CN107931076A - A kind of method for lifting clump weight surface abrasion resistance - Google Patents
A kind of method for lifting clump weight surface abrasion resistance Download PDFInfo
- Publication number
- CN107931076A CN107931076A CN201711232191.4A CN201711232191A CN107931076A CN 107931076 A CN107931076 A CN 107931076A CN 201711232191 A CN201711232191 A CN 201711232191A CN 107931076 A CN107931076 A CN 107931076A
- Authority
- CN
- China
- Prior art keywords
- parts
- clump weight
- resin
- powder
- abrasion resistance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of method for lifting clump weight surface abrasion resistance, including following operating procedure：（1）To match somebody with somebody overline block surface clean it is clean after, into blasting treatment, blasting powder use Zirconium oxide powder on surface, and blasting pressure is 0.2 0.3Mpa, and the sandblasting angle control of sandblasting is at 55 60 °；（2）Then spray coating powder paint is carried out on clump weight surface.Clump weight produced by the present invention, its surface roughness is low, almost pore-free, clump weight has excellent high temperature resistant, resistance to oxidation, corrosion resistance, especially its surface has higher hardness, and wear-resisting property is excellent, and clump weight is during use, be not in the phenomenon of superficial film cracking tear, greatly extend the service life of clump weight.
Description
Technical field
The invention belongs to clump weight preparing technical field, and in particular to a kind of side for lifting clump weight surface abrasion resistance
Method.
Background technology
Clump weight be for increase own wt keep balance weight, at present clump weight be using density it is larger
Metal material is made, and such as cast iron quality, during use surface oxidation corrosion easily occurs for these metal materials, in order to prolong
The service life of long clump weight on its surface, it is necessary to carry out brushing paint.In the prior art, the paint film formed after brushing paint,
The hardness on its surface is poor, during clump weight is carried, the phenomenon scratched easily occurs.
The content of the invention
In order to solve the above technical problem, the present invention provides a kind of method for lifting clump weight surface abrasion resistance.
The present invention is achieved by the following technical solutions.
A kind of method for lifting clump weight surface abrasion resistance, including following operating procedure：
（1）Will match somebody with somebody overline block surface clean it is clean after, surface uses Zirconium oxide powder, sandblasting pressure into blasting treatment, blasting powder
Power is 0.2-0.3Mpa, and the sandblasting angle of sandblasting is controlled at 55-60 °；
（2）Then spray coating powder paint is carried out on clump weight surface, wherein powdery paints is made of the component of following parts by weight：It is poly-
47-52 parts of carbonate resin, 18-20 parts of Polyphenylene sulfied resin, 8-12 parts of glass unicorn piece, 5-7 parts of polycaprolactam powder, aluminium borate
3-6 parts.
Specifically, above-mentioned steps（1）In, cleaning uses mass fraction to be cleaned for 10% degreasing liquid.
Specifically, the degreasing liquid is made of the component of following parts by weight：2-6 parts of sodium hydroxide, sodium gluconate 5-8
Part, 14-19 parts of sodium carbonate, 1-2 parts of nonylphenol polyoxyethylene ether, 55-65 parts of water.
Specifically, above-mentioned steps（2）In, powdery paints is made of following methods：By polycarbonate resin, Polyphenylene sulfied
Resin, glass unicorn piece, polycaprolactam powder, aluminium borate after mixing, are added into extruder, melting extrusion, obtains resin
Master batch, after masterbatch resin is dried, after being ground to 200-250 mesh, is made powdery paints.
From the above technical scheme, it can be seen that the beneficial effects of the invention are as follows：
Clump weight produced by the present invention, its surface roughness is low, almost pore-free, and clump weight has excellent high temperature resistant, oxytolerant
Change, especially corrosion resistance, its surface have higher hardness, and wear-resisting property is excellent, and clump weight is during use, no
The phenomenon of superficial film cracking tear occurs, greatly extends the service life of clump weight.In the present invention, first by clump weight
Blasting treatment is passed through on surface, can effectively lift adhesive force of the powdery paints on clump weight surface, powder produced by the present invention
Coating, adhesive force is high, and filming performance is excellent, and case hardness is high, greatly improves the crocking resistance of clump weight.
Embodiment
Following embodiments are used to illustrate the present invention, but cannot be used for limiting the scope of the invention.The reality used in embodiment
The condition of applying can be for further adjustments according to the condition of producer, and unaccounted implementation condition is usually conventional laboratory conditions.
Embodiment 1
A kind of method for lifting clump weight surface abrasion resistance, including following operating procedure：
（1）Will match somebody with somebody overline block surface clean it is clean after, surface uses Zirconium oxide powder, sandblasting pressure into blasting treatment, blasting powder
Power is 0.2Mpa, and the sandblasting angle of sandblasting is controlled at 55 °；
（2）Then spray coating powder paint is carried out on clump weight surface, wherein powdery paints is made of the component of following parts by weight：It is poly-
47 parts of carbonate resin, 18 parts of Polyphenylene sulfied resin, 8 parts of glass unicorn piece, 5 parts of polycaprolactam powder, 3 parts of aluminium borate.
Specifically, above-mentioned steps（1）In, cleaning uses mass fraction to be cleaned for 10% degreasing liquid.
Specifically, the degreasing liquid is made of the component of following parts by weight：2 parts of sodium hydroxide, 5 parts of sodium gluconate, carbon
Sour 14 parts of sodium, 1 part of nonylphenol polyoxyethylene ether, 55 parts of water.
