CN107881590A - A kind of environment-friendly type polyolefm chemistry fiber - Google Patents
A kind of environment-friendly type polyolefm chemistry fiber Download PDFInfo
- Publication number
- CN107881590A CN107881590A CN201711096390.7A CN201711096390A CN107881590A CN 107881590 A CN107881590 A CN 107881590A CN 201711096390 A CN201711096390 A CN 201711096390A CN 107881590 A CN107881590 A CN 107881590A
- Authority
- CN
- China
- Prior art keywords
- environment
- friendly type
- parts
- fiber
- polyolefm
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of environment-friendly type polyolefm chemistry fiber.Using crystalline state alpha olefin copolymer, polyvinyl resin or acrylic resin, olefin hydrocarbons thermoplasticity elastic body, Masterbatch, light absorber, hindered amine light stabilizer, polyolefin chemical fibre is made by certain step.The product can be used for production multifilament long filament, or the various chemical fibres such as chopped fiber, while have the good feature of environmental protection, uvioresistant, fire resistance, the harmful substance such as not chloride, and recovery is relatively easy to.
Description
Technical field
The present invention relates to chemical fibre material, specifically a kind of environment-friendly type polyolefm chemistry fiber.
Background technology
Conventional polyolefins class chemical fibre, such as：Polyethylene, polypropylene fibre chemical fibre etc., are widely used in all kinds of textile fabrics.But
Conventional polyolefins class chemical fibre generally existing synthetic fiber spinning is difficult, such as：The overwhelming majority is monofilament to polyethylene chemical fibre at present, multiple
Silk production is extremely difficult, or ageing-resistant performance is not strong, such as：All kinds of polypropylene fibre chemical fibres etc..Current existing sprunstron is resistance to old
Change poor-performing, although can be improved by adding age resister etc., room for improvement is little.Although polyethylene chemical fibre can be with
Reach higher weatherability, but have that spinning properties are poor, be only used for the thicker monofilament chemical fibre of production specification, such as：Circle silk
Or flat filament list drafting silk, it is not used to produce multifilament chemical fibre, can not be especially applied to fine dinier yarn chemical fibre.
The content of the invention
The present invention provides a kind of environment-friendly type polyolefm chemistry fiber, to solve current polyolefinic raw materials be difficult to make it is high resistance to
Wait multifilament the problem of, including simple polyethylene chemical fibre can not produce multifilament and sprunstron ageing resistace deficiency ask
Topic.
The weight proportion that this environment-friendly type polyolefm chemistry fiber of the present invention includes following raw materials forms：
Crystalline state alpha olefin copolymer：20~30 parts；
Polyvinyl resin or acrylic resin：40 parts；
Olefin hydrocarbons thermoplasticity elastic body：30~40 parts；
Masterbatch：3 parts；
Light absorber：0.5 part；
Hindered amine light stabilizer：0.5 part.
This environment-friendly type polyolefm chemistry fiber provided by the invention is to be based on opening on the basis of polyethylene+polyolefin copolymer
Send, available for production multifilament long filament, or various chemical fibres such as chopped fiber, while have the good feature of environmental protection, uvioresistant,
Fire resistance, the harmful substance such as not chloride, and also recovery is relatively easy to.
Embodiment
First take：25 parts of crystalline state alpha olefin copolymer, 40 parts of polyvinyl resin or 40 parts of acrylic resin, olefin type thermoplastic
35 parts of elastomer of property, 3 parts of Masterbatch, 0.5 part of light absorber, 0.5 part of hindered amine light stabilizer.
Then：Above-mentioned raw materials are mixed evenly, by screw extruder pelletizer, temperature control is in front-end temperature 190
DEG C, 195 DEG C of stage casing temperature, 190 DEG C of back segment temperature, if replacing polyvinyl resin using acrylic resin, more than each temperature
50 DEG C need to be accordingly improved, is uniformly cooled down after extrusion and is cut to uniform granular master batch, and weighed, pack.
Finally：Above-mentioned resulting materials are added into chemical fibre wire drawing machine hopper, hopper temperature is 195 DEG C~215 DEG C, melt material
Enter each section of screw extruder, 195 DEG C of extruder front-end temperature, 215 DEG C of stage casing temperature, 210 DEG C of back segment temperature afterwards, if used
Acrylic resin replaces polyvinyl resin, then each temperature need to accordingly improve 50 DEG C above, be produced after extruded wire drawing sizing winding
Chemical fibre, it is wound into a roll through tension force.
After tested, colorfastness to rubbing reaches fabric standard (AATCC 8-2007) to the product, and weather-proof test reaches fabric mark
Accurate (AATCC 186-2006), antisum color fastness reach fabric standard (IS0i05-B04：2004), coating bonding strength reaches
Fabric standard (AATCC 136-2009), flame retardant test reach plastic cement flammability standards UL94.
Claims (1)
1. a kind of environment-friendly type polyolefm chemistry fiber, it is characterised in that be made up of following raw materials according and weight proportion：
Crystalline state alpha olefin copolymer：20~30 parts；
Polyvinyl resin or acrylic resin：40 parts；
Olefin hydrocarbons thermoplasticity elastic body：30~40 parts；
Masterbatch：3 parts；
Light absorber：0.5 part；
Hindered amine light stabilizer：0.5 part.