by S100 at normal temperatures and pressures, is uniformly mixed, is obtained mixture;
And
Mixture is placed in the reaction kettle equipped with ultrasonic wave and ultrastrong magnetic field by S200, passes through the collaboration in ultrasonic wave and magnetic field
Dope is condensed under effect, the recirculated cooling water corrosion inhibiting and descaling agent is made.
Wherein, the power of the ultrasonic wave in the step S200 is 20w~100w, the intensity of ultrastrong magnetic field for 10T~
20T。
Preferably, the power of the ultrasonic wave is 50w, and the intensity of ultrastrong magnetic field is 20T.
The recirculated cooling water corrosion inhibiting and descaling agent is with raw material sources are extensive, production cost is low and exists in use
Excellent anticorrosion-antiscaling effect is can reach under low concentration, further saves processing cost.
In addition, the recirculated cooling water corrosion inhibiting and descaling agent is applied to industrial circulating cooling water system, can extend using week
Phase, ensures being smoothed out for enterprise's production, and substantially reduce enterprise uses water cost.The heat transfer coefficient of equipment, drop are improved at the same time
Low equipment energy consumption.
When measuring product corrosion and scale inhibition performance, product prepared by embodiment one to embodiment eight is revolved for Q255 steel discs
Turn coupon test.Experiment condition is Ca2+Concentration 800mg/L, Mg2+Concentration 600mg/L, Cl-Concentration 150000mg/L, pH value are
10, product adds concentration 30mg/L, and temperature 50 C, measures its anticorrosion-antiscaling effect after constant temperature 120h.
Embodiment one
The mass percentage of the recirculated cooling water corrosion inhibiting and descaling agent constitutive material is:20% polyacrylamide, 5% Portugal
Grape sodium saccharate, 10% aminotrimethylene phosphoric acid, 6% ammonium molybdate, 15% cyclohexylamine, 35% plant extracts, 5% surface-active
Agent and 4% preservative, remaining is deionized water.Wherein, the component in plant extracts using mass percent as:20% does not eat
Sub- acid, 25% chlorogenic acid, 35% nutgall tannin, 20% Ellagitannins.After above-mentioned each component is distinguished feeding according to mass ratio
Stirring 30min makes it after mixing at normal temperatures and pressures, then is placed in the reaction kettle equipped with ultrasonic wave and ultrastrong magnetic field into one
Step carry out concentration make mixed solution present it is thick, wherein the power of ultrasonic wave is 50w, and the intensity in ultrastrong magnetic field magnetic field is
20T.The corrosion inhibition rate of the measure of the results show present invention is 99.5%, scale inhibition performance 99.8%.
Embodiment two
The mass percentage of the recirculated cooling water corrosion inhibiting and descaling agent constitutive material is:30% polyacrylamide, 10%
Sodium gluconate, 15% aminotrimethylene phosphoric acid, 2% ammonium molybdate, 12% cyclohexylamine, 28% plant extracts, 0.5% surface
Activating agent and 2.5% preservative, remaining is deionized water.Wherein, the component in plant extracts using mass percent as:
20% gallic acid, 25% chlorogenic acid, 35% nutgall tannin, 20% Ellagitannins.By above-mentioned each component according to quality score
Stirring 30min at normal temperatures and pressures after other feeding makes it after mixing, then is placed in the reaction equipped with ultrasonic wave and ultrastrong magnetic field
Further carried out in kettle concentration make mixed solution present it is thick, wherein the power of ultrasonic wave is 50w, ultrastrong magnetic field magnetic field
Intensity is 20T.The corrosion inhibition rate of the measure of the results show present invention is 97.3%, scale inhibition performance 97.4%.
