CN107955564A - A kind of pressure gelatin with low peel strength and preparation method thereof - Google Patents
A kind of pressure gelatin with low peel strength and preparation method thereof Download PDFInfo
- Publication number
- CN107955564A CN107955564A CN201711277186.5A CN201711277186A CN107955564A CN 107955564 A CN107955564 A CN 107955564A CN 201711277186 A CN201711277186 A CN 201711277186A CN 107955564 A CN107955564 A CN 107955564A
- Authority
- CN
- China
- Prior art keywords
- parts
- peel strength
- pressure
- gelatin
- low peel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of pressure gelatin with low peel strength and preparation method thereof, the pressure gelatin includes the component of following parts by weight：60 80 parts of propyl methacrylate, 58 parts of methyl methacrylate, 36 parts of acrylic acid, 8 13 parts of diatom ooze, 25 parts of Nano titanium dioxide, 0.5 2 parts of initiator, 0.5 1 parts of dispersant, 0.5 1 parts of curing agent.A kind of pressure gelatin with low peel strength provided by the invention and preparation method thereof, mainly solve the problems, such as solve it is existing pressure gelatin binder present in peel strength it is excessive, it is easy residual matrix, by varying the formula and preparation process of existing pressure gelatin binder, make the peel strength of pressure gelatin binder only in below 6.58N/m, while ensureing that eye speculum can be fixed on circumference of eyes, eye speculum is facilitated to be taken off at circumference of eyes, after eye speculum is taken off, skin surface noresidue, without sticky sense when finger touches, surface lubricous dry, using effect are good.
Description
Technical field
The present invention relates to medical pressure sensitive adhesive technical field, more particularly to a kind of pressure gelatin and its system with low peel strength
Preparation Method.
Background technology
Eye speculum is hospital ophthalmology Special medical equipment, it is used to expand eyelid（Eyes above and below two during eyelid
Block tissue）, for majority for making ophthalmologic operation, it is the surgical field of view for expanding doctor that it, which is acted on,.General eye speculum is screw turn-knob
Eye speculum, its operating method are：Eyelid is caught on the hook portion of eye speculum, then precession screw rod, eyelid bar is driven at both ends（That is the application
Clamp arm）Outside diffusion, eyelid are expanded.It follows that need what both hands operated during traditional eye speculum, i.e. a hand need
Eye speculum is held, to stablize its position, its another hand needs rotary screw, and to expand eyelid, so operation is to main operation
For hand, it appears it is rather troublesome, particularly in ophthalmologic operation is done, general operating doctor when being not required secondary manipulator to help,
In order to expand surgical field of view, its temporary adandonment of having to is ongoing to be operated to operate eye speculum, and this operation midway is suspended
Situation be easy to cause operation contingency, be unfavorable for that operating doctor is smooth to perform the operation, and eyelid is operated out as secondary manipulator
During device, since the position of eye is narrow and small, space is limited, and double operated to eye undoubtedly increases operating difficulty, also easily
Accident surgery is caused, there are inconvenient problem with use for the traditional eye speculum operated therefore, it is necessary to both hands.
Realize that eye speculum and the fixation of circumference of eyes position are a kind of possible fixed forms by pressure sensitive adhesive binding agent,
Eye speculum is fixed and is bonded in around eye, a hand can be avoided the need for and go to buttress the trouble of eye speculum, and then can be
A hand is liberated in surgical procedure, unfortunately, traditional eye speculum simultaneously has this design, while existing medical pressure sensitive adhesive is used
In on medical adhesive tape, the peel strength of medical adhesive tape is not less than 1.541N/cm, and peel strength is excessive, when it is soft with circumference of eyes
After soft skin bonding, it is not easy to tear and, skin is drawn its length long, and secondary injury can be caused to patient, meanwhile, it is existing
Some pressure sensitive adhesives when in use, can still have the problem of leaving residual glue, after shutting down adhesive tape, the skin surface at glued place
Sticky sense is had after being touched with hand, the causative agent and residue being easily infected with surgical procedure, after patient carries out operated eye, contamination
Causative agent and residue easy infection eye, thereby result in circumference of eyes inflammation, redness, be unfavorable for the recovery of eyes of patients wound.
The content of the invention
The goal of the invention of the present invention is：For above-mentioned problem, there is provided a kind of pressure with low peel strength is bright
Glue and preparation method thereof, by varying the formula and preparation process of existing pressure gelatin binder, reduces the stripping of pressure gelatin binder
From intensity, so solve the problems, such as it is existing pressure gelatin binder present in peel strength it is excessive, it is easy residual matrix, ensure open
While eyelid device can be fixed on circumference of eyes, eye speculum is facilitated to be taken off at circumference of eyes.
