CN107955257A - One kind exhibition discoloration thick china - Google Patents

One kind exhibition discoloration thick china Download PDF

Info

Publication number
CN107955257A
CN107955257A CN201610908484.9A CN201610908484A CN107955257A CN 107955257 A CN107955257 A CN 107955257A CN 201610908484 A CN201610908484 A CN 201610908484A CN 107955257 A CN107955257 A CN 107955257A
Authority
CN
China
Prior art keywords
parts
thick china
discoloration
titanium dioxide
sorbierite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610908484.9A
Other languages
Chinese (zh)
Inventor
钱志刚
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Danyang Danli Exhibition Products Co Ltd
Original Assignee
Danyang Danli Exhibition Products Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Danyang Danli Exhibition Products Co Ltd filed Critical Danyang Danli Exhibition Products Co Ltd
Priority to CN201610908484.9A priority Critical patent/CN107955257A/en
Publication of CN107955257A publication Critical patent/CN107955257A/en
Pending legal-status Critical Current

Abstract

Puted on display the present invention relates to one kind and use discoloration thick china, mainly include photochromatic layer and thick china substrate；The photochromatic layer is made of the following component counted with mass fraction：5 10 parts of photochromic material, 30 50 parts of silica gel, 13 parts of adhesive, 23 parts of aniline, 12 parts of sodium hydrogensulfite, 0.5 1.5 parts of sorbierite；The thick china substrate is made of the following component counted with mass fraction：40 50 parts of polypropylene, 35 parts of titanium dioxide, 20 30 parts of expanded polystyrene (EPS), 15 parts of titanium dioxide, 35 parts of compound stabilizer, 34 parts of calcium phosphate, 25 parts of sorbierite, 5 10 parts of polyester fiber, 10 20 parts of epoxy resin.The thick china of the present invention has the characteristics that discoloration, colour fading excellent performance and good mechanical property.

Description

One kind exhibition discoloration thick china
Technical field
The present invention relates to exhibition thick china field, more particularly to a kind of exhibition discoloration thick china.
Background technology
With the development of the times, scientific and technological progress, especially in terms of construction industry finishing, to the smooth of sheet side, decorative pattern Beauty, it is corrosion-free and damage by worms, be easy to that the performance requirement of gluing etc. is higher and higher, and furniture industry and interior decoration want plate Ask also more and more diversified.General thick china has been unable to meet diversified development, and general thick china is there are of high cost, The shortcomings that heavier-weight, moisture-proof, high temperature resistant, poor wear-resisting property.Advertisement arrangement of the photosensitive color-changing thick china particularly suitable for outdoor, Can be photosensitive fine when and change colour, show very beautiful visual effect.
The content of the invention
In order to solve the above-mentioned technical problem, there is provided a kind of photochromic response is fast and fading rate also fast discoloration veneer Plate, the present invention provide technical solution：
One kind exhibition discoloration thick china, including photochromatic layer and thick china substrate；The photochromatic layer by with The following component composition of mass fraction meter：5-10 parts of photochromic material, 30-50 parts of silica gel, 1-3 parts of adhesive, aniline 2-3 Part, 1-2 parts of sodium hydrogensulfite, 0.5-1.5 parts of sorbierite；The thick china substrate is by the following component group in terms of mass fraction Into：40-50 parts of polypropylene, 3-5 parts of titanium dioxide, 20-30 parts of expanded polystyrene (EPS), 1-5 parts of titanium dioxide, compound stabilizer 3-5 Part, 3-4 parts of calcium phosphate, 2-5 parts of sorbierite, 5-10 parts of polyester fiber, 10-20 parts of epoxy resin.
Further, the non-0.1-0.2mm of the thickness of the photochromatic layer；The non-3-5mm of thickness of the thick china substrate.
Further, the thick china substrate is made of the following component counted with mass fraction：45 parts of polypropylene, titanium dioxide 4 parts, 25 parts of expanded polystyrene (EPS), 3 parts of titanium dioxide, 4 parts of compound stabilizer, 3.5 parts of calcium phosphate, 3.5 parts of sorbierite, polyester it is fine Tie up 7.5 parts, 15 parts of epoxy resin.
The beneficial effects of the present invention are：Enable to become using be combined as photochromic layer of the photochromic material in silica gel Chromatograph is more soft, and soft handle, meanwhile, the discoloration of discoloration thick china of the invention is all good in fading rate.
Embodiment
Embodiment 1,
One kind exhibition discoloration thick china, including photochromatic layer and thick china substrate；The photochromatic layer by with The following component composition of mass fraction meter：7.5 parts of photochromic material, 40 parts of silica gel, 2 parts of adhesive, 2.5 parts of aniline, sulfurous Sour 1.5 parts of hydrogen sodium, 1 part of sorbierite；The thick china substrate is made of the following component counted with mass fraction：45 parts of polypropylene, 4 parts of titanium dioxide, 25 parts of expanded polystyrene (EPS), 3 parts of titanium dioxide, 4 parts of compound stabilizer, 3.5 parts of calcium phosphate, 3.5 parts of sorbierite, 7.5 parts of polyester fiber, 15 parts of epoxy resin.The thickness of the photochromatic layer is 0.1-0.2mm；The thickness of the thick china substrate Spend for 3-5mm.
It is complete by above-mentioned description, relevant staff using above-mentioned foundation desirable embodiment of the present invention as enlightenment Various changes and amendments can be carried out without departing from the scope of the technological thought of the present invention'.This invention it is technical Scope is not limited to the content on specification, it is necessary to determines its technical scope according to right.

Claims (3)

1. one kind exhibition discoloration thick china, it is characterised in that：Including photochromatic layer and thick china substrate；The light-induced variable Chromatograph is made of the following component counted with mass fraction：5-10 parts of photochromic material, 30-50 parts of silica gel, 1-3 parts of adhesive, 2-3 parts of aniline, 1-2 parts of sodium hydrogensulfite, 0.5-1.5 parts of sorbierite；The thick china substrate is by following in terms of mass fraction Component forms：40-50 parts of polypropylene, 3-5 parts of titanium dioxide, 20-30 parts of expanded polystyrene (EPS), 1-5 parts of titanium dioxide, stable composition 3-5 parts of agent, 3-4 parts of calcium phosphate, 2-5 parts of sorbierite, 5-10 parts of polyester fiber, 10-20 parts of epoxy resin.
A kind of 2. exhibition discoloration thick china as claimed in claim 1, it is characterised in that：The thickness of the photochromatic layer is not 0.1-0.2mm；The non-3-5mm of thickness of the thick china substrate.
A kind of 3. exhibition discoloration thick china as claimed in claim 1, it is characterised in that：The thick china substrate is by with quality The following component composition of number meter：It is 45 parts of polypropylene, 4 parts of titanium dioxide, 25 parts of expanded polystyrene (EPS), 3 parts of titanium dioxide, compound steady Determine 4 parts of agent, 3.5 parts of calcium phosphate, 3.5 parts of sorbierite, 7.5 parts of polyester fiber, 15 parts of epoxy resin.
CN201610908484.9A 2016-10-18 2016-10-18 One kind exhibition discoloration thick china Pending CN107955257A (en)