Embodiment three
The mass percentage of the recirculated cooling water corrosion inhibiting and descaling agent constitutive material is:30% polyacrylamide, 10%
Sodium gluconate, 15% aminotrimethylene phosphoric acid, 2% ammonium molybdate, 12% cyclohexylamine, 28% plant extracts, 0.5% surface
Activating agent and 2.5% preservative, remaining is deionized water.Wherein, the component in plant extracts using mass percent as:
30% gallic acid, 17% chlorogenic acid, 25% nutgall tannin, 27% Ellagitannins.By above-mentioned each component according to quality score
Stirring 30min at normal temperatures and pressures after other feeding makes it after mixing, then is placed in the reaction equipped with ultrasonic wave and ultrastrong magnetic field
Further carried out in kettle concentration make mixed solution present it is thick, wherein the power of ultrasonic wave is 50w, ultrastrong magnetic field magnetic field
Intensity is 20T.The corrosion inhibition rate of the measure of the results show present invention is 98.6%, scale inhibition performance 98.5%.
Example IV
The mass percentage of the recirculated cooling water corrosion inhibiting and descaling agent constitutive material is:25% polyacrylamide, 15%
Sodium gluconate, 18% aminotrimethylene phosphoric acid, 4% ammonium molybdate, 8% cyclohexylamine, 20% plant extracts, 5% surface are lived
Property agent and 5% preservative, remaining is deionized water.Wherein, the component in plant extracts using mass percent as:40% does not have
Gallate-based, 15% chlorogenic acid, 15% nutgall tannin, 30% Ellagitannins.Above-mentioned each component is distinguished into feeding according to mass ratio
Afterwards at normal temperatures and pressures stirring 30min make it after mixing, then be placed in the reaction kettle equipped with ultrasonic wave and ultrastrong magnetic field into
One step carry out concentration make mixed solution present it is thick, wherein the power of ultrasonic wave is 50w, and the intensity in ultrastrong magnetic field magnetic field is
20T.The corrosion inhibition rate of the measure of the results show present invention is 99.6%, scale inhibition performance 99.8%.
Embodiment five
The mass percentage of the recirculated cooling water corrosion inhibiting and descaling agent constitutive material is:25% polyacrylamide, 15%
Sodium gluconate, 18% aminotrimethylene phosphoric acid, 4% ammonium molybdate, 8% cyclohexylamine, 25% plant extracts, 4% surface are lived
Property agent and 1% preservative, remaining is deionized water.Wherein, the component in plant extracts using mass percent as:35% does not have
Gallate-based, 10% chlorogenic acid, 15% nutgall tannin, 30% Ellagitannins.Above-mentioned each component is distinguished into feeding according to mass ratio
Afterwards at normal temperatures and pressures stirring 30min make it after mixing, then be placed in the reaction kettle equipped with ultrasonic wave and ultrastrong magnetic field into
One step carry out concentration make mixed solution present it is thick, wherein the power of ultrasonic wave is 50w, and the intensity in ultrastrong magnetic field magnetic field is
20T.The corrosion inhibition rate of the measure of the results show present invention is 98.9%, scale inhibition performance 99.1%.
Embodiment six
The mass percentage of the recirculated cooling water corrosion inhibiting and descaling agent constitutive material is:25% polyacrylamide, 15%
Sodium gluconate, 18% aminotrimethylene phosphoric acid, 4% ammonium molybdate, 8% cyclohexylamine, 20% plant extracts, 5% surface are lived
Property agent and 5% preservative, remaining is deionized water.Wherein, the component in plant extracts using mass percent as:40% does not have
Gallate-based, 15% chlorogenic acid, 15% nutgall tannin, 30% Ellagitannins.Above-mentioned each component is distinguished into feeding according to mass ratio
Afterwards at normal temperatures and pressures stirring 30min make it after mixing, then be placed in the reaction kettle equipped with ultrasonic wave and ultrastrong magnetic field into
One step carry out concentration make mixed solution present it is thick, wherein the power of ultrasonic wave is 20w, and the intensity in ultrastrong magnetic field magnetic field is
10T.The corrosion inhibition rate of the measure of the results show present invention is 90.2%, scale inhibition performance 91.6%.