The technical solution adopted by the present invention is as follows：A kind of pressure gelatin with low peel strength, it is characterised in that the pressure
Gelatin includes the component of following parts by weight：60-80 parts of propyl methacrylate, 5-8 parts of methyl methacrylate, acrylic acid 3-6
Part, 8-13 parts of diatom ooze, 2-5 parts of Nano titanium dioxide, 0.5-2 parts of initiator, 0.5-1 parts of dispersant, curing agent 0.5-1
Part.
Further, the granularity of diatom ooze is 300-400 mesh.
Further, dispersant is selected from sodium tripolyphosphate, calgon, methyl anyl alcohol, polyacrylamide and fatty acid polyglycol
One or more in glycol ester.
Further, the curing agent is the one or more in magnesium acetate, aluminium acetylacetonate and acetylacetone,2,4-pentanedione zirconium.
Present invention additionally comprises a kind of preparation method of the pressure gelatin with low peel strength, it is characterised in that including following
Step：
It is step 1, the propyl methacrylate of proportional quantity, methyl methacrylate, acrylic acid and initiator is molten in ethyl acetate
Dissolved in agent, mixing speed is controlled in 180rad/min in course of dissolution, is then heated to 40-50 DEG C and is reacted, is gathered
Polymer solution；
Step 2, add diatom ooze and dispersant into polymer solution, is uniformly mixed, and mixing speed control exists（300-
350）Rad/min, whipping temp are controlled below 45 DEG C, obtain mixed solution；
Step 3, add Nano titanium dioxide and curing agent into mixed solution, is stirred under the rotating speed of 500rad/min
Uniformly, obtain glue, glue is coated on matrix to obtain the final product.
In conclusion by adopting the above-described technical solution, the beneficial effects of the invention are as follows：A kind of tool provided by the invention
There is pressure gelatin of low peel strength and preparation method thereof, mainly solve the peel strength present in existing pressure gelatin binder
The problem of excessive, easy residual matrix, by varying the formula and preparation process of existing pressure gelatin binder, make pressure gelatin binder
Peel strength only in below 6.58N/m, while ensureing that eye speculum can be fixed on circumference of eyes, facilitate eye speculum from eye
Place takes off around portion, and after eye speculum is taken off, skin surface noresidue, without sticky sense when finger touches, surface lubricous dry, makes
With working well.
Brief description of the drawings
Fig. 1 is a kind of eye speculum three dimensional structure diagram with slab construction of the present invention；
Fig. 2 is the eye speculum polycrystalline substance schematic diagram of the present invention.
Marked in figure：1 is tablet pedestal, and 2 be action pane, and 3 be hook portion, and 4 be rack, and 5 be regulation button, and 6 be ratch,
7 be elastic layer, and 8 be hand compression bar, and 9 be briquetting, and 10 bottom out disk for flexibility, and 11 be light-emitting component, and 12 be adjustment portion.
Embodiment
Below in conjunction with the accompanying drawings, the present invention is described in detail.
In order to make the purpose , technical scheme and advantage of the present invention be clearer, with reference to the accompanying drawings and embodiments, it is right
The present invention is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, and
It is not used in the restriction present invention.
As depicted in figs. 1 and 2, a kind of eye speculum with slab construction, including tablet pedestal 1, the middle part of tablet pedestal 1
Perforate forms action pane 2, eye is operated for operator, the edge of action pane 2 is symmetrical arranged a pair and is used for
The hook portion 3 of eyelid is caught on, the connecting pin of hook portion 3 is fixedly connected with rack 4, and hook portion 3 is inserted into tablet pedestal 1 simultaneously by rack 4
It is connected with tablet pedestal 1, rack 4 can be slided relative to tablet pedestal 1, and then change the relative distance between hook portion, tablet
Adjusting knob 5 is provided with pedestal 1, adjusting knob 5 includes ratch 6, and ratch 6 and rack 4 are engaged to form telescoping mechanism, work as tooth
When bar 6 rotates, ratch 6 is slided with carry-over bar 4 along the length direction of rack 4.The bottom of tablet pedestal 1 is bonded with for buffering pressure
The elastic layer 7 of power, elastic layer 7 have annular coil structures, it arranges that the thickness of elastic layer 7 is not along the base circle of tablet pedestal 1
Less than 4mm, the lower surface of elastic layer 7 coats one layer of pressure-sensitive adhesive layer（It is not drawn into figure）, and pass through PE films（It is not drawn into figure）
Pressure-sensitive adhesive layer is covered, in use, tearing PE films, the installation site of adjustment tablet pedestal 1, is glued tablet pedestal using pressure-sensitive adhesive layer
It is connected on around eye, and then the installation for completing eye speculum is fixed.Further say, elastic layer 7 is layer of silica gel or is rubber
Layer.
