CN107892851A - A kind of wear-resisting spray painting and its preparation technology - Google Patents
A kind of wear-resisting spray painting and its preparation technology Download PDFInfo
- Publication number
- CN107892851A CN107892851A CN201711207888.6A CN201711207888A CN107892851A CN 107892851 A CN107892851 A CN 107892851A CN 201711207888 A CN201711207888 A CN 201711207888A CN 107892851 A CN107892851 A CN 107892851A
- Authority
- CN
- China
- Prior art keywords
- parts
- wear
- resisting
- powder
- spray painting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention provides a kind of wear-resisting spray painting, includes the raw material of following parts by weight：35 ~ 45 parts of acrylic resin, 18 ~ 23 parts of amino resins, 10 ~ 15 parts of polyisoprene, 8 ~ 12 parts of tetrafluoro powder, wear-resisting 8 ~ 12 parts of powder of filling, 8 ~ 12 parts of dispersant, 4 ~ 8 parts of antioxidant, 8 ~ 15 parts of pigment, 15 ~ 30 parts of water；Wherein, the wear-resisting filling powder is at least one of aluminum oxide, silica, zirconium oxide, bortz powder, boron nitride, SILICA FUME.Wear-resisting spray painting provided by the invention, it has the characteristics of attachment degree is high, water-resistance is strong, wearability is strong, also with the characteristics of caking property is strong, anti-aging, asepsis environment-protecting.
Description
Technical field
The invention belongs to foundry lacquering technologies field, and in particular to a kind of wear-resisting spray painting and its preparation technology.
Background technology
Paint and be mixed for artificial lacquer, generally use nitrocellulose, resin, pigment, solvent etc., using passing through spray gun
Equably be sprayed on body surface, there is water-fast, resistance to machine oil, do it is fast the characteristics of, be widely used in paint automobile, aircraft, woodenware, leather
Deng product.After being sprayed on product, paint film is formed in product surface, product and air exclusion are opened, so as to protect product not
It is affected by the surrounding environment, the time is grown, and the paint film of product surface can be because of reasons such as solar radiation, air oxidation, friction, collisions
And make alligatoring or even come off, particularly during product use, its wear damage being subject to is most universal, therefore it provides
A kind of strong spray painting of wearability has staple market value.
The content of the invention
Based on above prior art, it is an object of the invention to provide a kind of wear-resisting spray painting, and it has, and attachment degree is high, bonds
The characteristics of property is strong, wearability is strong, anti-aging, asepsis environment-protecting.
In order to realize the above object the technical solution adopted by the present invention is：A kind of wear-resisting spray painting, including following parts by weight
Raw material：It is 35~45 parts of acrylic resin, 18~23 parts of amino resins, 10~15 parts of polyisoprene, 8~12 parts of tetrafluoro powder, resistance to
8~12 parts of powder of mill filling, 8~12 parts of dispersant, 4~8 parts of antioxidant, 8~15 parts of pigment, 15~30 parts of water；Wherein, it is described
Wear-resisting filling powder is at least one of aluminum oxide, silica, zirconium oxide, bortz powder, boron nitride, SILICA FUME.
Preferably, wear-resisting paint includes the raw material of following parts by weight：40 parts of acrylic resin, amino resins 21
Part, 12 parts of polyisoprene, 10 parts of tetrafluoro powder, it is wear-resisting filling 10 parts of powder, 10 parts of dispersant, 6 parts of antioxidant, 12 parts of pigment,
22 parts of water；Wherein, the wear-resisting filling powder is aluminum oxide, the mixture of boron nitride.
As optimization, the acrylic resin is that weight ratio is 1：0.5~1 thermoplastic acrylic resin and thermosetting third
The mixture of olefin(e) acid resin, the relative molecular weight of thermoplastic acrylic resin is larger, has good guarantor's light colour retention, water-fast resistance to
Chemically, thermosetting acrylic resin relative molecular weight is relatively low, can react to form network structure with amino resins, make wear-resisting spray painting
Possess higher gloss, hardness, solvent resistance and weatherability, thermoplastic acrylic resin, thermosetting acrylic resin, amino tree
Fat makes wear-resisting spray painting form color and luster exquisiteness, the paint film that brightness is high, attached property is good for being sprayed at after product surface after combining.
As optimization, the grain graininess of the wear-resisting filling powder is less than 70 nanometers, and the granularity of wear-resisting inserts is smaller, resistance to
The quality of mill spray painting is finer and smoother, and quality is better after spray painting, but the undersized of wear-resisting filling powder, can use wear-resisting spray painting
During block spray gun, therefore the grain graininess of further preferably wear-resisting filling powder is 50~70 nanometers.
