CN107886930A - A kind of preparation method of the resistance to string that gets rusty - Google Patents
A kind of preparation method of the resistance to string that gets rusty Download PDFInfo
- Publication number
- CN107886930A CN107886930A CN201711367962.0A CN201711367962A CN107886930A CN 107886930 A CN107886930 A CN 107886930A CN 201711367962 A CN201711367962 A CN 201711367962A CN 107886930 A CN107886930 A CN 107886930A
- Authority
- CN
- China
- Prior art keywords
- string
- resistance
- gets rusty
- preparation
- stainless steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation method of the resistance to string that gets rusty, the resistance to string that gets rusty is by wire and parcel string crust, the wire is surface modified carbon stainless steel, the outer layer of the surface carbonation stainless steel applies one layer of anti-liquid covering of getting rusty again, the carbonization stainless steel is by metal carbon and manganese metal, and fusion forms metallic iron at high temperature jointly.The metal carbon accounts for wire mass percent 35 65%, and the manganese metal accounts for wire mass percent 55 75%, by the above-mentioned means, the present invention possesses high corrosion resistance, resistance to getting rusty property, can effectively improve the service life of string.
Description
Technical field
The present invention relates to a kind of musical instrument field, more particularly to a kind of preparation method of the resistance to string that gets rusty.
Background technology
With the sustainable and stable development of economy, the living standard of people gradually improves, and the life of most people is increasingly
Music is be unable to do without, either on market or bus, or in dining room, we can hear miscellaneous music,
All it is to be played out with miscellaneous string musical instrument come the tonequality that good string should have, fast, pitch of tuning up are stablized, are good
The good property played（Finger haves a sense of security, and string reaction is sharp）And the long life-span, generally use silk, sheep intestines, metal or
Long filament plastic optical fibre is made, and string is easily corroded and got rusty easily for a long time in a humidity environment, has a strong impact on making for string
Use the life-span.
The content of the invention
The present invention solves the technical problem of a kind of preparation method of the resistance to string that gets rusty is provided, preparation method is simple,
Possess higher tack, corrosion resistance, there is high resistance to feature of getting rusty.
In order to solve the above technical problems, one aspect of the present invention is：A kind of system of the resistance to string that gets rusty is provided
Preparation Method includes：For the resistance to string that gets rusty by wire and parcel string crust, the wire is that surface modified carbonization is stainless
Steel, the outer layer of the surface carbonation stainless steel apply one layer of anti-liquid covering of getting rusty again, the carbonization stainless steel be by metal carbon and
Manganese metal, fusion forms metallic iron at high temperature jointly.The metal carbon accounts for wire mass percent 35-65%, the metal
Manganese accounts for wire mass percent 55-75%；
The preparation method of the resistance to string that gets rusty comprises the following steps：
（1）, fusion：According to it is above-mentioned than row by carbon and manganese, iron be put into jointly in high temperature furnace carry out heat high temperature soldier fire after on surface
Handle the stainless steel that must be carbonized.
（2）, quenching：Quench heating, solution treatment, Er Qie are carried out by the carbonization stainless steel preheating after surface treatment again
During solution treatment, the soaking time of Quench heating will be grown.
（3）, cooling：Surface after being handled by Quench heating will use clear water cooling down, be cooled to lower temperature, enter
Row is drawn into wire.
（4）Bonding：String crust will be bonded by one layer of anti-liquid that gets rusty by adhesive, the resistance to string that gets rusty finally is made.
In a preferred embodiment of the present invention, the string crust is that have glass fibre parcel.
In a preferred embodiment of the present invention, the step（1）High temperature melting it is right be 950 DEG C.
In a preferred embodiment of the present invention, the step（2）Lower temperature be 320 DEG C.
In a preferred embodiment of the present invention, the step（4）The thickness of adhesive is 0.5-1.5mm.
In a preferred embodiment of the present invention, the antirust solution includes following mass percent composition：Sodium carbonate 8-
15%, antirust agent 12-22%, antioxidant 10-25%.
The beneficial effects of the invention are as follows：A kind of resistance to string preparation method got rusty of the present invention, technique is simple, easy to operate,
Easily realize, by reasonably matching, possess high corrosion resistance, resistance to getting rusty property, the service life of string can be effectively improved.
Embodiment
Presently preferred embodiments of the present invention is described in detail below so that advantages and features of the invention can be easier to by
It will be appreciated by those skilled in the art that apparent clearly defined so as to be made to protection scope of the present invention.
Embodiments of the invention include：
Embodiment 1
A kind of resistance to resistance to string that gets rusty described in the preparation method of string that gets rusty is by wire and wraps up string crust, and the wire is
Surface modified carbon stainless steel, the outer layer of the surface carbonation stainless steel apply one layer of anti-liquid covering of getting rusty again, and the carbonization is not
Rust steel is by metal carbon and manganese metal, and fusion forms metallic iron at high temperature jointly.The metal carbon accounts for metal yarn quality percentage
Than 35%, the manganese metal accounts for wire mass percent 75%；
The preparation method of the resistance to string that gets rusty comprises the following steps：
（1）, fusion：According to it is above-mentioned than row by carbon and manganese, iron be put into jointly in high temperature furnace carry out heat high temperature soldier fire after on surface
Handle the stainless steel that must be carbonized.
