CN107892813A - A kind of dust-removal cloth-bag prepares material - Google Patents
A kind of dust-removal cloth-bag prepares material Download PDFInfo
- Publication number
- CN107892813A CN107892813A CN201711434510.XA CN201711434510A CN107892813A CN 107892813 A CN107892813 A CN 107892813A CN 201711434510 A CN201711434510 A CN 201711434510A CN 107892813 A CN107892813 A CN 107892813A
- Authority
- CN
- China
- Prior art keywords
- dust
- bag
- removal cloth
- parts
- prepares material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Material is prepared the invention discloses a kind of dust-removal cloth-bag, is related to dedusting technology field.The dust-removal cloth-bag prepares material, including polyphenylene sulfide, polytetrafluoroethylene (PTFE), polyurethane resin, water-soluble polyester, graphene, polyvinylpyrrolidone, polypropylene-base carbon fiber, silicon fluoride, nanocrystal cellulose, citric acid, fire retardant, coupling agent, adhesive, antistatic additive, antiaging agent;By each material component of scientific matching, under mutually being acted synergistically between each component, temperature tolerance, acid resistance, static electricity resistance and the anti-denaturation of dust-removal cloth-bag are improved, complex environment can be applied to, had a wide range of application;Meanwhile silicon fluoride and citric acid comprehensive function improve the adhesive property of ptfe surface, improve adsorption effect;Nanocrystal cellulose and adhesive further increase the adsorption effect of dust-removal cloth-bag, improve the dust collection capacity of dust-removal cloth-bag.
Description
Technical field
The invention belongs to dedusting technology field, more particularly to a kind of dust-removal cloth-bag prepares material.
Background technology
The world today because all kinds of problems such as soil fail, climate change, energy waste and greenhouse effects for environmental protection
Dynamics also gradually increasing, thus the exploitation for environmental protection equipment is also increasing with application.Sack cleaner is Green Machine
Most common one kind among equipment, therefore structural principle is simple, technological parameter requires relatively low, turns into current popularization degree highest one
Kind deduster.And the dust-removal cloth-bag majority in existing sack cleaner be provided to improve dust removing effects and increase cloth bag diameter or
Cloth bag length, do not improved well in the practicality demand of dust-removal cloth-bag, make its temperature tolerance, static electricity resistance and anti-denaturation
It is not high.
The content of the invention
In view of the shortcomings of the prior art, what the present invention provided a kind of dust-removal cloth-bag prepares material.
The present invention is that solve above-mentioned technical problem by the following technical solutions:A kind of dust-removal cloth-bag prepares material
Material, including 20~30 parts of polyphenylene sulfide, 10~20 parts of polytetrafluoroethylene (PTFE), 5~10 parts of polyurethane resin, water-soluble polyester 10~20
Part, 2~5 parts of graphene, 1~3 part of polyvinylpyrrolidone, 20~35 parts of polypropylene-base carbon fiber, silicon fluoride 1~3 part, nanometer
It is 0.5~1 part of crystal fibre element, 1~2 part of citric acid, 2~4 parts of fire retardant, 1~2 part of coupling agent, 1~2 part of adhesive, antistatic
2~5 parts of agent, 2~5 parts of antiaging agent.
Further, the polyurethane resin selects modified polyurethane resin;The modified original of the modified polyurethane resin
The one or more that material is selected in nano silicon, nano aluminium oxide or nanometer silicon carbide.
Further, the fire retardant is one kind in brominated Polystyrene or diphenylphosphate.
Further, the coupling agent is fluorine containing silane coupling agent, and the fluorine containing silane coupling agent is emulsified by adding
Agent and catalyst the emulsion dispersion gained in water;The mass concentration of the fluorine containing silane coupling agent is 2~5ml/L, the emulsification
The mass concentration of agent is 0.5~1.5ml/L, and the mass concentration of the catalyst is 0.8~1.2g/L.
Further, the adhesive uses one in resistance to oxidation and acid proof Alumina gel, Ludox or silicon-aluminum sol
Kind is a variety of.