It is adhesively fixed for the ease of skin of the eye speculum preferably with circumference of eyes, hand splenium is provided with tablet pedestal 1,
Hand splenium includes running through tablet pedestal 1 and the hand compression bar 8 being fixedly connected vertical with tablet pedestal 1, and hand compression bar 8 is towards tablet pedestal
One end of 1 upper surface connects the briquetting 9 of disc-shaped structure, and the hand strut portion between 1 upper surface of briquetting 9 and tablet pedestal forms hand
Portion is held, in order to adjust the position of tablet pedestal 1 and circumference of eyes and angle, while easy to later stage eye speculum and skin phase point
From；Hand compression bar 8 is towards 1 lower face of tablet pedestal（That is bottom）One end connection bottom out disk 10 with the flexibility of horn shape, it is soft
Property bottom out disk 10 be used to preventing eye speculum during the pushing to eye and its around cause to damage, particularly prevent hook portion 3 from hitting
Hit eyeball.Correspondingly, along the axial direction of hand compression bar 8, flexibility bottoms out height of the height not less than elastic layer 7 of disk 10, with
It is Nian Jie with skin easy to tablet pedestal 1.
As an improvement embodiment, in order to adjust the visual field degree of action pane 2, the bottom of tablet pedestal 1 is also set
Lighting lamp device is equipped with, lighting device includes light-emitting component 11 and adjustment portion 12, and light-emitting component 11 and the bottom of tablet pedestal 1 are consolidated
Fixed connection, adjustment portion 12 are fixedly connected with the upper surface of tablet pedestal 1, and adjustment portion is with 12 in the luminance for adjusting light-emitting component 11
Degree, light-emitting component 11 and adjustment portion 12 are electrically connected with supply unit by circuit and form electrical circuit, and supply unit can be set
On tablet pedestal 1 or external power supply, i.e., when supply unit is external power supply, by external power lines with shining
Element connects to form electrical circuit with adjustment portion 12.
As an improvement embodiment, in order to solve traditional pressure sensitive glue sticking peel strength mistake when on soft skin
Greatly, easily residual matrix the problem of, the present invention provide it is a kind of there is relatively low peel strength, take off after without the remaining pressure-sensitive adhesive of matrix
Agent is tied, the pressure sensitive adhesive binding agent includes the component of following parts by weight：50-60 parts of acrylate soft monomer, acrylate is firmly single
4-7 parts of body, 3-5 parts of synthetic rubber, 4-7 parts of castor oil, 0.5-2 parts of initiator, 0.5-1 parts of vulcanizing agent.
In above-mentioned, the acrylate soft monomer is selected from ethyl methacrylate, propyl methacrylate, acrylic acid third
One or more in ester, isooctyl methacrylate and Isooctyl acrylate monomer, are preferably isooctyl methacrylate；Described third
One or more of the olefin(e) acid ester hard monomer in methyl methacrylate, methyl acrylate and vinylacetate, are preferably first
Base methyl acrylate；One or more of the synthetic rubber in butadiene-styrene rubber, Oppanol and butyl rubber, are preferably
Butadiene-styrene rubber；One kind in elemental sulfur, Vulcanization accelerator TMTD, benzoyl peroxide and urethanes of the vulcanizing agent or
It is a variety of, it is preferably Vulcanization accelerator TMTD.
In order to preferably implement pressure sensitive adhesive binding agent set forth above, the preparation method of pressure sensitive adhesive binding agent includes following step
Suddenly:
Step 1, weigh each component by weight, and acrylate soft monomer, acrylate hard monomer, initiator and castor oil are existed
60-90min is kneaded in open mill, obtains just mixed thing；
First mixed thing, be dissolved in suitable organic solvent by step 2, synthetic rubber is then added, under the rotating speed of 300rad/min
It is uniformly mixed in 50 DEG C, makes synthetic rubber dispersed, obtain milk；
Step 3, send milk into vulcanizing press and vulcanizing agent is added into milk vulcanized, and curing temperature is maintained at
40-60 DEG C, vulcanization time is controlled in 5-10s, and vulcanization pressure control obtains pressure sensitive adhesive after 1-2MPa, vulcanization.
Further, without the remaining pressure sensitive adhesive of matrix after there is relatively low peel strength, tear off the present invention also provides another kind,
The pressure gelatin includes the component of following parts by weight：60-80 parts of propyl methacrylate, 5-8 parts of methyl methacrylate, propylene
It is 3-6 parts sour, 8-13 parts of diatom ooze, 2-5 parts of Nano titanium dioxide, 0.5-2 parts of initiator, 0.5-1 parts of dispersant, curing agent
0.5-1 parts.