Embodiment seven
The mass percentage of the recirculated cooling water corrosion inhibiting and descaling agent constitutive material is:25% polyacrylamide, 15%
Sodium gluconate, 18% aminotrimethylene phosphoric acid, 4% ammonium molybdate, 8% cyclohexylamine, 20% plant extracts, 5% surface are lived
Property agent and 5% preservative, remaining is deionized water.Wherein, the component in plant extracts using mass percent as:40% does not have
Gallate-based, 15% chlorogenic acid, 15% nutgall tannin, 30% Ellagitannins.Above-mentioned each component is distinguished into feeding according to mass ratio
Afterwards at normal temperatures and pressures stirring 30min make it after mixing, then be placed in the reaction kettle equipped with ultrasonic wave and ultrastrong magnetic field into
That mixed solution is presented is thick for the concentration that carries out of one step, and the wherein power of ultrasonic wave is 100w, the intensity in ultrastrong magnetic field magnetic field
For 20T.The corrosion inhibition rate of the measure of the results show present invention is 95.3%, scale inhibition performance 94.6%.
Embodiment eight
The mass percentage of the recirculated cooling water corrosion inhibiting and descaling agent constitutive material is:25% polyacrylamide, 15%
Sodium gluconate, 18% aminotrimethylene phosphoric acid, 4% ammonium molybdate, 8% cyclohexylamine, 20% plant extracts, 5% surface are lived
Property agent and 5% preservative, remaining is deionized water.Wherein, the component in plant extracts using mass percent as:40% does not have
Gallate-based, 15% chlorogenic acid, 15% nutgall tannin, 30% Ellagitannins.Above-mentioned each component is distinguished into feeding according to mass ratio
Afterwards at normal temperatures and pressures stirring 30min make it after mixing, then be placed in the reaction kettle equipped with ultrasonic wave and ultrastrong magnetic field into
One step carry out concentration make mixed solution present it is thick, wherein the power of ultrasonic wave is 50w, and the intensity in ultrastrong magnetic field magnetic field is
15T.The corrosion inhibition rate of the measure of the results show present invention is 98.7%, scale inhibition performance 99.3%.
Embodiment nine
The mass percentage of the recirculated cooling water corrosion inhibiting and descaling agent constitutive material is:25% polyacrylamide, 15%
Sodium gluconate, 18% aminotrimethylene phosphoric acid, 4% ammonium molybdate, 8% cyclohexylamine, 20% plant extracts, 5% surface are lived
Property agent and 5% preservative, remaining is deionized water.Wherein, the component in plant extracts using mass percent as:40% does not have
Gallate-based, 15% chlorogenic acid, 15% nutgall tannin, 30% Ellagitannins.Above-mentioned each component is distinguished into feeding according to mass ratio
Afterwards at normal temperatures and pressures stirring 30min make it after mixing, then be placed in the reaction kettle equipped with ultrasonic wave and ultrastrong magnetic field into
One step carry out concentration make mixed solution present it is thick, wherein the power of ultrasonic wave is 50w, and the intensity in ultrastrong magnetic field magnetic field is
20T。
The product of preparation is tested for copper sheet rotary hanging plate.Experiment condition is Ca2+Concentration 800mg/L, Mg2+Concentration
600mg/L, Cl-Concentration 150000mg/L, pH value 10, product add concentration 30mg/L, and temperature 50 C, measures after constant temperature 120h
Its anticorrosion-antiscaling effect.
The corrosion inhibition rate of the measure of the results show present invention is 99.5%, scale inhibition performance 99.7%.