As further optimization, the wear-resisting filling powder is aluminum oxide, silica, bortz powder according to 1：1：2 weight
Than obtained mixture.
As optimization, the dispersant is DA types dispersant, DC types dispersant, PF-88 dispersants, AM-C dispersants, silicon
At least one of hydrochlorate dispersant.
As optimization, the antioxidant is antioxidant 168, hindered phenol anti-oxidants, in ethoxyquinoline extremely
Few one kind.
As optimization, the pigment is that weight ratio is 1：1~3：1~5 mica, titanium oxide, the mixture of colouring agent, institute
The common dyestuff with colourizing role of in the market can be used by stating colouring agent.
The present invention also provides a kind of technique for preparing wear-resisting spray painting, comprises the following steps：
Step 1：Weigh each raw material respectively according to parts by weight, it is standby.
Step 2：With 180~240r/min speed after acrylic resin, amino resins, polyisoprene, water are mixed
Stirring 30~60 minutes, then stirred 30~60 minutes, sequentially added during stirring point with 550~650r/min speed
Powder, tetrafluoro powder, wear-resisting filling powder, pigment, stirring obtain wear-resisting spray painting after terminating.
Beneficial effect
Beneficial effects of the present invention are as follows：
(1), wear-resisting spray painting provided by the invention, using acrylic resin as primary raw material, acrylic resin and amino
Wear-resisting spray painting is set to form color and luster exquisiteness, the paint film that brightness is high, attached property is good for being sprayed at after product surface after resin-bonded,
Polyisoprene increases viscosity, adhesive force and the water-resistance of wear-resisting spray painting, and tetrafluoro powder is combined the wear-resisting spray of increase with polyisoprene
The toughness of paint, the wearability for forming paint film is sprayed from wear-resisting paint is increased, wear-resisting filling powder is combined with tetrafluoro powder can make wear-resisting spray
The wearability increase by more than 80% of paint, dispersant makes each raw material be dispersed in wear-resisting spray painting, and antioxidant makes wear-resisting spray painting
It is unlikely to deteriorate, while lifts the weatherability of paint film, pigment assigns wear-resisting spray painting different colors, and water is as the wear-resisting spray of solvent adjustment
The density of paint.
(2), wear-resisting spray painting provided by the invention, each raw material are combined with each other, and the comprehensive bright color that forms is bright-coloured, glossiness
Height, the wear-resisting spray painting that toughness is strong, attachment degree is high, wearability is strong, and wear-resisting spray painting nontoxic pollution-free provided by the invention, to human body
Have no toxic side effect, it is environment-friendly.
Embodiment
The present invention is described in further detail with reference to specific embodiment.
Embodiment 1
The present embodiment provides a kind of wear-resisting spray painting, includes the raw material of following parts by weight：35 parts of acrylic resin, amino resins
18 parts, 10 parts of polyisoprene, 8 parts of tetrafluoro powder, it is wear-resisting filling 8 parts of powder, 8 parts of dispersant, 4 parts of antioxidant, 8 parts of pigment, water
15 parts；Wherein, the wear-resisting filling powder is aluminum oxide, boron nitride according to 1：Mixture made from 2 weight ratio, its grain graininess
For 50~70 nanometers, the acrylic resin is that weight ratio is 1：0.5 thermoplastic acrylic resin and thermoset acrylics tree
The mixture of fat, the dispersant are DA type dispersants, and the antioxidant is hindered phenol anti-oxidants, and the pigment is attached most importance to
Amount is than being 1：1：1 mica, titanium oxide, the mixture of colouring agent.
The present embodiment also provides a kind of preparation technology of wear-resisting spray painting, comprises the following steps：
Step 1：Weigh each raw material respectively according to parts by weight, it is standby.
Step 2：After acrylic resin, amino resins, polyisoprene, water are mixed 60 are stirred with 180r/min speed
Minute, then stirred 60 minutes with 550r/min speed, dispersant, tetrafluoro powder are sequentially added during stirring, wear-resisting is filled out
Powder, pigment are filled, stirring obtains wear-resisting spray painting after terminating.
