CN107955923A - A kind of mold materials and preparation method thereof - Google Patents
A kind of mold materials and preparation method thereof Download PDFInfo
- Publication number
- CN107955923A CN107955923A CN201610897731.XA CN201610897731A CN107955923A CN 107955923 A CN107955923 A CN 107955923A CN 201610897731 A CN201610897731 A CN 201610897731A CN 107955923 A CN107955923 A CN 107955923A
- Authority
- CN
- China
- Prior art keywords
- mold materials
- preparation
- mould
- quenched
- gear
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to a kind of mold materials and preparation method thereof, by weight including following component:C 0.35%~0.45%, Cr 13%~15%, Mn 0.5%~1.00%, Si 0.2%~1.00%, S≤0.035%, Ni0.1%~1.0%, Mo 0.8%~1.5%;Concrete technology is the three phases using smelting, forging and module modifier treatment.
Description
Technical field
The invention belongs to the design studies field of plastic mould material, material and preparation side in particular to a kind of mould
Method.
Background technology
With the development of modernization industry, the application of mould is more and more extensive, in automobile, electronics, instrument and meter, household electrical appliances, aviation
In the products such as space flight, building materials, motor and Communication Equipment, the parts of about 60%-80% will rely on mould machine-shaping, therefore quilt
Referred to as " mother of industry ".Mould is the important component of equipment manufacture, its interrelationship between industries is high, is industrial upgrading and technology
One of progressive important leverage.
Mould is the part of most critical in gear injection molding.The application range of gear die is broadly divided into three sides
Face:Plastic gear is with mould, powder metallurgical gear with mould and finish forge bevel gear mould.Wherein, plastic gear mould
Demand is bigger.Gear is more accurate part, and the deviation of little bit may influence the performance of whole gear.Plastics
Gear die seems simple, be in fact it is most complicated, such as module, helical angle size, hole position determine etc. factor all
Influence the design of gear die.Precision problem, life problems are the most important things of gear die research.
The content of the invention
The present invention uses following technical scheme:
A kind of mold materials and preparation method thereof, by weight including following component:C 0.35%~0.45%, Cr 13%~
15%th, Mn 0.5%~1.00%, Si 0.2%~1.00%, S≤0.035%, Mo 0.8%~1.5%,;The mould
Steel may be only available for manufacture effective dimensions 100-400mm sized molds, optional Ni0.1%~1.0%.
Embodiment
Embodiment 1
A kind of mold materials and preparation method thereof, by weight including following component:C 0.35%~0.45%, Cr 13%~
15%th, Mn 0.5%~1.00%, Si 0.2%~1.00%, Ni0.1%~1.0%, S≤0.035%, Mo 0.8%
~1.5%,;The mould steel may be only available for manufacture effective dimensions 100-400mm sized molds.
Concrete technology is the three phases using smelting, forging and module modifier treatment.
It is quenched or high temperature is quenched that low temperature is carried out in 430~550 or 700~800 temperature ranges.
Embodiment 2:
A kind of mold materials, specifically include following component by weight:
C 0.35%~0.45%, Cr 13%~15%, Mn 0.5%~1.00%, Si 0.2%~1.00%,
Ni0.1%~1.0%, S≤0.035%, Mo 0.8%~1.5%,;The mould steel may be only available for manufacture effective dimensions
100~400mm sized molds, Ni 0.1%~1.0%, concrete technology are using smelting, forging and module modifier treatment
Three phases.
Claims (2)
1. a kind of mold materials, it is characterised in that by weight including following component:C 0.35%~0.45%, Cr 13%~
15%th, Mn 0.5%~1.00%, Si 0.2%~1.00%, S≤0.035%, Mo 0.8%~1.5%;The mould steel
Manufacture effective dimensions 100-400mm sized molds are may be only available for, concrete technology is using smelting, forging and the quenched place of module
Manage three phases.
2. the material according to claim 1, it is characterised in that modifier treatment is:In 430~550 or 700~800 temperature
Section progress low temperature is quenched or high temperature is quenched.