Embodiment ten
The mass percentage of the recirculated cooling water corrosion inhibiting and descaling agent constitutive material is:25% polyacrylamide, 15%
Sodium gluconate, 18% aminotrimethylene phosphoric acid, 4% ammonium molybdate, 8% cyclohexylamine, 20% plant extracts, 5% surface are lived
Property agent and 5% preservative, remaining is deionized water.Wherein, the component in plant extracts using mass percent as:40% does not have
Gallate-based, 15% chlorogenic acid, 15% nutgall tannin, 30% Ellagitannins.Above-mentioned each component is distinguished into feeding according to mass ratio
Afterwards at normal temperatures and pressures stirring 30min make it after mixing, then be placed in the reaction kettle equipped with ultrasonic wave and ultrastrong magnetic field into
One step carry out concentration make mixed solution present it is thick, wherein the power of ultrasonic wave is 50w, and the intensity in ultrastrong magnetic field magnetic field is
20T。
The product of preparation is tested for stainless steel substrates rotary hanging plate.Experiment condition is Ca2+Concentration 800mg/L, Mg2+Concentration
600mg/L, Cl-Concentration 150000mg/L, pH value 10, product add concentration 30mg/L, and temperature 50 C, measures after constant temperature 120h
Its anticorrosion-antiscaling effect.
The corrosion inhibition rate of the measure of the results show present invention is 99.6%, scale inhibition performance 99.8%.
From specific embodiment one to embodiment ten, the recirculated cooling water corrosion inhibiting and descaling agent can be applied to highly concentrated demagnification
(such as make the benefit of cooling circulating water with high-salt wastewater or other intractable industrial wastewaters in number (more than 10 times), perishable water quality
Water-filling), it can almost reach the effect of not burn into non-scaling, it is industrial particularly when chlorine ion concentration is up to 10~150,000 mg/L
Circulation (carbon steel, stainless steel and copper material) can also reach anticorrosion, good antiscale property, thus both saved supplement water and
The burden of factory's water process is alleviated, and realizes the effect of waste water low-discharging.
The corrosion inhibiting and descaling agent of the present invention has that raw material sources are extensive, production cost is low and in use relatively low dense
Degree is lower to can reach excellent anticorrosion-antiscaling effect, further saves processing cost.
3) corrosion inhibiting and descaling agent of the invention is applied to industrial circulating cooling water system, can extend service life, ensures enterprise
Industry production is smoothed out, and substantially reduce enterprise uses water cost.The heat transfer coefficient of equipment is improved at the same time, reduces equipment energy
Consumption.
Basic principle, main feature and the advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and what is described in the above embodiment and the description is only the present invention
Principle, various changes and modifications of the present invention are possible without departing from the spirit and scope of the present invention, these change and
Improvement is both fallen within the range of claimed invention.The protection domain of application claims by appended claims and its
Equivalent defines.
Claims (1)
1. a kind of preparation method of recirculated cooling water corrosion inhibiting and descaling agent, it is characterised in that including step:
The mass percent of raw material is:20%~30% polyacrylamide, 5%~15% sodium gluconate, 10%~18% ammonia
Base trimethylene phosphoric acid, 2%~6% ammonium molybdate, 8~15% cyclohexylamine, 20%~35% plant extracts, 0.5%~5% table
Face activating agent and 1%~5% preservative, remaining is deionized water, wherein, preservative is selected from zinc sulfate, 1,3- dibutyl benzene
And the one or more of triazole and hexafluorophosphoric acid Diacetone Acrylamide, the component in plant extracts is with mass percent
For:20%~40% gallic acid, 10%~25% chlorogenic acid, 15%~35% nutgall tannin, 20%~30% tan spend list
Rather, the surfactant is selected from one or both of neopelex and polyethylene glycol;
The each component of corrresponding quality percentage is stirred 30min by S100 at normal temperatures and pressures, is uniformly mixed, is obtained mixture;And
Mixture is placed in the reaction kettle equipped with ultrasonic wave and ultrastrong magnetic field by S200, passes through ultrasonic wave and the synergistic effect in magnetic field
Under be condensed into dope, the recirculated cooling water corrosion inhibiting and descaling agent is made, wherein, the power of the ultrasonic wave is 50w, super-strong magnetic
The intensity of field is 20T.