In above-mentioned, the granularity of diatom ooze is 300-400 mesh, and dispersant is selected from sodium tripolyphosphate, calgon, methylpent
One or more in alcohol, polyacrylamide and fatty acid polyethylene glycol ester, are preferably polyacrylamide；The curing agent is second
One or more in sour magnesium, aluminium acetylacetonate and acetylacetone,2,4-pentanedione zirconium, are preferably magnesium acetate.
The preparation method of pressure sensitive adhesive in above-mentioned comprises the following steps：
It is step 1, the propyl methacrylate of proportional quantity, methyl methacrylate, acrylic acid and initiator is molten in ethyl acetate
Dissolved in agent, mixing speed is controlled in 180rad/min in course of dissolution, is then heated to 40-50 DEG C and is reacted, is gathered
Polymer solution；
Step 2, add diatom ooze and dispersant into polymer solution, is uniformly mixed, and mixing speed control exists（300-
350）Rad/min, whipping temp are controlled below 45 DEG C, obtain mixed solution；
Step 3, add Nano titanium dioxide and curing agent into mixed solution, is stirred under the rotating speed of 500rad/min
Uniformly, obtain glue, glue is coated on matrix to obtain the final product.
In order to which the pressure sensitive adhesive binding agent and pressure sensitive adhesive of the present invention is better described, it is specific that Tables 1 and 2 lists part respectively
Embodiment, as shown in table 1.
1 pressure sensitive adhesive binding agent embodiment A1-A6 of table is formulated（In parts by weight）
2 pressure sensitive adhesive embodiment B1-B6 of table is formulated（In parts by weight）
Main performance is tested
Above-described embodiment A1-A6 and B1-B6 are coated on medical adhesive tape（Adhesive tape is zinc oxide breathable adhesive tape）, carry out following property
Can test：
Tack is tested：Measured according to GB4852-84 standards；
Hold sticky test：Measured according to GB4851-84 standards；
180 ° of peel strength tests：Measured according to GB2792-81 standards；
Matrix surface residue：Noresidue is visually observed.
Main performance is as shown in Table 3 and Table 4：
The Specifeca tion speeification of 3 pressure sensitive adhesive binding agent embodiment A1-A6 of table
The Specifeca tion speeification of 4 pressure sensitive adhesive embodiment B1-B6 of table
Above-described embodiment A1-A6 and embodiment B1-B6 are coated on to the bottom surface of tablet pedestal elastic layer, by tablet pedestal and human body
After circumference of eyes bonding, tablet pedestal is firmly secured to around eye, when carrying out cornea refractive corrective procedure, eye speculum
Any relative movement does not occur relative to eye, when removing eye speculum, can easily take eye speculum off, skin is not drawn substantially
Rise, the skin surface change unobvious of abutting edge, without sticky sense, surface lubricous dry, the eye of postoperative patient when finger touches
Surrounding is good without obvious red and swollen, erythema, using effect.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all essences in the present invention
All any modification, equivalent and improvement made within refreshing and principle etc., should all be included in the protection scope of the present invention.
Claims (5)
1. a kind of pressure gelatin with low peel strength, it is characterised in that the pressure gelatin includes the component of following parts by weight：First
60-80 parts of base propyl acrylate, 5-8 parts of methyl methacrylate, 3-6 parts of acrylic acid, 8-13 parts of diatom ooze, nanoscale titanium dioxide
2-5 parts of titanium, 0.5-2 parts of initiator, 0.5-1 parts of dispersant, 0.5-1 parts of curing agent.
2. there is the pressure gelatin of low peel strength as claimed in claim 1, it is characterised in that the granularity of diatom ooze is 300-
400 mesh.
3. there is the pressure gelatin of low peel strength as claimed in claim 1, it is characterised in that dispersant is selected from tripolyphosphate
One or more in sodium, calgon, methyl anyl alcohol, polyacrylamide and fatty acid polyethylene glycol ester.
4. as claimed in claim 1 have low peel strength pressure gelatin, it is characterised in that the curing agent for magnesium acetate,
One or more in aluminium acetylacetonate and acetylacetone,2,4-pentanedione zirconium.
5. the preparation method of the pressure gelatin with low peel strength as claimed in claim 1, it is characterised in that including following step
Suddenly：
It is step 1, the propyl methacrylate of proportional quantity, methyl methacrylate, acrylic acid and initiator is molten in ethyl acetate
Dissolved in agent, mixing speed is controlled in 180rad/min in course of dissolution, is then heated to 40-50 DEG C and is reacted, is gathered
Polymer solution；
Step 2, add diatom ooze and dispersant into polymer solution, is uniformly mixed, and mixing speed control exists（300-
350）Rad/min, whipping temp are controlled below 45 DEG C, obtain mixed solution；
Step 3, add Nano titanium dioxide and curing agent into mixed solution, is stirred under the rotating speed of 500rad/min
Uniformly, obtain glue, glue is coated on matrix to obtain the final product.