（2）, quenching：Quench heating, solution treatment, Er Qie are carried out by the carbonization stainless steel preheating after surface treatment again
During solution treatment, the soaking time of Quench heating will be grown.
（3）, cooling：Surface after being handled by Quench heating will use clear water cooling down, be cooled to lower temperature, enter
Row is drawn into wire.
（4）Bonding：String crust will be bonded by one layer of anti-liquid that gets rusty by adhesive, the resistance to string that gets rusty finally is made.
Wherein described string crust is that have glass fibre parcel, the step（1）High temperature melting it is right be 950 DEG C, it is described
Step（2）Lower temperature be 320 DEG C, the step（4）The thickness of adhesive is 0.5mm, and the antirust solution includes following matter
Measure percent composition：Sodium carbonate 8%, antirust agent 12%, antioxidant 10%, water 8%.
Embodiment 2,
A kind of resistance to resistance to string that gets rusty described in the preparation method of string that gets rusty is by wire and wraps up string crust, and the wire is
Surface modified carbon stainless steel, the outer layer of the surface carbonation stainless steel apply one layer of anti-liquid covering of getting rusty again, and the carbonization is not
Rust steel is by metal carbon and manganese metal, and fusion forms metallic iron at high temperature jointly.The metal carbon accounts for metal yarn quality percentage
Than 45%, the manganese metal accounts for wire mass percent 55%；
The preparation method of the resistance to string that gets rusty comprises the following steps：
（1）, fusion：According to it is above-mentioned than row by carbon and manganese, iron be put into jointly in high temperature furnace carry out heat high temperature soldier fire after on surface
Handle the stainless steel that must be carbonized.
（2）, quenching：Quench heating, solution treatment, Er Qie are carried out by the carbonization stainless steel preheating after surface treatment again
During solution treatment, the soaking time of Quench heating will be grown.
（3）, cooling：Surface after being handled by Quench heating will use clear water cooling down, be cooled to lower temperature, enter
Row is drawn into wire.
（4）Bonding：String crust will be bonded by one layer of anti-liquid that gets rusty by adhesive, the resistance to string that gets rusty finally is made.
Wherein described string crust is that have glass fibre parcel, the step（1）High temperature melting it is right be 950 DEG C, it is described
Step（2）Lower temperature be 320 DEG C, the step（4）The thickness of adhesive is 1.5mm, and the antirust solution includes following matter
Measure percent composition：Sodium carbonate 15%, antirust agent 22%, antioxidant 25%, water 8%.
Distinguish prior art：A kind of resistance to string preparation method got rusty, technique is simple, easy to operate, easily realizes, by reasonable
Proportioning, possess high corrosion resistance, resistance to getting rusty property, the service life of string can be effectively improved.
Embodiments of the invention are the foregoing is only, are not intended to limit the scope of the invention, it is every to utilize this hair
The equivalent structure or equivalent flow conversion that bright description is made, or directly or indirectly it is used in other related technology necks
Domain, it is included within the scope of the present invention.
Claims (5)
- A kind of 1. preparation method of the resistance to string that gets rusty, it is characterised in that including：The resistance to string that gets rusty is by wire and parcel qin String crust, the wire are surface modified carbon stainless steel, and the outer layer of the surface carbonation stainless steel applies one layer of anti-life again The liquid that becomes rusty covers, and the carbonization stainless steel is by metal carbon and manganese metal, and fusion forms metallic iron at high temperature jointly；The metal carbon accounts for wire mass percent 35-65%, and the manganese metal accounts for wire mass percent 55-75%；The preparation method of the resistance to string that gets rusty comprises the following steps：（1）, fusion：According to it is above-mentioned than row by carbon and manganese, iron be put into jointly in high temperature furnace carry out heat high temperature soldier fire after on surface Handle the stainless steel that must be carbonized；（2）, quenching：Quench heating, solution treatment are carried out by the carbonization stainless steel preheating after surface treatment again, and are being dissolved During processing, the soaking time of Quench heating will be grown；（3）, cooling：Surface after being handled by Quench heating will use clear water cooling down, be cooled to lower temperature, drawn Pull into wire；（4）Bonding：String crust will be bonded by one layer of anti-liquid that gets rusty by adhesive, the resistance to string that gets rusty finally is made；The preparation method of the resistance to string that gets rusty according to claim 1, it is characterised in that the string crust is that have glass fibers Dimension parcel.
- 2. the preparation method of the resistance to string that gets rusty according to claim 1, it is characterised in that the step（1）High temperature melting Right is 950 DEG C.
- 3. the preparation method of the resistance to string that gets rusty according to claim 1, it is characterised in that the step（2）Relatively low temperature Spend for 320 DEG C.
- 4. the preparation method of the resistance to string that gets rusty according to claim 1, it is characterised in that the step（4）Adhesive Thickness is 0.5-1.5mm.
- 5. the preparation method of the resistance to string that gets rusty according to claim 1, it is characterised in that the antirust solution includes following matter Measure percent composition：Sodium carbonate 8-15%, antirust agent 12-22%, antioxidant 10-25%, water 8%.