Embodiment 2
The present embodiment provides a kind of wear-resisting spray painting, includes the raw material of following parts by weight：37 parts of acrylic resin, amino resins
19 parts, 11 parts of polyisoprene, 9 parts of tetrafluoro powder, it is wear-resisting filling 9 parts of powder, 9 parts of dispersant, 5 parts of antioxidant, 10 parts of pigment, water
18 parts；Wherein, the wear-resisting filling powder is zirconium oxide, bortz powder, SILICA FUME according to 1：1：2 weight ratio is obtained to be mixed
Thing, its grain graininess are 50~70 nanometers, and the acrylic resin is that weight ratio is 1：0.6 thermoplastic acrylic resin and heat
The mixture of solidity acrylic resin, the dispersant is AM-C dispersants, the mixture of silicic acid dipersant, described anti-oxidant
Agent is hindered phenol anti-oxidants, the mixture of ethoxyquinoline, and the pigment is that weight ratio is 1：1：1 mica, titanium oxide,
The mixture of colouring agent.
The present embodiment also provides a kind of preparation technology of wear-resisting spray painting, comprises the following steps：
Step 1：Weigh each raw material respectively according to parts by weight, it is standby.
Step 2：After acrylic resin, amino resins, polyisoprene, water are mixed 40 are stirred with 200r/min speed
Minute, then stirred 40 minutes with 570r/min speed, dispersant, tetrafluoro powder are sequentially added during stirring, wear-resisting is filled out
Powder, pigment are filled, stirring obtains wear-resisting spray painting after terminating.
Embodiment 3
The present embodiment provides a kind of wear-resisting spray painting, includes the raw material of following parts by weight：40 parts of acrylic resin, amino resins
21 parts, 12 parts of polyisoprene, 10 parts of tetrafluoro powder, it is wear-resisting filling 10 parts of powder, 10 parts of dispersant, 6 parts of antioxidant, pigment 12
Part, 22 parts of water；Wherein, the wear-resisting filling powder is aluminum oxide, silica, bortz powder according to 1：1：Made from 2 weight ratio
Mixture, its grain graininess are 50~70 nanometers, and the acrylic resin is that weight ratio is 1：0.7 thermoplastic acrylic resin
With the mixture of thermosetting acrylic resin, the dispersant is DC types dispersant, the mixture of silicic acid dipersant, described anti-
Oxidant is hindered phenol anti-oxidants, and the pigment is that weight ratio is 1：2：3 mica, titanium oxide, the mixture of colouring agent.
The present embodiment also provides a kind of preparation technology of wear-resisting spray painting, comprises the following steps：
Step 1：Weigh each raw material respectively according to parts by weight, it is standby.
Step 2：After acrylic resin, amino resins, polyisoprene, water are mixed 50 are stirred with 220r/min speed
Minute, then stirred 45 minutes with 600r/min speed, dispersant, tetrafluoro powder are sequentially added during stirring, wear-resisting is filled out
Powder, pigment are filled, stirring obtains wear-resisting spray painting after terminating.
Embodiment 4
The present embodiment provides a kind of wear-resisting spray painting, includes the raw material of following parts by weight：43 parts of acrylic resin, amino resins
22 parts, 13 parts of polyisoprene, 11 parts of tetrafluoro powder, it is wear-resisting filling 11 parts of powder, 11 parts of dispersant, 7 parts of antioxidant, pigment 14
Part, 26 parts of water；Wherein, the wear-resisting filling powder is aluminum oxide, silica according to 1：Mixture made from 1 weight ratio, its
Grain granularity is 50~70 nanometers, and the acrylic resin is that weight ratio is 1：0.9 thermoplastic acrylic resin and thermosetting third
The mixture of olefin(e) acid resin, the dispersant are PF-88 dispersants, the mixture of silicic acid dipersant, and the antioxidant is
Antioxidant 168, the pigment are that weight ratio is 1：2：4 mica, titanium oxide, the mixture of colouring agent.
The present embodiment also provides a kind of preparation technology of wear-resisting spray painting, comprises the following steps：
Step 1：Weigh each raw material respectively according to parts by weight, it is standby.
Step 2：After acrylic resin, amino resins, polyisoprene, water are mixed 50 are stirred with 230r/min speed
Minute, then stirred 50 minutes with 630r/min speed, dispersant, tetrafluoro powder are sequentially added during stirring, wear-resisting is filled out
Powder, pigment are filled, stirring obtains wear-resisting spray painting after terminating.