Further, the antistatic additive is to be etherified isohexyl alcohol, n-hexyl alcohol and glycerine, then is etherified with diethylene glycol (DEG), then
In the case where being passed through nitrogen, phosphorylation reaction is carried out with phosphorus pentoxide, then is hydrolyzed, in finally being carried out with sodium hydroxide
With and obtain.
Further, the antiaging agent is N- phenyl-N '-cyclohexyl p-phenylenediamine.
Compared with prior art, dust-removal cloth-bag provided by the present invention prepares material, including polyphenylene sulfide, polytetrafluoroethyl-ne
Alkene, polyurethane resin, water-soluble polyester, graphene, polyvinylpyrrolidone, polypropylene-base carbon fiber, silicon fluoride, nanocrystal
Cellulose, citric acid, fire retardant, coupling agent, adhesive, antistatic additive, antiaging agent;By each material component of scientific matching,
Under mutually being acted synergistically between each component, temperature tolerance, acid resistance, static electricity resistance and the anti-denaturation of dust-removal cloth-bag are improved, is made
It can be suitably used for complex environment, have a wide range of application;Meanwhile silicon fluoride and citric acid comprehensive function improve polytetrafluoroethylene (PTFE) table
The adhesive property in face, improves adsorption effect;Nanocrystal cellulose and adhesive further increase the absorption of dust-removal cloth-bag
Effect, improve the dust collection capacity of dust-removal cloth-bag;By adding coupling agent, dust-removal cloth-bag fiber and fiber at high temperature are improved
Between bonding it is weaker the problem of, improve the intensity of dust-removal cloth-bag.
Embodiment
The technical scheme in the present invention is clearly and completely described below, it is clear that described embodiment is only
Part of the embodiment of the present invention, rather than whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art
The every other embodiment obtained on the premise of creative work is not made, belongs to the scope of protection of the invention.
Embodiment 1
A kind of dust-removal cloth-bag prepares material, including 20 parts of polyphenylene sulfide, 20 parts of polytetrafluoroethylene (PTFE), 5 parts of polyurethane resin, water-soluble
10 parts of polyester of property, 5 parts of graphene, 1 part of polyvinylpyrrolidone, 20 parts of polypropylene-base carbon fiber, 3 parts of silicon fluoride, nanocrystal
0.5 part of cellulose, 2 parts of citric acid, 4 parts of fire retardant, 1 part of coupling agent, 1 part of adhesive, 2 parts of antistatic additive, 5 parts of antiaging agent.
Polyurethane resin selects modified polyurethane resin;The modified feedstock of modified polyurethane resin selects nano silicon
And nano aluminium oxide.
Fire retardant is brominated Polystyrene.
Coupling agent is fluorine containing silane coupling agent, and fluorine containing silane coupling agent is by adding emulsifying agent and catalyst emulsion dispersion
The gained in water;The mass concentration of fluorine containing silane coupling agent is 5ml/L, and the mass concentration of emulsifying agent is 0.5ml/L, catalyst
Mass concentration is 1.2g/L.
Adhesive uses resistance to oxidation and acid proof Alumina gel and silicon-aluminum sol.
Antistatic additive is to be etherified isohexyl alcohol, n-hexyl alcohol and glycerine, then is etherified with diethylene glycol (DEG), is then being passed through the feelings of nitrogen
Under condition, phosphorylation reaction is carried out with phosphorus pentoxide, then is hydrolyzed, is finally neutralized and is obtained with sodium hydroxide.
Antiaging agent is N- phenyl-N '-cyclohexyl p-phenylenediamine.
Embodiment 2
A kind of dust-removal cloth-bag prepares material, including 30 parts of polyphenylene sulfide, 10 parts of polytetrafluoroethylene (PTFE), 10 parts of polyurethane resin, water
It is 20 parts of dissolubility polyester, 2 parts of graphene, 3 parts of polyvinylpyrrolidone, 35 parts of polypropylene-base carbon fiber, 1 part of silicon fluoride, nanocrystalline
1 part of body cellulose, 1 part of citric acid, 2 parts of fire retardant, 2 parts of coupling agent, 2 parts of adhesive, 5 parts of antistatic additive, 2 parts of antiaging agent.