Specifically, above-mentioned steps（2）In, powdery paints is made of following methods：By polycarbonate resin, Polyphenylene sulfied
Resin, glass unicorn piece, polycaprolactam powder, aluminium borate after mixing, are added into extruder, melting extrusion, obtains resin
Master batch, after masterbatch resin is dried, after being ground to 200 mesh, is made powdery paints.
Clump weight made from the present embodiment, in normal use 3 years, superficial film is not in cracking, wear phenomenon.
Embodiment 2
A kind of method for lifting clump weight surface abrasion resistance, including following operating procedure：
（1）Will match somebody with somebody overline block surface clean it is clean after, surface uses Zirconium oxide powder, sandblasting pressure into blasting treatment, blasting powder
Power is 0.2Mpa, and the sandblasting angle of sandblasting is controlled at 58 °；
（2）Then spray coating powder paint is carried out on clump weight surface, wherein powdery paints is made of the component of following parts by weight：It is poly-
50 parts of carbonate resin, 19 parts of Polyphenylene sulfied resin, 10 parts of glass unicorn piece, 6 parts of polycaprolactam powder, 5 parts of aluminium borate.
Specifically, above-mentioned steps（1）In, cleaning uses mass fraction to be cleaned for 10% degreasing liquid.
Specifically, the degreasing liquid is made of the component of following parts by weight：4 parts of sodium hydroxide, 7 parts of sodium gluconate, carbon
Sour 18 parts of sodium, 1 part of nonylphenol polyoxyethylene ether, 60 parts of water.
Specifically, above-mentioned steps（2）In, powdery paints is made of following methods：By polycarbonate resin, Polyphenylene sulfied
Resin, glass unicorn piece, polycaprolactam powder, aluminium borate after mixing, are added into extruder, melting extrusion, obtains resin
Master batch, after masterbatch resin is dried, after being ground to 230 mesh, is made powdery paints.
Clump weight made from the present embodiment, in normal use 3 years, superficial film is not in cracking, wear phenomenon.
Embodiment 3
A kind of method for lifting clump weight surface abrasion resistance, including following operating procedure：
（1）Will match somebody with somebody overline block surface clean it is clean after, surface uses Zirconium oxide powder, sandblasting pressure into blasting treatment, blasting powder
Power is 0.3Mpa, and the sandblasting angle of sandblasting is controlled at 60 °；
（2）Then spray coating powder paint is carried out on clump weight surface, wherein powdery paints is made of the component of following parts by weight：It is poly-
52 parts of carbonate resin, 20 parts of Polyphenylene sulfied resin, 12 parts of glass unicorn piece, 7 parts of polycaprolactam powder, 6 parts of aluminium borate.
Specifically, above-mentioned steps（1）In, cleaning uses mass fraction to be cleaned for 10% degreasing liquid.
Specifically, the degreasing liquid is made of the component of following parts by weight：6 parts of sodium hydroxide, 8 parts of sodium gluconate, carbon
Sour 19 parts of sodium, 2 parts of nonylphenol polyoxyethylene ether, 65 parts of water.
Specifically, above-mentioned steps（2）In, powdery paints is made of following methods：By polycarbonate resin, Polyphenylene sulfied
Resin, glass unicorn piece, polycaprolactam powder, aluminium borate after mixing, are added into extruder, melting extrusion, obtains resin
Master batch, after masterbatch resin is dried, after being ground to 250 mesh, is made powdery paints.
Clump weight made from the present embodiment, in normal use 3 years, superficial film is not in cracking, wear phenomenon.
Certainly, it is limitation of the present invention that described above, which is not, and the present invention is also not limited to the example above, the art
Those of ordinary skill, the present invention essential scope in, change, change, addition or the replacement made, should all belong to the present invention
Protection domain.
Claims (4)
- A kind of 1. method for lifting clump weight surface abrasion resistance, it is characterised in that including following operating procedure：（1）Will match somebody with somebody overline block surface clean it is clean after, surface uses Zirconium oxide powder, sandblasting pressure into blasting treatment, blasting powder Power is 0.2-0.3Mpa, and the sandblasting angle of sandblasting is controlled at 55-60 °；（2）Then spray coating powder paint is carried out on clump weight surface, wherein powdery paints is made of the component of following parts by weight：It is poly- 47-52 parts of carbonate resin, 18-20 parts of Polyphenylene sulfied resin, 8-12 parts of glass unicorn piece, 5-7 parts of polycaprolactam powder, aluminium borate 3-6 parts.
- A kind of 2. method for lifting clump weight surface abrasion resistance according to claim 1, it is characterised in that above-mentioned steps （1）In, cleaning uses mass fraction to be cleaned for 10% degreasing liquid.
- A kind of 3. method for lifting clump weight surface abrasion resistance according to claim 2, it is characterised in that the degreasing Liquid is made of the component of following parts by weight：2-6 parts of sodium hydroxide, 5-8 parts of sodium gluconate, 14-19 parts of sodium carbonate, nonyl phenol gather 1-2 parts of ethylene oxide ether, 55-65 parts of water.
- A kind of 4. method for lifting clump weight surface abrasion resistance according to claim 1, it is characterised in that above-mentioned steps （2）In, powdery paints is made of following methods：By polycarbonate resin, Polyphenylene sulfied resin, glass unicorn piece, polycaprolactam Amine powder, aluminium borate after mixing, are added into extruder, and melting extrusion, obtains masterbatch resin, after masterbatch resin is dried, After being ground to 200-250 mesh, powdery paints is made.