CN107916358A - A kind of wearable lightweight mobile phone dorsal shield metal material - Google Patents
A kind of wearable lightweight mobile phone dorsal shield metal material Download PDFInfo
- Publication number
- CN107916358A CN107916358A CN201711037285.6A CN201711037285A CN107916358A CN 107916358 A CN107916358 A CN 107916358A CN 201711037285 A CN201711037285 A CN 201711037285A CN 107916358 A CN107916358 A CN 107916358A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- mobile phone
- alloy
- metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of wearable lightweight mobile phone dorsal shield metal material, it is characterized in that, including each component of following parts by weight is prepared:20 40 parts of copper powder, 5 15 parts of iron powder, 2 10 parts of metal oxide, 15 parts of zirconium powder, 14 parts of tungsten powder, 15 parts of rare earth metal, 5 15 parts of alloy in lightweight, 5 15 parts of polynary ferroalloy, 15 parts of indium-base alloy, 13 parts of chromium powder, 5 15 parts of aluminium powder, 18 parts of bronze, 5 12 parts of nanometer grade silica powder.Mobile phone metal-back made of the present invention, impact strength significantly improve, and moulding processability is good, have outstanding heat aging performance, wear-resisting property, and intensity is high, light weight, product excellent fireproof performance, product high temperature resistant, product strength are high, impact strength is good, of low cost, easy to operate, corrosion-resistant.
Description
Technical field
The present invention relates to a kind of material of mobile phone shell, especially a kind of wearable lightweight mobile phone dorsal shield metal material, belongs to hand
Machine accessory technical field.
Background technology
Metal is a kind of material with gloss, rich in the property such as ductility, easy conduction, heat conduction.It is tellurian big absolutely
Most metallic elements are to be present in compound state in nature.This is because the chemical property of most metals is more active, only
Metal such as gold, silver with the presence of only a few etc. are with free state.Metal is widespread in nature, using extremely general in life
Time, it is a kind of materials extremely important in modern industry and that application is most.
Phone housing is mainly made of metal or plastics.Plastic handset shell it is cheap, easy to process, color tolerance
Easily, insulation, the influence to signal are small, and its forming method mainly injection and compacting etc., and production efficiency is high, can give birth on a large scale
Production, thus occupation rate is of a relatively high in the market.The intensity of existing plastic handset shell is low, shielding property is poor, wear-resisting
Property is bad, anti-pressure ability is poor, heat dissipation effect is bad.
As the requirement of cell phone appearance fineness is higher and higher, such as slim degree, cruel degree of dazzling, metallic mobile phone shell is in mobile phone
Apparent use is also more and more.Metallic mobile phone shell has the advantages that texture is good, intensity is high, but it there are cost
It is high, not easy to be processed, wear-resisting property is bad, heat insulation is poor, shock resistance is weak, therefore it is commercially difficult to occupy advantage.
The content of the invention
The purpose of the present invention is in view of the above shortcomings of the prior art, there is provided a kind of wearable lightweight mobile phone dorsal shield metal material
Material.
Technical scheme is as follows:A kind of wearable lightweight mobile phone dorsal shield metal material, it is characterized in that, including it is following heavy
The each component of amount part is prepared:20-40 parts of copper powder, 5-15 parts of iron powder, 2-10 parts of metal oxide, 1-5 parts of zirconium powder, tungsten powder 1-
4 parts, 1-5 parts of rare earth metal, 5-15 parts of alloy in lightweight, ferroalloy 5-15 parts polynary, 1-5 parts of indium-base alloy, 1-3 parts of chromium powder, aluminium
5-15 parts of powder, 1-8 parts of bronze, 5-12 parts of nanometer grade silica powder.
The metal oxide is copper-molybdenum nickel alloy.
The rare earth metal is lanthanide rare metal.
The lanthanide rare metal is lanthanum, cerium, thulium or dysprosium.
The alloy in lightweight is titanium alloy or magnesium alloy.
Iron is distributed more widely in life, takes up an area the 4.75% of shell content, is only second to oxygen, silicon, aluminium, occupies the earth's crust and contain flow control four.
Pure iron is flexible and the preferably silvery white non-ferrous metal of ductility, and for generator processed and the iron core of motor, iron and its compound are also
It is one of industrial described " ferrous metal " for magnet processed, medicine, ink, pigment, abrasive material etc.(Other two kinds be chromium and
Manganese)(The pure pig iron is argenteous that it is because iron surface is usually covered with one that ferro element, which is referred to as " ferrous metal ", in fact
Layer main component is the protective film of black ferroferric oxide).
Rare earth has the laudatory title of " industrial vitamin ", nowadays becomes extremely important strategic resource, rare earth element is in stone
The fields such as oil, chemical industry, metallurgy, weaving, ceramics, glass, permanent-magnet material, which are obtained for, to be widely applied, with advances in technology and
The continuous breakthrough of application technology, the value of rare earth oxide will be higher and higher.Rare earth has the title of industrial " gold ", due to its tool
There are the physical characteristics such as excellent photoelectromagnetic, new material that can be different, various in style with other materials component property, it is most notable
Function be exactly to increase substantially the quality and performance of other products.