Polyurethane resin selects modified polyurethane resin;The modified feedstock of modified polyurethane resin selects nanometer silicon carbide.
Fire retardant is diphenylphosphate.
Coupling agent is fluorine containing silane coupling agent, and fluorine containing silane coupling agent is by adding emulsifying agent and catalyst emulsion dispersion
The gained in water;The mass concentration of fluorine containing silane coupling agent is 2ml/L, and the mass concentration of emulsifying agent is 1.5ml/L, catalyst
Mass concentration is 0.8g/L.
Adhesive uses resistance to oxidation and acid proof Alumina gel and Ludox.
Antistatic additive is to be etherified isohexyl alcohol, n-hexyl alcohol and glycerine, then is etherified with diethylene glycol (DEG), is then being passed through the feelings of nitrogen
Under condition, phosphorylation reaction is carried out with phosphorus pentoxide, then is hydrolyzed, is finally neutralized and is obtained with sodium hydroxide.
Antiaging agent is N- phenyl-N '-cyclohexyl p-phenylenediamine.
Above disclosed is only the embodiment of the present invention, but protection scope of the present invention is not limited thereto,
Any one skilled in the art the invention discloses technical scope in, can readily occur in change or modification, all
It should be included within the scope of the present invention.
Claims (7)
1. a kind of dust-removal cloth-bag prepares material, it is characterised in that:Including 20~30 parts of polyphenylene sulfide, polytetrafluoroethylene (PTFE) 10~20
Part, 5~10 parts of polyurethane resin, 10~20 parts of water-soluble polyester, 2~5 parts of graphene, 1~3 part of polyvinylpyrrolidone, gather
20~35 parts of propylene base carbon fibre, 1~3 part of silicon fluoride, 0.5~1 part of nanocrystal cellulose, 1~2 part of citric acid, fire retardant 2
~4 parts, 1~2 part of coupling agent, 1~2 part of adhesive, 2~5 parts of antistatic additive, 2~5 parts of antiaging agent.
2. dust-removal cloth-bag as claimed in claim 1 prepares material, it is characterised in that:The polyurethane resin is from modified poly-
Urethane resin;The modified feedstock of the modified polyurethane resin selects nano silicon, nano aluminium oxide or nanometer silicon carbide
In one or more.
3. dust-removal cloth-bag as claimed in claim 1 prepares material, it is characterised in that:The fire retardant is brominated Polystyrene
Or one kind in diphenylphosphate.
4. dust-removal cloth-bag as claimed in claim 1 prepares material, it is characterised in that:The coupling agent is coupled for fluorine containing silane
Agent, the fluorine containing silane coupling agent be as add emulsifying agent and catalyst emulsion dispersion in water obtained by;The fluorine containing silane
The mass concentration of coupling agent is 2~5ml/L, and the mass concentration of the emulsifying agent is 0.5~1.5ml/L, the matter of the catalyst
Amount concentration is 0.8~1.2g/L.
5. dust-removal cloth-bag as claimed in claim 1 prepares material, it is characterised in that:The adhesive is using resistance to oxidation and resistance to
One or more in acid Alumina gel, Ludox or silicon-aluminum sol.
6. dust-removal cloth-bag as claimed in claim 1 prepares material, it is characterised in that:The antistatic additive be by isohexyl alcohol,
N-hexyl alcohol is etherified with glycerine, then is etherified with diethylene glycol (DEG), and then in the case where being passed through nitrogen, phosphorylation is carried out with phosphorus pentoxide
Reaction, then be hydrolyzed, finally neutralized and obtained with sodium hydroxide.
7. dust-removal cloth-bag as claimed in claim 1 prepares material, it is characterised in that:The antiaging agent be N- phenyl-N '-
Cyclohexyl p-phenylenediamine.