CN107936401A - Heat resistant type PVC, CPVC, CPE tertiary blending formula - Google Patents
Heat resistant type PVC, CPVC, CPE tertiary blending formula Download PDFInfo
- Publication number
- CN107936401A CN107936401A CN201711152808.1A CN201711152808A CN107936401A CN 107936401 A CN107936401 A CN 107936401A CN 201711152808 A CN201711152808 A CN 201711152808A CN 107936401 A CN107936401 A CN 107936401A
- Authority
- CN
- China
- Prior art keywords
- parts
- cpvc
- cpe
- heat resistant
- resistant type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of heat resistant type PVC, CPVC, CPE tertiary blending formula, in every 100 parts of polyvinyl chloride resin, it is equipped with:84~89 parts of CPVC resins, 11~13 parts of 201 processing aids of ACR, 2.8~3.4 parts of tribasic lead sulfates, 2.2~2.5 parts of dibasic lead phosphites, 1.2~1.5 parts of disodium hydrogen phosphates, 0.3~0.4 part of BaSt, 1.0~1.3 parts of HSt lubricants, 1.0~1.3 parts of paraffin blendings form.The present invention significantly improves heat resistance.
Description
Technical field
The present invention relates to a kind of polymer composite formula, particularly a kind of PVC pipe formula.
Background technology
PVC pipe, be with Corvic and stabilizer, lubricant etc. after use pressure sintering extrusion forming, anti-corruption
Erosion ability is strong, be easy to bonding, price is low, quality is hard, but heat resistance also needs further to improve.
The content of the invention
In view of the deficiencies of the prior art, the present invention proposes a kind of heat resistant type PVC, CPVC that can significantly improve heat resistance,
CPE tertiary blending formulas.
The present invention is achieved through the following technical solutions technical goal.
Heat resistant type PVC, CPVC, CPE tertiary blending formula, it is theed improvement is that:In every 100 parts of polyvinyl chloride resin, it is equipped with:
84~89 parts of CPVC resins, 11~13 parts of ACR-201 processing aids, 2.8~3.4 parts of tribasic lead sulfates, 2.2~2.5 part two
Alkali formula lead phosphite, 1.2~1.5 parts of disodium hydrogen phosphates, 0.3~0.4 part of BaSt, 1.0~1.3 parts of HSt lubricants, 1.0~1.3
Part paraffin blending forms.
Further improvement lies in that:In every 100 parts of polyvinyl chloride resin, it is equipped with:85~87 parts of CPVC resins, 12~13 parts of ACR-201
Processing aid, 3.0~3.2 parts of tribasic lead sulfates, 2.3~2.4 parts of dibasic lead phosphites, 1.3~1.4 parts of phosphoric acid hydrogen two
Sodium, 0.3~0.35 part of BaSt, 1.1~1.2 parts of HSt lubricants, 1.0~1.3 parts of paraffin blendings form.
Compared with prior art, the present invention have the positive effect that:
1st, CPVC resins are added, heat resistance can be significantly improved.
2nd, in every 100 parts of polyvinyl chloride resin, it is equipped with:84~85 parts of CPVC resins, 11~12 parts of ACR-201 processing aids, 2.7
~2.9 parts of tribasic lead sulfates, 1.2~1.3 parts of disodium hydrogen phosphates, 0.5~0.6 part of PbSt, 0.3~0.4 part of BaSt, 1.2~
1.3 parts of paraffin blendings form, and can further improve heat resistance.
Embodiment
With reference to embodiment, the invention will be further described.
Embodiment 1:
Heat resistant type PVC, CPVC, CPE tertiary blending formula, in every 100 parts of polyvinyl chloride resin, is equipped with:84 parts of CPVC resins, 11 parts
ACR-201 processing aids, 2.8 parts of tribasic lead sulfates, 2.2 parts of dibasic lead phosphites, 1.2 parts of disodium hydrogen phosphates, 0.3 part
BaSt, 1.0 parts of HSt lubricants, 1.0 parts of paraffin blendings form.
Embodiment 2:
Heat resistant type PVC, CPVC, CPE tertiary blending formula, in every 100 parts of polyvinyl chloride resin, is equipped with:89 parts of CPVC resins, 13 parts
ACR-201 processing aids, 3.4 parts of tribasic lead sulfates, 2.5 parts of dibasic lead phosphites, 1.5 parts of disodium hydrogen phosphates, 0.4 part
BaSt, 1.3 parts of HSt lubricants, 1.3 parts of paraffin blendings form.
Embodiment 3:
Heat resistant type PVC, CPVC, CPE tertiary blending formula, 85~87 parts of CPVC resins, 12 parts of ACR-201 processing aids, 3.0 parts
Tribasic lead sulfate, 2.3 parts of dibasic lead phosphites, 1.3 parts of disodium hydrogen phosphates, 0.3 part of BaSt, 1.1 parts of HSt lubricants, 1.0
Part paraffin blending forms.
Embodiment 4:
Heat resistant type PVC, CPVC, CPE tertiary blending formula, 87 parts of CPVC resins, 13 parts of ACR-201 processing aids, 3.2 part three
Basic lead sulphate, 2.4 parts of dibasic lead phosphites, 1.4 parts of disodium hydrogen phosphates, 0.35 part of BaSt, 1.2 parts of HSt lubricants, 1.3
Part paraffin blending forms.
Claims (2)
- A kind of 1. heat resistant type PVC, CPVC, CPE tertiary blending formula, it is characterised in that:In every 100 parts of polyvinyl chloride resin, it is equipped with:84 ~89 parts of CPVC resins, 11~13 parts of ACR-201 processing aids, 2.8~3.4 parts of tribasic lead sulfates, 2.2~2.5 part of two alkali Formula lead phosphite, 1.2~1.5 parts of disodium hydrogen phosphates, 0.3~0.4 part of BaSt, 1.0~1.3 parts of HSt lubricants, 1.0~1.3 parts Paraffin blending forms.
- 2. heat resistant type PVC, CPVC, CPE tertiary blending formula according to claim 1, it is characterised in that:Every 100 parts of PVC In resin, it is equipped with:85~87 parts of CPVC resins, 12~13 parts of ACR-201 processing aids, 3.0~3.2 parts of tribasic lead sulfates, 2.3~2.4 parts of dibasic lead phosphites, 1.3~1.4 parts of disodium hydrogen phosphates, 0.3~0.35 part of BaSt, 1.1~1.2 parts of HSt profits Lubrication prescription, 1.0~1.3 parts of paraffin blendings form.