Nano silicon dioxide is a kind of inorganic chemical industry material, is commonly called as white carbon.Due to being ultrafine nanometer, size range exists
1-100nm, therefore there are many unique properties, such as have to anti-ultraviolet optical property, it is anti-ageing other materials to be improved
Change, intensity and chemical-resistance.Nanometer grade silica is amorphous white powder, nontoxic, tasteless, pollution-free, and micro-structure is
Spherical, in cotton-shaped and netted quasi- grain structure, molecular formula and structural formula are silica, not soluble in water.Utilize nano-silica
The huge specific surface area of SiClx, the more meso-hole structures in surface and superpower adsorption capacity and unusual physicochemical property, have superpower
Antibacterial ability.
Mobile phone metal-back made of the present invention, impact strength significantly improve, and moulding processability is good, have outstanding heat always
Change performance, wear-resisting property, intensity is high, light weight, product excellent fireproof performance, product high temperature resistant, and product strength is high, impact strength
It is good, it is of low cost, it is easy to operate, it is corrosion-resistant.
Embodiment
Embodiment 1
A kind of wearable lightweight mobile phone dorsal shield metal material, including each component of following parts by weight are prepared:20-40 parts of copper powder,
5-15 parts of iron powder, 2-10 parts of metal oxide, 1-5 parts of zirconium powder, 1-4 parts of tungsten powder, 1-5 parts of rare earth metal, 5-15 parts of alloy in lightweight,
Polynary ferroalloy 5-15 parts, 1-5 parts of indium-base alloy, 1-3 parts of chromium powder, 5-15 parts of aluminium powder, 1-8 parts of bronze, nanometer grade silica
5-12 parts of powder.
Metal oxide is copper-molybdenum nickel alloy, and rare earth metal is lanthanide rare metal, and lanthanide rare metal is lanthanum, cerium, thulium
Or dysprosium, alloy in lightweight are titanium alloy or magnesium alloy.
Embodiment 2
A kind of wearable lightweight mobile phone dorsal shield metal material, including each component of following parts by weight are prepared:20 parts of copper powder, iron powder
5 parts, 2 parts of metal oxide, 1 part of zirconium powder, 1 part of tungsten powder, 1 part of rare earth metal, 5 parts of alloy in lightweight, 5 parts of polynary ferroalloy, indium base
1 part of alloy, 1 part of chromium powder, 5 parts of aluminium powder, 1 part of bronze, 5 parts of nanometer grade silica powder.
Metal oxide is copper-molybdenum nickel alloy, and rare earth metal is lanthanide rare metal, and lanthanide rare metal is lanthanum, cerium, thulium
Or dysprosium, alloy in lightweight are titanium alloy or magnesium alloy.
Embodiment 3
A kind of wearable lightweight mobile phone dorsal shield metal material, including each component of following parts by weight are prepared:40 parts of copper powder, iron powder
15 parts, 10 parts of metal oxide, 5 parts of zirconium powder, 4 parts of tungsten powder, 5 parts of rare earth metal, 15 parts of alloy in lightweight, 15 parts of polynary ferroalloy,
5 parts of indium-base alloy, 3 parts of chromium powder, 15 parts of aluminium powder, 8 parts of bronze, 12 parts of nanometer grade silica powder.
Metal oxide is copper-molybdenum nickel alloy, and rare earth metal is lanthanide rare metal, and lanthanide rare metal is lanthanum, cerium, thulium
Or dysprosium, alloy in lightweight are titanium alloy or magnesium alloy.
Claims (5)
1. a kind of wearable lightweight mobile phone dorsal shield metal material, it is characterized in that, including each component of following parts by weight is prepared:Copper
20-40 parts of powder, 5-15 parts of iron powder, 2-10 parts of metal oxide, 1-5 parts of zirconium powder, 1-4 parts of tungsten powder, 1-5 parts of rare earth metal, lightweight
5-15 parts of alloy, ferroalloy 5-15 parts polynary, 1-5 parts of indium-base alloy, 1-3 parts of chromium powder, 5-15 parts of aluminium powder, 1-8 parts of bronze, nanometer
5-12 parts of grade silicon dioxide powder.
2. a kind of wearable lightweight mobile phone dorsal shield metal material according to claim 1, it is characterized in that, the metal oxide
For copper-molybdenum nickel alloy.
3. a kind of wearable lightweight mobile phone dorsal shield metal material according to claim 1, it is characterized in that, the rare earth metal is
Lanthanide rare metal.
4. a kind of wearable lightweight mobile phone dorsal shield metal material according to claim 3, it is characterized in that, the lanthanide rare gold
Belong to for lanthanum, cerium, thulium or dysprosium.
5. a kind of wearable lightweight mobile phone dorsal shield metal material according to claim 1, it is characterized in that, the alloy in lightweight is
Titanium alloy or magnesium alloy.