Embodiment 5
The present embodiment provides a kind of wear-resisting spray painting, includes the raw material of following parts by weight：45 parts of acrylic resin, amino resins
23 parts, 15 parts of polyisoprene, 12 parts of tetrafluoro powder, it is wear-resisting filling 2 parts of powder, 12 parts of dispersant, 8 parts of antioxidant, 15 parts of pigment,
30 parts of water；Wherein, the wear-resisting filling powder is zirconium oxide, bortz powder, SILICA FUME according to 1：1：2 weight ratio is obtained to be mixed
Thing, its grain graininess are 50~70 nanometers, and the acrylic resin is that weight ratio is 1：1 thermoplastic acrylic resin and thermosetting
Property acrylic resin mixture, the dispersant be PF-88 dispersants, the mixture of AM-C dispersants, the antioxidant
For ethoxyquinoline, the pigment is that weight ratio is 1：3：5 mica, titanium oxide, the mixture of colouring agent.
The present embodiment also provides a kind of preparation technology of wear-resisting spray painting, comprises the following steps：
Step 1：Weigh each raw material respectively according to parts by weight, it is standby.
Step 2：After acrylic resin, amino resins, polyisoprene, water are mixed 30 are stirred with 240r/min speed
Minute, then stirred 30 minutes with 650r/min speed, dispersant, tetrafluoro powder are sequentially added during stirring, wear-resisting is filled out
Powder, pigment are filled, stirring obtains wear-resisting spray painting after terminating.
The raw material used in above-described embodiment 1 to 5 and parts by weight are as shown in table 1 below, wherein, using wear-resisting in embodiment 5
The parts by weight of filling powder are outside parts by weight scope provided by the invention to be used as reference examples：
Table 1
The wear resistant paint that above-described embodiment 1 to 5 is prepared carries out attachment degree, water absorption rate, wearability test, its test side
Method is as follows：
Attachment degree is tested：Press《Paint film is typically prepared method》Wear-resisting spray painting paint film sample is made in (GB/T 1727-1992), makes
With the attachment degree of hundred lattice testers test paint film, 10 × 10 small nets of (100) 1mm × 1mm are drawn in coating surface with cross-cut tester
The bottom of lattice, each line depth and paint film, is afterwards cleaned down the fragment of test zone with hairbrush, with 3M600 gummed papers or
The gummed paper of equal efficiency firmly clings tested small grid, and firmly wipes adhesive tape with erasing rubber, to increase adhesive tape and tested area
The contact area and dynamics in domain, finally hold adhesive tape one end, and gummed paper, same position are shut down rapidly in vertical direction (90 °)
2 identical tests are carried out, according to its attachment degree of otch paint film spalling degree evaluation, incision paint film spalling is fewer, its attachment degree
It is higher, attachment degree is demarcated using ISO grades, wherein, ISO rankings rule is as follows：
5B：The edge of otch is completely smooth, and grid edge does not have any paint film spalling；
4B：There is small pieces paint film spalling in the intersection of otch, actual spoilage≤5% in Hua Ge areas；
3B：The edge and/or intersection of otch have paint film to be peeled off, and its area is more than 5%~15%；
2B：There are part paint film spalling or whole large stretch of paint film spalling, or the full wafer paint film spalling of partial grid along notching edge,
The area of peeling is more than 15%~35%；
1B：Notching edge sheet paint film spalling or some grids have part or all of paint film spalling, and its area, which is more than, to be drawn
The 35%~65% of lattice area；
0B：There is sheet of paint film spalling at the edge of line and intersection, and peel off the gross area and be more than 65%.
Water absorption rate test：As sample, three pieces of samples are taken vertically to be totally immersed into drying after dry copper sheet dipping lacquer
In the glass container for filling 23 ± 2 DEG C of distilled water, its surface should not have with bubble, not contact with each other or with chamber wall.
After immersion 24 hours, sample is taken out with tweezers, blots coating surface moisture with filter paper rapidly, its quality is weighed immediately, with it
The increased percentage of quality represents its water absorption rate, wherein, every piece of sample, which is taken out from water to weighing time for finishing, to be surpassed
2 minutes, after measurement are spent, water absorption rate is lower, and the quality of wear-resisting spray painting is higher.
Wearability test：Press《Paint film is typically prepared method》Wear-resisting spray painting paint film sample is made in (GB/T 1727-1992), surveys
Its weight is measured, wearability test is carried out using paint film wear resistant instrument, sample is fixed on wear resistant instrument working rotary table, is added on arm
Required load-carrying and the elastic grinding wheel through renewing, the end of arm add with emery wheel weight identical counterpoise, gently put down plus
Pressure arm.Dust absorption nozzle is put down, and is adjusted to from 1~1.5mm of sample.Master switch, vacuum cleaner switch, rotary disk shutter are opened successively.
Sample, which is first ground, turns 50 turns, is allowed to form smoother surface.Power supply is closed, sample is taken out, floating bits is gently erased with writing brush, is claimed
Weight, the difference of front and rear weight is paint film weightlessness, and parallel testing three times, seeks the average value that paint film is weightless three times, wherein, paint film is weightless
Measure smaller, the wearability of paint film is higher.
The wear resistant paint that above-described embodiment 1 to 5 is prepared carries out attachment degree, water absorption rate, wearability test, its test side
Method is as follows：
Table 2 is tested and test result
Obtained wear resistant paint in above-described embodiment 1 to 4, it is wear-resisting that its attachment degree, water absorption rate, wearability all reach high-quality
Paint, wherein, the parts by weight of wear-resisting filling powder are added in the raw material of embodiment 5 far fewer than parts by weight standard provided by the invention, its is resistance to
Mill property test test result is shown, the wearability of wear-resisting spray painting is made in embodiment 5 much smaller than the wear-resisting spray in other embodiment
Paint, it is seen that the addition of wear-resisting filling powder is the key factor for influenceing to be made wear-resisting spray painting wearability.
Describe embodiments of the present invention in detail above by embodiment, whereby to the present invention how application technology means
To solve technical problem, and the implementation process for reaching technique effect can fully understand and implement according to this.It should be clear that as long as
Conflict is not formed, each embodiment in the present invention and each feature in each embodiment can be combined with each other, and be formed
Technical scheme is within protection scope of the present invention.
Claims (10)
1. a kind of wear-resisting spray painting, it is characterised in that include the raw material of following parts by weight：35 ~ 45 parts of acrylic resin, amino resins
18 ~ 23 parts, 10 ~ 15 parts of polyisoprene, 8 ~ 12 parts of tetrafluoro powder, it is wear-resisting filling 8 ~ 12 parts of powder, 8 ~ 12 parts of dispersant, antioxidant
4 ~ 8 parts, 8 ~ 15 parts of pigment, 15 ~ 30 parts of water；Wherein, the wear-resisting filling powder is aluminum oxide, silica, zirconium oxide, diamond
At least one of powder, boron nitride, SILICA FUME.
2. wear-resisting spray painting according to claim 1, it is characterised in that include the raw material of following parts by weight：Acrylic resin
40 parts, it is 21 parts of amino resins, 12 parts of polyisoprene, 10 parts of tetrafluoro powder, wear-resisting 10 parts of powder of filling, 10 parts of dispersant, anti-oxidant
6 parts of agent, 12 parts of pigment, 22 parts of water；Wherein, the wear-resisting filling powder is aluminum oxide, the mixture of boron nitride.
3. wear-resisting spray painting according to claim 1 or 2, it is characterised in that the acrylic resin is that weight ratio is 1：0.5
~ 1 thermoplastic acrylic resin and the mixture of thermosetting acrylic resin.
4. wear-resisting spray painting according to claim 1, it is characterised in that the grain graininess of the wear-resisting filling powder is 50 ~ 70
Nanometer.
5. the wear-resisting spray painting according to claim 1 or 4, it is characterised in that the wear-resisting filling powder is aluminum oxide, oxidation
Silicon, bortz powder are according to 1：1：Mixture made from 2 weight ratio.
6. wear-resisting spray painting according to claim 1, it is characterised in that the dispersant is DA types dispersant, DC types disperse
At least one of agent, PF-88 dispersants, AM-C dispersants, silicic acid dipersant.
7. wear-resisting spray painting according to claim 1, it is characterised in that the antioxidant is antioxidant 168, hindered phenol
At least one of class antioxidant, ethoxyquinoline.
8. wear-resisting spray painting according to claim 1, it is characterised in that the pigment is that weight ratio is 1：1~3：1 ~ 5 cloud
Mother, titanium oxide, the mixture of colouring agent.
9. a kind of technique for preparing claim 1 to the 8 wear-resisting spray painting, it is characterised in that comprise the following steps：
Step 1：Weigh each raw material respectively according to parts by weight, it is standby.
10. step 2：Stirred after acrylic resin, amino resins, polyisoprene, water are mixed with 180 ~ 240r/min speed
Mix 30 ~ 60 minutes, then stirred 30 ~ 60 minutes with 550 ~ 650r/min speed, sequentially added during stirring dispersant,
Tetrafluoro powder, wear-resisting filling powder, pigment, stirring obtain wear-resisting spray painting after terminating.